CN112725848A - 一种硫酸体系光亮电镀液的添加剂 - Google Patents
一种硫酸体系光亮电镀液的添加剂 Download PDFInfo
- Publication number
- CN112725848A CN112725848A CN202011522617.1A CN202011522617A CN112725848A CN 112725848 A CN112725848 A CN 112725848A CN 202011522617 A CN202011522617 A CN 202011522617A CN 112725848 A CN112725848 A CN 112725848A
- Authority
- CN
- China
- Prior art keywords
- additive
- sulfuric acid
- acid system
- electroplating solution
- system bright
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种硫酸体系光亮电镀液的添加剂,由以下成份组成:30‑40wt%非离子表面活性剂、3‑5wt%抗氧化剂、4‑8wt%有机溶剂、5‑10wt%辅助光亮剂和余量的去离子水。本发明与现有技术相比的优点在于:制成的电镀液分散性很好,镀液抗氧化能力较好,电镀镀层致密平滑,且抗变色性能好,镀层的可焊性能优良。并且,电镀液中不产生生物不可降解物质,降低了废水处理难度,对环境友好,完全符合环保标准要求。
Description
技术领域
本发明涉及电镀液添加剂法技术领域,具体是指一种硫酸体系光亮电镀液的添加剂。
背景技术
电镀液是指可以扩大金属的阴极电流密度范围、改善镀层的外观、增加溶液抗氧化的稳定性等特点的液体,电镀液种类数不胜数,曾经在制造实验中应用过的种类就有十余之多。在生产中常用的镀液有四种:氰化镀锌、锌酸盐镀锌、氯化物镀锌和硫酸盐镀锌。根据主盐和其他成分的不同,而演化出众多镀液来只不过是大同小异而已。
电镀液中的添加剂较为重要,能改善镀层的性能和电镀质量的作用,如整平剂、光亮剂、抗针孔剂等。光亮剂主要用来增加镀层的光亮度,少去了抛光的工序。润湿剂的作用是提高各种金属和溶液间的界面张力。整平剂能够改变金属表面的微观平整性。应力消除剂则能降镀层的内应力,提高镀层的韧性。
但是现有的添加剂制成的电镀液分散性不好,镀液抗氧化能不好,电镀镀层不够平滑且疏松,同时且抗变色性能较差,镀层的可焊性能不好。并且,电镀液中会产生生物不可降解物质,提高了废水处理难度,从而污染环境,不符合环保标准要求。
发明内容
本发明要解决的技术问题是克服以上技术缺陷,提供一种硫酸体系光亮电镀液的添加剂,制成的电镀液分散性很好,镀液抗氧化能力较好,电镀镀层致密平滑,且抗变色性能好,镀层的可焊性能优良。并且,电镀液中不产生生物不可降解物质,降低了废水处理难度,对环境友好,完全符合环保标准要求。
为解决上述技术问题,本发明提供的技术方案为:一种硫酸体系光亮电镀液的添加剂,由以下成份组成:30-40wt%非离子表面活性剂、3-5wt%抗氧化剂、4-8wt%有机溶剂、5-10wt%辅助光亮剂和余量的去离子水。
所述非离子表面活性剂包括脂肪醇聚氧乙烯醚、脂肪胺聚氧乙烯醚、烷基醇酰胺聚氧乙烯醚、烷基醇酰胺中的一种。
所述抗氧化剂包括丁基羟基茴香醚、二丁基羟基甲苯、没食子酸丙酯、叔丁基对苯二酚、硫代二丙酸二月桂酯中的一种。
所述辅助光亮剂包括炔醇类添加剂、丙烷磺酸吡啶嗡盐、苯亚甲基丙酮中的一种。
