CN112774653A - Formaldehyde adsorption-catalytic decomposition composite material, preparation method and application - Google Patents
Formaldehyde adsorption-catalytic decomposition composite material, preparation method and application Download PDFInfo
- Publication number
- CN112774653A CN112774653A CN201911085558.3A CN201911085558A CN112774653A CN 112774653 A CN112774653 A CN 112774653A CN 201911085558 A CN201911085558 A CN 201911085558A CN 112774653 A CN112774653 A CN 112774653A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- composite material
- catalytic decomposition
- adsorption
- voc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a formaldehyde adsorption-catalytic decomposition composite material, a preparation method and application. The formaldehyde adsorption-catalytic decomposition composite material is mainly composed of particles with a core-shell structure, wherein: the core of the core-shell structure mainly comprises a VOC physical adsorbent; the shell of the core-shell structure is mainly composed of formaldehyde decomposition catalyst. The formaldehyde adsorption-catalytic decomposition composite material has a core-shell structure, so that the composite material has physical adsorption and chemical catalytic decomposition functions; the VOC physical adsorbent is used as a matrix to load the formaldehyde decomposition catalyst, so that the dispersity of the formaldehyde decomposition catalyst can be improved, and the catalytic efficiency is improved; the VOC physical adsorbent positioned in the core part can adsorb substances which cause poisoning of the formaldehyde decomposition catalyst, so that the service life of the formaldehyde decomposition catalyst is prolonged; the retention time of the formaldehyde is prolonged after the VOC physical adsorbent is adsorbed, so that the formaldehyde decomposition catalyst has enough time to catalytically decompose the formaldehyde.
Description
Technical Field
The invention relates to the technical field of formaldehyde purification, in particular to a formaldehyde adsorption-catalytic decomposition composite material, a preparation method and application.
Background
The pollutants in the air are mainly divided into solid pollutants and gaseous pollutants. For solid pollutant (such as PM10, PM2.5) pollution in air, the solid pollutant is generally removed by physical filtration (namely, the separation of a specific object is realized by a physical mode); gaseous contaminants such as VOCs, i.e., organic gaseous substances, in the air are generally removed by chemical filtration, i.e., separation of particular objects is achieved by using the chemical properties of the substances.
Formaldehyde is a substance which is harmful to human bodies and is contained in gaseous pollutants. In the removal of formaldehyde by chemical filtration, the use of manganese dioxide as a formaldehyde purification material in metal oxides has been considered a viable and in some respects advantageous way. Currently, the manganese dioxide used as formaldehyde purifying material is limited to nano-scale manganese dioxide, so that the specific surface area of the manganese dioxide is enough to reach the acceptable formaldehyde removing rate in use. However, the nano-sized manganese dioxide has large specific surface area and high surface energy, is easy to agglomerate to reduce the catalytic efficiency, is easily absorbed by human bodies to harm the health of the human bodies once being improperly placed or improperly used, and is easily inactivated due to the catalyst poisoning phenomenon.
Disclosure of Invention
Based on the above background art, the following inventions have been completed in the process of developing a novel air purification solution.
On the one hand, the first group of completed inventions comprises a formaldehyde adsorption-catalytic decomposition composite material, a preparation method of the formaldehyde adsorption-catalytic decomposition composite material, a formaldehyde purification porous film and a preparation method of the formaldehyde purification porous film, so as to solve the technical problems of short service life, low catalytic efficiency and inconvenient use of the formaldehyde purification material.
On the one hand, the second group of completed inventions comprises a formaldehyde purification porous film and a preparation method of the formaldehyde purification porous film, so as to solve the technical problems of short service life, low catalytic efficiency and inconvenient use of the formaldehyde purification material.
On one hand, the third group of completed inventions comprises a formaldehyde purification material preparation, a preparation method of the formaldehyde purification material preparation and a formaldehyde decomposition catalysis component, so as to solve the technical problem of inconvenient use of the formaldehyde purification material.
On one hand, the completed fourth invention comprises a formaldehyde purification material preparation, a preparation method of the formaldehyde purification material preparation and a formaldehyde decomposition catalysis component, so as to solve the technical problem of inconvenient use of the formaldehyde purification material.
The technical schemes of the formaldehyde adsorption-catalytic decomposition composite material, the preparation method of the formaldehyde adsorption-catalytic decomposition composite material, the formaldehyde purification porous film and the preparation method of the formaldehyde purification porous film in the first group of inventions are as follows:
the formaldehyde adsorption-catalytic decomposition composite material is mainly composed of particles with a core-shell structure, wherein: the core of the core-shell structure mainly comprises a VOC physical adsorbent; the shell of the core-shell structure is mainly composed of formaldehyde decomposition catalyst.
Further, the formaldehyde decomposition catalyst consists of MnO dispersed on the surface of the VOC physical adsorbent particles and mainly in delta crystal form2Submicron-micron flower spherical particles formed by the nano sheets.
Furthermore, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.1 and 5 microns; preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.3 and 5 microns; further preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 5 microns; even more preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 3 mu m.
Further, the VOC physical adsorbent is any of activated carbon, diatomite, silica gel, a molecular sieve and activated alumina; wherein the granularity of the activated carbon is preferably 100-400 meshes.
Further, the formaldehyde decomposition catalyst is generated in situ from a reaction liquid attached to the surface of the VOC physical adsorbent particles.
The preparation method of the formaldehyde adsorption-catalytic decomposition composite material comprises the following steps: dispersing the VOC physical adsorbent into reaction liquid, and enabling the reaction liquid to generate a formaldehyde decomposition catalyst on the surface of the VOC physical adsorbent particles in situ to obtain the formaldehyde adsorption-catalytic decomposition composite material.
Further, the reaction liquid is composed of potassium permanganate, manganese sulfate and water, and the preparation method specifically comprises the following steps:
A. placing a potassium permanganate solution in a first burette, placing a manganese sulfate solution in a second burette, wherein the mass ratio of potassium permanganate in the first burette to manganese sulfate in the second burette is (1-1.34) to 1, the concentration of the potassium permanganate solution in the first burette is 60-110 g/L, and the reference volume is not less than 50L if the volume of the potassium permanganate solution in the first burette or the volume of the manganese sulfate solution in the second burette is set as the reference volume;
B. adding a VOC physical adsorbent and bottom water with the volume more than 2 times of the reference volume into a mixing reactor;
C. respectively dropwise adding the potassium permanganate solution in the first titration tube and the manganese sulfate solution in the second titration tube into the bottom water in the mixing reactor, ensuring that the potassium permanganate solution in the first titration tube and the manganese sulfate solution in the second titration tube are completely dropwise added within 10-45 min, and fully stirring the mixed solution at 70-90 ℃ until the reaction is finished;
D. and (3) carrying out solid-liquid separation on the mixed solution after the reaction is finished to obtain the formaldehyde adsorption-catalytic decomposition composite material.
Further, the VOC physical adsorbent is activated carbon, the granularity of the activated carbon is 100-400 meshes, and the mass of the activated carbon is 5% -50% of that of potassium permanganate in the first titration tube.
Further, the volume ratio of the potassium permanganate solution in the first burette to the manganese sulfate solution in the second burette is 1: 1.
A formaldehyde-purifying porous membrane comprising an air-permeable support and a formaldehyde-purifying material attached to the air-permeable support, the formaldehyde-purifying material being: 1) the formaldehyde adsorption-catalytic decomposition composite material; or 2) the formaldehyde adsorption-catalytic decomposition composite material obtained by the preparation method.
The preparation method of the formaldehyde purification porous film comprises the following steps: providing a breathable support; providing feed liquid containing formaldehyde purification material;
extruding and dispersing the feed liquid on a breathable support, and drying the feed liquid to obtain the formaldehyde purification porous film; wherein, the formaldehyde purification material is: 1) the formaldehyde adsorption-catalytic decomposition composite material; or 2) the formaldehyde adsorption-catalytic decomposition composite material obtained by the preparation method.
