CN112111644A - 一种高效回收金银的方法 - Google Patents

一种高效回收金银的方法 Download PDF

Info

Publication number
CN112111644A
CN112111644A CN202010945443.3A CN202010945443A CN112111644A CN 112111644 A CN112111644 A CN 112111644A CN 202010945443 A CN202010945443 A CN 202010945443A CN 112111644 A CN112111644 A CN 112111644A
Authority
CN
China
Prior art keywords
gold
silver
reduced iron
extraction
iron powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010945443.3A
Other languages
English (en)
Inventor
柯柏友
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN202010945443.3A priority Critical patent/CN112111644A/zh
Publication of CN112111644A publication Critical patent/CN112111644A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高效回收金银的方法，涉及金属冶金领域。本发明针对含铁量较高又有一定金银含量的硫酸烧渣、氰化尾渣的一种提取方法。通过对硫酸烧渣、氰化尾渣添加煤炭等还原剂及脱硫剂混合，加入到焙烧窑进行还原焙烧，制得海绵状还原铁粉。使被包裹的微细粒金银在还原铁的海绵状态下形成裸露。再将制得的海绵状还原铁粉进行常规的金银提取，使这种特难浸出的含金银物料得到较高的浸取率。提取金银后的海绵铁是价值不菲的紧俏冶金化工原料，本专利可高效综合利用有价金属，充分地利用国家宝贵的矿产资源，可为社会创造具大财富。

