CN112159175A - 一种双组分保温砂浆、制备方法及其保温构造 - Google Patents
一种双组分保温砂浆、制备方法及其保温构造 Download PDFInfo
- Publication number
- CN112159175A CN112159175A CN202011045206.8A CN202011045206A CN112159175A CN 112159175 A CN112159175 A CN 112159175A CN 202011045206 A CN202011045206 A CN 202011045206A CN 112159175 A CN112159175 A CN 112159175A
- Authority
- CN
- China
- Prior art keywords
- component
- mortar
- heat
- thermal insulation
- insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种双组分保温砂浆、制备方法及其保温构造。这种双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:(2.5~4);甲组分包括:乳液5.0~20.0%、轻骨料20.0~35.0%、羟乙基纤维素醚0.2~0.5%、润湿分散剂0~0.2%、成膜助剂0~1.0%、纤维0.2~3.0%、防腐杀菌剂0.05~0.15%和余量水;乙组分为硅酸盐水泥。这种双组分保温砂浆的保温构造,基层墙体外表面由里向外依次设置有双组分保温砂浆层、柔性腻子层和涂料饰面层,柔性腻子层内嵌设有耐碱玻纤网。本发明制备的双组分保温砂浆的导热系数为0.055W/(m·K)以下,保温性能良好;干燥硬化时间短,上墙后1天即可进行第二遍施工,利于现场工人施工操作;本发明的保温构造,施工方便,保温性能好。
Description
技术领域
本发明涉及建筑用砂浆技术领域,尤其是一种双组分保温砂浆、制备方法及其保温构造。
背景技术
在国家节能政策的引导下,各省、市相继出台了建筑节能的地方法规,对建筑外墙外保温***实行强制推广政策,使得外墙外保温用商品砂浆得到了广泛的应用。其中的保温沙浆,由于具有不可燃性,施工方便,使用寿命长,已经得到了广泛的应用。随着城市建筑行业的快速发展和人民生活水平的日益提高,人们对保温砂浆的性能要求越来越高。作为建筑保温材料,保温砂浆从过去一直在使用,但是实际使用过程中仍存在保温隔热效果不尽如意的缺点,限制了其使用范围。
传统水泥基无机保温砂浆干燥硬化时间短,上墙后1天即可进行第二遍施工,但是传统无机保温砂浆一般导热系数在0.07W/(m·K)以上,保温性能差。
目前市场上一些单组份无机保温膏料一般用于外墙内保温,虽然导热系数也可以降低到0.06W/(m·K)以下,但是干燥硬化时间很长,一般上墙后要5天以上才可以进行第二遍施工,不利于现场工人施工操作;另外单组份无机保温膏料包含有灰钙,生产好了保质期只有2周左右,时间长了会硬化影响使用。
200710202196.2公开的一种双组分无机保温砂浆及其保温***和施工方法,包括粉体胶凝材料和玻化中空微珠,粉体胶凝材料包括可再分散乳胶粉、纤维、甲基纤维素醚和引气剂,其保温***包括基层墙体,基层墙体外表面由里向外依次设置有双组分玻化中空微珠保温砂浆层、抗裂砂浆层、耐碱玻纤网和饰面层。该专利双组分中甲组份(粉体胶凝材料)主要由可再分散乳胶粉组成,乙组分(玻化中空微珠)为轻骨料,这个体系现场加水搅拌后靠的是胶粉失水成膜将玻化中空微珠胶结在一起,由于这个体系中不含水泥、灰钙这种无机胶凝材料,单独靠可再分散乳胶粉失水成膜形成强度,这个体系可再分散乳胶粉掺量较高,价格贵,且单次粉刷厚度不能厚,干燥硬化时间很长(长于上述乳液+灰钙体系的无机保温膏料),性价比差且不利于施工控制。
