CN111621186A - 降低油性涂料voc排放的含水型溶剂 - Google Patents
降低油性涂料voc排放的含水型溶剂 Download PDFInfo
- Publication number
- CN111621186A CN111621186A CN202010677122.XA CN202010677122A CN111621186A CN 111621186 A CN111621186 A CN 111621186A CN 202010677122 A CN202010677122 A CN 202010677122A CN 111621186 A CN111621186 A CN 111621186A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- oil
- water
- organic solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种降低油性涂料VOC排放的含水型溶剂,包括有机溶剂及助溶剂;所述有机溶剂为与水部分相溶或全水溶性的溶剂,所述助溶剂为水。本发明在有机溶剂中加入助溶剂,使用本发明稀释油性涂料时,能保持涂料性质还是油性,使得油性涂料的性能仍能满足实际使用需求及性能测试,在不改变油性涂料的配方的前提下,能大幅度降低油性涂料VOC的排放,经济、节能又环保。
Description
技术领域
本发明涉及涂料领域,尤其涉及一种降低油性涂料VOC排放的含水型溶剂。
背景技术
挥发性有机物(Volatile Organic Compounds,VOC)排放可分为有组织排放与无组织排放,而排放源大多来自于工业制程中所使用的有机溶剂。尤其是涂料、油墨及涂装等行业,且该行业涂布制程为开放式制程,成为逸散性VOC的主要来源。
随着现代工业的发展以及人们环保意识的不断增强,环境友好型涂料将是当前和今后涂料的发展趋势。新版的VOC环保强制标准GB30981-2020<工业防护涂料中有害物质限量>将于2020年12月1日开始执行,这就意味着工业防护涂料类型的工厂面临着前所未有的挑战。如何在满足国家法令要求的前提下,既不降低涂料的性能,又不提高成本,还能降低产品的VOC排放,这是一个迫切而复杂的实际问题。
目前降低涂料或油墨VOC排放的方法主要有以下几种:
1、使用水溶性或半水溶性成膜树脂(包括但不限于水溶性环氧、丙烯酸、聚酯醇酸、UV紫外光固化树脂等)作为涂料或油墨的溶剂。但这种方法有很大的局限性,对于一些金属质感比较好的涂料,不但成本高,而且无法满足外观要求及性能要求。
2、借助于反应性乳化剂或扩链剂,通过调节乳化剂或扩链剂用量,使涂料或油墨具有一定亲水性,在水中乳化,而制成水性涂料或油墨,降低VOC排放,但由于制成的水性涂料或油墨亲水,会对产品性能产生影响,且不能满足性能测试要求,也无法满足外观要求。
发明内容
本发明的目的在于提供一种降低油性涂料VOC排放的含水型溶剂,在不改变油性涂料配方的条件下,能大幅度降低油性涂料VOC的排放。
为了达到上述目的,本发明提供了一种降低油性涂料VOC排放的含水型溶剂,包括有机溶剂及助溶剂;所述有机溶剂为与水部分相溶或全水溶性的溶剂,所述助溶剂为水。
所述有机溶剂包括丙酮、甲基异丁基酮、二丙酮醇、异丙醇、丙二醇甲醚醋酸酯、碳酸丙烯酯、乙二醇醚、及丙二醇醚类。
所述水为去离子水、纯净水中的一种。
所述降低油性涂料VOC排放的含水型溶剂中,所述有机溶剂为50至99重量份,所述助溶剂为1至50重量份。
所述有机溶剂中,丙酮为5至40重量份,甲基异丁基酮为5至20重量份,二丙酮醇为5至25重量份,异丙醇为0至40重量份,丙二醇甲醚醋酸酯为5至20重量份,碳酸丙烯酯为5至15重量份,乙二醇醚为0至25重量份、丙二醇醚类为0至25重量份。
所述有机溶剂中,丙酮为10至35重量份,甲基异丁基酮为10至20重量份,二丙酮醇为10至20重量份,异丙醇为5至30重量份,丙二醇甲醚醋酸酯为10至20重量份,碳酸丙烯酯为5至10重量份,乙二醇醚为5至20重量份、丙二醇醚类为5至20重量份。
所述助溶剂为5至50重量份。
所述降低油性涂料VOC排放的含水型溶剂用于稀释油性涂料。
所述有机溶剂用于溶解油性涂料。
本发明的有益效果:本发明提供的一种降低油性涂料VOC排放的含水型溶剂,包括有机溶剂及助溶剂;所述有机溶剂为与水部分相溶或全水溶性的溶剂,所述助溶剂为水。本发明在有机溶剂中加入助溶剂,利用水的助溶性,将丙酮、甲基异丁基酮、二丙酮醇、异丙醇、丙二醇甲醚醋酸酯、碳酸丙烯酯、乙二醇醚、及丙二醇醚类与水混合,制成含水型溶剂。使用本发明稀释油性涂料时,能保持涂料性质还是油性,使得油性涂料的性能仍能满足实际使用需求及性能测试,在不改变油性涂料的配方的前提下,能大幅度降低油性涂料VOC的排放。并且助溶剂采用水,而水的成本很低,对环境没有污染,因此本发明经济、节能又环保。
