CN111647270A - Insulating polyimide film and preparation method thereof - Google Patents
Insulating polyimide film and preparation method thereof Download PDFInfo
- Publication number
- CN111647270A CN111647270A CN202010472518.0A CN202010472518A CN111647270A CN 111647270 A CN111647270 A CN 111647270A CN 202010472518 A CN202010472518 A CN 202010472518A CN 111647270 A CN111647270 A CN 111647270A
- Authority
- CN
- China
- Prior art keywords
- polyimide film
- dianhydride
- monomer
- insulating polyimide
- diamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an insulating polyimide film, which comprises the following raw materials: diamine monomer, dianhydride monomer and octa (aminophenyltrioxysilane), wherein the diamine monomer is 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and fluorine-containing diamine, and the dianhydride monomer is pyromellitic dianhydride and fluorine-containing dianhydride. The invention also discloses a preparation method of the insulating polyimide film. The invention has good insulating property.
Description
Technical Field
The invention relates to the technical field of polyimide films, in particular to an insulating polyimide film and a preparation method thereof.
Background
Polyimide has good mechanical property, thermal stability and electrical property, is an important special high polymer material, and is widely applied to the microelectronic and photoelectric industries.
However, with the development of very large scale integrated circuits, the requirement for the insulation property of polyimide is also higher and higher. The dielectric constant of the conventional polyimide is about 3.5, and the dielectric property needs to be improved.
Disclosure of Invention
Based on the technical problems in the background art, the invention provides an insulating polyimide film and a preparation method thereof.
The invention provides an insulating polyimide film, which comprises the following raw materials: diamine monomer, dianhydride monomer and octa (aminophenyltrioxysilane), wherein the diamine monomer is 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and fluorine-containing diamine, and the dianhydride monomer is pyromellitic dianhydride and fluorine-containing dianhydride.
Preferably, the fluorine-containing dianhydride is 4,4' - (hexafluoroisopropylidene) diphthalic anhydride.
Preferably, the fluorine-containing diamine is 2, 2-bis (3-amino-4-hydroxyphenyl) -hexafluoropropane.
Preferably, the molar ratio of the 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene to the fluorine-containing diamine is 0.6-0.7: 0.3-0.4.
Preferably, the molar ratio of the pyromellitic dianhydride to the fluorine-containing dianhydride is 0.5-0.6: 0.4-0.5.
Preferably, the octakis (aminophenyltrioxysilane) comprises 4 to 5 weight percent of the total weight of the diamine monomer and the dianhydride monomer.
Preferably, the molar ratio of diamine monomer to dianhydride monomer is 1: 0.9-1.
The invention also provides a preparation method of the insulating polyimide film, which comprises the following steps: in an inert gas atmosphere, uniformly mixing a diamine monomer and an organic solvent, then adding a dianhydride monomer for reaction, then adding an octa (aminophenyltrioxasilane) solution, and continuing to react to obtain an intermediate material; and defoaming the intermediate material, coating the defoamed intermediate material on the surface of a substrate, imidizing and demoulding to obtain the insulating polyimide film.
Preferably, the procedure for imidization is: heating to 100 ℃ and 110 ℃, and preserving heat for 1 h; then heating to 200 ℃ and 210 ℃, and preserving the heat for 0.5 h; then heating to 300 ℃ and 310 ℃, and preserving the heat for 20 min; then the temperature is raised to 350 ℃, and the temperature is kept for 10 min.
Preferably, the reaction is carried out for 5 to 7 hours at room temperature, then an octa (aminophenyltrioxasilane) solution is added, and the reaction is continued for 1.5 to 2 hours to obtain an intermediate material.
Preferably, the organic solvent is N, N-dimethylacetamide.
Has the advantages that:
the preparation method selects 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and 2, 2-bis (3-amino-4-hydroxyphenyl) -hexafluoropropane to be matched in a proper proportion as diamine monomers, pyromellitic dianhydride and 4,4' - (hexafluoroisopropylene) diphthalic anhydride to be matched in a proper proportion as dianhydride monomers, so that a proper amount of fluorine and a large-volume side group are introduced into polyimide, the dielectric constant of the polyimide can be greatly reduced, the insulating property of the polyimide is improved, and meanwhile, the heat resistance of the preparation method can be further improved due to the introduction of the fluorine; in addition, a proper amount of octa (aminophenyltrioxysilane) is added, so that the dielectric constant can be further reduced, and the mechanical property of the invention can be further improved; and the mechanical property of the film can be further improved by selecting a proper imidization process.
