CN112517904A - 一种强韧减磨零件的制备方法 - Google Patents
一种强韧减磨零件的制备方法 Download PDFInfo
- Publication number
- CN112517904A CN112517904A CN202011361216.2A CN202011361216A CN112517904A CN 112517904 A CN112517904 A CN 112517904A CN 202011361216 A CN202011361216 A CN 202011361216A CN 112517904 A CN112517904 A CN 112517904A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- tough
- following
- steps
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种强韧减磨零件的制备方法,钛粉60‑65份、镁粉15‑20份、二硫化钼10‑15份、碳化硅10‑20份、氯化镓3‑11份、菱镁矿粉10‑15份、纳米氮化硅2‑8份、硼化铪1‑6份、酚醛树脂6‑8份、硒化镉6‑7份、助剂12‑16份,其中助剂由亚麻油、季戊四醇三丙烯酸酯、聚二甲基硅氧烷按照重量比3:5:6组成的。本发明方法制备得到的强韧减磨零件组织致密,微观结构良好,孔隙很少,摩擦系数小,结构刚度、硬度、耐疲劳性能、抗拉强度性能优良,且原料易得、加工成本低,制备工艺简单、参数易控,生产过程安全环保,适合大规模的工业化生产。
Description
技术领域
本发明涉及一种强韧减磨零件的制备方法。
技术背景
减摩材料是一类古老而用途又十分广泛的、机械制造工业中不可缺少的工业用材。减摩材料是用来制造各种耐磨损的滑动轴承、轴瓦、活塞环、滑块、滑板及精密机床导轨等的材料。传统铸造方法和机械加工方法工艺复杂,质量稳定性较差,费料,且无法制备复杂零件。而粉末冶金不受熔炼限制,既可以加入合金成分,也可以加入其它结构组分,并且在相当大的范围内根据要求进行调整,进而在力学性能上能达到与零件匹配的效果。粉末冶金机械化程度高,既能减少人员,又能提高效率,进而节约成本。所以本发明通过优化的原料组合,合理设置配比和生产工艺,设计出一种新的粉末冶金工艺,从而制得强度高、硬度大、耐磨的强韧减磨零件,对延长减磨零件的使用寿命具有重要的意义。
发明内容
本发明的目的在于针对现有技术的不足,提供一种强韧减磨零件的制备方法。
本发明的目的是通过以下技术方案实现的: 一种强韧减磨零件的制备方法,所述方法包括以下步骤:
步骤1、按重量份称取如下原料:铁粉70-90份、电解铜粉60-80份、醇酸树脂12-18份、碳化硅陶瓷粉20-30份、氧化锌粉3-5份、石墨4-6份、雾化锡粉3-6份、二硫化钼1.2-1.4份、硼化二钼1.2-1.4份、航空煤油6-10份、氟化钡2-4份、三盐基硫酸铅1-4份、硬酯酸锌2-3份、聚氧乙烯二胺15-20份、微晶蜡4-6份、杨梅蜡2-3份、铝酸醋偶联剂1-4份、三烯丙基异氰酸酯4-9份、莫来石10-15份、氧化铝2.1-2.5份;
步骤2、将上述粉末按重量份称取后,倒入双锥混料机中,混料筒不断回转使物料翻动,物料在混料筒中分散均匀,然后装入零件模具,压制成坯;
步骤3、将压制坯体于氢气氛中进行烧结,烧结温度为1000-1100℃,烧结压力为1-2MPa,保温时间30-45分钟;
