CN112144283A - Preparation method of moisture-absorbing and sweat-releasing fabric - Google Patents
Preparation method of moisture-absorbing and sweat-releasing fabric Download PDFInfo
- Publication number
- CN112144283A CN112144283A CN202011038147.1A CN202011038147A CN112144283A CN 112144283 A CN112144283 A CN 112144283A CN 202011038147 A CN202011038147 A CN 202011038147A CN 112144283 A CN112144283 A CN 112144283A
- Authority
- CN
- China
- Prior art keywords
- sweat
- moisture
- fabric
- absorbing
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a moisture-absorbing and sweat-releasing fabric, which comprises the following steps: 1) selecting 65-70% of nano modified cotton fiber and 30-35% of special-shaped polyester fiber with grooves, and weaving the nano modified cotton fiber and the special-shaped polyester fiber into base cloth on an air jet loom by adopting a twill weave method of warp and weft interweaving; the nanometer modified cotton fiber is prepared by activating cotton fiber with alkali solution, soaking in chitosan oligosaccharide solution, heating, oscillating, taking out, and vacuum drying; 2) carrying out deoiling and desizing treatment; 3) dyeing the base cloth treated in the step 2); 4) drying, tentering and shaping; 5) preparing mixed finishing liquor; 6) and (5) performing after-treatment on the fabric treated in the step 5). The process is simple and ingenious, is easy to control, can meet the requirements of the market on moisture-absorbing and sweat-releasing fabrics, particularly the requirements of outdoor wearing clothes such as police suits, sports suits and the like, is high in comfort and good in practicability, and is worthy of popularization.
Description
Technical Field
The invention relates to a preparation method of moisture-absorbing and sweat-releasing fabric.
Background
In recent years, with the development of economy and the continuous improvement of the living standard of people, people also put forward higher requirements on the aspect of wearing clothes, and the high-grade and comfortable fabrics are pursued more and more. And with the increasing severity of the global warming phenomenon, the fabric with comfortable air permeability and sweat releasing functions is very important. At present, garment materials are divided into two types, one type is natural fibers mainly made of cotton fibers, the natural fibers are good in moisture absorption and comfortable to wear, but the moisture diffusion speed is low, so that a wet and cold feeling is easily caused, the other type is synthetic fibers mainly made of terylene, the synthetic fibers are small in moisture absorption, poor in air permeability and easy to generate static electricity, and the moisture diffusion speed is high. Therefore, the fabric which is comfortable to absorb moisture, sweat and cool is difficult to obtain by simply depending on the traditional fiber, the dyeing and finishing process of the current moisture-absorbing and sweat-releasing fabric is not mature, and the moisture-absorbing and sweat-releasing effect is not obvious.
Disclosure of Invention
Aiming at the technical problems, the invention provides a preparation method of moisture-absorbing and sweat-releasing fabric.
In order to achieve the technical purpose, the invention adopts the following technical scheme:
the preparation method of the moisture-absorbing and sweat-releasing fabric comprises the following steps:
1) selecting 65-70% of nano modified cotton fiber and 30-35% of special-shaped polyester fiber with grooves, and weaving the nano modified cotton fiber and the special-shaped polyester fiber into base cloth on an air jet loom by adopting a twill weave method of warp and weft interweaving; the nanometer modified cotton fiber is prepared by activating cotton fiber with alkali solution, soaking in chitosan oligosaccharide solution, heating, oscillating, taking out, and vacuum drying;
2) adding a deoiling agent and a desizing agent to carry out deoiling and desizing treatment on the base cloth, wherein the base cloth is subjected to desizing treatment by taking NAOH as the desizing agent, and the concentration of the desizing agent is 6-8 g/ml;
3) dyeing the base cloth treated in the step 2): circularly coloring the base cloth in the dye vat continuously for 12 hours at the temperature of 210 ℃ and under the pressure of 500 kPa;
4) drying, tentering and setting the fabric treated in the step 3) at the temperature of 150 ℃ at the speed of 35-45 m/min;
5) preparing a mixed finishing liquid, wherein the mixed finishing liquid comprises 6-8% of a color fixing agent, 13-20% of a moisture absorption and sweat releasing finishing agent, 3-4% of a softening agent and 68-78% of water by weight; the moisture absorption and sweat release finishing agent is FC-226 moisture absorption and sweat release finishing agent;
6) carrying out after-treatment on the fabric treated in the step 5): and (2) soaking the fabric in the mixed finishing liquid at a bath ratio of 1: 12 at 175 ℃ for 5-10 minutes, and drying, tentering and shaping at the speed of 40-50 m/min at 190 ℃ to obtain the moisture-absorbing and sweat-releasing fabric.