In the invention and creation, the formaldehyde adsorption-catalytic decomposition composite material has a core-shell structure, so that the formaldehyde adsorption-catalytic decomposition composite material has physical adsorption and chemical catalytic decomposition functions; the VOC physical adsorbent is used as a matrix to load the formaldehyde decomposition catalyst, so that the dispersity of the formaldehyde decomposition catalyst can be improved, and the catalytic efficiency is improved; the VOC physical adsorbent positioned in the core part can adsorb substances which cause poisoning of the formaldehyde decomposition catalyst, so that the service life of the formaldehyde decomposition catalyst is prolonged; the retention time of the formaldehyde is prolonged after the VOC physical adsorbent is adsorbed, so that the formaldehyde decomposition catalyst has enough time to catalytically decompose the formaldehyde. The preparation method of the formaldehyde adsorption-catalytic decomposition composite material adopts a mode of generating the formaldehyde decomposition catalyst on the surface of the VOC physical adsorbent in situ, has simple process and low cost, can be generated in large scale, and has stronger binding force between the VOC physical adsorbent and the formaldehyde decomposition catalyst in the core-shell structure. The formaldehyde adsorption-catalytic decomposition composite material is extruded and dispersed in the pores among the materials forming the air-permeable support, so that the technical problem that the formaldehyde adsorption-catalytic decomposition composite material is difficult to uniformly distribute on the air-permeable support is well solved, and the formaldehyde removal effect of the formaldehyde adsorption-catalytic decomposition composite material is further improved.
The second group of invention creates the following technical scheme of the formaldehyde purification porous film and the preparation method of the formaldehyde purification porous film:
the formaldehyde purification porous membrane comprises a breathable support and a formaldehyde purification material attached to the breathable support, and is characterized in that: the formaldehyde purification material comprises a VOC physical adsorbent and a formaldehyde decomposition catalyst, wherein the formaldehyde decomposition catalyst mainly comprises MnO in a delta crystal form2Submicron-micron flower spherical particles formed by the nano sheets.
Furthermore, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.1 and 5 microns; preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.3 and 5 microns; further preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 5 microns; even more preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 3 mu m.
Further, the VOC physical adsorbent is any of activated carbon, diatomite, silica gel, a molecular sieve and activated alumina; wherein the granularity of the activated carbon is preferably 100-400 meshes.
Further, the mass ratio of the VOC physical adsorbent to the formaldehyde decomposition catalyst is (0.6-4): 1.
Further, the formaldehyde purification material is distributed on the outer side of the material for forming the air-permeable support and is mainly filled in the pores between the materials for forming the air-permeable support.
Further, the formaldehyde purifying material also comprises a bonding agent distributed on the formaldehyde purifying material; the adhesive is preferably, but not limited to, an acrylic adhesive or a polyurethane adhesive.
Furthermore, if the weight of the formaldehyde purification material is divided by the area of the windward side of the breathable support, the formaldehyde purification material is used for purifying formaldehydeThe relative adhesion amount of the formaldehyde purification material on the air-permeable support is 40g/m2The above; preferably, the relative adhesion amount is 40-120 g/m2(ii) a More preferably, the relative adhesion amount is 50-70 g/m2。
Further, the breathable support adopts PP fiber felt or PET fiber felt; or the breathable support adopts a foam-shaped porous support body or a support net; when the breathable support adopts a support net, the support net can be any one of a woven net, a punched net and a diagonal net.
The preparation method of the formaldehyde purification porous film comprises the following steps: providing a breathable support; providing feed liquid containing formaldehyde purification material; extruding and dispersing the feed liquid on a breathable support, and drying the feed liquid to obtain the formaldehyde purification porous film; wherein the formaldehyde purification material comprises a VOC physical adsorbent and a formaldehyde decomposition catalyst, and the formaldehyde decomposition catalyst mainly comprises MnO in delta crystal form2Submicron-micron flower spherical particles formed by the nano sheets.
Further, the feed liquid is attached to the air-permeable support through a pulp drawing process, and the extrusion dispersion process exists in the pulp drawing process.
In the invention and creation, the formaldehyde purification material is extruded and dispersed in the pores among the materials forming the breathable support, so that the technical problem that the formaldehyde purification material is difficult to uniformly distribute on the breathable support is well solved, and the formaldehyde removal effect of the formaldehyde purification material is further improved. The formaldehyde purification material comprises a VOC physical adsorbent and a formaldehyde decomposition catalyst, so that the obtained formaldehyde purification porous film has the functions of physical adsorption and chemical catalytic decomposition of formaldehyde. The VOC physical adsorbent can adsorb substances which cause poisoning of the formaldehyde decomposition catalyst, and the service life of the formaldehyde decomposition catalyst is prolonged. Compared with nano manganese dioxide, the manganese dioxide mainly consists of MnO with delta crystal form2The formaldehyde decomposition catalyst formed by submicron-micron flower-shaped spherical particles formed by the nanosheets has ideal formaldehyde removal rate, is not easy to agglomerate and is easy for secondary processing.
The third group of the invention creates the following technical schemes of the formaldehyde purification material preparation, the preparation method of the formaldehyde purification material preparation and the formaldehyde decomposition catalysis component:
a formulation of formaldehyde-purifying material, the formulation being in the form of particles, each particle being comprised of a formaldehyde-purifying material and a binder, the formaldehyde-purifying material comprising a formaldehyde-decomposing catalyst consisting essentially of MnO of the delta crystalline form2Submicron-micron flower spherical particles formed by the nano sheets.
Further, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.1 and 5 microns; preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.3 and 5 microns; further preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 5 microns; even more preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 3 mu m.
Further, the particles are cylindrical, the length of the particles is 1-20 mm, and the diameter of the particles is 0.18-8 mm.
Further, the adhesive is any of acrylic acid, polyurethane, molasses and starch.
Furthermore, the mass ratio of the formaldehyde purification material to the adhesive is 1 (0.3-1.0).
Further, the formaldehyde purification material is a formaldehyde adsorption-catalytic decomposition composite material, and the formaldehyde adsorption-catalytic decomposition composite material is mainly composed of particles with a core-shell structure, wherein the core of the core-shell structure is mainly composed of a VOC physical adsorbent, and the shell of the core-shell structure is mainly composed of a formaldehyde decomposition catalyst.
Further, the VOC physical adsorbent is any of activated carbon, diatomite, silica gel, a molecular sieve and activated alumina; wherein the granularity of the activated carbon is preferably 100-400 meshes.
The preparation method of the formaldehyde purification material preparation comprises the following steps: (1) preparing a paste precursor from a formaldehyde purification material and an adhesive; (2) granulating the pasty precursor to obtain the nailAn aldehyde purification material formulation. The formaldehyde purification material comprises a formaldehyde decomposition catalyst, and the formaldehyde decomposition catalyst mainly comprises MnO in a delta crystal form2Submicron-micron flower spherical particles formed by the nano sheets.
Further, the granulating process is to extrude the paste precursor through meshes of a porous net in a swing granulator to obtain a formaldehyde purification material preparation; or the granulating process is to extrude the paste precursor into strips and cut the strips to obtain the formaldehyde purification material preparation.
The formaldehyde decomposition catalysis component is provided with an air inlet plate, an air outlet plate and a cavity positioned between the air inlet plate and the air outlet plate, vent holes are formed in the air inlet plate and the air outlet plate, and the formaldehyde purification material preparation or the formaldehyde purification material preparation prepared by the preparation method is filled in the cavity.
Further, a honeycomb-shaped partition plate is placed in the cavity, and the formaldehyde purification material preparation is placed in each groove of the partition plate.
Further, a filtering component is arranged in the air inlet direction of the formaldehyde decomposition catalytic component.