发明内容
本发明要解决的技术问题是:克服现有技术中之不足,提供一种双组分保温砂浆、制备方法及其保温构造。
本发明解决其技术问题所采用的技术方案是:一种双组分保温砂浆,该双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:(2.5~4);
所述甲组分包括如下质量百分比的原料:
所述乙组分为硅酸盐水泥。
双组分中甲组份是乳液+轻骨料+助剂+水的膏状体系,乙组分是硅酸盐水泥,现场两个组分搅拌混合后,乳液失水成膜和水泥水化两个体系共同作用,水泥水化形成水化产物对轻骨料进行包裹,形成轻质高强的结构,同时乳液失水形成连续的膜,对体系的孔隙进行填充和包裹,通过两种胶结体系共同对轻骨料进行包裹,使得材料达到较佳的力学性能和热工性能,同时由于乳液形成了连续的膜还使得材料具备较好的憎水性和柔性。
助剂中羟乙基纤维素醚起增加体系粘度改善施工性的作用,润湿分散剂可以避免乳液成膜时表面结皮的情况发生,成膜助剂促进乳液成膜,纤维起到抗裂和增加触变性的作用,防腐剂主要防止膏状材料变质。
进一步地,所述甲组分中乳液为丙烯酸乳液或苯丙乳液。
进一步地,所述甲组分中轻骨料为玻化微珠、膨胀珍珠岩、气凝胶中的一种或多种。
进一步地,所述甲组分中纤维为矿物纤维、聚酯纤维和聚丙烯纤维中的一种或多种。
一种双组分保温砂浆的制备方法,具有以下步骤:
(1)、甲组分制备
a、将羟乙基纤维素醚在搅拌状态下加入水中预溶,预溶浓度5%左右,待羟乙基纤维素醚完全溶液成凝胶状后待用;
b、将乳液、预溶好的羟乙基纤维素醚、润湿分散剂、成膜助剂、防腐杀菌剂、纤维加入水中并充分搅拌均匀;
c、加入轻骨料搅拌均匀,包装得到甲组分成品;
(2)、乙组分为硅酸盐水泥单独包装;
(3)、工地现场将乙组分按比例加入甲组份中,搅拌均匀即可使用。
一种双组分保温砂浆的保温构造,基层墙体外表面由里向外依次设置有双组分保温砂浆层、柔性腻子层和涂料饰面层,柔性腻子层内嵌设有耐碱玻纤网。
本发明的有益效果是:本发明结构简单,设计合理,具有以下优点:
(1)、本发明制备的双组分保温砂浆的导热系数为0.055W/(m·K)以下,保温性能良好,材料柔性好,吸水率、粘结强度等性能也优良;干燥硬化时间短,上墙后1天即可进行第二遍施工,利于现场工人施工操作;
(2)、本发明中甲组份是乳液体系的膏状物,到现场直接水泥加进去搅拌即可,不要再加水,质量可控;
(3)、本发明中硅酸盐水泥和乳液的作用均为胶结材料,乳液失水成膜和水泥水化两个体系共同作用,使得双组分保温砂浆导热系数低、柔性好、吸水率低,且抗压强度高;
(4)、本发明制备的双组分保温砂浆保质期长;
(5)、本发明的保温构造具有基层墙体、双组分保温砂浆层、柔性腻子层和涂料饰面层,结构简单,施工方便,保温性能好。
附图说明
下面结合附图和实施例对本发明进一步说明。
图1是本发明中保温构造的结构示意图;
图中:1.基层墙体,2.双组分保温砂浆层,3.柔性腻子层,4.耐碱玻纤网,5.涂料饰面层。
具体实施方式
现在结合附图和优选实施例对本发明作进一步详细的说明。这些附图均为简化的示意图,仅以示意方式说明本发明的基本结构,因此其仅显示与本发明有关的构成。
实施例1
一种双组分保温砂浆,该双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:2.5;
甲组分包括如下质量百分比的原料:
乙组分为硅酸盐水泥。
一种双组分保温砂浆的制备方法,具有以下步骤:
(1)、甲组分制备
a、将羟乙基纤维素醚在搅拌状态下加入水中预溶,预溶浓度5%左右,待羟乙基纤维素醚完全溶液成凝胶状后待用;
