CN112656694A - 多层片材、外用贴剂、包装结构 - Google Patents

多层片材、外用贴剂、包装结构 Download PDF

Info

Publication number
CN112656694A
CN112656694A CN202010361768.7A CN202010361768A CN112656694A CN 112656694 A CN112656694 A CN 112656694A CN 202010361768 A CN202010361768 A CN 202010361768A CN 112656694 A CN112656694 A CN 112656694A
Authority
CN
China
Prior art keywords
sheet
present
fibers
main
multilayered
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010361768.7A
Other languages
English (en)
Inventor
中野智和
近藤未加
古川凉子
加藤纮将
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kanae Technos Co Ltd
Original Assignee
Kanae Technos Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kanae Technos Co Ltd filed Critical Kanae Technos Co Ltd
Publication of CN112656694A publication Critical patent/CN112656694A/zh
Pending legal-status Critical Current

Abstract

本发明的目的在于提供一种即使在因润湿而相互粘在一起的情况下也能轻松对其进行剥离的新型多层片材、将所述多层片材作为承载体使用的外用贴剂以及所述外用贴剂的包装结构。使用多层片材(1)作为外用贴剂(10)的承载体(2)，其中该多层片材具有通过在由亲水性纤维构成的主片材(11)的单面或双面上层压由疏水性纤维构成的辅片材(12)而形成的两层或三层的层叠结构。

