CN112810254A - 一种轻质环保pet复合板材及其制造方法 - Google Patents
一种轻质环保pet复合板材及其制造方法 Download PDFInfo
- Publication number
- CN112810254A CN112810254A CN202110025007.9A CN202110025007A CN112810254A CN 112810254 A CN112810254 A CN 112810254A CN 202110025007 A CN202110025007 A CN 202110025007A CN 112810254 A CN112810254 A CN 112810254A
- Authority
- CN
- China
- Prior art keywords
- pet
- panel
- board
- plate
- bottom plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种轻质环保PET复合板材，包括面板、芯材和底板，所述芯材为PET结构泡沫板，PET结构泡沫板通过表面热熔与面板及底板直接粘接。其制造方法，包括：芯材加热熔融，面板、底板预热，加压贴合，冷却等步骤。通过将PET泡沫表面熔融的方式将面板、底板粘接，避免了胶水的使用，满足人们对于环保、健康的要求。同时，加工程序简单，快捷，生产过程无需使用胶水等粘合材料，对生产工人的健康及环境也不会产生不良影响。
Description
技术领域
本发明涉及一种板材，具体为一种轻质环保PET复合板材及其制造方法。
背景技术
目前，最常见的家居、装饰装修材料有密度板、颗粒板及实木板，实木板优点在于使用天然木材，外观更自然，而且结实耐用，但一般价格较高且不可再生；密度板，是以木质纤维或其他植物纤维为原料，经打碎、纤维分离、干燥后施加脲醛树脂或其他适用的胶粘剂，再经热压后制成的一种人造板材，价格相对较低，但承重力小，粉末结构，破坏木质结构，横向受力，容易变形；颗粒板又称为刨花板，不同于密度板以木质纤维、植物纤维为原料，而是以原木颗粒(小径材、间伐材、木芯、板皮、枝桠材等)为原料，打碎后施胶粘剂经高温高压加工而成，原理同密度板一样，也是一种人造板材，且一般密度板及颗粒板都需要大量的胶水才能粘合，存在环保性差的问题。在用作室内家居、装饰装修原料时，难以满足人们日益提高的环保健康需求。即使实木板材往往表面也有油漆，也难以完全避免苯、甲醛等有害物质。
目前的外墙装饰板一般由聚酯烤漆或氟碳漆、雕花铝锌合金钢板、聚氨酯保温层、玻璃纤维布(铝塑、铝蜂窝)复合而成，主要应用于体育馆、图书馆、学校和医院的办公楼、别墅等各种建筑的外墙装饰和节能改造，主要功能为建筑装饰、保温节能、隔热隔音，但是这种装饰板一般使用寿命较短，耐久性较差，面层与聚氨酯保温层通常通过胶水粘接，长时间使用会产生脱落。
发明内容
本发明的目的在于提供一种新的板材，以达到轻质高强、可回收再生利用、环保无毒的要求。
为实现上述目的，本发明提供如下技术方案：一种轻质环保PET复合板材，包括面板、芯材和底板，所述芯材为PET结构泡沫板，PET结构泡沫板通过表面热熔与面板及底板直接粘接。
进一步的，所述PET结构泡沫板挤出方向与所述面板、底板相垂直。
进一步的，所述所述芯材厚度为5-60mm。
进一步的，所述面板和底板为防火贴面板或金属板。
进一步的，所述面板和底板厚0.2-5.0mm。
一种PET复合板材制造方法，包括以下步骤：
芯材加热熔融，将PET泡沫板表面加热到230-380℃，加热10-30秒，使其表面熔融；
面板、底板预热，将面板及底板预热至50-100℃；
加压贴合，将面板、底板贴合至表面熔融的PET泡沫板上，对贴合的板材施加压力0.2-0.8MPa，持续10-30秒；
冷却，将板材进行冷却降温；
裁切，将板材裁切成需要的尺寸。
