CN112194424A - 一种具有较高抗折强度的超高性能混凝土及其制备方法 - Google Patents
一种具有较高抗折强度的超高性能混凝土及其制备方法 Download PDFInfo
- Publication number
- CN112194424A CN112194424A CN202010685278.2A CN202010685278A CN112194424A CN 112194424 A CN112194424 A CN 112194424A CN 202010685278 A CN202010685278 A CN 202010685278A CN 112194424 A CN112194424 A CN 112194424A
- Authority
- CN
- China
- Prior art keywords
- parts
- ultra
- mass
- high performance
- performance concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种超高性能混凝土,按质量份计,原料包括:水泥550~850份,硅灰150~250份,超细粉煤灰100~300份,水150~300份,聚羧酸减水剂10~30份,细砂1000~1500份,超细钢纤维150~250份;其中所述水泥、硅灰和超细粉煤灰为混凝土胶凝材料;所述原料还包括环氧树脂E‑51、固化剂H103B和活性稀释剂,所述环氧树脂E‑51的质量为所述混凝土胶凝材料总质量的8~20%,所述环氧树脂E‑51和固化剂H103B的质量比为4:1,所述环氧树脂E‑51和所述活性稀释剂的质量比为4~5:1。本发明所述超高性能混凝土的60天折压比可以达到0.14左右。
Description
技术领域
本发明属于工程材料技术领域,具体涉及一种新型的超高性能混凝土及其制备方法。
背景技术
超高性能混凝土(Ultra-High Performance Concrete,简称UHPC),又称为活性粉末混凝土(RPC,Reactive Powder Concrete),是过去三十年来最具创新的水泥基工程材料,实现了工程材料性能的大跨越。适当配筋的UHPC力学性能接近钢材料;同时UHPC具有优良的抗碳化、抗冻融、抗侵蚀、抗渗能力、耐磨、抗爆性能。因此,UHPC特别适用于大跨径桥梁、抗爆结构(如军事工程、银行金库等)和薄壁结构,以及用于高磨蚀、高腐蚀环境中。在原料组成上UHPC与普通混凝土或高性能混凝土不同的方面包括:不使用粗骨料,必须使用硅灰和纤维(钢纤维或复合有机纤维),水泥用量较大,水胶比很低。UHPC的基本组成见表1所示。
表1超高性能混凝土UHPC(钢纤维)基本组成
以目前的技术手段,UHPC抗压强度一般都能达到120~180MPa,通过特殊手段成型的UHPC抗压强度最高甚至已达到800MPa。但是一般的UHPC的抗折强度(又称为“断裂模量”)仅7.5~15MPa。因此,抗折强度是制约UHPC应用范围的一个重要因素。为了提高UHPC的抗折强度,较为普遍的做法是提高超细钢纤维掺量或者多重纤维混掺。例如公开号CN101560082A(公开日2009年10月21日)、名称为“超高强活性粉末混凝土及其制造方法”的中国发明专利申请,公开了一种超高强活性粉末混凝土,以质量份数计,原料组成为:硅酸盐水泥1000份,石英砂600~1400份,硅灰90~400份,硅微粉200~400份,石英粉100~300份,高强钢纤维80~350份、高效减水剂15~30份,AEA膨胀剂60~120份、消泡剂0~2份和水250~350份。但是该发明说明书公开的实施例中,所述超高强活性粉末混凝土的高强钢纤维含量在约2%~10%之间变化,与此同时抗折强度在25MPa~100MPa,抗压强度在180MPa~500MPa,折压比(抗折强度/抗压强度)在0.09~0.2之间变化。该发明的高强钢纤维含量与混凝土的抗折强度、抗压强度和折压比之间没有相关性。如实施例8,高强钢纤维350份(占比9.9%),抗折强度仅37MPa,折压比0.106。经发明人试验研究发现,当钢纤维掺量达到9.9%时,混凝土基本没有工作性可言,施工性能极差,无法实际应用。因此,该发明的技术方案对实际生产中如何提高UPHC的抗折强度和折压比缺乏指导意义。