Preferably, a continuous loose type desizing machine is adopted in the step 2), the rotating speed of the desizing machine is 30-35m/min, and the desizing temperature is 90-100 ℃.
Preferably, the base cloth is dyed at high temperature and high pressure by adopting the dye with high light fastness in the step 3), so that the color fastness of the base cloth can be greatly improved.
Preferably, the drying speed in the step 4) is 30Y/min.
Preferably, the softening agent in the step 5) is polyester quaternary ammonium salt; the color fixing agent is sodium nitrilotriacetate.
Due to the adoption of the technical scheme, the invention has the following technical effects:
the preparation method of the moisture-absorbing and sweat-releasing fabric has the advantages that the process is simple and ingenious and is easy to control, firstly, the physical structure of raw materials is used for endowing the fabric with soft and breathable natural texture and permanent moisture-absorbing and sweat-releasing functions, then, the fabric is subjected to deoiling and desizing treatment in the desizing step, and the fabric keeps high color fastness and soft and comfortable hand feeling through special process and chemical finishing, so that the fabric has comfortable breathability of the nano modified cotton fiber on one hand; on the other hand, the polyester fiber has high elasticity and high toughness, and is blended with natural fiber, so that the elasticity and the strength of the fabric are greatly improved, and the grooved special-shaped polyester fiber adopted by the invention can conduct moisture and sweat, endow the fabric with the characteristics of moisture absorption, sweat guiding and quick drying, can meet the market requirements on the moisture absorption and sweat guiding fabric, particularly the requirements of outdoor wearing clothes such as police uniform, sports wear and the like, has strong comfort and good practicability, and is worthy of popularization.
Detailed Description
All of the features disclosed in this specification, or all of the steps in any method or process so disclosed, may be combined in any combination, except combinations of features and/or steps that are mutually exclusive.
Any feature disclosed in this specification may be replaced by alternative features serving equivalent or similar purposes, unless expressly stated otherwise. That is, unless expressly stated otherwise, each feature is only an example of a generic series of equivalent or similar features.
A preparation method of the moisture-absorbing and sweat-releasing fabric comprises the following steps:
1) selecting 65-70% of nano modified cotton fiber and 30-35% of special-shaped polyester fiber with grooves, and weaving the nano modified cotton fiber and the special-shaped polyester fiber into base cloth on an air jet loom by adopting a twill weave method of warp and weft interweaving; the nanometer modified cotton fiber is prepared by activating cotton fiber with alkali solution, soaking in chitosan oligosaccharide solution, heating, oscillating, taking out, and vacuum drying;
2) adding a deoiling agent and a desizing agent to carry out deoiling and desizing treatment on the base cloth, wherein the base cloth is subjected to desizing treatment by taking NAOH as the desizing agent, and the concentration of the desizing agent is 6-8 g/ml;
3) dyeing the base cloth treated in the step 2): circularly coloring the base cloth in the dye vat continuously for 12 hours at the temperature of 210 ℃ and under the pressure of 500 kPa;
4) drying, tentering and setting the fabric treated in the step 3) at the temperature of 150 ℃ at the speed of 35-45 m/min;
5) preparing a mixed finishing liquid, wherein the mixed finishing liquid comprises 6-8% of a color fixing agent, 13-20% of a moisture absorption and sweat releasing finishing agent, 3-4% of a softening agent and 68-78% of water by weight; the moisture absorption and sweat release finishing agent is FC-226 moisture absorption and sweat release finishing agent;
6) carrying out after-treatment on the fabric treated in the step 5): and (2) soaking the fabric in the mixed finishing liquid at a bath ratio of 1: 12 at 175 ℃ for 5-10 minutes, and drying, tentering and shaping at the speed of 40-50 m/min at 190 ℃ to obtain the moisture-absorbing and sweat-releasing fabric.