Compared with the formaldehyde purifying materials in the first and second inventions, the formaldehyde purifying material preparation in the invention can be directly used without a carrier. The formaldehyde decomposition catalysis component can be used independently, and can also be put into the air treatment equipment such as the existing air filter, air conditioner and the like which are matched with the formaldehyde decomposition catalysis component for use, so that the air is cleaned to the maximum extent.
The formaldehyde purification material preparation, the preparation method of the formaldehyde purification material preparation and the technical scheme of the formaldehyde decomposition catalytic assembly in the fourth invention creation are as follows:
a formulation of formaldehyde-purifying material, the formulation being in the form of particles, each particle being comprised of a formaldehyde-purifying material and a binder, the formaldehyde-purifying material comprising a VOC physical adsorbent and a formaldehyde-decomposing catalyst, the formaldehyde-decomposing catalyst consisting essentially of MnO of the delta crystalline form2Submicron-micron flower spherical particles formed by the nano sheets.
Further, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.1 and 5 microns; preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.3 and 5 microns; further preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 5 microns; even more preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 3 mu m.
Further, the particles are cylindrical, the length of the particles is 1-20 mm, and the diameter of the particles is 0.18-8 mm.
Further, the adhesive is any of acrylic acid, polyurethane, molasses and starch.
Furthermore, the mass ratio of the formaldehyde purification material to the adhesive is 1 (0.3-1.0).
Further, the VOC physical adsorbent is any of activated carbon, diatomite, silica gel, a molecular sieve and activated alumina; wherein the granularity of the activated carbon is preferably 100-400 meshes.
Further, the mass ratio of the VOC physical adsorbent to the formaldehyde decomposition catalyst is (0.6-4): 1.
The preparation method of the formaldehyde purification material preparation comprises the following steps: (1) preparing a paste precursor from a formaldehyde purification material and an adhesive; (2) and granulating the paste precursor to obtain the formaldehyde purification material preparation. The formaldehyde purification material comprises a VOC physical adsorbent and a formaldehyde decomposition catalyst, wherein the formaldehyde decomposition catalyst mainly comprises MnO in a delta crystal form2Submicron-micron flower spherical particles formed by the nano sheets.
Further, the granulating process is to extrude the paste precursor through meshes of a porous net in a swing granulator to obtain a formaldehyde purification material preparation; or the granulating process is to extrude the paste precursor into strips and cut the strips to obtain the formaldehyde purification material preparation.
The formaldehyde decomposition catalysis component is provided with an air inlet plate, an air outlet plate and a cavity positioned between the air inlet plate and the air outlet plate, vent holes are formed in the air inlet plate and the air outlet plate, and the formaldehyde purification material preparation or the formaldehyde purification material preparation prepared by the preparation method is filled in the cavity.
Further, a honeycomb-shaped partition plate is placed in the cavity, and the formaldehyde purification material preparation is placed in each groove of the partition plate.
Furthermore, a filtering component is arranged in the air inlet direction of the formaldehyde decomposition catalytic component.
Compared with the formaldehyde purifying materials in the first and second inventions, the formaldehyde purifying material preparation in the invention can be directly used without a carrier. And the formaldehyde purification material preparation has the functions of physical adsorption and chemical catalytic decomposition. The formaldehyde decomposition catalysis component can be used independently, and can also be put into the air treatment equipment such as the existing air filter, air conditioner and the like which are matched with the formaldehyde decomposition catalysis component for use, so that the air is cleaned to the maximum extent.
The term "submicron-micron petal-shaped particles" as used herein refers to a combination of submicron petal-shaped particles having a diameter of 0.1-1 μm and micron petal-shaped particles having a diameter of 1-10 μm. Generally, the diameter distribution range of the submicron-micron petal-shaped particles is more than or equal to 0.5 μm. I.e. the diameter of the largest micron-sized petal-shaped particle of these submicron-micron-sized petal-shaped particles is at least 0.5 μm larger than the diameter of the smallest submicron-sized petal-shaped particle.
The invention is further described with reference to the following figures and detailed description. Additional aspects and advantages of the invention will be set forth in part in the description which follows and, in part, will be obvious from the description, or may be learned by practice of the invention.
Drawings
The accompanying drawings, which are incorporated in and constitute a part of this specification, are included to assist in understanding the invention, and are included to explain the invention and their equivalents and not limit it unduly. In the drawings:
FIG. 1 is a scanning electron micrograph of a formaldehyde decomposition catalyst of example A1, and FIGS. 1 (a) to (d) are photographs showing selected fields of view on a slide glass which are not apt to be observed at microscopic level, respectively.
FIG. 2 is an X-ray diffraction (XRD) pattern of the formaldehyde decomposition catalyst of example A1.
FIG. 3 is a scanning electron micrograph of the formaldehyde decomposition catalyst of example A5, and FIGS. 3 (a) to (d) are photographs showing selected fields of view on a slide glass showing no tendency at microscopic observation, respectively.
FIG. 4 is a scanning electron micrograph of the formaldehyde decomposition catalyst of example A6, and FIGS. (a) to (b) in FIG. 4 are photographs showing the selected field of view on a slide glass showing no tendency at microscopic observation, respectively.
FIG. 5 is a graph of formaldehyde concentration over time in the experimental chamber from formaldehyde removal performance tests conducted on the formaldehyde decomposition catalyst of example A1.
FIG. 6 is a graph of formaldehyde concentration over time in the experimental chamber from formaldehyde removal performance tests conducted on the formaldehyde decomposition catalyst of example A5.
FIG. 7 is a graph of formaldehyde concentration over time in the experimental chamber from formaldehyde removal performance tests conducted on the formaldehyde decomposition catalyst of example A6.
FIG. 8 is a scanning electron micrograph of the activated carbon of example B3.
FIG. 9 is a scanning electron micrograph of a formaldehyde adsorbing-catalytic decomposing composite of example B3.
FIG. 10 is a graph showing the comprehensive properties of the porous formaldehyde-purifying films of examples C1-C5.
FIG. 11 is a graph showing the distribution uniformity of the formaldehyde scavenger materials in the porous films for formaldehyde scavenger of examples C2 and C6.
FIG. 12 SEM image of a formaldehyde-purified porous film of example C2.
FIG. 13 is a schematic structural view of a formaldehyde decomposition catalyst assembly.
Detailed Description
The invention will be described more fully hereinafter with reference to the accompanying drawings. Those skilled in the art will be able to implement the invention based on these teachings. Before the present invention is described in detail with reference to the accompanying drawings, it is to be noted that:
the technical solutions and features provided in the present invention in the respective sections including the following description may be combined with each other without conflict.
Moreover, the embodiments of the present invention described in the following description are generally only some embodiments of the present invention, and not all embodiments. Therefore, all other embodiments obtained by a person of ordinary skill in the art based on the embodiments of the present invention without any creative effort shall fall within the protection scope of the present invention.
With respect to terms and units in the present invention. The terms "comprising," "having," and any variations thereof in the description and claims of this invention and the related sections are intended to cover non-exclusive inclusions.
The method for preparing the formaldehyde decomposition catalyst by taking potassium permanganate, manganese sulfate and water as raw materials through mixed reaction comprises the following steps:
A. placing a potassium permanganate solution into a first burette, placing a manganese sulfate solution into a second burette, wherein the quantity ratio of substances between potassium permanganate in the first burette and manganese sulfate in the second burette (the quantity ratio of the substances is abbreviated in table 1) is (1-1.34): 1, the concentration of the potassium permanganate solution in the first burette is 60-110 g/L, if the volume of the potassium permanganate solution in the first burette or the volume of the manganese sulfate solution in the second burette is set as a reference volume, the reference volume is not less than 50L, the volume ratio of the solutions in the first burette and the second burette is 1:1, and the concentration of the manganese sulfate solution in the second burette is calculated according to the values;
B. adding bottom water with the volume more than 2 times of the reference volume into the mixing reactor;
C. respectively dripping the potassium permanganate solution in the first titration tube and the manganese sulfate solution in the second titration tube into bottom water in the mixing reactor, ensuring that the potassium permanganate solution in the first titration tube and the manganese sulfate solution in the second titration tube are completely dripped within 10-45 min (corresponding to the titration time in the table 1), and fully stirring the mixed solution at 80 ℃ for 2 hours to complete the reaction;
D. and (3) carrying out solid-liquid separation on the mixed liquid after the reaction is finished, and then cleaning, drying and dispersing the solid to obtain the formaldehyde decomposition catalyst.
