CN112144279A - Environment-friendly fabric and processing technology thereof - Google Patents
Environment-friendly fabric and processing technology thereof Download PDFInfo
- Publication number
- CN112144279A CN112144279A CN202010873579.8A CN202010873579A CN112144279A CN 112144279 A CN112144279 A CN 112144279A CN 202010873579 A CN202010873579 A CN 202010873579A CN 112144279 A CN112144279 A CN 112144279A
- Authority
- CN
- China
- Prior art keywords
- environment
- parts
- fiber
- fabric
- friendly fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly fabric and a processing technology thereof, wherein the environment-friendly fabric comprises the following raw material components in parts by weight: 20-30 parts of fluorine fiber, 50-65 parts of organic cotton, 30-40 parts of bamboo fiber, 20-25 parts of fibrilia, 500 parts of benzyl acetate 200-. The processing technology comprises the following steps: selecting materials, preparing a softener, softening at a first time, drying and shaping at a first time, spinning, stretching, softening at a second time, and drying and shaping at a second time. Compared with the traditional process, the method has the advantages that the yarns are smoothened and dried before the fabric is woven, the flexibility of the yarns is improved and enhanced from the raw materials, the flexibility of the woven finished product is processed and enhanced again after the weaving is finished, and the flexibility of the fabric is better and the market competitiveness is higher through two times of flexibility processing before and after the production. The problems of low flexibility, high production cost and complex production process of the environment-friendly fabric in the prior art are solved.
Description
Technical Field
The invention belongs to the field of environment-friendly fabrics, and particularly relates to an environment-friendly fabric and a processing technology thereof.
Background
Human clothing has been worn for 7 thousand years. The function of the clothes changes from covering the body and resisting wind cold to pursuing comfort and beauty. The change not only reflects the progress of science and technology, but also reflects the continuous improvement of the requirements of people on the quality of life, and the progress of science and technology makes the change possible. People hope that the clothes not only care themselves, but also protect the environment, and the environment-friendly fiber clothes are the development trend in the future.
The fabric on the market is very easy to have the indentation after being laminated, and even if the fabric is laid with the indentation after the indentation, the indentation is difficult to eliminate. And current environmental protection surface fabric course of working is loaded down with trivial details, and manufacturing cost is high, compares and wears more comfortablely with traditional textile fabric, and the environmental protection is better, nevertheless will the case possess stronger market competition and just need improve the technology.
Aiming at the problems, the environment-friendly fabric processing technology which can enhance the flexibility of the fabric, simplify the production flow and reduce the production cost while ensuring the quality meets the actual needs.
Disclosure of Invention
Aiming at the defects of the prior art, the invention aims to provide a processing technology of an environment-friendly fabric, and solves the problems of low flexibility, high production cost and complicated production process of the environment-friendly fabric in the prior art.
The purpose of the invention can be realized by the following technical scheme:
the environment-friendly fabric comprises the following raw material components in parts by weight: 20-30 parts of fluorine fiber, 50-65 parts of organic cotton, 30-40 parts of bamboo fiber, 20-25 parts of fibrilia, 500 parts of benzyl acetate 200-.
Further, the environment-friendly fabric comprises the following raw material components in parts by weight: the special-purpose detergent comprises the following components of teflon 25, organic cotton 55, bamboo fiber 35, fibrilia 23, benzyl acetate 350, benzyl alcohol 400, limonene 550, linalool 700, chloroform 125, purified water 850, synthetic resin 125 and seaweed collagen 75.
