CN112025889A - Production process of antibacterial reinforced wood floor - Google Patents
Production process of antibacterial reinforced wood floor Download PDFInfo
- Publication number
- CN112025889A CN112025889A CN202010943910.9A CN202010943910A CN112025889A CN 112025889 A CN112025889 A CN 112025889A CN 202010943910 A CN202010943910 A CN 202010943910A CN 112025889 A CN112025889 A CN 112025889A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- insect
- plate blank
- parts
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of an antibacterial reinforced wood floor, and particularly relates to the technical field of wood floor production, and the production process specifically comprises the following steps: the raw material enters a processing factory for manufacturing, the plate for manufacturing is cut into plate blanks with the same size and the thickness of 1.2-3cm, and the second step is as follows: and (3) conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 40-80 minutes. The wood floor manufactured by the production process has the advantages of strong stability, difficult water absorption, strong cracking resistance, capability of inhibiting and killing bacteria in the solid wood floor, capability of avoiding the bacteria from damaging the solid wood floor, effective prolonging of the service life of the floor, less released formaldehyde, small harm to human bodies, simple process, low equipment requirement, strong operability and good social popularization and application.
Description
Technical Field
The invention belongs to the technical field of wood floor production, and particularly relates to a production process of an antibacterial reinforced wood floor.
Background
The wood floor is made of wood, the wood floors produced in China mainly include solid wood floors, reinforced wood floors, solid wood composite floors, multilayer composite floors, bamboo wood floors and cork floors, and newly-developed wood-plastic floors, and impregnated paper laminated wood floors enter the China market, which starts to mainly import products, mainly import products from Europe, take products of Germany enterprises as the majority, and in recent years, new products such as finger-joint floors, laminated wood floors, bamboo wood composite floors and stone-plastic floors appear in the market, wherein the bamboo wood composite floors and the stone-plastic floors are not produced in batches at the starting stage, and other products are gradually increased.
But during the in-service use, along with the floor in the extensive application of indoor house, public place, often can become the passerby of bacterium and threaten people's health, in order to prevent this kind of cross infection because of the floor uses and form, need improve the antibacterial property on floor, the timber apron on the market is mainly painted on the surface covering on the floor in addition, and paint is along with the passage of time, also can slowly age, and then moisture will enter into the solid wood floor inside very easily, more can arouse bacterial growing.
Disclosure of Invention
The invention provides a production process of an antibacterial reinforced wood floor, and aims to solve the problems of low service life and poor antibacterial property.
The invention is realized in such a way, and provides the following technical scheme: a production process of an antibacterial reinforced wood floor specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing materials, and the plates for manufacturing are cut into plate blanks with the same size and the thickness of 1.2-3 cm;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 40-80 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 7-14%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 20-50 parts of water-based resin, 30-80 parts of formaldehyde remover, 10-100 parts of insect repellent, 50-100 parts of defoamer, 100-150 parts of antibacterial liquid, 70-120 parts of clear water, 100-150 parts of polyvinyl chloride and 70-120 parts of silver nitrate;
step six: and D, spraying the waterproof antibacterial insect-proof adhesive prepared in the step five to the outer surface of the plate blank, and performing air drying solidification for 7-20 minutes.
Step seven: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, and heating the semi-finished plate blank at 130-150 ℃ for 20-35 minutes;
step eight: and (4) edge sealing is carried out on the board blank subjected to wax sealing in the seventh step by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
In a preferred embodiment, the waterproof antibacterial insect-resist glue agent in the step 5, specifically containing aqueous resin, formaldehyde remover, insect repellent, defoamer, antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, is added into a planetary mixer to be mixed, and the mixing time is not less than 30 minutes.
In a preferred embodiment, the slab air-drying in the sixth step is carried out by placing the slab into a drying room for cold air-drying.