Examples A1-A5 are examples of formaldehyde decomposition catalysts prepared by the above method, with specific parameters as shown in Table 1.
TABLE 1
Numbering | Ratio of amounts of substances | Concentration of potassium permanganate solution | Reference volume | Volume of bottom water | Titration time |
A1 | 1.34:1 | 95g/L | 50L | 100L | 10min |
A2 | 1:1 | 60g/L | 50L | 100L | 10min |
A3 | 1.1:1 | 90g/L | 50L | 100L | 10min |
A4 | 1.34:1 | 110g/L | 100L | 200L | 18min |
A5 | 1.34:1 | 95g/L | 300L | 600L | 35min |
FIG. 1 is a scanning electron micrograph of a formaldehyde decomposition catalyst of example A1, and FIGS. 1 (a) to (d) are photographs showing selected fields of view on a slide glass which are not apt to be observed at microscopic level, respectively. Fig. 2 is an X-ray diffraction (XRD) pattern of the formaldehyde decomposition catalyst shown in fig. 1.
As shown in fig. 1, the formaldehyde decomposition catalyst of example a1 consisted primarily of submicron-micron petal shaped particles. Wherein, the diameter (i.e. the particle diameter) of the micron-scale petal-shaped particles is mainly distributed between 1 and 3 mu m, and the diameter of the submicron-scale petal-shaped particles is mainly distributed between 0.1 and 1 mu m. Further observation shows that the submicron-micron petal-shaped particles are often in an agglomerated state, and because the diameters of the particles are not uniformly distributed, a large number of submicron-micron petal-shaped particles are irregularly distributed around the micron petal-shaped particles, so that the specific surface area of the agglomerated submicron-micron petal-shaped particles is increased.
In combination with a delta crystalline MnO as shown in FIG. 22(JCPDS 80-1089) standard diffraction peaks of (001), (002) and (111) crystal planes, and as can be confirmed by the literature "controllable preparation conditions of manganese dioxide of different crystal forms research, Wanggang, etc., inorganic salt industry, 8.2017" that the submicron-micron petal-shaped particles of the formaldehyde decomposition catalyst of example A1 are MnO of delta crystal form2。
It was confirmed by scanning electron microscopy that the formaldehyde decomposition catalysts of examples a2 and A3 also met the same characteristics consisting essentially of submicron-micron petal-shaped particles having a specific diameter distribution similar to that of the formaldehyde decomposition catalyst of example a 1. MnO with submicron-micron petal-shaped particles of the formaldehyde decomposition catalysts of example A2 and example A3 both in the delta crystalline form as determined by X-ray diffraction testing2。
The formaldehyde decomposition catalyst of example a4 was determined by scanning electron microscopy to conform to the characteristics consisting essentially of submicron-micron petal-shaped particles, the non-uniformity of the diameter distribution of which was all greater than that of the formaldehyde decomposition catalyst of example a 1. MnO with a delta crystalline form in submicron-micron petal-like particles of the formaldehyde decomposition catalyst of example A4 as determined by X-ray diffraction testing2。
FIG. 3 is a scanning electron micrograph of the formaldehyde decomposition catalyst of example A5, and FIGS. 3 (a) to (d) are photographs showing selected fields of view on a slide glass showing no tendency at microscopic observation, respectively. As shown in fig. 3, the formaldehyde decomposition catalyst of example a5 consisted primarily of submicron-micron petal shaped particles. Wherein, the diameter of the micron-scale petal-shaped particles is mainly distributed between 1 and 4 mu m, and the diameter of the submicron-scale petal-shaped particles is mainly distributed between 0.3 and 1 mu m. Further observation revealed that these submicron-micron petal-shaped particles tended to be in an agglomerated state, and due to the uneven diameter distribution of the particles, a large number of submicron petal-shaped particles were irregularly distributed around the micron petal-shaped particles (this phenomenon was more pronounced than the formaldehyde decomposition catalyst of example a 1), which caused the agglomeration of the submicron-micron petal-shaped particlesThe specific surface area is larger after the process is finished. MnO with a delta crystalline form in submicron-micron petal-like particles of the formaldehyde decomposition catalyst of example A5 as determined by X-ray diffraction testing2。
Speculation of delta crystalline MnO2The nonuniformity of the particle diameter distribution is related to the volume of the raw material potassium permanganate solution or manganese sulfate solution and the corresponding titration time, and it is further presumed that when the volume of the raw material potassium permanganate solution or manganese sulfate solution is large and the corresponding titration time is long, the grains that are the primary nuclei grow.
In addition to examples A1-A5, the preparation of examples A6-A7 was used to prepare formaldehyde decomposition catalysts as follows:
in the embodiment A6, the formaldehyde decomposition catalyst is obtained by mixing and reacting potassium permanganate and absolute ethyl alcohol as raw materials, and specifically comprises the following steps: preparing potassium permanganate into a potassium permanganate solution with the concentration (mass percentage) of 1.25%, mixing and stirring 4L of the potassium permanganate solution and 1L of absolute ethyl alcohol, reacting at normal temperature for 10 hours, centrifugally dewatering the mixed solution after the reaction is finished to obtain a formaldehyde decomposition catalyst, and cleaning, drying and dispersing the obtained formaldehyde decomposition catalyst.
FIG. 4 is a scanning electron micrograph of the formaldehyde decomposition catalyst of example A6, and FIGS. (a) to (b) in FIG. 4 are photographs showing the selected field of view on a slide glass showing no tendency at microscopic observation, respectively. As shown in FIG. 4, the formaldehyde decomposition catalyst of example A6 was mainly formed by agglomeration of nano-sized particles. The formaldehyde decomposition catalyst of example A6 was determined by X-ray diffraction testing to be MnO in the delta crystalline form2。
The formaldehyde-removing performance test was carried out using the formaldehyde-decomposing catalysts of example A1, example A5, and example A6, respectively. The test principle and the method are as follows: the method comprises the steps of manufacturing a closed experiment chamber, wherein the size of the experiment chamber is 550mm multiplied by 415mm multiplied by 315mm, the experiment chamber is provided with a formaldehyde injection port and a formaldehyde concentration test instrument, the two sides of the experiment chamber are respectively provided with an air outlet and an air inlet, the air outlet and the air inlet are connected through a pipeline with the diameter of 200mm, the pipeline is provided with a fan, and in addition, the pipeline is also provided with a group of flanges for loading and unloading formaldehyde decomposition catalysts for test.
Before testing, a certain mass of formaldehyde decomposition catalyst is uniformly laid on a piece of PP breathable film, the laying amount refers to QBT2761-2006 method for measuring the purification effect of indoor air purification products, a sample to be measured is added through corresponding conversion of the volume of a test chamber, then the formaldehyde decomposition catalyst is covered by another piece of PP breathable film, and then the two pieces of PP breathable films which are wrapped with the formaldehyde decomposition catalyst are clamped between flanges, so that the formaldehyde decomposition catalyst is fixed in a pipeline.
