CN112341928A - 一种水溶性聚氨酯防水涂料及其制备方法 - Google Patents
一种水溶性聚氨酯防水涂料及其制备方法 Download PDFInfo
- Publication number
- CN112341928A CN112341928A CN202011142627.2A CN202011142627A CN112341928A CN 112341928 A CN112341928 A CN 112341928A CN 202011142627 A CN202011142627 A CN 202011142627A CN 112341928 A CN112341928 A CN 112341928A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- waterproof coating
- soluble polyurethane
- polyurethane waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种隔热涂料的制备方法，特别是一种水溶性聚氨酯防水涂料及其制备方法，属于化学组合物及其制备技术领域，水溶性聚氨酯防水涂料，其特征在于，制成该涂料包括以下重量份数的原料：聚氨酯预聚体 40 ‑ 50 份；N‑ 羟甲基丙烯酰胺 1‑2 份；邻苯二甲酸二丁酯 3‑9份；高钛粉8‑ 22 份；消泡剂 0.1 ‑ 0.3 份；竹纤维素3 ‑10 份；混合溶剂 9 ‑ 15 份；所述的混合溶剂是木醇‑芥子醇‑对羟基苯木质素与乙二醇丁醚加水的混合物，重量比例为4:3:10，本发明的有益效果是：耐化学性强、耐温高、耐候性好、耐沾污性好、自洁性强的特点，还保证具有反射、隔热、保温作用功能的材料牢固的粘接在涂料中，延长涂料寿命。
Description
技术领域
本发明涉及一种隔热涂料的制备方法，特别是一种水溶性聚氨酯防水涂料及其制备方法，属于化学组合物及其制备技术领域。
背景技术
建筑节能是我国节能工作的重点之一，而外墙外保温已成为建筑节能的主产品。对于热工设计时以保温为主的地区，如严寒地区和寒冷地区，外墙外保温不仅合理，而且适用，发展较快。而对于热工设计时一般只考虑隔热的夏热冬暖地区，或热工设计时以隔热为主的夏热冬冷地区，目前的一些外墙外保温存在进一步完善的空间。针对不同地区的气候特点，合理选择和使用各种隔热保温涂料，组成复合体系，既保温又隔热，达到室内热环境舒适和节能降耗的目的。
而说到隔热保温涂料，人们还要考虑其耐候性和防污性，因为外墙涂料是与外界大气环境直接接触的，需要经受气候、雨水、紫外线等的挑战，因此需要具备耐酸雨、耐沾污以及易清洗等性能， 目前在建筑防水领域，溶剂型聚氨酯涂料（WPU ）应用比较广泛， 但随着环保的力度的加大，涂料势必要向无溶剂、水性化方向发展。WPU由于引入亲水集团，涂料的耐水性不佳，无法满足建筑防水涂料的需求，所以可以通过改性来提高和改善相应性能。目前公开文献报道了许多改性方法，例如 CN201310545598.8，公开了一种水性聚氨酯丙烯酸酯、水性聚氨酯紫外光固化涂料及其制备方法，解决了现有技术中水性聚氨酯涂料危害环境、不能进行紫外光固化的技术问题， 但要制备一种具有轻质、高耐火、高耐候、环保、不易老化、长效性的外保温隔热的涂料，进而达到建筑节能的目的，还没有很成熟的技术，因此目前人们还在水性涂料方面还在 不断的研究试验。
发明内容
本发明的目的提供一种水溶性聚氨酯防水涂料及其制备方法，该涂料具有隔热效果好、高耐候、环保、不易老化、长效的效果。
本发明是这样实现的 ：水溶性聚氨酯防水涂料，其特征在于，制成该涂料包括以下重量份数的原料 ：聚氨酯预聚体 40 - 50 份 ；N- 羟甲基丙烯酰胺 1-2 份 ；邻苯二甲酸二丁酯 3-9份 ；高钛粉8- 22 份 ；消泡剂 0.1 - 0.3 份 ；竹纤维素3 -10 份 ；混合溶剂 9 - 15 份 ；所述的混合溶剂是木醇-芥子醇-对羟基苯木质素与乙二醇丁醚加水的混合物，重量比例为 4:3:10。
所述的消泡剂是甲基硅油。
所述的高钛粉的二氧化钛纯度在97以上％，通过加入高钛粉，能增强光线的折射与散射。因此，具有较优的反射和隔热性能，还具有很好的光线遮盖效果，从而反射太阳近红外波段，提高太阳热辐射反射，降低太阳热吸收，不让太阳在物体表面累计升温。