Description

一种高效回收金银的方法
技术领域
本发明公开了一种高效回收金银的方法，涉及金属冶金领域。
背景技术
硫酸烧渣是硫酸生产过程中排出的废渣，每生产一吨硫酸的废渣视黄铁矿含硫而定，一般为0.8～1.1吨，而我国是硫酸生产大国，每年都有数千万吨的废烧渣排出，这些废渣一部分以低价售给水泥厂作添加剂使用，或炼铁厂添加炼铁；有相当的一部分采用露天堆放，不仅占用大量耕地，而且久置还会在细菌的作用下氧化成水溶性硫酸盐污染地层水系，影响生态平衡，同时也是一种资源浪费。硫酸烧渣除含有丰富的铁外，还含有其它有价金属元素，如金、银、铜、钴等。但硫酸烧渣里面的有价金属，由于嵌布粒度细，附存状况基本属包裹状，提选起来比较困难，特别是金银的提取，制酸焙烧温度偏高对微细粒金形成重包裹，浸出率低下而失去提取价值。开展烧渣的高效综合利用研究是一条变废为宝的理想途径，对企业提高经济效益、防治环境污染有重要的意义。
氰化尾渣，是浮选金精矿经焙烧后氰化提金的尾渣，我国是黄金生产比较多的国家，生产中产生大量的氰化尾渣。氰化尾渣多为粉末状，粒度很细，里面除含有品位比较低的金外，还有Ag、Fc、S、Cu、Pb、As、Zn等元素。但氰化尾渣里面的有价金属，提选起来比较困难，特别是金银的提取，本身就是氰化时没有被浸出的，是包裹在铁、硫、砷及其他脉石中的微细粒纳米级金，在重度包裹状况之中。决定了浸出率低下而失去提取价值。也有科技工作者研究采用重选、磁选、浮选等选矿工艺进行富聚，但因回收率低，富聚效果不好而鲜有应用。然而，大量的氰化尾渣不但占用土地，而且氰渣粉尘对空气造成污染，若被雨水冲入河道，氰渣中的重金属还会污染水体。氰化尾渣的高效综合回收利用既有社会效益又有经济效益，对解决环境污染具有现实意义。
目前，我国硫酸渣、氰化尾渣产量都很大，把硫酸渣、氰化尾渣作为二次资源进行综合利用，综合回收其中的有价金属意义重大。
发明内容
针对现有技术中的缺陷和不足，本发明公开了一种高效回收金银的方法，对含铁量较高又有一定金银含量的硫酸烧渣、氰化尾渣添加煤炭等还原剂及脱硫剂混合，加入到焙烧窑进行还原焙烧，制得海绵状还原铁粉。使被包裹的微细粒金银在还原铁的海绵状态下形成裸露。再将制得的海绵状还原铁粉进行常规的金银提取，使这种特难浸出的含金银物料得到超高的浸取率。
一种高效回收金银的方法，其特征在于：先将含铁量较高又有一定金银含量的硫酸烧渣、氰化尾渣添加20～35％煤炭粉等还原剂及3～5％脱硫剂炭酸钙石粉混合，加入到焙烧窑进行还原焙烧，焙烧温度控制在1100～1200℃，焙烧1～4小时出窑，通过磨矿、磁选制得海绵状还原铁粉，含铁量在91％以上，再将制得的海绵状还原铁粉加入搅拌槽调浆，加石灰调PH值至11，加入***或环保提金剂，进行常规的金银浸取。原被包裹的微细粒金银在还原铁的海绵状态下形成裸露，大大的有利于金银的浸出。所以金银回收率可高达90％以上。提取金银后的海绵铁是价值不菲的紧俏冶金化工原料，其价值充抵还原铁还原焙烧成本绰绰有余。提取金银的利润价值是净赚！本专利可高效综合利用有价金属，充分地利用国家宝贵的矿产资源，社会效益和经济效益都非常显著。
具体实施方式
下面结合具体实施例来进一步理解本发明。
实施例1
安徽安庆某硫酸厂硫酸烧渣，含铁56％，含硫1.7％，含金2.65g/T，含银36g/T，硫酸烧渣通过添加35％焦炭粉等还原剂及3％脱硫剂炭酸钙石粉混合搅拌均匀，加入到焙烧窑进行还原焙烧，焙烧温度控制在1100～1150℃，焙烧4小时出窑，通过磨矿、磁选制得海绵状还原铁粉，含铁量在91.5％。再将制得的海绵状还原铁粉加入搅拌槽调浆，加石灰调PH值至11，加入环保提金剂1.5kg/吨矿，加入活性碳进行全泥炭浆提金银，浸出24小时。化验尾渣金残留0.17g/T，银7.3g/T，金的浸出率高达93.5％，银的浸出率79.7％，取得满意效果。
实施例2
河南灵宝某黄金冶厂氰化尾渣，含铁59.3％，含硫2.3％，含金4.65g/T，含银47g/T，氰化尾渣通过添加30％焦炭粉等还原剂及5％脱硫剂炭酸钙石粉混合搅拌均匀，加入到焙烧窑进行还原焙烧，焙烧温度控制在1100～1150℃，焙烧3.5小时出窑，通过磨矿、磁选制得海绵状还原铁粉，含铁量在92.3％。再将制得的海绵状还原铁粉加入搅拌槽调浆，加石灰调PH值至11，加入环保提金剂1.8kg/吨矿，加入活性碳进行全泥炭浆提金银，浸出24小时。化验尾渣金残留0.33g/T，银9.0g/T，金的浸出率高达92.9％，银的浸出率80.8％，取得满意效果。
实施例3
山东招远某黄金冶厂氰化尾渣，含铁55.7％，含硫2.3％，含金5.75g/T，含银53g/T，氰化尾渣通过添加30％焦炭粉等还原剂及5％脱硫剂炭酸钙石粉混合搅拌均匀，加入到焙烧窑进行还原焙烧，焙烧温度控制在1100～1150℃，焙烧4小时出窑，通过磨矿、磁选制得海绵状还原铁粉，含铁量在91.0％。再将制得的海绵状还原铁粉加入搅拌槽调浆，加石灰调PH值至11，加入环保提金剂2.3kg/吨矿，加入活性碳进行全泥炭浆提金银，浸出24小时.化验尾渣金残留0.35g/T，银8.7g/T，金的浸出率高达93.9％，银的浸出率83.5％，取得满意效果。

Claims (2)

1.一种高效回收金银的方法，通过对含铁量较高又有一定金银含量的硫酸烧渣、氰化尾渣添加煤炭等还原剂及脱硫剂混合，加入到焙烧窑进行还原焙烧，制得海绵状还原铁粉。使被包裹的微细粒金银在还原铁的海绵状态下形成裸露。再将制得的海绵状还原铁粉进行常规的金银提取，使这种特难浸出的含金银物料得到较高的浸取率。
2.如权利要求1所述的一种高效回收金银的方法，其特征在于：先将含铁量较高又有一定金银含量的硫酸烧渣、氰化尾渣添加煤炭等还原剂及脱硫剂混合，加入到焙烧窑进行还原焙烧，制得海绵状还原铁粉后，再将制得的海绵状还原铁粉进行常规的金银提取。
CN202010945443.3A 2020-08-31 2020-08-31 一种高效回收金银的方法 Pending CN112111644A (zh)