Detailed Description
The technical solution of the present invention will be described in detail below with reference to specific examples.
Example 1
An insulating polyimide film, the raw materials of which comprise: diamine monomers, dianhydride monomers and octa (aminophenyltrioxasilane), wherein the diamine monomers are 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and 2, 2-bis (3-amino-4-hydroxyphenyl) -hexafluoropropane, and the dianhydride monomers are pyromellitic dianhydride and 4,4' - (hexafluoroisopropylidene) diphthalic anhydride;
wherein the molar ratio of the 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene to the fluorine-containing diamine is 0.6: 0.4;
the molar ratio of pyromellitic dianhydride to fluorine-containing dianhydride is 0.5: 0.5;
the eight (aminophenyltrioxysilane) comprises 4% by weight of the total amount of diamine monomer and dianhydride monomer;
the molar ratio of diamine monomer to dianhydride monomer is 1: 1.
The preparation method of the insulating polyimide film comprises the following steps: in the nitrogen atmosphere, uniformly mixing a diamine monomer and N, N-dimethylacetamide, adding a dianhydride monomer, reacting at room temperature for 5 hours, adding an N, N-dimethylacetamide solution of octa (aminophenyltrioxasilane), and continuously reacting for 2 hours to obtain an intermediate material; defoaming the intermediate material, coating the intermediate material on the surface of a substrate, imidizing and demoulding to obtain the insulating polyimide film, wherein the imidizing procedure comprises the following steps: heating to 100 ℃, and keeping the temperature for 1 h; then heating to 200 ℃, and preserving heat for 0.5 h; then heating to 300 ℃, and preserving heat for 20 min; then the temperature is raised to 350 ℃, and the temperature is kept for 10 min.
Example 2
An insulating polyimide film, the raw materials of which comprise: diamine monomers, dianhydride monomers and octa (aminophenyltrioxasilane), wherein the diamine monomers are 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and 2, 2-bis (3-amino-4-hydroxyphenyl) -hexafluoropropane, and the dianhydride monomers are pyromellitic dianhydride and 4,4' - (hexafluoroisopropylidene) diphthalic anhydride;
wherein the molar ratio of the 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene to the fluorine-containing diamine is 0.7: 0.3;
the molar ratio of pyromellitic dianhydride to fluorine-containing dianhydride is 0.6: 0.4;
the eight (aminophenyltrioxysilane) comprises 5% by weight of the total amount of the diamine monomer and the dianhydride monomer;
the molar ratio of diamine monomer to dianhydride monomer is 1: 0.9.
The preparation method of the insulating polyimide film comprises the following steps: in the nitrogen atmosphere, uniformly mixing a diamine monomer and N, N-dimethylacetamide, adding a dianhydride monomer, reacting at room temperature for 7 hours, adding an N, N-dimethylacetamide solution of octa (aminophenyltrioxasilane), and continuously reacting for 1.5 hours to obtain an intermediate material; defoaming the intermediate material, coating the intermediate material on the surface of a substrate, imidizing and demoulding to obtain the insulating polyimide film, wherein the imidizing procedure comprises the following steps: heating to 110 ℃, and preserving heat for 1 h; then heating to 210 ℃, and preserving heat for 0.5 h; then heating to 310 ℃, and preserving heat for 20 min; then the temperature is raised to 350 ℃, and the temperature is kept for 10 min.
