CN112322023A - Environment-friendly plastic additive and preparation method thereof - Google Patents
Environment-friendly plastic additive and preparation method thereof Download PDFInfo
- Publication number
- CN112322023A CN112322023A CN202011322880.6A CN202011322880A CN112322023A CN 112322023 A CN112322023 A CN 112322023A CN 202011322880 A CN202011322880 A CN 202011322880A CN 112322023 A CN112322023 A CN 112322023A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- stirring
- friendly plastic
- plastic additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of environment-friendly plastics and discloses an environment-friendly plastic additive which comprises the following components in parts by weight: 80-90 parts of aqueous polyurethane dispersion; 20-50 parts of negative ion spraying diluent; 25-40 parts of polyurethane diluent; 2-4 parts of a thickening agent; 2-35 parts of deionized water; 2-20 parts of pigment; 22-35 parts of aqueous polymer emulsion; 20-30 parts of EPDM particles; 10-19 parts of nano silicon dioxide; 3-8 parts of resin liquid; 4-8 parts of chloroprene rubber; 20-25 parts of silicon carbide micro powder. Add pigment and carborundum miropowder after mixing to the mixture, increased the affinity between pigment and the mixture, avoid the later stage to fade, carry out the in-process of rubbing in the finished product later stage, can avoid adsorbing too much particulate matter, at the in-process of retrieving the decomposition, these materials can be absorbed to the inside fertilizer as green plants such as trees of soil after the lateral wall department of soil decomposes, use the environmental protection.
Description
Technical Field
The invention relates to the technical field of environment-friendly plastics, in particular to an environment-friendly plastic additive and a preparation method thereof.
Background
Plastics are applied to various materials, and are very extensive in the use, and it has replaced various glassware's convenient splendid attire etc. also can regard as the support object material to use, under the condition of using, can avoid glassware's breakable sense, compares with the metal material, and the article of plastics material has certain elasticity, can regard as the elasticity to support in some support objects and amusement facilities, not only can regard as safe supporting pad to use, has certain interest in some toys.
The plastics material is after using a period, especially the plastics of using in the concatenation toy, and most lateral walls all can receive wearing and tearing, and are wear-resisting, and at the in-process of using, have certain fading, need retrieve the decomposition, then carry out the shaping again and color, and the extravagant resource is the environmental protection inadequately, and at the in-process of back recovery processing, and traditional plastics material is difficult to decompose, exists in natural environment for a long time, causes the pollution easily, is extremely unfavorable for the environmental protection.
Disclosure of Invention
In order to solve the above problems, the present invention provides the following technical solutions: an environment-friendly plastic additive comprises the following components in percentage by weight: 80-90 parts of aqueous polyurethane dispersion; 20-50 parts of negative ion spraying diluent; 25-40 parts of polyurethane diluent; 2-4 parts of a thickening agent; 2-35 parts of deionized water; 2-20 parts of pigment; 22-35 parts of aqueous polymer emulsion; 20-30 parts of EPDM particles; 10-19 parts of nano silicon dioxide; 3-8 parts of resin liquid; 4-8 parts of chloroprene rubber; 20-25 parts of silicon carbide micro powder.
Preferably, the aqueous polyurethane dispersion includes an organosiloxane and an acrylic emulsion.
Preferably, the polyurethane diluent is mixed with a plasticizer, an antioxidant and an antidote in a ratio of 2:1: 5.
Preferably, the thickener is mixed with an anti-slip layer auxiliary agent: 15-20 parts.
Preferably, the aqueous polymer emulsion is obtained by emulsion polymerization of a silane coupling agent monomer, a lipophilic radical polymerizable monomer, and a hydrophilic radical polymerizable monomer.
Preferably, the resin liquid contains an aqueous resin emulsion: 22-29 parts of propylene carbonate: 10-15 parts of styrene: 4-10 parts of acetone: 3-10 parts.
Preferably, the silicon carbide micropowder is black silicon carbide and has a particle size of 2-6 μm.
