CN1127186A - 细石混凝土水泥管材及其制造方法 - Google Patents
细石混凝土水泥管材及其制造方法 Download PDFInfo
- Publication number
- CN1127186A CN1127186A CN 95100348 CN95100348A CN1127186A CN 1127186 A CN1127186 A CN 1127186A CN 95100348 CN95100348 CN 95100348 CN 95100348 A CN95100348 A CN 95100348A CN 1127186 A CN1127186 A CN 1127186A
- Authority
- CN
- China
- Prior art keywords
- cement
- pipe
- stone
- concrete pipe
- stone powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种细石混凝土水泥管材及其制造方法,这种水泥管材是选用新鲜具有活性的石粉和水泥、碎石按一定比例混合,先干拌2分钟以上后加水,再搅拌5分钟,并控制其塌落度在2~5cm的范围内,然后投入离心机中离心成型,通过蒸汽养护,脱模后洒水养护3天,再缠上钢丝并涂上保护层。这种不用河砂的细石混凝土水泥管材不渗漏,经受水压超过9kg/cm2,管材的抗化学侵蚀能力增强,延长其使用寿命,增强管材的密实度。
Description
本发明涉及一种细石混凝土水泥管材,它主要用作输水管道,还用于作为输气和输油的管道,其实用管径为600~1800mm。
由于经济的迅速发展,引水工程在各地变成为关键的项目,需要大量的输水管道。现在常用方法制造水泥管材的材料是水泥、砂和石子,采用预应力或自应力方法制造钢筋混凝土管,但是这些管材都有不同程度的渗漏现象,经常要用环氧树脂涂补,这是由于河砂没有活性,不能与水泥水化时释放的氢氧化钙反应,使流离氢氧化钙残留在管材中,并在其中占有一定的位置,当水泥管通水或者浸水时,流离氢氧化钙便逐渐溶解于水中,被水带走,从而形成空穴,这样增加了管的空隙率,也削弱水泥管材的强度,降低水管的抗渗能力。中国专利CN1042892A关于“水泥管材的制造方法”中提出一种采用玻璃纤维,塑料纤维麻、棕一类的复合纤维、细铁丝、水泥、高岭土或石灰石粉、粉煤组成的增强水泥复合材料,采用挤压成型制作水泥管材,这种管材具有抗压、抗拉、防渗、防漏的优点,但工艺复杂、成本高,且只能制造φ200mm的管材。
本发明的任务是提供一种能承受高压的水泥管材及其制造方法,其管径为600~1800mm,承受压力超过9kg/cm2,防渗漏性能好,选用材料独特,制造工艺简单,操作容易,可节约水泥用量。
本发明的任务是以如下的方式完成的,这种管材是选用具有一定活性的新鲜石粉,它和水泥、碎石先干拌2分钟以上后加水,再搅拌5分钟,然后投入离心机中离心成形,通过蒸汽养护,脱模后洒水养护3天,再缠上钢丝并涂上保护层,制成钢筋混凝土管材。这种水泥管材的主要原料配比为:水泥为15%~40%,石粉20%~40%,碎石20%~60%,对选用的石粉要求是新鲜的,最大不超过0.2cm,碎石选用大小在0.2~1.2cm范围内,生产这种水泥管材的塌落度控制在2~5cm之间,利用这种制造方法生产的水泥管材管径在600~1800mm之间,其长度为5米。
生产这种细石混凝土水泥管材时,水泥水化的化学反应表示式为:
由此可知,采用具有活性的石粉替代没有活性的河砂拌制生产水泥管材,具有活性的新鲜石粉(SiO2)能与水泥水化时释放出的氢氧化钙反应,生成具有一定强度的新水泥石,从而增加了水泥管材的强度;如果管材的强度要求不变化,采用这种制造方法可以减少水泥用量达20%。用新鲜的石粉替代河砂生产的水泥管材能增加抗渗能力,经受水压9kg/cm2的试验,做到滴水不漏,同时增强水泥管材抗化学侵蚀的能力,延长其使用寿命,增加管材的密实度和抗渗能力。
Claims (3)
1、一种细石混凝土水泥管材,其特征是:这种水泥管材的主要原料为水泥、石粉和碎石,其中水泥为15~40%,新鲜的石粉为20~40%,碎石20~60%。
2、按权利要求1所规定细石混凝土水泥管材的制造方法,其特征是:按照配比选用新鲜具有活性的石粉,与水泥、碎石均匀混合,先干拌2分钟以上后加水,再搅拌5分钟,控制其塌落度在2~5cm的范围内,然后投入离心机中离心成形,并通过蒸汽养护,脱模后洒水养护3天,再缠上钢丝并涂上保护层,制成这种细石混凝土管材。
3、按权利要求2所规定的细石混凝土水泥管材制造方法,其特征是:选用石粉最大不超过0.2cm,碎石的大小在0.2~1.2cm范围内。