During testing, firstly, the formaldehyde solution with certain volume and concentration is heated and injected into the experiment cabin through the formaldehyde injection port, so that the initial concentration of formaldehyde in the experiment cabin is 1.4-2.0 mg/m3And when the concentration of the formaldehyde in the experimental cabin is increased to the maximum value and stabilized for 1min, starting a fan and starting timing, recording the concentration of the formaldehyde in the experimental cabin every 5min, setting the testing time to be 15min, and keeping the power of the fan to be constant (the wind speed is about 3 m/s). After 15min, formaldehyde was again injected as described above and the test repeated for 15 min. The test was repeated 4 times for each formaldehyde decomposition catalyst.
The graphs of the change of the formaldehyde concentration with time in the experimental chamber obtained by the above formaldehyde removal performance test using the formaldehyde decomposition catalysts of example A1, example A5 and example A6, respectively, are shown in FIG. 5, FIG. 6 and FIG. 7, respectively.
From the calculations shown in fig. 5, 6 and 7: the formaldehyde removal rate 10min before the above formaldehyde removal performance test procedure using the formaldehyde decomposition catalyst of example a1 was 76.2%, the formaldehyde removal rate 10min before the above formaldehyde removal performance test procedure using the formaldehyde decomposition catalyst of example a5 was 81.2%, and the formaldehyde removal rate 10min before the above formaldehyde removal performance test procedure using the formaldehyde decomposition catalyst of example a6 was 64%.
The formaldehyde removal rates of the formaldehyde decomposition catalysts of example a1 and example a5 were better than the formaldehyde removal rate of the formaldehyde decomposition catalyst of example a6, presumably due to: although the formaldehyde decomposition catalyst of example a6 was composed of nano-sized particles, they were easily agglomerated, and particularly when attached to an air-permeable support, these fine particles aggregated into a lump, which was not favorable for sufficient contact with formaldehyde in the air; the formaldehyde decomposition catalysts of examples a1 and a5, however, have non-uniform particle diameter distribution, and a large number of submicron petal-shaped particles are irregularly distributed around the micron petal-shaped particles, so that the submicron-micron petal-shaped particles are agglomerated and are in favor of fully contacting with formaldehyde in the air. The formaldehyde decomposition catalysts of example a1 and example a5 have similar formaldehyde removal rates, but the synthesis required for example a1 is significantly shorter, and therefore example a1 has a higher economic benefit.
Example a7 is a control of example a1, with the exception that step E is added after step D: and D, adding the formaldehyde decomposition catalyst obtained in the step D into deionized water, adding a certain amount of alkali liquor to adjust the pH value of the solution to 9-11, and finally performing centrifugal dehydration to obtain the formaldehyde decomposition catalyst.
Olfactory tests by a number of testers (test samples were placed 15 cm under the testers' nose) showed that the formaldehyde decomposition catalyst of example a7 had significantly reduced odor compared to the formaldehyde decomposition catalysts of examples a1-a 5. It was confirmed that the formaldehyde decomposition catalyst of example a7 and example a1 had approximately the same formaldehyde removal rate.
The method comprises the following steps of taking potassium permanganate, manganese sulfate and water as reaction liquid, and enabling the reaction liquid on the surface of VOC physical adsorbent particles to generate a formaldehyde adsorption-catalytic decomposition composite material in situ:
A. placing a potassium permanganate solution into a first burette, placing a manganese sulfate solution into a second burette, wherein the mass ratio of substances between potassium permanganate in the first burette and manganese sulfate in the second burette is (1-1.34) to 1, the concentration of the potassium permanganate solution in the first burette is 60-110 g/L, if the volume of the potassium permanganate solution in the first burette or the volume of the manganese sulfate solution in the second burette is set as a reference volume, the reference volume is not less than 50L, the volume ratio of the solutions of the first burette and the second burette is 1 to 1, and the concentration of the manganese sulfate solution in the second burette is calculated according to the values;
B. adding a VOC physical adsorbent into a mixing reactor, wetting by adopting absolute ethyl alcohol, and then adding 100L of bottom water, wherein the VOC physical adsorbent is activated carbon, the mass of the activated carbon is 5% -50% of that of potassium permanganate in a first titration tube (the activated carbon is simply referred to as the usage amount in the table 2), and the granularity of the activated carbon is 100-400 meshes;
C. respectively dripping the potassium permanganate solution in the first burette and the manganese sulfate solution in the second burette into bottom water in the mixing reactor, ensuring that the potassium permanganate solution in the first burette and the manganese sulfate solution in the second burette are completely dripped within 10-45 min, and fully stirring the mixed solution for 2 hours at 80 ℃ to complete the reaction;
D. and (3) carrying out solid-liquid separation on the mixed solution after the reaction is finished, and then cleaning, drying and dispersing the solid.
E. And D, adding the solid obtained in the step D into deionized water, adding a certain amount of alkali liquor to adjust the pH value of the solution to 9-11, and finally performing centrifugal dehydration to obtain the formaldehyde adsorption-catalytic decomposition composite material.
Examples B1-B9 are examples of formaldehyde adsorption-catalytic decomposition composites prepared by the above method, some of the parameters are shown in table 2, and the remaining parameters are the same as those of example a 1. The formaldehyde-removing performance test was carried out using the formaldehyde adsorption-catalytic decomposition composite materials of examples B1-B9, respectively, according to the same principle and method as above, and the test results are shown in Table 2. As can be seen from Table 2, the formaldehyde adsorption-catalytic decomposition composite materials of examples B1-B9 all had superior formaldehyde removal performance, and the formaldehyde removal rate was superior to that of the formaldehyde decomposition catalyst of example A1.
TABLE 2
FIG. 8 is a scanning electron micrograph of the activated carbon of example B3, and FIG. 9 is a scanning electron micrograph of the formaldehyde adsorbing-catalytic decomposing composite of example B3. As can be seen from fig. 1, 8 and 9, the formaldehyde adsorption-catalytic decomposition composite material of example B3 is composed of particles having a core-shell structure, wherein the core of the core-shell structure is the activated carbon shown in fig. 8, and the shell of the core-shell structure is the formaldehyde decomposition catalyst mainly composed of the submicron-micron flower-shaped spherical particles shown in fig. 1, and it can be seen that the morphology of manganese dioxide is not affected after the activated carbon is added. Further observation revealed that the submicron-micron flower-like spherical particles are deposited on the surface of the activated carbon and form pores communicating with the surface of the activated carbon, so that the pores can serve as flow channels for the gas flow to be adsorbed by the activated carbon and can be sufficiently contacted with manganese dioxide on the surface of the activated carbon during the adsorption of the gas flow by the activated carbon. The submicron-micron petal particles of fig. 9 have a slightly larger size than the submicron-micron petal particles of fig. 1, which may provide sites for nucleation of manganese dioxide on the surface of a portion of the activated carbon particles, thereby accelerating the growth of manganese dioxide.
The formaldehyde decomposition catalyst and the formaldehyde adsorption-catalytic decomposition composite material related to the invention creation in the specification of the application can be directly used as a product to conduct the actions of manufacturing, selling, using and the like on the product, can also be further processed into a preparation to conduct the actions of manufacturing, selling, using and the like on the preparation, and can also be applied to a formaldehyde purification porous film to conduct the actions of manufacturing, selling, using and the like on the formaldehyde purification porous film.
The formaldehyde purification porous membrane comprises an air-permeable support, and a formaldehyde purification material and a bonding agent which are attached to the air-permeable support, wherein the formaldehyde purification material can be a combination of any several of the formaldehyde decomposition catalyst of the embodiment A1-A7, the formaldehyde adsorption-catalytic decomposition composite material of the embodiment B1-B9 and the VOC physical adsorbent, for example, the formaldehyde purification material can be the formaldehyde decomposition catalyst of the embodiment A1-A7, a mixed catalyst composed of the formaldehyde decomposition catalyst of the embodiment A1-A7 and the VOC physical adsorbent, or the formaldehyde adsorption-catalytic decomposition composite material of the embodiment B1-B9. The formaldehyde purification material is distributed on the outer side of the materials forming the air-permeable support and is mainly filled in the pores among the materials forming the air-permeable support. The adhesive is preferably an acrylic adhesive or a polyurethane adhesive, and the two adhesives do not adversely affect the use performance of the formaldehyde purification material.