b、将乳液、预溶好的羟乙基纤维素醚、润湿分散剂、成膜助剂、防腐杀菌剂、纤维加入水中并充分搅拌均匀;
c、加入轻骨料搅拌均匀,包装得到甲组分成品;
(2)、乙组分为硅酸盐水泥单独包装;
(3)、工地现场将乙组分按比例加入甲组份中,搅拌均匀即可使用。
如图1所示的一种双组分保温砂浆的保温构造,包括基层墙体1,基层墙体1外表面由里向外依次设置有双组分保温砂浆层2、柔性腻子层3和涂料饰面层5,柔性腻子层3内嵌设有耐碱玻纤网4。
实施例2
一种双组分保温砂浆,与实施例1不同之处在于,该双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:2.8;
甲组分包括如下质量百分比的原料:
实施例3
一种双组分保温砂浆,与实施例1不同之处在于,该双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:3.25;
甲组分包括如下质量百分比的原料:
实施例4
一种双组分保温砂浆,与实施例1不同之处在于,该双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:3.6;
甲组分包括如下质量百分比的原料:
实施例5
一种双组分保温砂浆,与实施例1不同之处在于,该双组分保温砂浆由甲组分和乙组分组成,质量配比为甲组分:乙组分=10:4;
甲组分包括如下质量百分比的原料:
实施例1~5制得的双组分保温砂浆、传统无机保温砂浆以及无机保温膏料(灰钙体系)的性能参数如表1所示。
表1实施例、传统无机保温砂浆以及无机保温膏料的性能参数
综上所述,本发明结构简单,设计合理,具有以下优点:
(1)、本发明制备的双组分保温砂浆的导热系数为0.055W/(m·K)以下,保温性能良好,材料柔性好,吸水率、粘结强度等性能也优良;干燥硬化时间短,上墙后1天即可进行第二遍施工,利于现场工人施工操作;
(2)、本发明中甲组份是乳液体系的膏状物,到现场直接水泥加进去搅拌即可,不要再加水,质量可控;
(3)、本发明中硅酸盐水泥和乳液的作用均为胶结材料,乳液失水成膜和水泥水化两个体系共同作用,使得双组分保温砂浆导热系数低、柔性好、吸水率低,且抗压强度高;
(4)、本发明制备的双组分保温砂浆保质期长;
(5)、本发明的保温构造具有基层墙体、双组分保温砂浆层、柔性腻子层和涂料饰面层,结构简单,施工方便,保温性能好。
以上说明书中描述的只是本发明的具体实施方式,各种举例说明不对本发明的实质内容构成限制,所属技术领域的普通技术人员在阅读了说明书后可以对以前所述的具体实施方式做修改或变形,而不背离发明的实质和范围。
Claims (6)
2.根据权利要求1所述的双组分保温砂浆,其特征在于:所述甲组分中乳液为丙烯酸乳液或苯丙乳液。
3.根据权利要求1所述的双组分保温砂浆,其特征在于:所述甲组分中轻骨料为玻化微珠、膨胀珍珠岩、气凝胶中的一种或多种。
4.根据权利要求1所述的双组分保温砂浆,其特征在于:所述甲组分中纤维为矿物纤维、聚酯纤维和聚丙烯纤维中的一种或多种。
5.一种如权利要求1~4任一项所述双组分保温砂浆的制备方法,其特征在于:具有以下步骤:
(1)、甲组分制备
a、将羟乙基纤维素醚在搅拌状态下加入水中预溶,预溶浓度5%左右,待羟乙基纤维素醚完全溶液成凝胶状后待用;
b、将乳液、预溶好的羟乙基纤维素醚、润湿分散剂、成膜助剂、防腐杀菌剂、纤维加入水中并充分搅拌均匀;
c、加入轻骨料搅拌均匀,包装得到甲组分成品;
(2)、乙组分为硅酸盐水泥单独包装;
(3)、工地现场将乙组分按比例加入甲组份中,搅拌均匀即可使用。
6.一种应用权利要求1~4任一项所述双组分保温砂浆的保温构造,其特征在于:包括基层墙体,基层墙体外表面由里向外依次设置有双组分保温砂浆层、柔性腻子层和涂料饰面层,柔性腻子层内嵌设有耐碱玻纤网。