Description

多层片材、外用贴剂、包装结构
技术领域
本发明涉及一种具有两层或三层层叠结构的多层片材、将所述多层片材作为承载体使用的外用贴剂以及所述外用贴剂的包装结构。
背景技术
一般的外用贴剂大多单张或者多张一起被封装入不透气的包装袋或容器中以进行流通和保存，即在被容器包装的状态下进行流通和保存，在使用时只需将其开封即可。在这种外用贴剂中，贴在脸上使用的“面罩”相对较大，所以通常在折叠的状态下对其进行容器包装。
然而，面罩的形态多为用化妆水等浸泡由无纺布之类的材料制成的承载体而得到的润湿的薄片，因折叠而相互重叠的部分彼此粘在一起，需要用手指对粘在一起的薄片进行分离并将其展开，这项操作是极为烦杂的。因此，下述专利文献1提出了一种能轻松展开的面罩(面膜)用折叠构造。
【现有技术文献】
【专利文献】
【专利文献1】特开2006-42981号公报
发明内容
发明所要解决的技术问题
然而，在大多数情况下，即使设计者用心设计了承载体的折叠方法，使用者也无法领悟到设计者所设想的展开方法，展开操作依旧困难重重。
本发明是为了解决上述技术问题而进行的发明，目的在于提供一种即使在因润湿而相互粘在一起的情况下也能轻松对其进行剥离的新型多层片材、将所述多层片材作为承载体使用的外用贴剂以及所述外用贴剂的包装结构。
解决技术问题所采用的技术方案
可采用本发明的多层片材解决上述技术问题，该多层片材具有在主片材的单面或双面上层压辅片材而形成的两层或三层的层叠结构，其特征在于：其中所述主片材为由亲水性纤维构成的无纺布，所述辅片材为由疏水性纤维构成的无纺布(以下称为“本发明所述多层片材”)。
在本发明所述多层片材中，其优选形态为所述主片材由公定回潮率大于等于7.0％的亲水性纤维构成，所述辅片材由公定回潮率小于等于5.5％的疏水性纤维构成。
在本发明所述多层片材中，其优选形态为所述主片材由人造丝纤维或者棉纤维构成，而所述辅片材由PET纤维或者聚乳酸纤维构成。
在本发明所述多层片材中，其优选形态为所述辅片材的单位面积重量大于所述主片材的单位面积重量。
在本发明所述多层片材中，其优选形态为所述主片材的单位面积重量为10～50g/m2，而所述辅片材的单位面积重量为15～60g/m2。
可采用本发明的外用贴剂解决上述技术问题，该外用贴剂是通过贴在皮肤表面上进行使用的，其特征在于，具备：承载体，其由本发明所述多层片材构成；药液，其用于浸泡所述承载体(以下称为“本发明所述外用贴剂”)。
可采用本发明的包装结构解决上述技术问题，该包装结构用于对本发明所述外用贴剂进行容器包装，其特征在于：所述承载体在被折叠的状态下与所述药液一起被封装入容器中(以下称为“本发明所述包装结构”)。
发明效果
本发明所述多层片材即使在因润湿而相互粘在一起的情况下也能轻松剥离。此外，通过采用将本发明所述多层片材作为承载体的外用贴剂和用于容器包装所述外用贴剂的本发明所述包装结构，即使对所述承载体进行折叠也可轻松将其展开。
附图说明
【图1】图1(a)是本发明所述多层片材一实施方式的剖面图，图1(b)是显示被加工成人脸形状的本发明所述多层片材的正面图。
【图2】图2(a)是本发明所述包装结构一实施方式的斜视图，图2(b)是本发明所述包装结构的局部破损状态的斜视图，以便能用肉眼确认包装袋中的本发明所述外用贴剂。
【图3】图3(a)～(e)是支撑体的折叠过程的斜视图，依次示出了构成本发明所述外用贴剂的支撑体的折叠过程。
【图4】图4(a)是显示从本发明所述包装结构中取出本发明所述外用贴剂时的状态的正面图，图4(b)是本发明所述外用贴剂的展开状态的斜视图。
【图5】图5是本发明所述多层片材的另一实施方式的剖面图。
符号说明
1 本发明所述多层片材(多层片材)
11 主片材
12 辅片材
2 承载体
3 药液
4 容器
10 本发明所述外用贴剂(外用贴剂)
100 本发明所述包装结构
具体实施方式
以下，对本发明的实施方式进行说明，但需要注意的是本发明并不局限于这些实施方式。
＜本发明所述多层片材1＞
图1所示为本发明所述多层片材1的一个实施方式。如图1(a)所示，本发明所述多层片材1具有在“主片材(11)”的单面层压“辅片材(12)”而形成的双层层叠结构。
-主片材11-
所述主片材11是由亲水性纤维构成的无纺布。在本实施方式中，选择棉纤维(公定回潮率：8.5％)作为亲水性纤维，并将由该纤维形成的薄片状无纺布(单位面积重量：25g/m2)作为所述主片材11使用。
-辅片材12-
所述辅片材12是由疏水性纤维构成的无纺布。在本实施方式中，选择聚乳酸纤维(公定回潮率：0.5％)作为疏水性纤维，并将由该纤维形成的薄片状无纺布(单位面积重量：30g/m2)作为所述辅片材12使用。
需要说明的是，在本实施方式中，在将所述主片材11和所述辅片材12叠合在一起之后，由片材的一侧向另一侧喷射水流，使存在于边界处的亲水性纤维和疏水性纤维相互缠结，从而构建本发明所述多层片材1的层叠结构。因此，所述主片材11与所述辅片材12的边界并不一定是清晰明确的。
另外，如图1(b)所示，在本实施方式中本发明所述多层片材1被切割成模仿人脸的形状，并且在与眼睛和嘴巴相对应的部位设有开口(2E、2M)。此外，在与鼻子对应的部位设置有U形切口2N，在边缘的多个位置上设置有直线状切口2S，由此，在将其贴在脸上时可以更好的贴合面部的立体形状。
＜本发明所述外用贴剂10、本发明所述包装结构100＞
图2所示为用于对本发明所述外用贴剂10进行容器包装的本发明所述包装结构100的一个实施方式。本发明所述外用贴剂10具备“承载体(2)”和“药液(3)”。另外，本发明所述包装结构100具有可将本发明所述外用贴剂10封装在“容器(4)”中的结构。
-承载体2-
所述承载体2由本发明所述多层片材1构成。在本实施方式中，将被切割成模仿人脸形状的本发明所述多层片材1作为所述承载体2使用(参照图1(b))。此外，在本实施方式中，所述承载体2处于经由图3(a)～(e)所示工序被折叠在一起的状态。
-药液3-
所述药液3用于浸泡所述承载体2。在本实施方式中，使用化妆水作为所述药液3。
-容器4-
所述容器4用于将折叠状态下的所述承载体2和所述药液3一起封装。在本实施方式中，所述容器4采用对相互重叠在一起的两片矩形的不透气膜(镀铝膜)的周缘进行热压封合而构建的四边密封结构的扁平包装袋材。
在使用本发明所述包装结构100中的本发明所述外用贴剂10时，首先，如图4(a)所示，打开所述容器4，并将本发明所述外用贴剂10取出。因为取出的本发明所述外用贴剂10处于被折叠在一起的状态，所以需要如图4(b)所示用手指进行展开操作。
在进行展开操作时，由于本发明所述外用贴剂10采用本发明所述多层片材1作为所述承载体2，在所述主片材11和所述辅片材12面对面重叠在一起的部分及在所述辅片材12彼此面对面重叠在一起的部分中，片材之间具有良好的滑动性，因此即使重叠部分因润湿而相互粘在一起也能轻松将其剥离。因此，在本发明所述外用贴剂10中，即使对所述承载体2进行折叠也可轻松将其展开。
然而，在本实施方式中，本发明所述多层片材1采用了具有双层层叠结构的片材，而在本发明中，如图5所示，本发明所述多层片材1可采用在主片材11的双面层压辅片材12而形成的具有三层层叠结构的片材。将具有三层层叠结构的本发明所述多层片材1作为本发明所述外用贴剂10的承载体2使用，并将其构建为本发明所述包装结构100时，在重叠部分中将不存在所述主片材11彼此面对面重叠在一起的部位，因此，能更轻易的将其展开。
此外，虽然在本实施方式中采用棉纤维作为构成所述主片材11的亲水性纤维并采用聚乳酸纤维作为构成所述辅片材12的疏水性纤维，但是亲水性纤维和疏水性纤维并不局限于这些材料。如果利用由公定回潮率大于等于7.0％(更优选为大于等于8.5％)的亲水性纤维构成的主片材11和由公定回潮率小于等于5.5％(更优选为小于等于4.5％)的疏水性纤维构成的辅片材12构建本发明所述多层片材1，那么即使在因润湿而相互粘在一起的情况下也能轻松对其进行剥离。另外，在本发明中“公定回潮率”是根据JIS0105《纤维制品的物理试验方法通则》以及与该标准对应的国际标准ISO139(Textiles-Standardatmospheres for conditioning and testing(MOD)测定出的数值。
作为用于构建所述主片材11的亲水性纤维的具体实例，除了棉花(棉)以外，还可列举如下：丝绸、羊毛、麻、人造丝、铜氨纤维等纤维(长纤维以及短纤维)。另一方面，作为用于构建所述辅片材12的疏水性纤维的具体实例，除了聚乳酸纤维以外，还可列举如下：维纶、尼龙、亚乙烯纤维、涤纶、亚克力纤维、聚乙烯纤维、聚丙烯纤维、PET纤维等纤维(长纤维以及短纤维)。其中，在本发明中所述主片材11优选采用由人造丝纤维或棉纤维构成的无纺布，而所述辅片材12优选采用由PET纤维或聚乳酸纤维构成的无纺布。
此外，在本发明中，本发明所述多层片材1优选为所述辅片材12的单位面积重量大于所述主片材11的单位面积重量。所述主片材11的单位面积重量优选为10～50g/m2(更优选为25～35g/m2)，而所述辅片材12的单位面积重量优选为15～60g/m2(更优选为20～40g/m2)。
此外，虽然在本实施方式中，在构建本发明所述多层片材1时利用喷射水流使纤维缠结在一起从而对所述主片材11和所述辅片材12进行层压，但是对于所述主片材11和所述辅片材12的层压方式并没有特别的限制。也可以通过粘接、黏合或热熔等方式来进行所述主片材11和所述辅片材12的层压。
虽然在本实施方式中，利用作为药液3使用的化妆水来浸泡被切割成模仿人脸形状的所述承载体2以构建本发明所述外用贴剂10，但是对所述承载体2的形状和药液3的种类并没有特别的限制。
除此之外，虽然在本实施方式中选择包装袋作为构建本发明所述包装结构100的容器4，但是对于所述容器4的形式和所述容器4的构成材料并没有特别的限制，只要能对本发明所述外用贴剂10进行封装即可。
另外，本发明能够在不脱离其精神或主要特征的前提下以其他各种形式实施。因此，上述实施例在所有方面都被看作是示例性的而并非是限定性的。本发明的范围如权利要求书所示，并且不受说明书正文的制约。此外，权利要求书等同范围内所有的变形和改变都在本发明的范围内。
【工业实用性】
本发明所述多层片材优选用作以折叠状态被封装入容器内的本发明所述外用贴剂的承载体。