现有技术中还出现了在UPHC中添加聚合物乳液,在混凝土内部形成连续致密的高分子涂膜,填充在混凝土内部的微裂纹、孔隙以及钢纤维表面留下的孔隙通道,从而有效地提高了混凝土的性能。所述聚合物乳液包括水性环氧树脂乳液、苯丙乳液、丁苯乳液、丁二烯~苯乙烯共聚乳液等等。如公开号为CN108358566A的中国发明专利申请(公开日2018年8月3日)“一种超高性能混凝土及其制造方法”,公开的超高性能混凝土包括:水泥500~850kg/m3、粉煤灰50~150kg/m3、硅灰80~150kg/m3、砂1000~1300kg/m3、钢纤维80~160kg/m3、聚合物乳液20~60kg/m33、水160~180kg/m3、减水剂30~40kg/m3、成膜助剂0.1~1kg/m3,其中聚合物乳液为丁二烯~苯乙烯共聚乳液、乙烯~醋酸乙烯共聚物乳液、丙烯酸酯共聚物乳液、苯丙乳液、丁苯乳液中的一种或两种以上组合,所述成膜助剂为醇类、或醇脂类、或醇醚类。该发明的超高性能混凝土,除了使用聚合物乳液外,还采用了较大掺量的钢纤维,虽然该混凝土的抗氯离子渗透等抗渗性能得到提升,但是混凝土的成本大幅度上升,且其28天抗压强度仅148MPa。
发明内容
为了克服现有技术的不足,本发明提供一种新的超高性能混凝土及其制备方法。本发明的超高性能混凝土具有较高抗折强度,混凝土的工作性基本不受影响,且成本相对低廉。
为了实现上述发明目的,本发明采用了如下的技术方案:
一种超高性能混凝土,按质量份计,原料包括:
水泥550~850份,硅灰150~250份,超细粉煤灰100~300份,水150~300份,聚羧酸减水剂10~30份,细砂1000~1500份,超细钢纤维150~250份;其中所述水泥、硅灰和超细粉煤灰为混凝土胶凝材料;
所述原料还包括环氧树脂E-51、固化剂H103B和活性稀释剂,所述环氧树脂E-51的质量为所述混凝土胶凝材料总质量的8~20%,所述环氧树脂E-51和固化剂H103B的质量比为4:1,所述环氧树脂E-51和所述活性稀释剂的质量比为4~5:1。
优选地,水泥的质量份为650份。
进一步优选地,所述水泥为PII52.5硅酸盐水泥。
优选地,所述硅灰的质量份为250份。
进一步优选地,所述硅灰中二氧化硅含量>95%,比表面积约为19m2/g,经45μm方孔筛筛余率≤3%。
优选地,所述超细粉煤灰的质量份为100份。
优选地,水的质量份为200份。
优选地,所述聚羧酸减水剂的质量份为15份。
优选地,所述细河砂的质量份为1000份。
进一步优选地,所述细河砂为最大粒径不大于1mm的天然河砂或石英砂。
优选地,所述超细钢纤维的质量份为150份。
进一步优选地,所述超细钢纤维为超细镀铜钢纤维,直径为0.15mm~0.2mm,长度为10mm~15mm。
优选地,所述活性稀释剂为N-丁基缩水甘油醚(BGE)。
本发明还有一个目的在于提供上述超高性能混凝土的制备方法,包括如下步骤:
I.按照配比制备好原料中的各组分;
II.将水泥、细河砂、硅灰、超细粉煤灰加入搅拌设备中搅拌2~5分钟,使之均匀;然后加入环氧树脂E-51、固化剂H103B和活性稀释剂搅拌1~3分钟;再将聚羧酸减水剂和水混合好后加入所述搅拌设备中搅拌2~5分钟,最后倒入超细钢纤维搅拌2~5分钟,得到搅拌好的混凝土浆体;
III.将步骤II得到的所述混凝土浆体通过浇注方式置于模具中成型;
IV.放入标准养护室带模养护28天,然后拆模,或拆模后养护28天。
所述步骤IV中,优选带模养护28天。
本发明在UHPC的原料中掺入水性环氧树脂E-51以及固化剂和活性稀释剂,显著提高了UHPC的抗折强度。原因在于:UHPC水化反应大量消耗掉了内部水分,促进了水性环氧树脂与固化剂的固化反应,环氧树脂在固化剂及活性稀释剂作用下能够短时间内在UHPC内部形成均匀且较高强度的聚合物网络结构,从而有效且快速的提高UHPC的抗折强度。虽然抗折强度提高,但是本发明所述水性环氧树脂组合物(环氧树脂E-51、固化剂和活性稀释剂的组合)的掺入对UHPC工作性影响较小。
本发明提供的UPHC,其中的硅灰能够有效改善混凝土孔结构,减少UHPC内部缺陷,提高混凝土的抗酸盐侵蚀和抗磨蚀性。
具体实施方式
以下参照具体的实施例来说明本发明。本领域技术人员能够理解,这些实施例仅用于说明本发明,其不以任何方式限制本发明的范围。
下述实施例中的实验方法,如无特殊说明,均为常规方法。下述实施例中所用的原料、试剂材料等,如无特殊说明,均为市售购买的符合有关标准和规定的产品。
实施例1一种超高性能混凝土
本实施例所述超高性能混凝土的原料组成,见表2所示;按照如下方法制备:
I.按照配比制备好原料中的各组分;