According to the environment-friendly plastic additive, a preparation method of the environment-friendly plastic additive is provided, and comprises the following steps:
s1, mixing 80-90 parts of aqueous polyurethane dispersoid, 25-40 parts of polyurethane diluent, 2-35 parts of deionized water and 2-4 parts of thickener, and uniformly stirring for about 60 minutes;
s2, adding 22 to 35 parts of waterborne polymer emulsion, 20 to 30 parts of EPDM particles and 10 to 19 parts of nano silicon dioxide, and stirring for about 30 minutes under the conditions that the vacuum degree is 0.1 to 0.2Mpa and the rotating speed is 40 to 50 rpm;
s3, after stirring, standing for 30 minutes, pouring 10-19 parts of nano silicon dioxide into the air holes after the mixture has air holes, and standing for 10 minutes;
s4, mixing 3-8 parts of resin liquid and 4-8 parts of chloroprene rubber, and stirring to generate bubbles;
s5, adding a mixture of 3-8 parts of resin liquid and 4-8 parts of chloroprene rubber into the solution for fusion and stirring;
s6, uniformly spraying 20-50 parts of negative ion spraying diluent in the process of stirring the mixture;
s7, mixing and stirring 2-20 parts of pigment and 20-25 parts of silicon carbide micro powder, adding into the mixture, and pouring into a mold for molding.
The invention has the beneficial effects that:
1. according to the invention, the pigment and the silicon carbide micro powder are mixed with each other, stirred again and then added into the mixture again, so that the affinity between the pigment and the mixture can be increased, the later fading is avoided, the trouble of recovering and coloring is reduced, and the environment is protected.
2. According to the invention, after the anion spraying diluent and the EPDM particles are mixed, excessive particles can be prevented from being adsorbed in the later friction process of a finished product, so that the object abrasion caused by excessive friction force can be reduced in the using process.
3. According to the invention, various resin materials are added, so that the materials are easy to decompose in the recycling and decomposing process, and can be absorbed into the soil to serve as fertilizer for green plants such as trees after being decomposed at the side wall of the soil, and the problem that plastics are not easy to decompose for a long time and pollute the environment is avoided.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
An environment-friendly plastic additive comprises the following components in percentage by weight: 80-90 parts of aqueous polyurethane dispersion; 20-50 parts of negative ion spraying diluent; 25-40 parts of polyurethane diluent; 2-4 parts of a thickening agent; 2-35 parts of deionized water; 2-20 parts of pigment; 22-35 parts of aqueous polymer emulsion; 20-30 parts of EPDM particles; 10-19 parts of nano silicon dioxide; 3-8 parts of resin liquid; 4-8 parts of chloroprene rubber; 20-25 parts of silicon carbide micro powder.
Wherein the aqueous polyurethane dispersion comprises organosiloxane and acrylic emulsion.
Wherein, the polyurethane diluent is mixed with a plasticizer, an antioxidant and a toxin-proofing agent in a ratio of 2:1: 5.
Wherein, the thickener is mixed with an anti-skid layer auxiliary agent: 15-20 parts.
The aqueous polymer emulsion is obtained by emulsion polymerization of a silane coupling agent monomer, a lipophilic free radical polymerization monomer and a hydrophilic free radical polymerization monomer.
Wherein the resin liquid contains water-based resin emulsion: 22-29 parts of propylene carbonate: 10-15 parts of styrene: 4-10 parts of acetone: 3-10 parts.
Wherein the silicon carbide micropowder is black silicon carbide and has a particle size of 2-6 μm.
