CN111764024A - Preparation method of low-stretch yarn antistatic polyester fabric - Google Patents
Preparation method of low-stretch yarn antistatic polyester fabric Download PDFInfo
- Publication number
- CN111764024A CN111764024A CN202010395657.8A CN202010395657A CN111764024A CN 111764024 A CN111764024 A CN 111764024A CN 202010395657 A CN202010395657 A CN 202010395657A CN 111764024 A CN111764024 A CN 111764024A
- Authority
- CN
- China
- Prior art keywords
- polyester
- warp
- yarn
- grey cloth
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a low-stretch antistatic polyester fabric, which comprises the following steps: weaving grey cloth; b, dyeing and sizing, wherein the weaving of the grey cloth comprises the following steps of (1) purchasing raw materials; (2) warping the yarn; (3) adopting polyester filament yarn and polyester flat low stretch yarn as warp A, 75D conductive yarn as warp B, warp A and warp B1: 1 arranged on a loom to be woven into grey cloth, and the ratio of the polyester filament yarns to the polyester flat yarns is 1: 2. The prepared terylene fabric has good antistatic effect, good velvet feeling, good durability and comfort, and is suitable for sofa fabrics.
Description
The technical field is as follows:
the invention relates to the field of textiles, in particular to a preparation method of a low-stretch antistatic polyester fabric.
Background art:
the existing velvet fabric is complex in weaving method, poor in velvet feeling, poor in antistatic performance, poor in durability and comfort and limited in application range.
The invention content is as follows:
the invention aims to solve the technical problem of providing the preparation method of the low-stretch antistatic polyester fabric with good fabric velvet feeling, durability and comfort, and the polyester fabric prepared by the method has good antistatic property.
The technical scheme of the invention is to provide a preparation method of a low-stretch antistatic polyester fabric, which comprises the following steps:
weaving grey cloth;
b, dyeing and shaping the fabric,
wherein the weaving of the grey cloth comprises the following steps,
(1) raw material purchasing;
(2) warping the yarn;
(3) adopting polyester filament yarn and polyester flat low stretch yarn as warp A, 75D conductive yarn as warp B, warp A and warp B1: 1, arranging the polyester filaments on a loom to weave to form grey cloth, wherein the ratio of the polyester filaments to the polyester flat filaments is 1: 2;
the dyeing and setting process includes the following steps,
(1) the horizontal setting machine carries out grey cloth design, and horizontal setting machine speed is: 35 ± 2m/min, temperature: 180 ℃ and 190 +/-2 ℃;
(2) plucking by a plucking machine;
(3) ironing;
(4) shearing;
(5) dyeing, wherein the dyeing temperature is as follows: 125 + -2 deg.C, speed: 95 +/-2 m/min;
(6) shaping;
(7) hair tidying;
(8) ironing;
(9) and (5) finishing.
Preferably, the method also comprises the steps of finishing and shaping again, wherein the shaping temperature is 165-175 ℃, the time is 30-60s, 9g/L of clear water softening agent is added, 8g/L of nonionic antistatic is achieved, the vehicle speed is 50m/min, the overfeeding is 4-5%, the process adopts one-dipping-one-rolling, and the mangle liquor rate is 7-8%.
Furthermore, the front of the hair grabbing machine grabs the hair twice during grabbing the hair, and the hair grabbing frequency for the first time is less than that for the second time.
Compared with the prior art, the invention has the following beneficial effects that the design is unique, the operation is simple and convenient, the realization is easy, the terylene flat elastic fiber with excellent performance and the conductive yarn are adopted as raw materials, the front plush structure is woven under specific process conditions, the plush feeling and the wearability of the fabric are improved, the antistatic effect is realized, meanwhile, the terylene flat elastic fiber with excellent performance and the conductive yarn are endowed with good durability and comfortableness, and the terylene flat elastic fiber with excellent performance is very suitable for being used as sofa fabric.
The specific implementation mode is as follows:
the invention is further illustrated with respect to specific embodiments below:
a preparation method of a low-stretch antistatic polyester fabric comprises the following steps:
weaving grey cloth;
b, dyeing and shaping the fabric,
wherein the weaving of the grey cloth comprises the following steps,
(1) raw material purchasing;
(2) warping the yarn;
(3) adopting polyester filament yarn and polyester flat low stretch yarn as warp A, 75D conductive yarn as warp B, warp A and warp B1: 1, arranging the polyester filaments on a loom to weave to form grey cloth, wherein the ratio of the polyester filaments to the polyester flat filaments is 1: 2;
the dyeing and setting process includes the following steps,
(1) the horizontal setting machine carries out grey cloth design, and horizontal setting machine speed is: 35 ± 2m/min, temperature: 180 ℃ and 190 +/-2 ℃;
(2) plucking by a plucking machine; the front side of the hair grabbing machine grabs hair twice when the hair grabbing machine grabs hair, and the first hair grabbing frequency is less than the second hair grabbing frequency;
(3) ironing;
(4) shearing;
(5) dyeing, wherein the dyeing temperature is as follows: 125 + -2 deg.C, speed: 95 +/-2 m/min;
(6) shaping;
(7) hair tidying;
(8) ironing;
(9) and (5) finishing.
In order to enable the cloth cover to have better hand feeling, style and breadth, the cloth after dehydration can be finished and shaped again. Setting the setting temperature at 165-175 deg.c for 30-60 sec, adding clear water softening agent TF-480A9g/L, non-ionic antistatic agent 8g/L, vehicle speed at 50m/min, overfeeding 4-5%, and soaking-rolling in water at 7-8%.
Claims (3)
1. The preparation method of the low-stretch antistatic polyester fabric is characterized by comprising the following steps of:
weaving grey cloth;
b, dyeing and shaping the fabric,
wherein the weaving of the grey cloth comprises the following steps,
(1) raw material purchasing;
(2) warping the yarn;
(3) adopting polyester filament yarn and polyester flat low stretch yarn as warp A, 75D conductive yarn as warp B, warp A and warp B1: 1, arranging the polyester filaments on a loom to weave to form grey cloth, wherein the ratio of the polyester filaments to the polyester flat filaments is 1: 2;
the dyeing and setting process includes the following steps,
(1) the horizontal setting machine carries out grey cloth design, and horizontal setting machine speed is: 35 ± 2m/min, temperature: 180 ℃ and 190 +/-2 ℃;
(2) plucking by a plucking machine;
(3) ironing;
(4) shearing;
(5) dyeing, wherein the dyeing temperature is as follows: 125 + -2 deg.C, speed: 95 +/-2 m/min;
(6) shaping;
(7) hair tidying;
(8) ironing;
(9) and (5) finishing.
2. The preparation method of the low stretch antistatic polyester fabric as claimed in claim 1, further comprising finishing and sizing again at the sizing temperature of 165-.
3. The preparation method of the low stretch yarn antistatic polyester fabric according to claim 1, wherein the front surface of the wool grabber grabs the wool twice, and the first wool grabbing frequency is less than the second wool grabbing frequency.