CN111187068A - 一种纪念珠及其制备方法 - Google Patents
一种纪念珠及其制备方法 Download PDFInfo
- Publication number
- CN111187068A CN111187068A CN202010069227.7A CN202010069227A CN111187068A CN 111187068 A CN111187068 A CN 111187068A CN 202010069227 A CN202010069227 A CN 202010069227A CN 111187068 A CN111187068 A CN 111187068A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- raw material
- functional raw
- bone ash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纪念珠及其制备方法。本发明一实施例的纪念珠,包括如下重量份数的原料:骨灰粉50‑70份;功能性原料粉20‑80份;粘合剂5‑8份;水25‑30份;其中,所述功能性原料粉包括朱砂粉,糯米粉、黑曜石粉、孔雀石粉、碧玺粉、红珊瑚粉、水晶粉、石榴石粉、珍珠粉和玳瑁粉中的一种或多种原料。本发明实施例的纪念珠由于添加了功能性原料粉,因此能够起到缓解疲劳、安神、提高人体免疫力的作用。本发明实施例的纪念珠可镶嵌在吊坠等随身携带的挂件上,以便随时缅怀先人;这样不仅节约了土地资源,减轻了家属经济负担;而且传统的祭拜节日也不再需要去墓地,减缓由集中祭拜时导致的交通拥堵。
Description
技术领域
本发明属于材料制备技术领域,尤其涉及一种纪念珠及其制备方法。
背景技术
我国民族众多,殡葬习俗纷繁庞杂。历史上,中国各民族有天葬、水葬、土葬、火葬、野葬、崖葬、保存干尸等多种葬法,广大汉族地区以土葬最为普遍。在国内,目前遗体的处理方式一般为火葬,遗体火化处理成骨灰后,家属将骨灰放入骨灰盒中存放到墓地里面;但是修建墓地占用了大量的土地资源,也破坏了环境资源。
随着社会经济的发展,人们对葬式也在不断的探索;树葬、花坛葬、海葬等新型的节地环保葬不断的推出,从一定程度上缓解了土地危机,但是依然不能从根本上解决土地资源被占用的问题。
发明内容
鉴于此,为了解决现有技术中殡葬占用土地资源的问题,本发明提供一种纪念珠及其制备方法。
本发明在第一方面提供了一种纪念珠,包括如下重量份数的原料:
骨灰粉50-70份;功能性原料粉20-80份;粘合剂5-8份;水25-30份;其中,所述功能性原料粉包括朱砂粉,糯米粉、黑曜石粉、孔雀石粉、碧玺粉、红珊瑚粉、水晶粉、石榴石粉、珍珠粉和玳瑁粉中的一种或多种原料。
进一步,所述骨灰粉和功能性原料粉的粒径均为500-1000目。
进一步,所述的纪念珠还包括如下重量份数的原料:颗粒镶嵌物10-40份,所述颗粒镶嵌物的粒径为2-4mm;所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种。
进一步,所述粘合剂为膨润土。
进一步,所述的纪念珠包括如下重量份数的原料:骨灰粉50-70份,所述骨灰粉的粒径为500-800目;功能性原料粉20-80份,所述功能性原料粉的粒径为500-800目,所述功能性原料粉包括:朱砂粉2-8份,糯米粉2-8份、黑曜石粉2-8份、孔雀石粉2-8份、碧玺粉2-8份、红珊瑚粉2-8份、水晶粉2-8份、石榴石粉2-8份、珍珠粉2-8份和玳瑁粉2-8份;颗粒镶嵌物10-40份,所述颗粒镶嵌物的粒径为2-4mm,所述颗粒镶嵌物包括黑曜石2-8份、孔雀石2-8份、碧玺2-8份、水晶2-8份,以及石榴石2-8份;粘合剂5-8份;水25-30份。
本发明在第二方面提供由本发明在第一方面所述纪念珠的制备方法。
一种纪念珠的制备方法,包括如下步骤:将所述功能性原料中每种原料组分进行研磨,得到功能性原料粉;其中,所述功能性原料包括朱砂,糯米、黑曜石、孔雀石、碧玺、红珊瑚、水晶、石榴石、珍珠和玳瑁中的一种或多种原料;将人体骨灰进行研磨,得到骨灰粉;将所述功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体;对所述中间体进行烧结,得到纪念珠。
进一步,所述对所述中间体进行烧结,得到纪念珠,包括:对所述中间体的表面嵌入颗粒镶嵌物,其中,所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种;将所述嵌入颗粒镶嵌物的中间体进行烧结,然后降温至室温后得到纪念珠。
进一步,所述将所述功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体,包括:将所述功能性原料粉和骨灰粉按比例混合均匀,得到第一混合原料;将所述第一混合原料、粘合剂和水混合均匀,得到第二混合原料;将所述第二混合原料通过模具注塑成型,得到中间体。