Example 3
An insulating polyimide film, the raw materials of which comprise: diamine monomers, dianhydride monomers and octa (aminophenyltrioxasilane), wherein the diamine monomers are 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and 2, 2-bis (3-amino-4-hydroxyphenyl) -hexafluoropropane, and the dianhydride monomers are pyromellitic dianhydride and 4,4' - (hexafluoroisopropylidene) diphthalic anhydride;
wherein the molar ratio of the 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene to the fluorine-containing diamine is 0.65: 0.35;
the molar ratio of pyromellitic dianhydride to fluorine-containing dianhydride is 0.55: 0.45;
the eight (aminophenyltrioxysilane) is 4.5% of the total weight of the diamine monomer and the dianhydride monomer;
the molar ratio of diamine monomer to dianhydride monomer is 1: 1.
The preparation method of the insulating polyimide film comprises the following steps: in the nitrogen atmosphere, uniformly mixing a diamine monomer and N, N-dimethylacetamide, adding a dianhydride monomer, reacting at room temperature for 6 hours, adding an N, N-dimethylacetamide solution of octa (aminophenyltrioxasilane), and continuously reacting for 1.8 hours to obtain an intermediate material; defoaming the intermediate material, coating the intermediate material on the surface of a substrate, imidizing and demoulding to obtain the insulating polyimide film, wherein the imidizing procedure comprises the following steps: heating to 105 ℃, and preserving heat for 1 h; then heating to 205 ℃, and preserving heat for 0.5 h; then heating to 305 ℃, and preserving the heat for 20 min; then the temperature is raised to 350 ℃, and the temperature is kept for 10 min.
The results of the tests performed in examples 1-3 are shown in the following table:
as can be seen from the above table, the invention has good insulation property, heat resistance and good light transmittance.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.
Claims (10)
1. An insulating polyimide film, characterized in that its raw materials include: diamine monomer, dianhydride monomer and octa (aminophenyltrioxysilane), wherein the diamine monomer is 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene and fluorine-containing diamine, and the dianhydride monomer is pyromellitic dianhydride and fluorine-containing dianhydride.
2. The insulating polyimide film according to claim 1, wherein the fluorine-containing dianhydride is 4,4' - (hexafluoroisopropylidene) diphthalic anhydride.
3. The insulating polyimide film according to claim 1 or 2, wherein the fluorine-containing diamine is 2, 2-bis (3-amino-4-hydroxyphenyl) -hexafluoropropane.
4. The insulating polyimide film according to any one of claims 1 to 3, wherein the molar ratio of 9, 9-bis [4- (4-aminophenoxy) phenyl ] fluorene to fluorine-containing diamine is 0.6 to 0.7:0.3 to 0.4.
5. The insulating polyimide film according to any one of claims 1 to 4, wherein the molar ratio of pyromellitic dianhydride to fluorine-containing dianhydride is 0.5 to 0.6:0.4 to 0.5.
6. The insulating polyimide film according to any one of claims 1 to 5, wherein the octa (aminophenyltrioxysilane) is 4 to 5% by weight based on the total weight of the diamine monomer and the dianhydride monomer.
7. The insulating polyimide film according to any one of claims 1 to 6, wherein a molar ratio of the diamine monomer to the dianhydride monomer is 1:0.9 to 1.
8. A method for preparing an insulating polyimide film according to any one of claims 1 to 7, comprising the steps of: in an inert gas atmosphere, uniformly mixing a diamine monomer and an organic solvent, then adding a dianhydride monomer for reaction, then adding an octa (aminophenyltrioxasilane) solution, and continuing to react to obtain an intermediate material; and defoaming the intermediate material, coating the defoamed intermediate material on the surface of a substrate, imidizing and demoulding to obtain the insulating polyimide film.
9. The method for preparing an insulating polyimide film according to claim 8, wherein the imidization procedure is: heating to 100 ℃ and 110 ℃, and preserving heat for 1 h; then heating to 200 ℃ and 210 ℃, and preserving the heat for 0.5 h; then heating to 300 ℃ and 310 ℃, and preserving the heat for 20 min; then the temperature is raised to 350 ℃, and the temperature is kept for 10 min.
10. The method for preparing the insulating polyimide film according to claim 8 or 9, wherein the reaction is carried out for 5 to 7 hours at room temperature, then an octa (aminophenyltrioxasilane) solution is added, and the reaction is continued for 1.5 to 2 hours to obtain an intermediate material; preferably, the organic solvent is N, N-dimethylacetamide.