The preparation process of the formaldehyde purification porous film is as follows: the formaldehyde purification material is mixed with a dispersant and a bonding agent to prepare feed liquid, wherein the dispersant is water. And attaching the feed liquid to the PP fiber felt through a pulp pulling process. When the formaldehyde purification material is subjected to size pulling, a belt material formed by the PP fiber felt is immersed into the feed liquid under the driving of the conveying roller, then vertically rises from the surface of the feed liquid, and then passes through a channel formed between a pair of scrapers positioned above the feed liquid, each scraper in the pair of scrapers moves in parallel along the surface of the corresponding PP fiber felt, so that extrusion force vertical to the surface of the PP fiber felt is applied to the formaldehyde purification material, the formaldehyde purification material attached to the PP fiber felt is extruded and dispersed in pores among materials forming the breathable support, and finally, the formaldehyde purification porous film is dried to obtain the formaldehyde purification porous film.
When the weight of the formaldehyde purification material is divided by the area of the windward side of the air-permeable support to obtain the relative adhesion amount of the formaldehyde purification material to the air-permeable support, the relative adhesion amount is generally 40g/m based on the formaldehyde removal rate of the formaldehyde purification material invented in the invention according to the present specification2The formaldehyde decomposition catalyst felt basically has commercially acceptable formaldehyde removal effect. After the formaldehyde purifying material is attached to the air-permeable support, particularly when the relative attachment amount is 40g/m2In order to make the formaldehyde decomposition catalysis felt have good formaldehyde removal effect and reasonable air permeability, the air permeable support is suggested to have air permeability of more than or equal to 3000m under 100Pa pressure difference3/m2H air-permeable fiber mats.
When the formaldehyde decomposition catalyst felt is used together with other air treatment devices such as a filter, in order to ensure the air permeability of the whole filter material, the air permeable support preferably has an air permeability of 5500m or more at a pressure difference of 100Pa3/m2H air-permeable fiber mats. The above-mentioned "air permeability at 100Pa pressure difference" may be in terms of the unit "m3/m2H "is understood. Specifically, "air permeability at a pressure difference of 100 Pa" means: cubic meters of air passing over the formaldehyde decomposition catalytic mat per unit square meter area per hour at a pressure differential of 100 Pa. Airfelt fibers having a permeability meeting the above-mentioned requirements can be obtained from the prior art, such as PP fiber felt, PET fiber felt, and the like. The PP fiber felt and the PET fiber felt not only have good air permeability, but also have proper performances such as strength and the like.
The shape, performance and other aspects of the air-permeable support in the formaldehyde purification porous film can be greatly changed according to different use occasions. In a place with higher formaldehyde concentration (such as furniture factory, coating factory, etc.), for better formaldehyde removal, a foam-like porous support can be used as a breathable support in the formaldehyde purification porous film, so as to attach more formaldehyde purification material. In order to independently install the formaldehyde purification porous membrane on a specific channel, the air-permeable support can adopt a support net, and the support net can be a woven net, a punching net, a diagonal net and the like.
Examples C1-C5 illustrate the preparation of a formaldehyde scavenging porous membrane using the formaldehyde decomposition catalyst of example a1 as the formaldehyde scavenging material, PP fiber felt as the air permeable support, and acrylic acid as the binder. The relative adhesion amounts of the formaldehyde purifying materials in examples C1-C5 were 40g/m2、60g/m2、80g/m2、100g/m2、120g/m2。
The formaldehyde-removing performance tests were conducted using the formaldehyde-purifying porous films of examples C1-C5, respectively, and the test principles and methods were substantially identical to those of the above-described formaldehyde-removing performance tests, except that the formaldehyde-purifying porous films were directly sandwiched between flanges without using PP breathable films.
The formaldehyde-purifying porous films of examples C1-C5 were each used to conduct an air permeability test that measures the cubic meter value of air passing over the formaldehyde decomposition catalyst felt per unit square meter area per hour at a pressure differential (specifically, 10Pa differential) that was determined. Due to flow meter reading limitations, when permeability tests were performed using the formaldehyde purification porous membranes of examples C1-C5, a formaldehyde purification porous membrane was tested by stacking six identical formaldehyde purification porous membranes, which allowed the flow rate to be reduced to meet the flow meter reading limitations.
FIG. 10 is a graph showing the comprehensive properties of the porous formaldehyde-purifying films of examples C1-C5. In FIG. 10, the abscissa represents the relative adhesion of the formaldehyde purifying material to the PP fiber felt, wherein "40" means an adhesion of about 40g/m2This corresponds to the formaldehyde-purifying porous membrane of example C1, and so on. The left ordinate of FIG. 10 is the air volume in m3/m2H means the cubic meter value of air passing per unit square meter area of formaldehyde decomposition catalyst mat per hour, with larger values indicating better air permeability of the formaldehyde-purifying porous film and vice versa. The right ordinate of fig. 10 is the formaldehyde removal rate, which can be calculated from the same data as shown in fig. 5-7.
As shown in FIG. 10, the formaldehyde removal rate 10min before the formaldehyde removal performance test using the formaldehyde-purifying porous films of examples C1-C5 gradually increased from about 66% to 72%, although the increase was slight.
As shown in FIG. 10, the formaldehyde-purifying porous films of examples C1 to C5 had successively lower air permeabilities when the relative attachment amounts were 70g/m2About (60 g/m)2~70g/m2And (b) the air permeability and formaldehyde removal rate of the formaldehyde purification porous film are comprehensively optimal.
Further, when the test duration is prolonged to 6 hours with reference to QBT2761-2006 "method for measuring purification effect of indoor air purification product", the removal rate of formaldehyde in the test chamber by the porous formaldehyde purification film of example C2 is 92.1%, and when the test duration is further prolonged to 24 hours, the removal rate of formaldehyde in the test chamber by the porous formaldehyde purification film of example C2 is 96.5%.
Although it is shown in FIG. 10 that the relative adhesion amount is 120g/m2The air permeability of the formaldehyde-purifying porous film was 0, but this phenomenon did not indicate that the formaldehyde-purifying porous film was air impermeable because six identical formaldehyde-purifying porous films were laminated in the test, and actually each of the formaldehyde-purifying porous films was usedThe film has a certain air permeability.
Example C6 is a comparative example of example C2, and example C6 adds an extrusion step between the pulling process and the drying step on the basis of example C2. The pressing process comprises a pair of pressing rollers, a channel is formed between the pair of pressing rollers, and each pressing roller of the pair of pressing rollers rolls along the surface of the corresponding formaldehyde purification porous film in parallel, so that the formaldehyde purification material attached to the PP fiber felt is further pressed and dispersed in pores between materials forming the air-permeable support.
FIG. 11 is a graph showing the distribution uniformity of the formaldehyde scavenger materials in the porous films for formaldehyde scavenger of examples C2 and C6. The comparison chart is a light-transmitting observation of two formaldehyde purification porous films, and the observation clearly shows that the formaldehyde purification material of the formaldehyde purification porous film of the embodiment C6 is obviously more uniformly and finely distributed. FIG. 12 is a scanning electron micrograph of the formaldehyde-scavenging porous film of example C2, which is shown in FIG. 12 and comprises an air-permeable support 110 and a formaldehyde-scavenging material 120 attached to the air-permeable support 110.