II.将水泥、细河砂、硅灰、超细粉煤灰加入搅拌设备中搅拌2~5分钟,使之均匀;然后加入环氧树脂E-51、固化剂和活性稀释剂搅拌1~3分钟;再将聚羧酸减水剂和水混合好后加入所述搅拌设备中搅拌2~5分钟,最后倒入超细钢纤维搅拌2~5分钟,得到搅拌好的混凝土浆体;
III.将步骤II得到的所述混凝土浆体通过浇注方式置于尺寸为40mm×40mm×160mm钢模中成型;
IV.放入标准养护室带模养护28天,拆模,即得。
实施例2~5一种超高性能混凝土
实施例2~5所述超高性能混凝土的原料组成,见表2所示;参照实施例1的方法制备。
测试例实施例1~5的超高性能混凝土的性能测定
按照《GB50081普通混凝土力学性能试验方法标准》的规定测定实施例1~5制备得到的超高性能混凝土的各项性能,结果见表2。
表2实施例1~5的超高性能混凝土的原料组成及性能测定结果(1份=1kg)
对比例1一种混凝土
本对比例所述的混凝土的原料组成与实施例1的基本相同,不同之处在于:
水性环氧树脂:广州东凤化工有限公司生产的水性环氧树脂E-44,固含量为60%;
固化剂:广州东风化工有限公司生产的水性胺类固化剂DFG-190;
活性稀释剂:无。
按照实施例1相同的步骤制备混凝土,但是出现混凝土无法拌和的现象,混凝土制备失败。
对比例2一种混凝土
本对比例所述的混凝土的原料组成与实施例1的基本相同,不同之处在于:
环氧树脂E-51的用量为64kg,
固化剂的用量为16kg,
活性稀释剂的用量为16kg。
按照实施例1相同的步骤制备混凝土,拆模后测定抗折强度(60天)、抗压强度(60天),计算折压比。结果如下:
60天抗折强度:28.7MPa,60天抗压强度:224.3MPa,折压比:0.128。
对比例3一种混凝土
本对比例所述的混凝土的原料组成与实施例1的基本相同,不同之处在于:
环氧树脂E-51的用量为160kg,
固化剂H103B的用量为40kg,
活性稀释剂BGE的用量为40kg。
按照实施例1相同的步骤制备混凝土,结果混凝土无法拌和,失去工作性,制备失败。
Claims (10)
1.一种超高性能混凝土,按质量份计,原料包括:
水泥550~850份,硅灰150~250份,超细粉煤灰100~300份,水150~300份,聚羧酸减水剂10~30份,细砂1000~1500份,超细钢纤维150~250份;其中所述水泥、硅灰和超细粉煤灰为混凝土胶凝材料;
所述原料还包括环氧树脂E-51、固化剂H103B和活性稀释剂,所述环氧树脂E-51的质量为所述混凝土胶凝材料总质量的8~20%,所述环氧树脂E-51和固化剂H103B的质量比为4:1,所述环氧树脂E-51和所述活性稀释剂的质量比为4~5:1。
2.根据权利要求1所述的超高性能混凝土,其特征在于,水泥的质量份为650份;
进一步优选地,所述水泥为PII52.5硅酸盐水泥。
3.根据权利要求1或2所述的超高性能混凝土,其特征在于,所述硅灰的质量份为250份;
进一步优选地,所述硅灰中二氧化硅含量>95%,比表面积约为19m2/g,经45μm方孔筛筛余率≤3%。
4.根据权利要求1至3中任一项所述的超高性能混凝土,其特征在于,所述超细粉煤灰的质量份为100份。
5.根据权利要求1至4中任一项所述的超高性能混凝土,其特征在于,水的质量份为200份。
6.根据权利要求1至5中任一项所述的超高性能混凝土,其特征在于,所述聚羧酸减水剂的质量份为15份。
7.根据权利要求1至6中任一项所述的超高性能混凝土,其特征在于,所述细河砂的质量份为1000份;
进一步优选地,所述细河砂为最大粒径不大于1mm的天然河砂或石英砂。
8.根据权利要求1至7中任一项所述的超高性能混凝土,其特征在于,所述超细钢纤维的质量份为150份;
进一步优选地,所述超细钢纤维为超细镀铜钢纤维,直径为0.15mm~0.2mm,长度为10mm~15mm。
9.根据权利要求1至8中任一项所述的超高性能混凝土,其特征在于,所述活性稀释剂为N-丁基缩水甘油醚。
10.权利要求1至9中任一项所述超高性能混凝土的制备方法,包括如下步骤:
I.按照配比制备好原料中的各组分;
II.将水泥、细河砂、硅灰、超细粉煤灰加入搅拌设备中搅拌2~5分钟,使之均匀;然后加入环氧树脂E-51、固化剂H103B和活性稀释剂搅拌1~3分钟;再将聚羧酸减水剂和水混合好后加入所述搅拌设备中搅拌2~5分钟,最后倒入超细钢纤维搅拌2~5分钟,得到搅拌好的混凝土浆体;
III.将步骤II得到的所述混凝土浆体通过浇注方式置于模具中成型;
IV.放入标准养护室带模养护28天,然后拆模,或拆模后养护28天;
所述步骤IV中,优选带模养护28天。