本发明所述的水溶性聚氨酯防水涂料，其制备方法包括以下步骤 ： 将N-羟甲基丙烯酰胺与聚氨酯预聚体在反应釜中混合，反应温度 80-150℃，反应2h后加入邻苯二甲酸二丁酯 、高钛粉 、竹纤维素 ；混合溶剂，混合均匀即可得到水溶性聚氨酯防水涂料产品。
本发明所述的水溶性聚氨酯防水涂料，其原料还包括 ：流平剂、抗冻剂和防沉剂中的一种或多种，重量份数为 1-5 ；所述的流平剂是聚丙烯酸酯溶液 ；所述的抗冻剂是1,3- 丙二醇 ；所述的防沉剂是改性聚脲的 N- 甲基吡咯烷酮溶液。
本发明所述的聚氨酯预聚体是以异氰酸酯、聚醚为主要原料，进行聚合而成，带有NCO 端基的预聚体，分子量在 1000-4000 之间，它具有良好的物理性能，粘结力强，常温湿固化。
本发明所述的 N-羟甲基丙烯酰胺，为白色结晶粉末，熔点 74 ～ 75℃， 易溶于水、乙醇，溶于脂肪酸酯类，不溶于烃、卤代烃等疏水性溶剂。当水溶液有酸存在时，加热会迅速聚合成不溶的树脂。由于分子结构中含有聚合性能的乙烯基和缩合性能的羟甲基，因此使线型聚合物交联最为有效。如果与丙烯酸酯类单体共聚合，羟甲基被引入，仅加热即可交联。
本发明所述的邻苯二甲酸二丁酯是一种增塑剂，可使制品具有良好的柔软性，稳定性、耐挠曲性、黏结性和防水性均优于其他增塑剂。
本发明所述的水溶性聚氨酯防水涂料，可以在普通墙体、屋面、钢架 结构、船体或石油储罐涂覆上的应用。
本发明的竹纤维素有较强的耐磨性，具有天然抗菌、抑菌、除螨、防臭和抗紫外线功能。
本发明的有益效果是 ：耐化学性强、耐温高、耐候性好、耐沾污性好、自 洁性强的特点，还保证具有反射、隔热、保温作用功能的材料牢固的粘接在涂料中，延长涂 料寿命。
具体实施方式
实施例 1 ： 聚氨酯预聚体 40份 ；N- 羟甲基丙烯酰胺 1 份 ；邻苯二甲酸二丁酯 3份 ；高钛粉8 份 ；消泡剂 0.1份 ；竹纤维素3 份 ；混合溶剂 9 份 ；所述的混合溶剂是木醇-芥子醇-对羟基苯木质素与乙二醇丁醚加水的混合物，重量比例为 4:3:10，将N-羟甲基丙烯酰胺与聚氨酯预聚体在反应釜中混合，反应温度 80℃，反应2h后加入邻苯二甲酸二丁酯 、高钛粉 、竹纤维素 ；混合溶剂，混合均匀即可得到水溶性聚氨酯防水涂料产品。
实施例 2 ：聚氨酯预聚体 45 份 ；N- 羟甲基丙烯酰胺 1 份 ；邻苯二甲酸二丁酯 6份 ；高钛粉16 份 ；消泡剂 0.2 份 ；竹纤维素6份 ；混合溶剂12 份 ；所述的混合溶剂是木醇-芥子醇-对羟基苯木质素与乙二醇丁醚加水的混合物，重量比例为 4:3:10，将N-羟甲基丙烯酰胺与聚氨酯预聚体在反应釜中混合，反应温度100℃，反应2h后加入邻苯二甲酸二丁酯 、高钛粉 、竹纤维素 ；混合溶剂，混合均匀即可得到水溶性聚氨酯防水涂料产品。
实施例 3 ： 聚氨酯预聚体50 份 ；N- 羟甲基丙烯酰胺2 份 ；邻苯二甲酸二丁酯9份 ；高钛粉 22 份 ；消泡剂0.3 份 ；竹纤维素10 份 ；混合溶剂 15 份 ；所述的混合溶剂是木醇-芥子醇-对羟基苯木质素与乙二醇丁醚加水的混合物，重量比例为 4:3:10，将N-羟甲基丙烯酰胺与聚氨酯预聚体在反应釜中混合，反应温度 150℃，反应2h后加入邻苯二甲酸二丁酯 、高钛粉 、竹纤维素 ；混合溶剂，混合均匀即可得到水溶性聚氨酯防水涂料产品。
Claims (4)
1.一种水溶性聚氨酯防水涂料，其特征在于，制成该涂料包括以下重量份数的原料 ：聚氨酯预聚体 40 - 50 份 ；N- 羟甲基丙烯酰胺 1-2 份 ；邻苯二甲酸二丁酯 3-9份 ；高钛粉8- 22 份 ；消泡剂 0.1 - 0.3 份 ；竹纤维素3 -10 份 ；混合溶剂 9 - 15 份 ；所述的混合溶剂是木醇-芥子醇-对羟基苯木质素与乙二醇丁醚加水的混合物，重量比例为 4:3:10。
2.根据权利要求1所述的一种水溶性聚氨酯防水涂料，其特征在于，所述的消泡剂是甲基硅油。
3.根据权利要求1所述的一种水溶性聚氨酯防水涂料，其特征在于，所述的高钛粉的二氧化钛纯度在97以上％。
4. 一种水溶性聚氨酯防水涂料，其特征在于，制备方法包括以下步骤： 将N-羟甲基丙烯酰胺与聚氨酯预聚体在反应釜中混合，反应温度 80-150℃，反应2h后加入邻苯二甲酸二丁酯 、高钛粉 、竹纤维素 ；混合溶剂，混合均匀即可得到水溶性聚氨酯防水涂料产品。