Examples D1-D5 show that the formaldehyde adsorbing-catalytic decomposing mixture was used as a formaldehyde purifying material, the PP fiber felt was used as an air permeable support, the adhesive was acrylic acid, and the relative adhesion amount was 60g/m2An example of preparing a formaldehyde-purifying porous film, wherein the formaldehyde adsorption-catalytic decomposition mixed material was composed of the formaldehyde decomposition catalyst of example a1 and a VOC physical adsorbent, which was activated carbon having a particle size of 150 mesh. Examples D1-D5 differ in the proportions of formaldehyde decomposition catalyst and activated carbon, and the proportions and resulting formaldehyde removal rates of the resulting formaldehyde-purified porous film are shown in Table 3.
TABLE 3
Numbering | Mass ratio of formaldehyde decomposition catalyst to activated carbon | Formaldehyde removal rate in the first 10min |
D1 | 0.6:1 | 70.8% |
D2 | 1:1 | 71.9% |
D3 | 1.5:1 | 73.2% |
D4 | 2.3:1 | 75.6% |
D5 | 4:1 | 74.8% |
The formaldehyde removal rates of the formaldehyde purification porous films of examples D1-D5 were all higher than that of the formaldehyde purification porous film of example C2, because the formaldehyde decomposition catalyst and the activated carbon mixed together, the activated carbon can adsorb odor and some volatile gases, and formaldehyde in these adsorbed volatile gases can stay on the activated carbon for a long time, so that it can sufficiently perform catalytic decomposition reaction with the formaldehyde decomposition catalyst, thereby enhancing the formaldehyde removal effect. When the content of activated carbon was further increased on the basis of example D4, the formaldehyde removal rate was somewhat lowered because activated carbon was easily saturated by adsorption, and the supported amount of the formaldehyde decomposition catalyst was too small to sufficiently decompose formaldehyde.
When the test duration was extended to 6 hours, the removal rate of formaldehyde from the test chamber by the formaldehyde-purifying porous film of example D4 was 94.8%, and when the test duration was further extended to 24 hours, the removal rate of formaldehyde from the test chamber by the formaldehyde-purifying porous film of example D4 was 97.4%.
Examples E1-E5 are examples of formaldehyde-purifying porous films prepared using the formaldehyde adsorbing-catalytic decomposing composite of example B3 as a formaldehyde purifying material, PP fiber mats as a breathable support, and an acrylic acid as a binder. The relative adhesion amounts of the formaldehyde adsorbing-catalytic decomposing composites in examples E1 to E5 were 40g/m, respectively2、60g/m2、80g/m2、100g/m2、120g/m2The formaldehyde removal rates for the first 10min were 74.4%, 76.1%, 77.9%, 79.6% and 81.5%, respectively. It was verified that the formaldehyde removal rates of the formaldehyde-purifying porous films of examples E1-E5 have similar laws as those of examples C1-C5. Wherein, when the test duration is prolonged to 6 hours, the formaldehyde removal rate of the formaldehyde purification porous film of example E3 in the test chamber is 96.3%, and when the test duration is further prolonged to 24 hours, the formaldehyde removal rate of the formaldehyde purification porous film of example E3 in the test chamber is 99.6%.
Overall comparison of the formaldehyde removal rates of examples C1-C5, examples D1-D5, and examples E1-E5 shows that the formaldehyde removal rates are: the formaldehyde adsorption-catalytic decomposition composite material is larger than the formaldehyde adsorption-catalytic decomposition mixed material is larger than the formaldehyde decomposition catalyst.
The formaldehyde decomposition catalyst and the formaldehyde adsorption-catalytic decomposition composite material are prepared into another important application.
The formulation is in the form of particles, each particle is composed of a formaldehyde purification material and a binder, the formaldehyde purification material can be a combination of any of the formaldehyde decomposition catalyst of example A1-A7, the formaldehyde adsorption-catalytic decomposition composite material of example B1-B9 and the VOC physical adsorbent, for example, the formaldehyde purification material can be the formaldehyde decomposition catalyst of example A1-A7, the formaldehyde adsorption-catalytic decomposition mixed material composed of the formaldehyde decomposition catalyst of example A1-A7 and the VOC physical adsorbent, or the formaldehyde adsorption-catalytic decomposition composite material of example B1-B9.
The preparation method of the preparation comprises the following steps: (1) preparing a paste precursor from a formaldehyde purification material and an adhesive according to a certain mass ratio; (2) and granulating the paste precursor to obtain the formaldehyde purification material preparation. The granulation process is to extrude the paste precursor through meshes of a porous net in a swing granulator to obtain a formaldehyde purification material preparation; the oscillating granulator is a special device which can make the wet powdery mixture into granules by forcibly passing through the meshes of the porous net under the positive and negative rotation of the rotary drum. Or the granulating process is to extrude the paste precursor into strips and cut the strips to obtain the formaldehyde purification material preparation.
The solid content of the paste precursor is preferably 30-35%, so that a high formaldehyde removal rate can be ensured, and granulation and forming are facilitated.
The preparation is preferably made of cylindrical particles, and when the diameter is 0.18-8 mm and the length is 1-20 mm, the preparation is most convenient to use and can keep high formaldehyde removal rate. Wherein the diameter of the granules is controlled by the aperture of the porous net or the specification of the die, and the length of the granules is controlled by the positive and negative rotation frequency of the roller of the swing granulator or the cutting frequency. In specific implementation, the diameter and the length may be configured as follows: diameter 0.18mm, length 20mm, or diameter 0.38mm, length 15mm, or diameter 4mm, length 9mm, or diameter 8mm, length 1mm, etc.
When the mass ratio of the formaldehyde purifying material to the adhesive is 1 (0.3-1.0), good preparation form and formaldehyde removing effect can be ensured. In specific implementation, the mass ratio of the formaldehyde purifying material to the adhesive can be 1:0.3, 1:0.4, 1:0.5, 1:0.6, 1:0.7, 1:0.8, 1:0.9, 1:1, and the like.
The adhesive is any one of acrylic acid, polyurethane, molasses and starch, and the adhesive cannot influence the formaldehyde removing performance of the formaldehyde purifying material.
The VOC physical adsorbent is activated carbon with the granularity of 100-400 meshes, and in specific implementation, the granularity of the activated carbon can be 100 meshes, 120 meshes, 150 meshes, 200 meshes, 250 meshes, 400 meshes and the like.
Proved by verification, the formaldehyde decomposition catalyst in the embodiment A1 and acrylic acid are prepared into a paste precursor with the solid content of 30-35% according to the mass ratio of 1:0.5, then a formaldehyde decomposition catalyst preparation consisting of particles with the diameter of 4mm and the length of 9mm is prepared by adopting a swing granulator, the removal rate of the formaldehyde decomposition catalyst preparation to formaldehyde in an experimental cabin is 91.4% when the formaldehyde decomposition catalyst preparation is tested for 6 hours, and the removal rate of the formaldehyde decomposition catalyst preparation to formaldehyde in the experimental cabin is 96.1% when the formaldehyde decomposition catalyst preparation is further prolonged to 24 hours.
The formaldehyde adsorption-catalytic decomposition composite material obtained in the example B3 and acrylic acid are prepared into a paste precursor with a solid content of 30-35% according to a mass ratio of 1:0.5, and then a formaldehyde adsorption-catalytic decomposition composite material preparation consisting of particles with a diameter of 4mm and a length of 9mm is prepared by using a swing granulator, wherein the formaldehyde adsorption-catalytic decomposition composite material preparation has a formaldehyde removal rate of 96.4% in a test cabin when the test time is 6 hours, and has a formaldehyde removal rate of 99.1% in the test cabin when the test time is further prolonged to 24 hours.