A production process of an environment-friendly fabric comprises the following steps:
s1 selecting materials
Weighing all the raw materials according to the formula ratio;
s2 preparation of softener
Stirring and mixing the weighed benzyl acetate, benzyl alcohol, limonene, linalool, chloroform, purified water and synthetic resin uniformly, heating while stirring, standing and cooling to room temperature after heating and stirring are completed;
s3, primary compliance
Soaking the weighed fluorine fiber, organic cotton, bamboo fiber and hemp fiber in the prepared softener;
s4, drying and shaping for one time
Taking out the soaked fluorine fiber, organic cotton, bamboo fiber and hemp fiber, and placing the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber on a dryer for drying;
s5 spinning
Spinning and molding the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber through a spinning machine;
s6, stretching
Clamping two ends of the woven environment-friendly fabric and then stretching;
s7, secondary compliance
Soaking the stretched environment-friendly fabric in the prepared softener again;
s8, secondary drying and shaping
And taking out the soaked environment-friendly fabric, placing the fabric on a dryer for drying, and uniformly spraying the weighed seaweed collagen on the upper surface and the lower surface of the fabric while drying.
Furthermore, the stirring speed in the S2 is 900-1200 r/min, the heating temperature is 55-70 ℃, and the heating time is 10-20 min.
Further, the soaking time in the S3 is 2-3 h.
Further, the drying temperature in the S4 is 55-70 ℃, and the water content is controlled to be 1% -4%.
Further, the stretching tension in S6 is 300-450N.
Further, the soaking temperature in the S7 is 1-2.5 h.
Further, the drying temperature in the S8 is 63-70 ℃, and the water content is controlled to be 0.5% -1.5%.
The invention has the beneficial effects that:
1. compared with the traditional process, the method has the advantages that the yarns are subjected to softening and drying before the fabric is woven, the flexibility of the yarns is improved and enhanced from the raw materials, the flexibility of the woven finished product is processed and enhanced again after the weaving is finished, and the flexibility of the woven fabric is better and the market competitiveness is higher through two times of flexibility processing before and after the production;
2. according to the invention, unhairing and polishing are not needed to be carried out on the produced finished product, and after drying and shaping are carried out in the prior art, disordered curly hair is generated on the surface of the textile fabric, so that unhairing and polishing are carried out on the surface of the textile fabric before delivery, but in the invention, the synthetic resin is added in a softening process, the compactness degree among the spun yarns is enhanced, and a small amount of seaweed collagen is sprayed on the surface of the textile fabric during drying and shaping, so that the surface of the textile fabric is not curled hair during drying and shaping, the flexibility of the textile fabric is further enhanced, and the finished textile fabric is not easy to have indentation wrinkles.
Drawings
In order to more clearly illustrate the embodiments or technical solutions in the prior art of the present invention, the drawings used in the description of the embodiments or prior art will be briefly described below, and it is obvious for those skilled in the art that other drawings can be obtained based on these drawings without creative efforts.
FIG. 1 is an overall process flow diagram of an embodiment of the present invention.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
In the description of the present invention, it is to be understood that the terms "opening," "upper," "lower," "thickness," "top," "middle," "length," "inner," "peripheral," and the like are used in an orientation or positional relationship that is merely for convenience in describing and simplifying the description, and do not indicate or imply that the referenced component or element must have a particular orientation, be constructed and operated in a particular orientation, and thus should not be considered as limiting the present invention.
The environment-friendly fabric comprises the following raw material components in parts by weight: 20-30 parts of fluorine fiber, 50-65 parts of organic cotton, 30-40 parts of bamboo fiber, 20-25 parts of fibrilia, 500 parts of benzyl acetate 200-.
The invention is further described below by reference to several examples.
Example 1
The environment-friendly fabric comprises the following raw material components in parts by weight: 20 parts of fluorine fiber, 50 parts of organic cotton, 30 parts of bamboo fiber, 20 parts of hemp fiber, 200 parts of benzyl acetate, 300 parts of benzyl alcohol, 400 parts of limonene, 600 parts of linalool, 100 parts of chloroform, 700 parts of purified water, 100 parts of synthetic resin and 50 parts of seaweed collagen.