步骤4、将烧结得到的材料在保护气氛下加热,碳势0.75-0.85、淬火温度780-840℃、淬火介质为机械油,然后在280-340℃回火2-3小时得热处理后产品;
步骤5、将热处理后产品真空浸油,油温为80℃-100℃,真空气压值为4-10KPa,浸油时间为30-60分钟,取出后经过磨削加工即得强韧减磨零件。
进一步,按重量份称取如下原料:铁粉80份、电解铜粉70份、醇酸树脂15份、碳化硅陶瓷粉25份、氧化锌粉4份、石墨5份、雾化锡粉3-6份、二硫化钼1.3份、硼化二钼1.3份、航空煤油8份、氟化钡3份、三盐基硫酸铅3份、硬酯酸锌2.5份、聚氧乙烯二胺18份、微晶蜡5份、杨梅蜡2.5份、铝酸醋偶联剂3份、三烯丙基异氰酸酯6份、莫来石13份、氧化铝2.3份。
进一步,所述保护气氛为氢气和氮气按体积比为1:1-3组成的混合气体。
进一步,所述压制压力为450-600MPa,在常温下保压15-30s。
进一步,所述真空浸油处理中的油温为80℃-100℃,真空气压值为4-10KPa,浸油时间为30-60分钟。
本发明具有以下有益效果:本发明方法制备得到的强韧减磨零件组织致密,微观结构良好,孔隙很少,摩擦系数小,结构刚度、硬度、耐疲劳性能、抗拉强度性能优良,且原料易得、加工成本低,制备工艺简单、参数易控,生产过程安全环保,适合大规模的工业化生产。
具体实施方式
实施例1
一种强韧减磨零件的制备方法,所述方法包括以下步骤:
步骤1、按重量份称取如下原料:铁粉70份、电解铜粉60份、醇酸树脂12份、碳化硅陶瓷粉20份、氧化锌粉3份、石墨4份、雾化锡粉3份、二硫化钼1.2份、硼化二钼1.2份、航空煤油6份、氟化钡2份、三盐基硫酸铅1份、硬酯酸锌2份、聚氧乙烯二胺15份、微晶蜡4份、杨梅蜡2份、铝酸醋偶联剂1份、三烯丙基异氰酸酯4份、莫来石10份、氧化铝2.1份;
步骤2、将上述粉末按重量份称取后,倒入双锥混料机中,混料筒不断回转使物料翻动,物料在混料筒中分散均匀,然后装入零件模具,压制成坯,压制压力为450MPa,在常温下保压15s;
步骤3、将压制坯体于氢气氛中进行烧结,烧结温度为1000℃,烧结压力为1MPa,保温时间30分钟;
步骤4、将烧结得到的材料在保护气氛(氢气和氮气按体积比为1:1组成的混合气体)下加热,碳势0.75-0.85、淬火温度780℃、淬火介质为机械油,然后在280℃回火2小时得热处理后产品;
步骤5、将热处理后产品真空浸油,油温为80℃,真空气压值为4KPa,浸油时间为30-60分钟,取出后经过磨削加工即得强韧减磨零件。
实施例2
一种强韧减磨零件的制备方法,所述方法包括以下步骤:
步骤1、按重量份称取如下原料:铁粉80份、电解铜粉70份、醇酸树脂15份、碳化硅陶瓷粉25份、氧化锌粉4份、石墨5份、雾化锡粉3-6份、二硫化钼1.3份、硼化二钼1.3份、航空煤油8份、氟化钡3份、三盐基硫酸铅3份、硬酯酸锌2.5份、聚氧乙烯二胺18份、微晶蜡5份、杨梅蜡2.5份、铝酸醋偶联剂3份、三烯丙基异氰酸酯6份、莫来石13份、氧化铝2.3份;
步骤2、将上述粉末按重量份称取后,倒入双锥混料机中,混料筒不断回转使物料翻动,物料在混料筒中分散均匀,然后装入零件模具,压制成坯,压制压力为550MPa,在常温下保压20s;
步骤3、将压制坯体于氢气氛中进行烧结,烧结温度为1050℃,烧结压力为1.5MPa,保温时间40分钟;
步骤4、将烧结得到的材料在保护气氛(氢气和氮气按体积比为1:2组成的混合气体)下加热,碳势0.75-0.85、淬火温度810℃、淬火介质为机械油,然后在310℃回火2.5小时得热处理后产品;