When the formaldehyde purification material is the formaldehyde adsorption-catalytic decomposition mixed material, the mass ratio of the activated carbon to the formaldehyde decomposition catalyst is (0.6-4): 1; in specific implementation, the mass ratio of the activated carbon to the formaldehyde decomposition catalyst can be 0.6:1, 1:1, 1.5:1, 2.3:1, 4:1, and at this time, the change rule of the formaldehyde removal rate of the obtained preparation is the same as the formaldehyde removal rate of the formaldehyde purification porous thin films of examples D1-D5. When the mass ratio of the activated carbon to the formaldehyde decomposition catalyst is 2.3:1, preparing the obtained formaldehyde adsorption-catalytic decomposition mixed material and acrylic acid into a paste precursor with the solid content of 30-35% according to the mass ratio of 1:0.5, and preparing a formaldehyde adsorption-catalytic decomposition mixed material preparation consisting of particles with the diameter of 4mm and the length of 9mm by using a swing granulator, wherein the removal rate of the formaldehyde adsorption-catalytic decomposition mixed material preparation to formaldehyde in the experimental cabin is 95.3% when the formaldehyde adsorption-catalytic decomposition mixed material preparation is tested for 6 hours, and the removal rate of the formaldehyde in the experimental cabin is 98.2% when the formaldehyde adsorption-catalytic decomposition mixed material preparation is further prolonged to 24 hours.
The preparation can be directly used, for example, directly spread in a room to remove formaldehyde, and can also be used as an active component of a formaldehyde decomposition catalytic component, so that the use is more convenient.
As shown in fig. 13, the formaldehyde decomposition catalytic assembly includes an air inlet plate 210, an air outlet plate 220, and a cavity between the air inlet plate 210 and the air outlet plate 220, wherein the air inlet plate 210 and the air outlet plate 220 are provided with air vents 240, and the cavity is filled with any of the above-mentioned agents.
In order to distribute the agent more uniformly in the cavity, a honeycomb-shaped partition 230 may be placed in the cavity, and then the agent may be placed in each groove of the partition 230, so that excellent formaldehyde removal rate may be obtained with less agent.
The formaldehyde decomposition catalysis component can be used independently, and can also be put into the air treatment equipment such as the existing air filter, air conditioner and the like which are matched with the formaldehyde decomposition catalysis component for use, so that the air is cleaned to the maximum extent. Preferably place this formaldehyde decomposition catalysis subassembly in filter assembly's leeward side during the use, can make the impurity in the air contact with the formaldehyde purification material in the formaldehyde decomposition catalysis subassembly again after being filtered by filter assembly like this to prolong the life-span of formaldehyde evolution material, promote except that formaldehyde efficiency.
The iodine value of the activated carbon in all the examples in the specification is more than or equal to 950mg/g, and the iodine value is measured by the method specified in GB/T7702.7-1977. In addition to activated carbon, any one of diatomaceous earth, silica gel, molecular sieves, and activated alumina may be used as the VOC physical adsorbent and applied to the formaldehyde purifying porous membrane, the formaldehyde purifying material preparation, and the formaldehyde decomposition catalytic module in the above embodiments. These VOC physical adsorbents, in combination with the formaldehyde decomposition catalysts of examples A1-A7, or as cores of the core-shell structures of examples B1-B9, all achieved formaldehyde removal efficiencies significantly better than the single formaldehyde decomposition catalyst. And when the manganese dioxide is used as a core of a core-shell structure, the crystal form and the appearance of a scanning electron microscope of the manganese dioxide are not influenced.
The contents of the present invention have been explained above. Those skilled in the art will be able to implement the invention based on these teachings. All other embodiments, which can be derived by a person skilled in the art from the above description without inventive step, shall fall within the scope of protection of the present invention.
Claims (10)
1. The formaldehyde adsorption-catalytic decomposition composite material is characterized in that: the formaldehyde adsorption-catalytic decomposition composite material is mainly composed of particles with a core-shell structure, wherein:
the core of the core-shell structure mainly comprises a VOC physical adsorbent;
the shell of the core-shell structure is mainly composed of formaldehyde decomposition catalyst.
2. The formaldehyde adsorption-catalytic decomposition composite according to claim 1, wherein: the formaldehyde decomposition catalyst consists of MnO which is mainly delta crystal form and is dispersed on the surface of the VOC physical adsorbent particles2Submicron-micron flower spherical particles formed by the nano sheets.
3. The formaldehyde adsorption-catalytic decomposition composite according to claim 1, wherein: the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.1 and 5 mu m; preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.3 and 5 microns; further preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 5 microns; even more preferably, the diameters of the submicron-micron petal-shaped particles are mainly distributed between 0.5 and 3 mu m.
4. The formaldehyde adsorption-catalytic decomposition composite according to claim 3, wherein: the VOC physical adsorbent is any of activated carbon, diatomite, silica gel, molecular sieve and activated alumina; wherein the granularity of the activated carbon is preferably 100-400 meshes.
5. The formaldehyde adsorption-catalytic decomposition composite according to claim 1, wherein: the formaldehyde decomposition catalyst is generated in situ from a reaction liquid attached to the surface of the VOC physical adsorbent particles.
6. The preparation method of the formaldehyde adsorption-catalytic decomposition composite material is characterized by comprising the following steps: dispersing the VOC physical adsorbent into reaction liquid, and enabling the reaction liquid to generate a formaldehyde decomposition catalyst on the surface of the VOC physical adsorbent particles in situ to obtain the formaldehyde adsorption-catalytic decomposition composite material.
7. The method for preparing the formaldehyde adsorption-catalytic decomposition composite material according to claim 6, wherein: the reaction solution consists of potassium permanganate, manganese sulfate and water, and the preparation method specifically comprises the following steps:
A. placing a potassium permanganate solution in a first burette, placing a manganese sulfate solution in a second burette, wherein the mass ratio of potassium permanganate in the first burette to manganese sulfate in the second burette is (1-1.34) to 1, the concentration of the potassium permanganate solution in the first burette is 60-110 g/L, and the reference volume is not less than 50L if the volume of the potassium permanganate solution in the first burette or the volume of the manganese sulfate solution in the second burette is set as the reference volume;
B. adding a VOC physical adsorbent and bottom water with the volume more than 2 times of the reference volume into a mixing reactor;
C. respectively dropwise adding the potassium permanganate solution in the first titration tube and the manganese sulfate solution in the second titration tube into the bottom water in the mixing reactor, ensuring that the potassium permanganate solution in the first titration tube and the manganese sulfate solution in the second titration tube are completely dropwise added within 10-45 min, and fully stirring the mixed solution at 70-90 ℃ until the reaction is finished;
D. and (3) carrying out solid-liquid separation on the mixed solution after the reaction is finished to obtain the formaldehyde adsorption-catalytic decomposition composite material.
8. The method for preparing the formaldehyde adsorption-catalytic decomposition composite material according to claim 7, wherein: the VOC physical adsorbent is activated carbon, the granularity of the activated carbon is 100-400 meshes, and the mass of the activated carbon is 5-50% of that of potassium permanganate in the first titration tube; the volume ratio of the potassium permanganate solution in the first burette to the manganese sulfate solution in the second burette is 1: 1.
9. The formaldehyde purification porous membrane comprises a breathable support and a formaldehyde purification material attached to the breathable support, and is characterized in that: the formaldehyde purification material is as follows:
1) the formaldehyde adsorption-catalytic decomposition composite material according to any one of claims 1 to 5; or
2) The formaldehyde adsorption-catalytic decomposition composite material obtained by the preparation method according to any one of claims 6 to 8.
10. The preparation method of the formaldehyde purification porous film is characterized by comprising the following steps: the method comprises the following steps:
providing a breathable support;
providing feed liquid containing formaldehyde purification material;
extruding and dispersing the feed liquid on a breathable support, and drying the feed liquid to obtain the formaldehyde purification porous film;
wherein, the formaldehyde purification material is:
1) the formaldehyde adsorption-catalytic decomposition composite material according to any one of claims 1 to 5; or
2) The formaldehyde adsorption-catalytic decomposition composite material obtained by the preparation method according to any one of claims 6 to 8.