In a preferred embodiment, in the sixth step, the specific way of spraying the waterproof, antibacterial and insect-proof adhesive on the outer surface of the slab is to spray the first layer of waterproof, antibacterial and insect-proof adhesive, the thickness of the first layer of waterproof, antibacterial and insect-proof adhesive is 1mm, the first layer of waterproof, antibacterial and insect-proof adhesive is left for 30 minutes to solidify the first layer of waterproof, antibacterial and insect-proof adhesive, and then the second layer of waterproof, antibacterial and insect-proof adhesive is sprayed on the second layer of waterproof, antibacterial and insect-proof adhesive, the thickness of the second layer of waterproof, antibacterial and insect-proof adhesive is 1mm, the second layer of waterproof, antibacterial and insect-proof adhesive is left for 30 minutes to solidify the second layer of waterproof, and the antibacterial property.
In a preferred embodiment, the step five insect repellent agent is one of a termiticide or a cockroach repellent.
In a preferred embodiment, the formaldehyde removing agent in the fifth step is specifically a broad leaf mud material.
Compared with the prior art, the invention has the beneficial effects that:
1. the wood floor manufactured by the production process has strong stability, is not easy to absorb water, has strong cracking resistance, can inhibit and kill bacteria in the solid wood floor, avoids the bacteria from damaging the solid wood floor, effectively prolongs the service life of the floor, releases less formaldehyde and has little harm to human bodies;
2. the generated chemical substance has good flame retardance by combining the chloroethylene with the silver nitrate, the flame retardant effect of the whole material is improved, and the whole material has wide range, simple process, low equipment requirement, strong operability and good social popularization and application.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.
Example 1:
the invention provides a production process of an antibacterial reinforced wood floor, which specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing materials, and the plates for manufacturing are cut into plate blanks with the same size and the thickness of 1.3 mm;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 45 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 8%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 30 parts of aqueous resin, 40 parts of formaldehyde remover, 20 parts of insect repellent, 60 parts of defoamer, 100 parts of antibacterial liquid, 70 parts of clear water, 110 parts of polyvinyl chloride and 73 parts of silver nitrate, wherein the 30 parts of aqueous resin, 40 parts of formaldehyde remover, 20 parts of insect repellent, 60 parts of defoamer, 100 parts of antibacterial liquid and 70 parts of clear water, the 110 parts of polyvinyl chloride and 73 parts of silver nitrate are placed in a planetary mixer for stirring, and the stirring time is not less than 30 minutes, wherein the insect repellent is an ant repellent, and the formaldehyde remover is a broad leaf mud material;
step six: and spraying the waterproof antibacterial insect-proof adhesive prepared in the fifth step onto the outer surface of the plate blank, air-drying and solidifying for 8 minutes, wherein the specific mode of spraying the waterproof antibacterial insect-proof adhesive on the outer surface of the plate blank is that a first layer of waterproof antibacterial insect-proof adhesive is sprayed firstly, the thickness of the first layer of waterproof antibacterial insect-proof adhesive is 1mm, the first layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the first layer of waterproof antibacterial insect-proof adhesive, then a second layer of spraying is carried out, the thickness of the second layer of waterproof antibacterial insect-proof adhesive is 1mm, the second layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the second layer of waterproof antibacterial insect-proof adhesive, in the process of spraying the waterproof antibacterial insect-proof adhesive for multiple times through the plate blank, the antibacterial property, the durability and the waterproof property of the plate blank are higher, and the sprayed semi.