The processing technology of the environment-friendly fabric comprises the following steps:
s1 selecting materials
Preferably 20 kg of polyfluorene, 50 kg of organic cotton, 30 kg of bamboo fiber, 20 kg of hemp fiber, 200 kg of benzyl acetate, 300 kg of benzyl alcohol, 400 kg of limonene, 600 kg of linalool, 100 kg of chloroform, 700 kg of purified water, 100 kg of synthetic resin and 50 kg of seaweed collagen;
s2 preparation of softener
Stirring and mixing the weighed benzyl acetate, benzyl alcohol, limonene, linalool, chloroform, purified water and synthetic resin uniformly, heating while stirring, controlling the stirring speed at 1200r/min, the heating temperature at 60 ℃, heating for 10min, and standing to cool the mixture to room temperature after the heating and stirring are finished;
s3, primary compliance
Soaking the weighed fluorine fiber, organic cotton, bamboo fiber and hemp fiber in the prepared softener for 2 hours;
s4, drying and shaping for one time
Taking out the soaked fluorine fiber, organic cotton, bamboo fiber and hemp fiber, and placing the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber on a dryer for drying, wherein the drying temperature is controlled to be 60 ℃, and the water content is controlled to be 3%;
s5 spinning
Spinning and molding the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber through a spinning machine;
s6, stretching
Clamping two ends of the woven environment-friendly fabric, and then properly stretching, wherein the tension is controlled to be 300N;
s7, secondary compliance
Soaking the stretched environment-friendly fabric in the prepared softener for 1 h;
s8, secondary drying and shaping
Taking out the soaked environment-friendly fabric, placing the fabric on a dryer for drying, uniformly spraying the weighed seaweed collagen on the upper surface and the lower surface of the fabric while drying, controlling the drying temperature to be 70 ℃ and controlling the water content to be 1%.
Example 2
The environment-friendly fabric comprises the following raw material components in parts by weight: 30 parts of fluorine fiber, 65 parts of organic cotton, 40 parts of bamboo fiber, 25 parts of fibrilia, 500 parts of benzyl acetate, 500 parts of benzyl alcohol, 700 parts of limonene, 800 parts of linalool, 150 parts of chloroform, 1000 parts of purified water, 150 parts of synthetic resin and 100 parts of seaweed collagen.
The processing technology of the environment-friendly fabric comprises the following steps:
s1 selecting materials
Preferably 30 kg of polyfluorene, 65 kg of organic cotton, 40 kg of bamboo fiber, 25 kg of hemp fiber, 500 kg of benzyl acetate, 500 kg of benzyl alcohol, 700 kg of limonene, 800 kg of linalool, 150 kg of chloroform, 1000 kg of purified water, 150 kg of synthetic resin and 100 kg of seaweed collagen;
s2 preparation of softener
Stirring and mixing the weighed benzyl acetate, benzyl alcohol, limonene, linalool, chloroform, purified water and synthetic resin uniformly, heating while stirring, controlling the stirring speed to be 1000r/min, the heating temperature to be 65 ℃, heating for 20min, and standing to cool the mixture to room temperature after the heating and stirring are finished;
s3, primary compliance
Soaking the weighed fluorine fiber, organic cotton, bamboo fiber and hemp fiber in the prepared softener for 1.5 h;
s4, drying and shaping for one time
Taking out the soaked fluorine fiber, organic cotton, bamboo fiber and hemp fiber, and drying on a dryer, wherein the drying temperature is controlled to be 70 ℃, and the water content is controlled to be 4%;
s5 spinning
Spinning and molding the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber through a spinning machine;
s6, stretching
Clamping two ends of the woven environment-friendly fabric, and then properly stretching, wherein the tension is controlled to be 400N;
s7, secondary compliance
Soaking the stretched environment-friendly fabric in the prepared softener for 2 h;
s8, secondary drying and shaping
Taking out the soaked environment-friendly fabric, placing the fabric on a dryer for drying, uniformly spraying the weighed seaweed collagen on the upper surface and the lower surface of the fabric while drying, controlling the drying temperature to be 65 ℃ and controlling the water content to be 0.5%.
Example 3
The environment-friendly fabric comprises the following raw material components in parts by weight: the special-purpose detergent comprises the following components of teflon 25, organic cotton 55, bamboo fiber 35, fibrilia 23, benzyl acetate 350, benzyl alcohol 400, limonene 550, linalool 700, chloroform 125, purified water 850, synthetic resin 125 and seaweed collagen 75.