In the step 2), a continuous loose type desizing machine is adopted, the rotating speed of the desizing machine is 30-35m/min, and the desizing temperature is 90-100 ℃.
And 3) the base cloth is dyed at high temperature and high pressure by adopting the dye with high light fastness, so that the color fastness of the base cloth can be greatly improved.
The drying speed in the step 4) is 30Y/min.
The softening agent in the step 5) is polyester quaternary ammonium salt; the color fixing agent is sodium nitrilotriacetate.
The preparation method of the moisture-absorbing and sweat-releasing fabric has the advantages that the process is simple and ingenious and is easy to control, firstly, the physical structure of raw materials is used for endowing the fabric with soft and breathable natural texture and permanent moisture-absorbing and sweat-releasing functions, then, the fabric is subjected to deoiling and desizing treatment in the desizing step, and the fabric keeps high color fastness and soft and comfortable hand feeling through special process and chemical finishing, so that the fabric has comfortable breathability of the nano modified cotton fiber on one hand; on the other hand, the polyester fiber has high elasticity and high toughness, and is blended with natural fiber, so that the elasticity and the strength of the fabric are greatly improved, and the grooved special-shaped polyester fiber adopted by the invention can conduct moisture and sweat, endow the fabric with the characteristics of moisture absorption, sweat guiding and quick drying, can meet the market requirements on the moisture absorption and sweat guiding fabric, particularly the requirements of outdoor wearing clothes such as police uniform, sports wear and the like, has strong comfort and good practicability, and is worthy of popularization.
The invention is not limited to the foregoing embodiments. The invention extends to any novel feature or any novel combination of features disclosed in this specification and any novel method or process steps or any novel combination of features disclosed.
Claims (5)
1. The preparation method of the moisture-absorbing and sweat-releasing fabric is characterized by comprising the following steps:
1) selecting 65-70% of nano modified cotton fiber and 30-35% of special-shaped polyester fiber with grooves, and weaving the nano modified cotton fiber and the special-shaped polyester fiber into base cloth on an air jet loom by adopting a twill weave method of warp and weft interweaving; the nanometer modified cotton fiber is prepared by activating cotton fiber with alkali solution, soaking in chitosan oligosaccharide solution, heating, oscillating, taking out, and vacuum drying;
2) adding a deoiling agent and a desizing agent to carry out deoiling and desizing treatment on the base cloth, wherein the base cloth is subjected to desizing treatment by taking NAOH as the desizing agent, and the concentration of the desizing agent is 6-8 g/ml;
3) dyeing the base cloth treated in the step 2): circularly coloring the base cloth in the dye vat continuously for 12 hours at the temperature of 210 ℃ and under the pressure of 500 kPa;
4) drying, tentering and setting the fabric treated in the step 3) at the temperature of 150 ℃ at the speed of 35-45 m/min;
5) preparing a mixed finishing liquid, wherein the mixed finishing liquid comprises 6-8% of a color fixing agent, 13-20% of a moisture absorption and sweat releasing finishing agent, 3-4% of a softening agent and 68-78% of water by weight; the moisture absorption and sweat release finishing agent is FC-226 moisture absorption and sweat release finishing agent;
6) carrying out after-treatment on the fabric treated in the step 5): and (2) soaking the fabric in the mixed finishing liquid at a bath ratio of 1: 12 at 175 ℃ for 5-10 minutes, and drying, tentering and shaping at the speed of 40-50 m/min at 190 ℃ to obtain the moisture-absorbing and sweat-releasing fabric.
2. The method for preparing moisture-absorbing and sweat-releasing fabric according to claim 1, wherein a continuous loose type desizing machine is adopted in the step 2), the rotating speed of the desizing machine is 30-35m/min, and the desizing temperature is 90-100 ℃.
3. The method for preparing moisture-absorbing and sweat-releasing fabric according to claim 1, wherein the color fastness of the base fabric can be greatly improved by performing high-temperature high-pressure dyeing treatment on the base fabric by using the dye with high light fastness in the step 3).
4. The method for preparing moisture-absorbing and sweat-releasing fabric according to claim 1, wherein the drying speed in the step 4) is 30Y/min.
5. The method for preparing moisture-absorbing and sweat-releasing fabric according to claim 1, wherein the softening agent in step 5) is polyester quaternary ammonium salt; the color fixing agent is sodium nitrilotriacetate.