And 7: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, heating the semi-finished plate blank at the temperature of 130 ℃, and controlling the heating time to be 20 minutes;
and 8: and (4) edge sealing is carried out on the plate blank subjected to wax sealing in the step (7) by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
Example 2:
the invention provides a production process of an antibacterial reinforced wood floor, which specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing materials, and the plates for manufacturing are cut into plate blanks with the same size and the thickness of 1.4 mm;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 46 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 9%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 40 parts of aqueous resin, 45 parts of formaldehyde remover, 35 parts of insect repellent, 78 parts of defoamer, 110 parts of antibacterial liquid, 80 parts of clear water, 115 parts of polyvinyl chloride and 80 parts of silver nitrate, wherein the 40 parts of aqueous resin, 45 parts of formaldehyde remover, 35 parts of insect repellent, 78 parts of defoamer, 110 parts of antibacterial liquid, 80 parts of clear water, 115 parts of polyvinyl chloride and 80 parts of silver nitrate are placed in a planetary mixer for stirring, and the stirring time is not less than 30 minutes, wherein the insect repellent is an ant repellent, and the formaldehyde remover is a broad leaf mud material;
step six: and spraying the waterproof antibacterial insect-proof adhesive prepared in the fifth step onto the outer surface of the plate blank, air-drying and solidifying for 8 minutes, wherein the specific mode of spraying the waterproof antibacterial insect-proof adhesive on the outer surface of the plate blank is that a first layer of waterproof antibacterial insect-proof adhesive is sprayed firstly, the thickness of the first layer of waterproof antibacterial insect-proof adhesive is 1mm, the first layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the first layer of waterproof antibacterial insect-proof adhesive, then a second layer of spraying is carried out, the thickness of the second layer of waterproof antibacterial insect-proof adhesive is 1mm, the second layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the second layer of waterproof antibacterial insect-proof adhesive, in the process of spraying the waterproof antibacterial insect-proof adhesive for multiple times through the plate blank, the antibacterial property, the durability and the waterproof property of the plate blank are higher, and the sprayed semi.
And 7: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, heating the semi-finished plate blank at 135 ℃, and controlling the heating time at 25 minutes;
and 8: and (4) edge sealing is carried out on the plate blank subjected to wax sealing in the step (7) by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
Example 3:
the invention provides a production process of an antibacterial reinforced wood floor, which specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing materials, and the plates for manufacturing are cut into plate blanks with the same size and the thickness of 1.41 mm;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 50 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 8%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 45 parts of aqueous resin, 50 parts of formaldehyde remover, 40 parts of insect repellent, 80 parts of defoaming agent, 115 parts of antibacterial liquid, 85 parts of clear water, 120 parts of polyvinyl chloride and 81 parts of silver nitrate, wherein the 45 parts of aqueous resin, 50 parts of formaldehyde remover, 40 parts of insect repellent, 80 parts of defoaming agent, 115 parts of antibacterial liquid and 85 parts of clear water, 120 parts of polyvinyl chloride and 81 parts of silver nitrate are placed in a planetary mixer for stirring, and the stirring time is not less than 30 minutes, wherein the insect repellent is an ant repellent, and the formaldehyde remover is a broad leaf mud material;
step six: and spraying the waterproof antibacterial insect-proof adhesive prepared in the fifth step onto the outer surface of the plate blank, air-drying and solidifying for 8 minutes, wherein the specific mode of spraying the waterproof antibacterial insect-proof adhesive on the outer surface of the plate blank is that a first layer of waterproof antibacterial insect-proof adhesive is sprayed firstly, the thickness of the first layer of waterproof antibacterial insect-proof adhesive is 1mm, the first layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the first layer of waterproof antibacterial insect-proof adhesive, then a second layer of spraying is carried out, the thickness of the second layer of waterproof antibacterial insect-proof adhesive is 1mm, the second layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the second layer of waterproof antibacterial insect-proof adhesive, in the process of spraying the waterproof antibacterial insect-proof adhesive for multiple times through the plate blank, the antibacterial property, the durability and the waterproof property of the plate blank are higher, and the sprayed semi.
And 7: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, heating the semi-finished plate blank at 140 ℃, and controlling the heating time at 28 minutes;
and 8: and (4) edge sealing is carried out on the plate blank subjected to wax sealing in the step (7) by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
Example 4:
the invention provides a production process of an antibacterial reinforced wood floor, which specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing, and the plates for manufacturing are cut into plate blanks with the same size and thickness of 1.6;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature of the drying room is controlled to be 159 ℃, and the drying time is 55 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 8%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 50 parts of aqueous resin, 51 parts of formaldehyde remover, 43 parts of insect repellent, 81 parts of defoaming agent, 116 parts of antibacterial liquid, 50 parts of clear water, 121 parts of polyvinyl chloride and 85 parts of silver nitrate, and placing the 50 parts of aqueous resin, 51 parts of formaldehyde remover, 43 parts of insect repellent, 81 parts of defoaming agent, 116 parts of antibacterial liquid and 50 parts of clear water into a planetary mixer for stirring, wherein the stirring time is not less than 30 minutes, the insect repellent is an ant repellent, and the formaldehyde remover is a broad leaf mud material;
step six: and spraying the waterproof antibacterial insect-proof adhesive prepared in the fifth step onto the outer surface of the plate blank, air-drying and solidifying for 8 minutes, wherein the specific mode of spraying the waterproof antibacterial insect-proof adhesive on the outer surface of the plate blank is that a first layer of waterproof antibacterial insect-proof adhesive is sprayed firstly, the thickness of the first layer of waterproof antibacterial insect-proof adhesive is 1mm, the first layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the first layer of waterproof antibacterial insect-proof adhesive, then a second layer of spraying is carried out, the thickness of the second layer of waterproof antibacterial insect-proof adhesive is 1mm, the second layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the second layer of waterproof antibacterial insect-proof adhesive, in the process of spraying the waterproof antibacterial insect-proof adhesive for multiple times through the plate blank, the antibacterial property, the durability and the waterproof property of the plate blank are higher, and the sprayed semi.