具体实施方式
为更进一步阐述本发明所采取的技术手段及其效果,以下进行详细描述。
本发明提供一种降低油性涂料VOC排放的含水型溶剂,该含水型溶剂包括有机溶剂及助溶剂;所述有机溶剂为与水部分相溶或全水溶性的溶剂,所述助溶剂为水。所述含水型溶剂通过在有机溶剂中添加助溶剂,能大幅度降低VOC的排放,并且使用该含水型溶剂作为稀释剂稀释油性涂料时,涂料性质还是油性,油性涂料的性能仍能满足实际使用需求及性能测试。
具体地,所述有机溶剂包括丙酮、甲基异丁基酮、二丙酮醇、异丙醇、丙二醇甲醚醋酸酯、碳酸丙烯酯、乙二醇醚、及丙二醇醚类。由于丙酮、甲基异丁基酮、二丙酮醇、异丙醇、丙二醇甲醚醋酸酯、碳酸丙烯酯、乙二醇醚、及丙二醇醚类与油性涂料有良好的相溶性,因此所述有机溶剂可以溶解较多的油性涂料,从而作为油性涂料的溶剂来溶解油性涂料。
具体地,所述水为去离子水、纯净水中的一种。
具体地,所述含水型溶剂中,所述有机溶剂为50至99重量份,所述助溶剂为1至50重量份。
具体地,所述有机溶剂中,丙酮为5至40重量份,甲基异丁基酮为5至20重量份,二丙酮醇为5至25重量份,异丙醇为0至40重量份,丙二醇甲醚醋酸酯为5至20重量份,碳酸丙烯酯为5至15重量份,乙二醇醚为0至25重量份、丙二醇醚类为0至25重量份。
优选地,所述有机溶剂中,丙酮为10至35重量份,甲基异丁基酮为10至20重量份,二丙酮醇为10至20重量份,异丙醇为5至30重量份,丙二醇甲醚醋酸酯为10至20重量份,碳酸丙烯酯为5至10重量份,乙二醇醚为5至20重量份、丙二醇醚类为5至20重量份
优选地,所述助溶剂为5至50重量份。
具体地,所述含水型溶剂用于稀释油性涂料。
具体地,所述有机溶剂用于溶解油性涂料。
综上所述,本发明提供一种降低油性涂料VOC排放的含水型溶剂。本发明的降低油性涂料VOC排放的含水型溶剂在有机溶剂中添加助溶剂,利用水的助溶性,将丙酮、甲基异丁基酮、二丙酮醇、异丙醇、丙二醇甲醚醋酸酯、碳酸丙烯酯、乙二醇醚、及丙二醇醚类与水混合,制成含水型溶剂。使用本发明稀释油性涂料时,能保持涂料性质还是油性,使得油性涂料的性能仍能满足实际使用需求及性能测试,在不改变油性涂料的配方的前提下,能大幅度降低油性涂料VOC的排放。并且助溶剂采用水,而水的成本很低,对环境没有污染,因此本发明经济、节能又环保。
以上所述,对于本领域的普通技术人员来说,可以根据本发明的技术方案和技术构思作出其他各种相应的改变和变形,而所有这些改变和变形都应属于本发明后附的权利要求的保护范围。
Claims (9)
1.一种降低油性涂料VOC排放的含水型溶剂,其特征在于,包括有机溶剂及助溶剂;所述有机溶剂为与水部分相溶或全水溶性的溶剂,所述助溶剂为水。
2.如权利要求1所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述有机溶剂包括丙酮、甲基异丁基酮、二丙酮醇、异丙醇、丙二醇甲醚醋酸酯、碳酸丙烯酯、乙二醇醚、及丙二醇醚类。
3.如权利要求1所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述水为去离子水、纯净水中的一种。
4.如权利要求2所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述有机溶剂为50至99重量份,所述助溶剂为1至50重量份。
5.如权利要求4所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述有机溶剂中,丙酮为5至40重量份,甲基异丁基酮为5至20重量份,二丙酮醇为5至25重量份,异丙醇为0至40重量份,丙二醇甲醚醋酸酯为5至20重量份,碳酸丙烯酯为5至15重量份,乙二醇醚为0至25重量份、丙二醇醚类为0至25重量份。
6.如权利要求5所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述有机溶剂中,丙酮为10至35重量份,甲基异丁基酮为10至20重量份,二丙酮醇为10至20重量份,异丙醇为5至30重量份,丙二醇甲醚醋酸酯为10至20重量份,碳酸丙烯酯为5至10重量份,乙二醇醚为5至20重量份、丙二醇醚类为5至20重量份。
7.如权利要求4所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述助溶剂为5至50重量份。
8.如权利要求1所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,用于稀释油性涂料。
9.如权利要求1所述的降低油性涂料VOC排放的含水型溶剂,其特征在于,所述有机溶剂用于溶解油性涂料。