The processing technology of the environment-friendly fabric comprises the following steps:
s1 selecting materials
Preferably 25 kg of polyfluorene, 55 kg of organic cotton, 35 kg of bamboo fiber, 23 kg of hemp fiber, 350 kg of benzyl acetate, 400 kg of benzyl alcohol, 550 kg of limonene, 700 kg of linalool, 125 kg of chloroform, 850 kg of purified water, 125 kg of synthetic resin and 75 kg of seaweed collagen;
s2 preparation of softener
Stirring and mixing the weighed benzyl acetate, benzyl alcohol, limonene, linalool, chloroform, purified water and synthetic resin uniformly, heating while stirring, controlling the stirring speed at 1100r/min, the heating temperature at 70 ℃, heating for 15min, and standing to cool the mixture to room temperature after the heating and stirring are finished;
s3, primary compliance
Soaking the weighed fluorine fiber, organic cotton, bamboo fiber and hemp fiber in the prepared softener for 2.5 hours;
s4, drying and shaping for one time
Taking out the soaked fluorine fiber, organic cotton, bamboo fiber and hemp fiber, and drying on a dryer, wherein the drying temperature is controlled to be 55 ℃, and the water content is controlled to be 2%;
s5 spinning
Spinning and molding the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber through a spinning machine;
s6, stretching
Clamping two ends of the woven environment-friendly fabric, and then properly stretching, wherein the pulling force is controlled to be 350N;
s7, secondary compliance
Soaking the stretched environment-friendly fabric in the prepared softener again for 1.5 h;
s8, secondary drying and shaping
Taking out the soaked environment-friendly fabric, placing the fabric on a dryer for drying, uniformly spraying weighed seaweed collagen on the upper surface and the lower surface of the fabric while drying, controlling the drying temperature to be 67 ℃ and controlling the water content to be 1.5%.
Example 4
The environment-friendly fabric comprises the following raw material components in parts by weight: the anti-bacterial fabric comprises the following components of a fluorine fiber 28, organic cotton 60, bamboo fiber 36, hemp fiber 22, benzyl acetate 400, benzyl alcohol 450, limonene 600, linalool 680, chloroform 120, purified water 900, synthetic resin 135 and seaweed collagen 80.
The processing technology of the environment-friendly fabric comprises the following steps:
s1 selecting materials
Preferably 28 kg of polyfluorene, 60 kg of organic cotton, 36 kg of bamboo fiber, 22 kg of hemp fiber, 400 kg of benzyl acetate, 450 kg of benzyl alcohol, 600 kg of limonene, 680 kg of linalool, 120 kg of chloroform, 900 kg of purified water, 135 kg of synthetic resin and 80 kg of seaweed collagen;
s2 preparation of softener
Stirring and mixing the weighed benzyl acetate, benzyl alcohol, limonene, linalool, chloroform, purified water and synthetic resin uniformly, heating while stirring, controlling the stirring speed at 900r/min, the heating temperature at 55 ℃, heating for 20min, and standing to cool the mixture to room temperature after the heating and stirring are finished;
s3, primary compliance
Soaking the weighed fluorine fiber, organic cotton, bamboo fiber and hemp fiber in the prepared softener for 3 hours;
s4, drying and shaping for one time
Taking out the soaked fluorine fiber, organic cotton, bamboo fiber and hemp fiber, and drying on a dryer, wherein the drying temperature is controlled to be 70 ℃, and the water content is controlled to be 1%;
s5 spinning
Spinning and molding the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber through a spinning machine;
s6, stretching
Clamping two ends of the woven environment-friendly fabric, and then properly stretching, wherein the tensile force is controlled to be 450N;
s7, secondary compliance
Soaking the stretched environment-friendly fabric in the prepared softener again for 2.5 h;
s8, secondary drying and shaping
Taking out the soaked environment-friendly fabric, placing the fabric on a dryer for drying, uniformly spraying the weighed seaweed collagen on the upper surface and the lower surface of the fabric while drying, controlling the drying temperature to be 63 ℃ and controlling the water content to be 1.3%.