Claims (7)

1.一种多层片材，其具有在主片材的单面或双面上层压辅片材而形成的两层或三层的层叠结构，其特征在于：
所述主片材是由亲水性纤维构成的无纺布，而所述辅片材是由疏水性纤维构成的无纺布。
2.如权利要求1所述的多层片材，其特征在于，
在所述多层片材中，所述主片材由公定回潮率大于等于7.0％的亲水性纤维构成，而所述辅片材由公定回潮率小于等于5.5％的疏水性纤维构成。
3.如权利要求1或2所述的多层片材，其特征在于，
在所述多层片材中，所述主片材由人造丝纤维或棉纤维构成，所述辅片材由PET纤维或聚乳酸纤维构成。
4.如权利要求1至3任意一项所述的多层片材，其特征在于，
所述辅片材的单位面积重量大于所述主片材的单位面积重量。
5.如权利要求1至4任意一项所述的多层片材，其特征在于，
所述主片材的单位面积重量为10～50g/m2，所述辅片材的单位面积重量为15～60g/m2。
6.一种外用贴剂，该外用贴剂是通过贴在皮肤表面上进行使用的，其特征在于，具备：承载体，其由权利要求1至5任意一项所述的多层片材构成；药液，其用于浸泡所述承载体。
7.一种包装结构，其用于对权利要求6所述的外用贴剂进行容器包装，其特征在于：所述承载体在被折叠的状态下与所述药液一起被封装入容器中。
CN202010361768.7A 2019-10-15 2020-04-30 多层片材、外用贴剂、包装结构 Pending CN112656694A (zh)