CN111515493A - 一种适用于节Ni型低温钢焊条电弧焊焊接方法 - Google Patents
一种适用于节Ni型低温钢焊条电弧焊焊接方法 Download PDFInfo
- Publication number
- CN111515493A CN111515493A CN202010299807.5A CN202010299807A CN111515493A CN 111515493 A CN111515493 A CN 111515493A CN 202010299807 A CN202010299807 A CN 202010299807A CN 111515493 A CN111515493 A CN 111515493A
- Authority
- CN
- China
- Prior art keywords
- welding
- equal
- less
- percent
- type low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开一种适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于采用合适的焊接材料和焊接工艺保证焊接接头力学综合性能,采用本发明焊接方法,焊接接头焊缝及热影响区‑120℃冲击功KV2≥27J、抗拉强度Rm:≥530MPa、焊接接头侧弯d=4a,180°合格,焊接接头具有优良的力学综合性能。
Description
技术领域
本发明属于钢铁材料焊接技术领域,特别是涉及一种焊接接头力学综合性能优良的16~30mm厚节Ni型低温钢N390UD的焊条电弧焊焊接方法。
背景技术
Ni是提高钢低温韧性的主要元素,但其昂贵的价格以及我国镍资源贫乏的现状,限制了Ni在低温钢的应用,阻碍了Ni系列低温钢的发展。以得到低温钢力学性能和使用性能为前提,通过其它元素,如Mn元素,替代Ni元素,既可以合理利用资源,又可有效降低钢材的成本,成为近年来新型低温钢研发的热点和趋势。
仅含0.85~1.25%Ni的节Ni型N390UD低温钢,通过Q-L-T热处理工艺,获得了以贝氏体+残余奥氏体为主的显微组织,保证屈服强度达到390MPa、抗拉强度达到530MPa的同时,实现了-120℃不低于80J的优良的冲击韧性。
该低温钢仍然以焊接技术进行连接,以形成用于储备和运输低温储罐等的结构。该新型低温钢是否有较宽的焊接工艺窗口,焊接后其接头性能,特别是焊接接头的低温冲击韧性,能否达到标准或用户要求,成为该钢种进入市场的第一道门槛。合理的节Ni型低温钢N390UD焊接工艺对于结构安全使用具有重要的现实意义
发明内容
本发明的目的就是提供一种适用于16~30mm厚节Ni型低温钢N390UD焊条电弧焊焊接方法,保证焊接接头力学综合性能满足要求。
本发明的目的是通过以下技术方案来实现的:
一种适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于采用合适的焊接材料和焊接工艺保证焊接接头力学综合性能,具体如下:
(1)采用的母材:
母材化学成分及重量百分比为C:0.03~0.08%,Si:0.05~0.20%,Mn:0.85~1.75%,Ni:0.85~1.25%,Mo:≤0.20%,Al:0.015~0.06%,P:≤0.010%,S:≤0.002%,,余量为Fe和不可避免的杂质;
(2)采用的焊接材料:
焊条化学成分及重量百分比为:C:0.01~0.12%,Mn:3.0~5.0%,Si:0.20~0.30%,S:≤0.01%,P:≤0.02%,Ni:13.0~16.0%,Cr:16.0~20.0%,Mo:≤0.01%,V:≤0.01%,余量为Fe及不可避免杂质;
(3)采用的焊接参数:
坡口形式:对称X型坡口,坡口角度为55~65°,钝边尺寸为0~2mm;
焊前不预热,层间温度≤100℃;反面焊接前进行清根处理;
采用焊条电弧焊,焊接电流110~150A,电弧电压20~26,焊接速度13~20cm/min,焊接热输入7~18kJ/cm。
本发明焊接方法满足焊接接头力学综合性能优良的16~30mm厚节Ni型低温钢N390UD的焊条电弧焊焊接关键技术,采用合适的焊接材料和焊接工艺能够保证焊接接头抗拉强度,焊缝及热影响区-120℃冲击功KV2≥27J、抗拉强度Rm:≥530MPa、焊接接头侧弯d=4a,180°合格,焊接接头具有优良的力学综合性能。
附图说明
图1是焊接坡口图。
具体实施方式
下面对本发明技术方案做进一步详细说明。
实施例1
一种适用于节Ni型低温钢焊条电弧焊焊接方法,采用屈服强度≥390MPa,抗拉强度≥530MPa,延伸率≥20%,-120℃冲击功KV2≥80J性能优良的16mm厚节Ni型低温钢,焊接试板组合为16mm+16mm,试板尺寸为500mm(长)×200mm(宽)×16mm(厚);
母材化学成分及重量百分比为C:0.03~0.08%,Si:0.05~0.20%,Mn:0.85~1.75%,Ni:0.85~1.25%,Mo:≤0.20%,Al:0.015~0.06%,P:≤0.010%,S:≤0.002%,,余量为Fe和不可避免的杂质。
为了保证焊缝-120℃低温冲击功KV2≥27J,且焊缝金属的强度与母材尽可能匹配,匹配的焊接材料:化学成分及重量百分比为:C:0.01~0.12%,Mn:3.0~5.0%,Si:0.20~0.30%,S:≤0.01%,P:≤0.02%,Ni:13.0~16.0%,Cr:16.0~20.0%,Mo:≤0.01%,V:≤0.01%,余量为Fe及不可避免杂质。焊条直径为Φ4.0mm,焊丝抗拉强度≥570MPa。
坡口型式为X型坡口,坡口角度为55°,钝边为1mm,坡口装配间隙为0.5mm;