由以下成份组成:32-38wt%非离子表面活性剂、4-4.5wt%抗氧化剂、5-7wt%有机溶剂、6-9wt%辅助光亮剂和余量的去离子水。
本发明与现有技术相比的优点在于:制成的电镀液分散性很好,镀液抗氧化能力较好,电镀镀层致密平滑,且抗变色性能好,镀层的可焊性能优良。并且,电镀液中不产生生物不可降解物质,降低了废水处理难度,对环境友好,完全符合环保标准要求。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明公开一种硫酸体系光亮电镀液的添加剂,由以下成份组成:30-40wt%非离子表面活性剂、3-5wt%抗氧化剂、4-8wt%有机溶剂、5-10wt%辅助光亮剂和余量的去离子水。
所述非离子表面活性剂包括脂肪醇聚氧乙烯醚、脂肪胺聚氧乙烯醚、烷基醇酰胺聚氧乙烯醚、烷基醇酰胺中的一种。
所述抗氧化剂包括丁基羟基茴香醚、二丁基羟基甲苯、没食子酸丙酯、叔丁基对苯二酚、硫代二丙酸二月桂酯中的一种。
所述辅助光亮剂包括炔醇类添加剂、丙烷磺酸吡啶嗡盐、苯亚甲基丙酮中的一种。
由以下成份组成:32-38wt%非离子表面活性剂、4-4.5wt%抗氧化剂、5-7wt%有机溶剂、6-9wt%辅助光亮剂和余量的去离子水。
实施例1
一种硫酸体系光亮电镀液的添加剂,由以下成份组成:30wt%非离子表面活性剂、3wt%抗氧化剂、4wt%有机溶剂、5wt%辅助光亮剂和余量的去离子水。
实施例2
一种硫酸体系光亮电镀液的添加剂,由以下成份组成:35wt%非离子表面活性剂、4wt%抗氧化剂、6wt%有机溶剂、7wt%辅助光亮剂和余量的去离子水。
实施例3
一种硫酸体系光亮电镀液的添加剂,由以下成份组成:40wt%非离子表面活性剂、5wt%抗氧化剂、8wt%有机溶剂、10wt%辅助光亮剂和余量的去离子水。
本发明纯锡添加剂以及其配成的镀液分散性很好,镀液抗氧化能力较好,电镀镀层致密平滑,且抗变色性能好,镀层的可焊性能优良。并且,电镀液中不产生生物不可降解物质,降低了废水处理难度,对环境友好,完全符合环保标准要求。
以上公开的本发明优选实施例只是用于帮助阐述本发明。优选实施例并没有详尽叙述所有的细节,也不限制该发明仅为所述的具体实施方式。显然,根据本说明书的内容,可作很多的修改和变化。本说明书选取并具体描述这些实施例,是为了更好地解释本发明的原理和实际应用,从而使所属技术领域技术人员能很好地理解和利用本发明。本发明仅受权利要求书及其全部范围和等效物的限制。
Claims (5)
1.一种硫酸体系光亮电镀液的添加剂,其特征在于:由以下成份组成:30-40wt%非离子表面活性剂、3-5wt%抗氧化剂、4-8wt%有机溶剂、5-10wt%辅助光亮剂和余量的去离子水。
2.根据权利要求1所述的一种硫酸体系光亮电镀液的添加剂,其特征在于:所述非离子表面活性剂包括脂肪醇聚氧乙烯醚、脂肪胺聚氧乙烯醚、烷基醇酰胺聚氧乙烯醚、烷基醇酰胺中的一种。
3.根据权利要求1所述的一种硫酸体系光亮电镀液的添加剂,其特征在于:所述抗氧化剂包括丁基羟基茴香醚、二丁基羟基甲苯、没食子酸丙酯、叔丁基对苯二酚、硫代二丙酸二月桂酯中的一种。
4.根据权利要求1所述的一种硫酸体系光亮电镀液的添加剂,其特征在于:所述辅助光亮剂包括炔醇类添加剂、丙烷磺酸吡啶嗡盐、苯亚甲基丙酮中的一种。
5.根据权利要求1所述的一种硫酸体系光亮电镀液的添加剂,其特征在于:由以下成份组成:32-38wt%非离子表面活性剂、4-4.5wt%抗氧化剂、5-7wt%有机溶剂、6-9wt%辅助光亮剂和余量的去离子水。