与现有技术相比，本发明的有益效果如下：PET结构泡沫板为发泡挤出型材，质量轻，具有较好的力学性能，因此本板材能够满足一般家居或装饰的需求；加工时产生的废料容易回收再利用；同时，通过将PET泡沫表面熔融的方式将面板、底板粘接，避免了胶水的使用，PET结构泡沫性质稳定，面板及底板选取无醛材料如防火贴面板或金属板，可完全消除甲醛等污染物，满足人们对于环保、健康的要求。
同时金属-PET结构泡沫复合板可用作外墙保温装饰板、公共场所地板，PET结构泡沫层会起到隔音、保温隔热的作用，而且无胶水粘接，耐老化，长时间使用面层不会脱落安全性能高。
附图说明
图1为本发明的结构示意图。
图中：1、面板；2、芯材；3、底板。
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
在本发明的描述中，需要说明的是，术语“上”、“下”、“内”、“外”“前端”、“后端”、“两端”、“一端”、“另一端”等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。此外，术语“第一”、“第二”仅用于描述目的，而不能理解为指示或暗示相对重要性。
在本发明的描述中，需要说明的是，除非另有明确的规定和限定，术语“安装”、“设置有”、“连接”等，应做广义理解，例如“连接”，可以是固定连接，也可以是可拆卸连接，或一体地连接；可以是机械连接，也可以是电连接；可以是直接相连，也可以通过中间媒介间接相连，可以是两个元件内部的连通。对于本领域的普通技术人员而言，可以具体情况理解上述术语在本发明中的具体含义。
如图1所示：一种PET轻质保温复合板材，包括面板、芯材和底板，所述芯材为PET结构泡沫板，PET泡沫板通过表面热熔与面板及底板直接粘接。
通过将PET泡沫表面熔融的方式将面板、底板粘接，避免了胶水的使用，PET结构泡沫性质稳定，面板及底板选取无醛材料防火贴面板或金属板，可完全消除甲醛等污染物，满足人们对于环保、健康的要求。
如果用作外墙装饰板、地板，PET结构泡沫层会起到隔音、保温隔热的效果，而且无胶水粘接，耐老化，长时间使用面层不会脱落安全性能高。
为得到上述板材，可采用以下步骤：
芯材加热熔融，将PET结构泡沫板表面加热到230-380℃，加热10-30秒，使其表面熔融；
面板、底板预热，将面板及底板预热至50-100℃；
加压贴合，将面板、底板贴合至表面熔融的PET泡沫板上，对贴合的板材施加压力0.2-0.8MPa，持续10-30秒；
冷却，将板材进行冷却降温；
裁切，将板材裁切成需要的尺寸。
加工程序简单，快捷，生产过程无需使用胶水等粘合材料，对生产工人的健康及环境也不会产生不良影响。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。不应将权利要求中的任何附图标记视为限制所涉及的权利要求。
Claims (6)
1.一种轻质环保PET复合板材，包括面板、芯材和底板，其特征在于：所述芯材为PET结构泡沫板，PET结构泡沫板通过表面热熔与面板及底板直接粘接。
2.根据权利要求1所述的PET复合板材，其特征在于：所述PET结构泡沫板挤出方向与所述面板、底板相垂直。
3.根据权利要求1所述的PET复合板材，其特征在于：所述所述芯材厚度为5-60mm。
4.根据权利要求1所述的PET复合板材，其特征在于：所述面板和底板为防火贴面板或金属板。
5.根据权利要求1所述的PET复合板材，其特征在于：所述面板和底板厚0.2-5.0mm。
6.一种PET复合板材制造方法，其特征在于：包括以下步骤：
芯材加热熔融，将PET结构泡沫板表面加热到230-380℃，加热10-30秒，使其表面熔融；
面板、底板预热，将面板、底板预热至50-100℃；
加压贴合，将面板、底板贴合至表面熔融的PET结构泡沫板上，对贴合的板材施加压力0.2-0.8MPa，持续10-30秒；
冷却，将板材进行冷却降温；
裁切，将板材裁切成需要的尺寸。