焊前不预热,层间温度60~100℃;反面焊接前进行砂轮机清根处理,根部成金属光泽;
采用焊条电弧焊,焊接电流115A,电弧电压22V,焊接速度17cm/min,焊接热输入量9kJ/cm。
实施例2
一种适用于节Ni型低温钢焊条电弧焊焊接方法,采用屈服强度≥390MPa,抗拉强度≥530MPa,延伸率≥20%,-120℃冲击功KV2≥80J性能优良的20mm厚节Ni型低温钢,焊接试板组合为20mm+20mm,试板尺寸为500mm(长)×200mm(宽)×20mm(厚);
母材化学成分及重量百分比为C:0.03~0.08%,Si:0.05~0.20%,Mn:0.85~1.75%,Ni:0.85~1.25%,Mo:≤0.20%,Al:0.015~0.06%,P:≤0.010%,S:≤0.002%,,余量为Fe和不可避免的杂质。
为了保证焊缝-120℃低温冲击功KV2≥27J,且焊缝金属的强度与母材尽可能匹配,匹配的焊接材料:化学成分及重量百分比为:C:0.01~0.12%,Mn:3.0~5.0%,Si:0.20~0.30%,S:≤0.01%,P:≤0.02%,Ni:13.0~16.0%,Cr:16.0~20.0%,Mo:≤0.01%,V:≤0.01%,余量为Fe及不可避免杂质。焊条直径为Φ4.0mm,焊丝抗拉强度≥570MPa。
坡口型式为X型坡口,坡口角度为60°,钝边为1mm,坡口装配间隙为1mm;
焊前不预热,层间温度60~100℃;反面焊接前进行砂轮机清根处理,根部成金属光泽;
采用焊条电弧焊,焊接电流130A,电弧电压24V,焊接速度15cm/min,焊接热输入量13kJ/cm。
实施例3
一种适用于节Ni型低温钢焊条电弧焊焊接方法,采用屈服强度≥390MPa,抗拉强度≥530MPa,延伸率≥20%,-120℃冲击功KV2≥80J性能优良的30mm厚节Ni型低温钢,焊接试板组合为30mm+30mm,试板尺寸为500mm(长)×200mm(宽)×30mm(厚);
母材化学成分及重量百分比为C:0.03~0.08%,Si:0.05~0.20%,Mn:0.85~1.75%,Ni:0.85~1.25%,Mo:≤0.20%,Al:0.015~0.06%,P:≤0.010%,S:≤0.002%,,余量为Fe和不可避免的杂质。
为了保证焊缝-120℃低温冲击功KV2≥27J,且焊缝金属的强度与母材尽可能匹配,匹配的焊接材料:化学成分及重量百分比为:C:0.01~0.12%,Mn:3.0~5.0%,Si:0.20~0.30%,S:≤0.01%,P:≤0.02%,Ni:13.0~16.0%,Cr:16.0~20.0%,Mo:≤0.01%,V:≤0.01%,余量为Fe及不可避免杂质。焊条直径为Φ4.0mm,焊丝抗拉强度≥570MPa。
坡口型式为X型坡口,坡口角度为58°,钝边为1mm,坡口装配间隙为0.5mm;
焊前不预热,层间温度60~100℃;反面焊接前进行砂轮机清根处理,根部成金属光泽;
采用焊条电弧焊,焊接电流145A,电弧电压25V,焊接速度13cm/min,焊接热输入量17kJ/cm。
经过上述实施例1~3的焊接方法对节Ni型低温钢进行焊条电弧焊后,对焊接接头的力学性能进行检测。焊接接头的冲击、拉伸和弯曲性能如表1所示。
表1焊接接头的拉伸及侧弯性能
可见,实施例1~3得到的焊接接头的综合力学性能优良。焊缝及热影响区-120℃冲击功KV2≥27J、抗拉强度Rm:≥530MPa、焊接接头侧弯d=4a,180°合格。并且本发明焊接方法简单易操作,适用性很强。
Claims (6)
1.一种适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于采用合适的焊接材料和焊接工艺保证焊接接头力学综合性能,具体如下:
(1)采用的母材:
母材化学成分及重量百分比为C:0.03~0.08%,Si:0.05~0.20%,Mn:0.85~1.75%,Ni:0.85~1.25%,Mo:≤0.20%,Al:0.015~0.06%,P:≤0.010%,S:≤0.002%,,余量为Fe和不可避免的杂质;
(2)采用的焊接材料:
焊条化学成分及重量百分比为:C:0.01~0.12%,Mn:3.0~5.0%,Si:0.20~0.30%,S:≤0.01%,P:≤0.02%,Ni:13.0~16.0%,Cr:16.0~20.0%,Mo:≤0.01%,V:≤0.01%,余量为Fe及不可避免杂质;
(3)采用的焊接参数:
坡口形式:对称X型坡口,坡口角度为55~65°,钝边尺寸为0~2mm;
焊前不预热,层间温度≤100℃;反面焊接前进行清根处理;
采用焊条电弧焊,焊接电流110~150A,电弧电压20~26,焊接速度13~20cm/min,焊接热输入7~18kJ/cm。
2.如权利要求1所述的适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于焊接接头焊缝及热影响区-120℃低温冲击功KV2≥27J、抗拉强度≥530MPa、焊接接头侧弯d=4a,180°合格。
3.如权利要求1所述的适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于母材的屈服强度≥390MPa,抗拉强度≥530MPa,延伸率≥20%,-120℃冲击功KV2≥80J。
4.如权利要求1所述的适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于坡口装配留0~2mm间隙。
5.如权利要求1所述的适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于层间温度60~100℃。
6.如权利要求1所述的适用于节Ni型低温钢焊条电弧焊焊接方法,其特征在于焊条直径Φ4.0mm,焊丝抗拉强度≥570MPa。