CN111648152A - 一种高密度云母纸的生产方法 - Google Patents
一种高密度云母纸的生产方法 Download PDFInfo
- Publication number
- CN111648152A CN111648152A CN202010466687.3A CN202010466687A CN111648152A CN 111648152 A CN111648152 A CN 111648152A CN 202010466687 A CN202010466687 A CN 202010466687A CN 111648152 A CN111648152 A CN 111648152A
- Authority
- CN
- China
- Prior art keywords
- mica
- paper
- mica paper
- pulp
- carrying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于云母纸生产领域,提供一种高密度云母纸的生产方法,包括以下步骤:对选取的云母料进行两次热处理;二次破碎;通过三道旋流器和三道分级筛分级;用12000高斯高磁进行吸附;将云母浆片导入***池;将***池的云母浆提取到圆网纸机进行抄纸;将抄造的云母纸,经过多道压榨,经过纸机烘缸干燥、冷缸降温,再进行压光处理;对压光处理后的云母纸进行卷取、分切。本发明生产方法制得的云母纸密度较高,制作成板状或者带状耐高温绝缘材料后体积更小,厚度均匀,能适应于新能源行业的发展需要;提高了工业、家用电器的安全性;提高了生产作业的效率,为企业生产节省了人工成本。
Description
技术领域
本发明属于云母纸生产领域,具体涉及一种高密度云母纸的生产方法。
背景技术
我国的新能源工业是发展重点,众多的工业、家用电器需要大量的高密度绝缘云母纸等产品,它具有优良的电气性能和耐高温性能,有良好的渗透性和透气度,能用环氧树脂、有机硅树脂等浸渍压制成高品质的板状耐温绝缘材料,也可与玻纤布、薄膜、陶瓷纤维等通过环氧或有机硅树脂浸渍复合成高品质的带状耐高温绝缘材料。现有云母纸密度较小,制作成板状或者带状耐高温绝缘材料后体积较大,厚度不均匀且云母含量较小。
发明内容
本发明的目的就是为了克服上述现有技术中的不足,提供一种高密度云母纸的生产方法,该方法生产的云母纸密度较高,制作成板状或者带状耐高温绝缘材料后体积更小,厚度均匀,能适应于新能源行业的发展需要。
本发明目的是通过如下技术方案实现的。
一种高密度云母纸的生产方法,包括以下步骤:
(1)选取片径均匀、无斑点、干净的云母料,对选取的云母料进行两次热处理;
(2)将热处理后的云母料通过二次破碎***进行破碎;
(3)将二次破碎后的云母浆片通过三道旋流器和三道分级筛分级;
(4)将通过旋流器和分级筛分级的云母浆片,用12000高斯高磁进行吸附处理;
(5)将吸附处理的云母浆片导入***池;
(6)将***池的云母浆提取到圆网纸机进行抄纸;
(7)将抄造的云母纸,经过多道压榨处理,减少厚度,增大密度;
(8)将压榨处理后的云母纸,经过纸机烘缸干燥、冷缸降温再进行压光处理;
(9)对压光处理后的云母纸进行卷取、分切处理。
在上述技术方案中,步骤(1)中两次热处理的温度分别为720℃和350℃,保持时间分别为2小时和1小时。
在上述技术方案中,步骤(2)中云母料通过二次破碎***进行破碎,破碎压力分别为6MPa和4MPa。
在上述技术方案中,步骤(3)中旋流器的旋流压力为3MPa,分级筛目数为250目。
本发明生产方法制得的云母纸密度较高,制作成板状或者带状耐高温绝缘材料后体积更小,厚度均匀,能适应于新能源行业的发展需要;提高了工业、家用电器的安全性;提高了生产作业的效率,为企业生产节省了人工成本。
具体实施方式
下面结合实施例对本发明做进一步的详细说明,以令本领域技术人员参照说明书文字能够据以实施。
本实施例提供一种高密度云母纸的生产方法,包括以下步骤:
(1)选取片径均匀、无斑点、干净的云母料,对选取的云母料进行两次热处理,两次热处理的温度分别为720℃和350℃,保持时间分别为2小时和1小时;
(2)将热处理后的云母料通过二次破碎***进行破碎,破碎压力分别为6MPa和4MPa;
(3)将二次破碎后的云母浆片通过三道旋流器和三道分级筛分级,旋流器的旋流压力为3MPa,分级筛目数为250目;
(4)将通过旋流器和分级筛分级的云母浆片,用12000高斯高磁进行吸附处理;
(5)将吸附处理的云母浆片导入***池;
(6)将***池的云母浆提取到圆网纸机进行抄纸;
(7)将抄造的云母纸,经过三对辊筒进行压榨处理,减少厚度,增大密度;
(8)将压榨处理后的云母纸,经过纸机烘缸干燥、冷缸降温再进行压光处理;
(9)对压光处理后的云母纸进行卷取、分切处理。
性能分析:
表1高密度云母纸性能
从表1可以看出,通过本实施例生产方法制得的云母纸已经可以达到现有云母纸的高耐温和高绝缘性能,同时具有高的密度。
本说明书未作详细描述的内容属于本领域专业技术人员公知的现有技术。
尽管本发明的实施方案已公开如上,但其并不仅仅限于说明书和实施方式中所列运用,它完全可以被适用于各种适合本发明的领域,对于熟悉本领域的人员而言,可容易地实现另外的修改,因此在不背离权利要求及等同范围所限定的一般概念下,本发明并不限于特定的细节和这里示出与描述的图例。
Claims (5)
1.一种高密度云母纸的生产方法,其特征在于该生产方法包括以下步骤:
(1)选取片径均匀、无斑点、干净的云母料,对选取的云母料进行两次热处理;
(2)将热处理后的云母料通过二次破碎***进行破碎;
(3)将二次破碎后的云母浆片通过三道旋流器和三道分级筛分级;
(4)将通过旋流器和分级筛分级的云母浆片,用12000高斯高磁进行吸附处理;
(5)将吸附处理的云母浆片导入***池;
(6)将***池的云母浆提取到圆网纸机进行抄纸;
(7)将抄造的云母纸,经过多道压榨处理,减少厚度,增大密度;
(8)将压榨处理后的云母纸,经过纸机烘缸干燥、冷缸降温再进行压光处理;
(9)对压光处理后的云母纸进行卷取、分切处理。
2.如权利要求1所述的高密度云母纸的生产方法,其特征在于:步骤(1)中两次热处理的温度分别为720℃和350℃,保持时间分别为2小时和1小时。
3.如权利要求1所述的高密度云母纸的生产方法,其特征在于:步骤(2)中云母料通过二次破碎***进行破碎,破碎压力分别为6MPa和4MPa。
4.如权利要求1所述的高密度云母纸的生产方法,其特征在于:步骤(3)中旋流器的旋流压力为3MPa,分级筛目数为250目。
5.如权利要求1所述的高密度云母纸的生产方法,其特征在于:步骤(7)中对抄造的云母纸进行三道压榨处理。