The first embodiment is as follows:
an environment-friendly plastic additive and a preparation method thereof, comprising the following steps:
s1, mixing 80-90 parts of aqueous polyurethane dispersoid, 25-40 parts of polyurethane diluent, 2-35 parts of deionized water and 2-4 parts of thickener, and uniformly stirring for about 60 minutes;
s2, adding 22 to 35 parts of waterborne polymer emulsion, 20 to 30 parts of EPDM particles and 10 to 19 parts of nano silicon dioxide, and stirring for about 30 minutes under the conditions that the vacuum degree is 0.1 to 0.2Mpa and the rotating speed is 40 to 50 rpm;
s3, after stirring, standing for 30 minutes, pouring 10-19 parts of nano silicon dioxide into the air holes after the mixture has air holes, and standing for 10 minutes;
s4, mixing 3-8 parts of resin liquid and 4-8 parts of chloroprene rubber, and stirring to generate bubbles;
s5, adding a mixture of 3-8 parts of resin liquid and 4-8 parts of chloroprene rubber into the solution for fusion and stirring;
s6, uniformly spraying 20-50 parts of negative ion spraying diluent in the process of stirring the mixture;
s7, mixing and stirring 2-20 parts of pigment and 20-25 parts of silicon carbide micro powder, adding into the mixture, and pouring into a mold for molding.
Example two:
an environment-friendly plastic additive and a preparation method thereof, comprising the following steps:
s1, mixing 75-85 parts of aqueous polyurethane dispersoid, 20-45 parts of polyurethane diluent, 3-30 parts of deionized water and 3-5 parts of thickener, and uniformly stirring for about 60 minutes;
s2, adding 25 to 40 parts of waterborne polymer emulsion, 15 to 25 parts of EPDM particles and 5 to 15 parts of nano silicon dioxide, and stirring for about 30 minutes under the conditions that the vacuum degree is 0.1 to 0.2Mpa and the rotating speed is 40 to 50 rpm;
s3, after stirring, standing for 30 minutes, pouring 10-19 parts of nano silicon dioxide into the air holes after the mixture has air holes, and standing for 10 minutes;
s4, mixing 2-6 parts of resin liquid and 4-8 parts of chloroprene rubber, and stirring to generate bubbles;
s5, adding a mixture of 2-7 parts of resin liquid and 3-7 parts of chloroprene rubber into the solution for fusion and stirring;
s6, uniformly spraying 20-50 parts of negative ion spraying diluent in the process of stirring the mixture;
s7, mixing and stirring 1-15 parts of pigment and 15-20 parts of silicon carbide micro powder, adding into the mixture, and pouring into a mold for molding.
Example three:
an environment-friendly plastic additive and a preparation method thereof, comprising the following steps:
s1, mixing 85-95 parts of aqueous polyurethane dispersoid, 30-45 parts of polyurethane diluent, 3-40 parts of deionized water and 3-5 parts of thickener, and uniformly stirring for about 60 minutes;
s2, adding 25 to 40 parts of waterborne polymer emulsion, 25 to 35 parts of EPDM particles and 15 to 23 parts of nano silicon dioxide, and stirring for about 30 minutes under the conditions that the vacuum degree is 0.1 to 0.2Mpa and the rotating speed is 40 to 50 rpm;
s3, after stirring, standing for 30 minutes, pouring 15-23 parts of nano silicon dioxide into air holes after the mixture has air holes, and standing for 10 minutes;
s4, mixing 5-10 parts of resin liquid and 5-10 parts of chloroprene rubber, and stirring to generate bubbles;
s5, adding a mixture of 5-10 parts of resin liquid and 5-10 parts of chloroprene rubber into the solution for fusion and stirring;
s6, uniformly spraying 25 to 55 parts of negative ion spraying diluent in the process of stirring the mixture;
s7, mixing and stirring 5-25 parts of pigment and 25-30 parts of silicon carbide micro powder, adding into the mixture, and pouring into a mold for molding.