步骤5、将热处理后产品真空浸油,油温为90℃,真空气压值为7KPa,浸油时间为30-60分钟,取出后经过磨削加工即得强韧减磨零件。
实施例3
一种强韧减磨零件的制备方法,所述方法包括以下步骤:
步骤1、按重量份称取如下原料:铁粉90份、电解铜粉80份、醇酸树脂18份、碳化硅陶瓷粉30份、氧化锌粉5份、石墨6份、雾化锡粉6份、二硫化钼1.4份、硼化二钼1.4份、航空煤油10份、氟化钡4份、三盐基硫酸铅4份、硬酯酸锌3份、聚氧乙烯二胺20份、微晶蜡6份、杨梅蜡3份、铝酸醋偶联剂4份、三烯丙基异氰酸酯9份、莫来石15份、氧化铝2.5份;
步骤2、将上述粉末按重量份称取后,倒入双锥混料机中,混料筒不断回转使物料翻动,物料在混料筒中分散均匀,然后装入零件模具,压制成坯,压制压力为600MPa,在常温下保压30s;
步骤3、将压制坯体于氢气氛中进行烧结,烧结温度为1100℃,烧结压力为2MPa,保温时间45分钟;
步骤4、将烧结得到的材料在保护气氛(氢气和氮气按体积比为1:3组成的混合气体)下加热,碳势0.75-0.85、淬火温度840℃、淬火介质为机械油,然后在340℃回火3小时得热处理后产品;
步骤5、将热处理后产品真空浸油,油温为100℃,真空气压值为10KPa,浸油时间为60分钟,取出后经过磨削加工即得强韧减磨零件。
Claims (5)
1.一种强韧减磨零件的制备方法,其特征在于所述方法包括以下步骤:
步骤1、按重量份称取如下原料:铁粉70-90份、电解铜粉60-80份、醇酸树脂12-18份、碳化硅陶瓷粉20-30份、氧化锌粉3-5份、石墨4-6份、雾化锡粉3-6份、二硫化钼1.2-1.4份、硼化二钼1.2-1.4份、航空煤油6-10份、氟化钡2-4份、三盐基硫酸铅1-4份、硬酯酸锌2-3份、聚氧乙烯二胺15-20份、微晶蜡4-6份、杨梅蜡2-3份、铝酸醋偶联剂1-4份、三烯丙基异氰酸酯4-9份、莫来石10-15份、氧化铝2.1-2.5份;
步骤2、将上述粉末按重量份称取后,倒入双锥混料机中,混料筒不断回转使物料翻动,物料在混料筒中分散均匀,然后装入零件模具,压制成坯;
步骤3、将压制坯体于氢气氛中进行烧结,烧结温度为1000-1100℃,烧结压力为1-2MPa,保温时间30-45分钟;
步骤4、将烧结得到的材料在保护气氛下加热,碳势0.75-0.85、淬火温度780-840℃、淬火介质为机械油,然后在280-340℃回火2-3小时得热处理后产品;
步骤5、将热处理后产品真空浸油处理,取出后经过磨削加工即得强韧减磨零件。
2.根据权利要求1所述的一种强韧减磨零件的制备方法,其特征在于:按重量份称取如下原料:铁粉80份、电解铜粉70份、醇酸树脂15份、碳化硅陶瓷粉25份、氧化锌粉4份、石墨5份、雾化锡粉3-6份、二硫化钼1.3份、硼化二钼1.3份、航空煤油8份、氟化钡3份、三盐基硫酸铅3份、硬酯酸锌2.5份、聚氧乙烯二胺18份、微晶蜡5份、杨梅蜡2.5份、铝酸醋偶联剂3份、三烯丙基异氰酸酯6份、莫来石13份、氧化铝2.3份。
3.根据权利要求1所述的一种强韧减磨零件的制备方法,其特征在于:所述保护气氛为氢气和氮气按体积比为1:1-3组成的混合气体。
4.根据权利要求1所述的一种强韧减磨零件的制备方法,其特征在于:所述压制压力为450-600MPa,在常温下保压15-30s。
5.根据权利要求1所述的一种强韧减磨零件的制备方法,其特征在于:所述真空浸油处理中的油温为80℃-100℃,真空气压值为4-10KPa,浸油时间为30-60分钟。