CN112625337A - 一种环保可降解塑料杯加工工艺 - Google Patents
一种环保可降解塑料杯加工工艺 Download PDFInfo
- Publication number
- CN112625337A CN112625337A CN202011355878.9A CN202011355878A CN112625337A CN 112625337 A CN112625337 A CN 112625337A CN 202011355878 A CN202011355878 A CN 202011355878A CN 112625337 A CN112625337 A CN 112625337A
- Authority
- CN
- China
- Prior art keywords
- plastic cup
- auxiliary agent
- environment
- processing technology
- friendly degradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种环保可降解塑料杯加工工艺，其特征在于：该塑料杯主要包括食品级PP、主料、食用色素和改性助剂，10‑20份的食用PP和15‑18份的主料作为基体，达到可降解的目的，主料为玉米淀粉、木薯淀粉或竹粉，生产成本低，供货较为稳定，3‑6份的改性助剂，0.1‑1份的食用色素，可生产出颜色各异的塑料杯，增强了塑料杯的市场竞争力，性助剂包括增塑剂，增塑剂为柠檬酸酯类增塑剂，以改变原料的可塑性，从而避免原料太脆影响塑料杯的质量，改性助剂还包括偶联剂，偶联剂为硅烷偶联剂，偶联剂将所有的物料偶联起来，使其紧密结合，改性助剂还包括光降解促进剂，可加快塑料杯的降解速度，改性助剂还包括抗菌剂，抗菌剂为酸角叶提取液和地榆水浸出液的混合物。
Description
技术领域
本发明涉及塑料杯生产技术领域，具体为一种环保可降解塑料杯加工工艺。
背景技术
目前，一次性塑料杯已经广泛应用于人们的日常生活，但是存在降解困难，造成了严重的白色污染问题，随着人们环保意识的提高，人们越来越重视环境问题，所以开发出一款可降解的一次性塑料杯是人们必须解决的问题。为此，我们提出了环保可降解塑料杯加工工艺，以生产出可降解的塑料杯。
发明内容
本发明要解决的技术问题是克服现有的缺陷，提供一种环保可降解塑料杯加工工艺，采用食用级PP和玉米淀粉或竹粉作为基体，大幅提高了塑料杯的降解速度，较为环保，可以有效解决背景技术中的问题。
为实现上述目的，本发明提供如下技术方案：一种环保可降解塑料杯加工工艺，该塑料杯主要包括食品级PP、主料、食用色素和改性助剂，各组分的重量份为：
作为本发明的一种优选技术方案，具体生产流程如下：
步骤A，首先将各成分进行过筛，然后将筛选好的各成分进行配比称重；
步骤B，接着将配比称重好的原料放入高速搅拌机中，进行搅拌混合，并且在搅拌过程中，对高速搅拌机内部进行加热，加热到所需温度后，并在相应转速作用下，使得各成分混合均匀充分，得到混料；
步骤C，紧接着将具有一定温度的混料投入冷却机中进行冷却，冷却到所需温度后，得到处理后的混料；
步骤D，然后将冷却处理后的混料投入锥形双螺杆挤出机中，再以熔体形式挤出得到半熔融状态的塑料管坯；
步骤E，接着将得到的半熔融状态塑料管坯置入模具中，随即向管坯中通入压缩空气使其膨胀，使得塑料管坯的外壁紧紧贴在模具内壁上，在此过程中，保证模具处于所需温度即可；
步骤F，紧接着停止对模具加热，对经吹胀处理并紧紧贴在模具内壁上的塑料管坯进行冷却操作，冷却一段时间后，再将上压模模具打开，然后取出已形成杯状的半成品放置在空气中自然冷却；
步骤G：最后将完全冷却后的半成品塑料杯多余的边料、边刺切除，在此切除过程中，需要同时对半成品塑料杯进行加水调湿操作，操作结束后即可得到成品塑料杯。
作为本发明的一种优选技术方案，所述主料为玉米淀粉、木薯淀粉或竹粉中的一种。
作为本发明的一种优选技术方案，所述改性助剂包括增塑剂，增塑剂为柠檬酸酯类增塑剂。
作为本发明的一种优选技术方案，所述改性助剂包括偶联剂，偶联剂为硅烷偶联剂。
作为本发明的一种优选技术方案，所述改性助剂包括光降解促进剂。
作为本发明的一种优选技术方案，所述改性助剂包括抗菌剂，抗菌剂为酸角叶提取液和地榆水浸出液的混合物。
作为本发明的一种优选技术方案，所述改性助剂包括流平剂，流平剂为聚醚改质聚硅氧烷。
作为本发明的一种优选技术方案，所述改性助剂包括热稳定剂，热稳定剂为硬脂酸锌。