Example four:
an environment-friendly plastic additive and a preparation method thereof, comprising the following steps:
s1, mixing 75-95 parts of aqueous polyurethane dispersoid, 20-45 parts of polyurethane diluent, 1-40 parts of deionized water and 1-5 parts of thickener, and uniformly stirring for about 60 minutes;
s2, adding 20 to 40 parts of waterborne polymer emulsion, 15 to 35 parts of EPDM particles and 8 to 22 parts of nano silicon dioxide, and stirring for about 30 minutes under the conditions that the vacuum degree is 0.1 to 0.2Mpa and the rotating speed is 40 to 50 rpm;
s3, after stirring, standing for 30 minutes, pouring 8-23 parts of nano silicon dioxide into air holes after the mixture has air holes, and standing for 10 minutes;
s4, mixing 5-10 parts of resin liquid and 3-10 parts of chloroprene rubber, and stirring to generate bubbles;
s5, adding a mixture of 2-10 parts of resin liquid and 3-10 parts of chloroprene rubber into the solution for fusion and stirring;
s6, uniformly spraying 15-55 parts of negative ion spraying diluent in the process of stirring the mixture;
s7, mixing and stirring 1-15 parts of pigment and 15-30 parts of silicon carbide micro powder, adding into the mixture, and pouring into a mold for molding.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be able to cover the technical scope of the present invention and the equivalent alternatives or modifications according to the technical solution and the inventive concept of the present invention within the technical scope of the present invention.
Claims (8)
1. An environment-friendly plastic additive is characterized in that: the formula comprises the following components in percentage by weight:
80-90 parts of aqueous polyurethane dispersion;
20-50 parts of negative ion spraying diluent;
25-40 parts of polyurethane diluent;
2-4 parts of a thickening agent;
2-35 parts of deionized water;
2-20 parts of pigment;
22-35 parts of aqueous polymer emulsion;
20-30 parts of EPDM particles;
10-19 parts of nano silicon dioxide;
3-8 parts of resin liquid;
4-8 parts of chloroprene rubber;
20-25 parts of silicon carbide micro powder.
2. The environment-friendly plastic additive as claimed in claim 1, wherein: the aqueous polyurethane dispersion includes an organosiloxane and an acrylic emulsion.
3. The environment-friendly plastic additive as claimed in claim 1, wherein: the polyurethane diluent is mixed with a plasticizer, an antioxidant and an antidote in a ratio of 2:1: 5.
4. The environment-friendly plastic additive as claimed in claim 1, wherein: the thickener is mixed with an anti-skid layer auxiliary agent: 15-20 parts.
5. The environment-friendly plastic additive as claimed in claim 1, wherein: the aqueous polymer emulsion is obtained by emulsion polymerization of a silane coupling agent monomer, a lipophilic free radical polymerization monomer and a hydrophilic free radical polymerization monomer.
6. The environment-friendly plastic additive as claimed in claim 1, wherein: the resin liquid contains aqueous resin emulsion: 22-29 parts of propylene carbonate: 10-15 parts of styrene: 4-10 parts of acetone: 3-10 parts.
7. The environment-friendly plastic additive as claimed in claim 1, wherein: the silicon carbide micro powder is black silicon carbide and has the particle size of 2-6 mu m.
8. The environment-friendly plastic additive according to claim 1, wherein the preparation method of the environment-friendly plastic additive is characterized by comprising the following steps:
s1, mixing 80-90 parts of aqueous polyurethane dispersoid, 25-40 parts of polyurethane diluent, 2-35 parts of deionized water and 2-4 parts of thickener, and uniformly stirring for about 60 minutes;
s2, adding 22 to 35 parts of waterborne polymer emulsion, 20 to 30 parts of EPDM particles and 10 to 19 parts of nano silicon dioxide, and stirring for about 30 minutes under the conditions that the vacuum degree is 0.1 to 0.2Mpa and the rotating speed is 40 to 50 rpm;
s3, after stirring, standing for 30 minutes, pouring 10-19 parts of nano silicon dioxide into the air holes after the mixture has air holes, and standing for 10 minutes;
s4, mixing 3-8 parts of resin liquid and 4-8 parts of chloroprene rubber, and stirring to generate bubbles;
s5, adding a mixture of 3-8 parts of resin liquid and 4-8 parts of chloroprene rubber into the solution for fusion and stirring;
s6, uniformly spraying 20-50 parts of negative ion spraying diluent in the process of stirring the mixture;
s7, mixing and stirring 2-20 parts of pigment and 20-25 parts of silicon carbide micro powder, adding into the mixture, and pouring into a mold for molding.