The results of the comparison of the above examples with the prior art are shown in the following table:
example (A) | Cost (per kilogram) | Degree of flexibility | Length of production |
Example 1 | 10RMB | High strength | 6h |
Example 2 | 11RMB | High strength | 8h |
Example 3 | 10.5RMB | High strength | 7.5h |
Example 4 | 10.5RMB | High strength | 8.5h |
Prior art technique | 13RMB | Is stronger | 13h |
In conclusion, compared with the prior art, the processing technology provided by the invention has the advantages of lower production cost, stronger flexibility and higher production speed.
In the description herein, references to the description of "one embodiment," "an example," "a specific example" or the like are intended to mean that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the invention. In this specification, the schematic representations of the terms used above do not necessarily refer to the same embodiment or example. Furthermore, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples.
The foregoing shows and describes the general principles, essential features, and advantages of the invention. It will be understood by those skilled in the art that the present invention is not limited to the embodiments described above, which are described in the specification and illustrated only to illustrate the principle of the present invention, but that various changes and modifications may be made therein without departing from the spirit and scope of the present invention, which fall within the scope of the invention as claimed.
Claims (9)
1. The environment-friendly fabric is characterized by comprising the following raw material components in parts by weight: 20-30 parts of fluorine fiber, 50-65 parts of organic cotton, 30-40 parts of bamboo fiber, 20-25 parts of fibrilia, 500 parts of benzyl acetate 200-.
2. The environment-friendly fabric as claimed in claim 1, which comprises the following raw material components in parts by weight: the special-purpose detergent comprises the following components of teflon 25, organic cotton 55, bamboo fiber 35, fibrilia 23, benzyl acetate 350, benzyl alcohol 400, limonene 550, linalool 700, chloroform 125, purified water 850, synthetic resin 125 and seaweed collagen 75.
3. The production process of the environment-friendly fabric according to any one of claims 1 or 2, characterized by comprising the following steps:
s1 selecting materials
Weighing all the raw materials according to the formula ratio;
s2 preparation of softener
Stirring and mixing the weighed benzyl acetate, benzyl alcohol, limonene, linalool, chloroform, purified water and synthetic resin uniformly, heating while stirring, standing and cooling to room temperature after heating and stirring are completed;
s3, primary compliance
Soaking the weighed fluorine fiber, organic cotton, bamboo fiber and hemp fiber in the prepared softener;
s4, drying and shaping for one time
Taking out the soaked fluorine fiber, organic cotton, bamboo fiber and hemp fiber, and placing the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber on a dryer for drying;
s5 spinning
Spinning and molding the fluorine fiber, the organic cotton, the bamboo fiber and the hemp fiber through a spinning machine;
s6, stretching
Clamping two ends of the woven environment-friendly fabric and then stretching;
s7, secondary compliance
Soaking the stretched environment-friendly fabric in the prepared softener again;
s8, secondary drying and shaping
And taking out the soaked environment-friendly fabric, placing the fabric on a dryer for drying, and uniformly spraying the weighed seaweed collagen on the upper surface and the lower surface of the fabric while drying.
4. The processing technology of the environment-friendly fabric as claimed in claim 3, wherein the stirring speed in S2 is 900-1200 r/min, the heating temperature is 55-70 ℃, and the heating time is 10-20 min.
5. The processing technology of the environment-friendly fabric as claimed in claim 3, wherein the soaking time in the S3 is 2-3 h.
6. The processing technology of the environment-friendly fabric as claimed in claim 3, wherein the drying temperature in the S4 is 55-70 ℃, and the water content is controlled to be 1% -4%.
7. The processing technology of the environment-friendly fabric as claimed in claim 3, wherein the stretching tension in the S6 is 300-450N.
8. The processing technology of the environment-friendly fabric as claimed in claim 3, wherein the soaking temperature in the S7 is 1-2.5 h.
9. The processing technology of the environment-friendly fabric as claimed in claim 3, wherein the drying temperature in the S8 is 63-70 ℃, and the water content is controlled to be 0.5% -1.5%.