与现有技术相比，本发明的有益效果是：本环保可降解塑料杯加工工艺，采用食用级PP和玉米淀粉或竹粉作为基体，大幅提高了塑料杯的降解速度，较为环保，还可添加食用级色素，生产出颜色各异的可降解塑料杯，提高市场竞争力。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供一种技术方案：一种环保可降解塑料杯加工工艺，该塑料杯主要包括食品级PP、主料、食用色素和改性助剂，10-20份的食用PP和15-18份主料作为基体，达到可降解的目的，主料为玉米淀粉、木薯淀粉或竹粉中的一种，生产成本低，供货较为稳定，3-6份的改性助剂，0.1-1份的食用色素，可生产出颜色各异的塑料杯，增强了塑料杯的市场竞争力，改性助剂包括增塑剂，增塑剂为柠檬酸酯类增塑剂，以改变原料的可塑性，从而避免原料太脆影响塑料杯的质量，改性助剂还包括偶联剂，偶联剂为硅烷偶联剂，偶联剂将所有的物料偶联起来，使其紧密结合，改性助剂还包括光降解促进剂，可加快塑料杯的降解速度，改性助剂还包括抗菌剂，抗菌剂为酸角叶提取液和地榆水浸出液的混合物，采用酸角叶提取液和地榆水浸出液的混合物作为抗菌剂，无毒，生产过程环保，且抑菌效果好，可以抑制细菌的滋生，改性助剂还包括流平剂，流平剂为聚醚改质聚硅氧烷，用于改善原料的流动性，改性助剂还包括热稳定剂，热稳定剂为硬脂酸锌，用于改善原料的稳定性；
该塑料杯的生产流程如下：
步骤A，首先将各成分进行过筛，然后将筛选好的各成分进行配比称重；
步骤B，接着将配比称重好的原料放入高速搅拌机中，进行搅拌混合，并且在搅拌过程中，对高速搅拌机内部进行加热，加热到所需温度后，并在相应转速作用下，使得各成分混合均匀充分，得到混料；
步骤C，紧接着将具有一定温度的混料投入冷却机中进行冷却，冷却到所需温度后，得到处理后的混料；
步骤D，然后将冷却处理后的混料投入锥形双螺杆挤出机中，再以熔体形式挤出得到半熔融状态的塑料管坯；
步骤E，接着将得到的半熔融状态塑料管坯置入模具中，随即向管坯中通入压缩空气使其膨胀，使得塑料管坯的外壁紧紧贴在模具内壁上，在此过程中，保证模具处于所需温度即可；
步骤F，紧接着停止对模具加热，对经吹胀处理并紧紧贴在模具内壁上的塑料管坯进行冷却操作，冷却一段时间后，再将上压模模具打开，然后取出已形成杯状的半成品放置在空气中自然冷却；
步骤G：最后将完全冷却后的半成品塑料杯多余的边料、边刺切除，在此切除过程中，需要同时对半成品塑料杯进行加水调湿操作，操作结束后即可得到成品塑料杯。
Claims (9)
1.一种环保可降解塑料杯加工工艺，其特征在于：该塑料杯主要包括食品级PP、主料、食用色素和改性助剂，各组分的重量份为：
2.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于，具体流程如下：
步骤A，首先将各成分进行过筛，然后将筛选好的各成分进行配比称重；
步骤B，接着将配比称重好的原料放入高速搅拌机中，进行搅拌混合，并且在搅拌过程中，对高速搅拌机内部进行加热，加热到所需温度后，并在相应转速作用下，使得各成分混合均匀充分，得到混料；
步骤C，紧接着将具有一定温度的混料投入冷却机中进行冷却，冷却到所需温度后，得到处理后的混料；
步骤D，然后将冷却处理后的混料投入锥形双螺杆挤出机中，再以熔体形式挤出得到半熔融状态的塑料管坯；
步骤E，接着将得到的半熔融状态塑料管坯置入模具中，随即向管坯中通入压缩空气使其膨胀，使得塑料管坯的外壁紧紧贴在模具内壁上，在此过程中，保证模具处于所需温度即可；
步骤F，紧接着停止对模具加热，对经吹胀处理并紧紧贴在模具内壁上的塑料管坯进行冷却操作，冷却一段时间后，再将上压模模具打开，然后取出已形成杯状的半成品放置在空气中自然冷却；
步骤G：最后将完全冷却后的半成品塑料杯多余的边料、边刺切除，在此切除过程中，需要同时对半成品塑料杯进行加水调湿操作，操作结束后即可得到成品塑料杯。
3.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述主料为玉米淀粉、木薯淀粉或竹粉中的一种。
4.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述改性助剂包括增塑剂，增塑剂为柠檬酸酯类增塑剂。
5.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述改性助剂包括偶联剂，偶联剂为硅烷偶联剂。
6.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述改性助剂包括光降解促进剂。
7.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述改性助剂包括抗菌剂，抗菌剂为酸角叶提取液和地榆水浸出液的混合物。
8.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述改性助剂包括流平剂，流平剂为聚醚改质聚硅氧烷。
9.根据权利要求1所述的一种环保可降解塑料杯加工工艺，其特征在于：所述改性助剂包括热稳定剂，热稳定剂为硬脂酸锌。