And 7: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, heating the semi-finished plate blank at 145 ℃, and controlling the heating time at 30 minutes;
and 8: and (4) edge sealing is carried out on the plate blank subjected to wax sealing in the step (7) by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
Example 5:
the invention provides a production process of an antibacterial reinforced wood floor, which specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing materials, and the plates for manufacturing are cut into plate blanks with the same size and the thickness of 2 mm;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 70 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 8%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 55 parts of aqueous resin, 52 parts of formaldehyde remover, 45 parts of insect repellent, 82 parts of defoaming agent, 117 parts of antibacterial liquid, 60 parts of clear water, 122 parts of polyvinyl chloride and 86 parts of silver nitrate, wherein the 55 parts of aqueous resin, 52 parts of formaldehyde remover, 45 parts of insect repellent, 82 parts of defoaming agent, 117 parts of antibacterial liquid and 60 parts of clear water, the 122 parts of polyvinyl chloride and 86 parts of silver nitrate are placed in a planetary mixer for stirring, and the stirring time is not less than 30 minutes, wherein the insect repellent is an ant repellent, and the formaldehyde remover is a broad leaf mud material;
step six: and spraying the waterproof antibacterial insect-proof adhesive prepared in the fifth step onto the outer surface of the plate blank, air-drying and solidifying for 8 minutes, wherein the specific mode of spraying the waterproof antibacterial insect-proof adhesive on the outer surface of the plate blank is that a first layer of waterproof antibacterial insect-proof adhesive is sprayed firstly, the thickness of the first layer of waterproof antibacterial insect-proof adhesive is 1mm, the first layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the first layer of waterproof antibacterial insect-proof adhesive, then a second layer of spraying is carried out, the thickness of the second layer of waterproof antibacterial insect-proof adhesive is 1mm, the second layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the second layer of waterproof antibacterial insect-proof adhesive, in the process of spraying the waterproof antibacterial insect-proof adhesive for multiple times through the plate blank, the antibacterial property, the durability and the waterproof property of the plate blank are higher, and the sprayed semi.
And 7: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, heating the semi-finished plate blank at the temperature of 150 ℃, and controlling the heating time to be 35 minutes;
and 8: and (4) edge sealing is carried out on the plate blank subjected to wax sealing in the step (7) by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
The following data were obtained from 5 types of antibacterial laminate flooring obtained in the above examples 1 to 5, respectively:
five antibacterial type laminate flooring can be obtained through the five groups of examples, and the five antibacterial type laminate flooring is respectively subjected to performance tests, wherein the antibacterial type laminate flooring in example 2 has the best performance and the highest value, and in the test process, the obtained parameters are as follows:
environmental protection rate | Antibacterial rate | Combination property | |
Example 1 | 0.07Mg/m3 | η=93% | 93% |
Example 2 | 0.02Mg/m3 | η=98% | 98% |
Example 3 | 0.03Mg/m3 | η=94% | 94% |
Example 4 | 0.05Mg/m3 | η=96% | 96% |
Example 5 | 0.09Mg/m3 | η=97% | 97% |
As can be seen from the above table, the material mixing proportion in the embodiment 2 is moderate, the effect of the antibacterial type laminate flooring prepared by the invention in the use process is obviously superior to that of the existing laminate flooring, the combination of the chloroethylene and the silver nitrate can generate chemical substances with good flame retardance, the flame retardant effect of the whole material is increased, the whole material has wider range, simple process, low equipment requirement and strong operability, and the antibacterial type laminate flooring has good social popularization and application.
The present invention is not limited to the above preferred embodiments, and any modifications, equivalent substitutions and improvements made within the spirit and principle of the present invention should be included in the protection scope of the present invention.
Claims (6)
1. The production process of the antibacterial reinforced wood floor is characterized by comprising the following steps: the method specifically comprises the following steps;
the method comprises the following steps: the raw materials enter a processing factory for manufacturing materials, and the plates for manufacturing are cut into plate blanks with the same size and the thickness of 1.2-3 cm;
step two: conveying the plate blank obtained by cutting in the step one to a drying room for drying treatment, wherein the temperature controlled in the drying room is set to be 150 ℃, and the drying time is 40-80 minutes;
step three: detecting the moisture content of the plate blank dried in the step two to control the moisture content of the plate blank to be 7-14%;
step four: fine polishing and grinding the plate blank manufactured in the third step by using fine abrasive paper;
step five: preparing a waterproof antibacterial insect-proof adhesive agent, wherein the waterproof antibacterial insect-proof adhesive agent specifically contains water-based resin, a formaldehyde remover, an insect-proof agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate, wherein the proportions of the materials are respectively; 20-50 parts of water-based resin, 30-80 parts of formaldehyde remover, 10-100 parts of insect repellent, 50-100 parts of defoamer, 100-150 parts of antibacterial liquid, 70-120 parts of clear water, 100-150 parts of polyvinyl chloride and 70-120 parts of silver nitrate;
step six: spraying the waterproof antibacterial insect-proof adhesive prepared in the fifth step on the outer surface of the plate blank, and performing air drying and solidification for 7-20 minutes;
step seven: sealing wax on the plate blank manufactured in the sixth step, ensuring that the thickness of a wax layer reaches more than 0.4mm, putting the plate blank into a drying room for wax infiltration, and heating the semi-finished plate blank at 130-150 ℃ for 20-35 minutes;
step eight: and (4) edge sealing is carried out on the plate blank subjected to wax sealing in the step (7) by using an edge sealing machine, and finally the antibacterial type laminate flooring is obtained.
2. The process for producing antibacterial laminate flooring according to claim 1, wherein: and 5, adding the waterproof antibacterial insect-preventing adhesive specifically containing aqueous resin, a formaldehyde remover, an insect-preventing agent, a defoaming agent, an antibacterial liquid, clear water, polyvinyl chloride and silver nitrate into a planetary stirrer for stirring, wherein the stirring time is not less than 30 minutes.
3. The process for producing antibacterial laminate flooring according to claim 1, wherein: and in the sixth step, the plate blank is dried by cold air in a drying room.
4. The process for producing antibacterial laminate flooring according to claim 1, wherein: and in the sixth step, the concrete mode of spraying the waterproof antibacterial insect-proof adhesive on the outer surface of the plate blank is that the first layer of waterproof antibacterial insect-proof adhesive is sprayed firstly, the thickness of the first layer of waterproof antibacterial insect-proof adhesive is 1mm, the first layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the first layer of waterproof antibacterial insect-proof adhesive, then the second layer of waterproof antibacterial insect-proof adhesive is sprayed, the thickness of the second layer of waterproof antibacterial insect-proof adhesive is 1mm, the second layer of waterproof antibacterial insect-proof adhesive is placed for 30 minutes to solidify the second layer of waterproof antibacterial insect-proof adhesive, and in the spraying process of carrying out multiple waterproof antibacterial insect-proof adhesive on the plate blank, the antibacterial property.
5. The process for producing antibacterial laminate flooring according to claim 1, wherein: the five insect-proof agents in the step are one of termite-proof agents or cockroach-proof agents.
6. The process for producing antibacterial laminate flooring according to claim 1, wherein: and the formaldehyde removing agent in the fifth step is specifically a broad leaf mud material.