进一步,所述烧结的温度为1000-2000℃,所述烧结的时间为2-3h。
进一步,所述模具的材料为耐火陶瓷材料;更进一步,所述模具为耐火的球形模具、柱形模具或其他造型的模具。
本发明与现有技术相比至少具有如下有益效果:
1)本发明实施例基于骨灰制备的纪念珠外表晶莹光泽,质地坚硬,具有多种天然矿物颜色,绚丽多彩。
2)本发明实施例制备的纪念珠由于添加了功能性原料粉,因此能够起到缓解疲劳、安神、提高人体免疫力的作用。
3)本发明实施例的基于骨灰制备的纪念珠可镶嵌在吊坠、手链、汽车摆件,以及挂坠等工艺品上,以便随时缅怀先人;这样不仅节约了土地资源,减轻了家属经济负担。而且传统的祭拜节日也不再需要去墓地,减缓由集中祭拜时导致的交通拥堵。
附图说明
图1为本发明实施例3中一种纪念珠的制备方法的流程图。
具体实施方式
为使本发明的目的、特征、优点能够更加的明显和易懂,下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而非全部实施例。基于本发明中的实施例,本领域技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
朱砂,中药名。为硫化物类矿物辰砂族辰砂,主含硫化汞(HgS)。本品为粒状或块状集合体,呈颗粒状或块片状。鲜红色或暗红色,条痕红色至褐红色,具光泽。朱砂有清心镇惊,安神,明目,解毒的功效。
黑曜石是一种常见的黑色宝石,又称“龙晶”、“十胜石”,是一种自然形成的二氧化硅,通常呈黑色。黑曜石是从火山熔岩流出来的岩浆突然冷却后形成的天然琉璃,属于非晶质的宝石,其主要成分为二氧化硅(SiO2)。
孔雀石是一种古老的玉料,主要成分为碱式碳酸铜。孔雀石由于颜色酷似孔雀羽毛上斑点的绿色而获得如此美丽的名字。孔雀石产于铜的硫化物矿床氧化带,常与其它含铜矿物共生(蓝铜矿、辉铜矿、赤铜矿、自然铜等)。孔雀石是一种含铜碳盐的蚀变产物,常作为铜矿的伴生产物。它的硬度是3.5-4,呈不透明的深绿色,且具有色彩浓淡的条状花纹,这种独一无二的美丽是其它任何宝石所没有的。“孔雀石”一词具有“妻子幸福”的寓意。天然孔雀石呈现浓绿,翠绿的光泽,虽不具备珠宝的璀璨,但是却是一种高贵之石,有种独一无二的高雅气质。
碧玺是电气石的工艺品名,是电气石族里达到珠宝级的一个种类,是一种硼硅酸盐结晶体,含有铝、铁、镁、钠、锂、钾等化学元素,呈现各式各样的颜色。碧玺艳丽鲜艳的彩虹色彩,可以给人开心高兴、神往自在的感觉,有助于开拓胸怀和视界,并对治愈懊丧等心理疾病具有必定的辅佐治疗效果。碧玺包含的能量,具有镇静的效果,可以使人集中精力。而且多变的色彩可以激发构思和创意,从而使人行事稳当、竭尽全力,使事业欣欣向荣。
碧玺被认为是榜首旺夫石,这种称法来源于广东文明。在广东,面相姣好的女子被认为是旺夫的。俗话说“相由心生”,碧玺会使人心境转好,因而常常佩带的人也会变得水润光泽、非常美丽,具有旺夫相。碧玺可以放射出极具亲和力的磁场,可以消除人与人之间的隔膜,对爱情和友谊有着天然的招引效果。与此同时,具有首领气质的人佩带碧玺,可以开释更多魅力,招引更多人聚拢而来。除了上述效果以外,红绿碧玺,还具有敛财纳富的涵义。其间,赤色碧玺因为色彩与血液挨近,因而,人们认为赤色碧玺还具有促进血液循环的保健效果,对治疗头晕、贫血具有较好效果。
红珊瑚属有机宝石,色泽喜人,质地莹润,生长于远离人类的100至2000米的深海中。与珍珠、琥珀并列为三大有机宝石,在东方佛典中亦被列为七宝之一,自古即被视为富贵祥瑞之物。红珊瑚由无机质和有机质两部分组成。无机质:高镁方解石、少量磷灰石,碳酸钙,碳酸镁,少量水,氧化亚铁,羟基磷酸钙。有机质:以角质为主。红珊瑚文化在中国以及印度、印第安民族传统文化中都有悠久的历史,尤其是印第安土著民族和中国藏族等游牧民族对红珊瑚更是喜爱有加,甚至把红珊瑚作为护身和祈祷“上天(帝)”保佑的寄托物。红珊瑚还有定惊、明目的功能。也可作惊痫、角膜炎的药物。
水晶是稀有矿物,宝石的一种,石英结晶体,在矿物学上属于石英族。主要化学成份是二氧化硅,化学式为SiO2。纯净时形成无色透明的晶体。当含微量元素Al、Fe等时呈粉色、紫色、黄色,茶色等。经辐照微量元素形成不同类型的色心,产生不同的颜色,如紫色、黄色、茶色,粉色等。含伴生包裹体矿物的被称之为包裹体水晶,如发晶、绿幽灵、红兔毛等,内包物为金红石、电气石、阳起石、云母,绿泥石等。水晶在一定程度上能增强人的体质和活力,提升精气神,对筋骨和神经***有很好的作用。
石榴石,中国古时称为紫鸦乌或子牙乌,是一组在青铜时代已经使用为宝石及研磨料的矿物。常见的石榴石为红色。石榴石是一种形状像石榴一样的矿物、矿石,它可以打磨成我们的饰品,包括手镯、链或者是其他的饰品来佩戴,它对身体有一定的保健作用,主要的体现在这几个方面,第一个,它能够改善咱们的血液循环,促进血液循环、增强活力,进而达到这个美容养颜的功效,第二个,它能够有助于改善生殖***的功能,增强身体的再生能力,第三个,对于经常熬夜的或者加班的或者是工作生活比较疲劳的人,它能够帮助恢复体力。
珍珠是一种古老的有机宝石,主要产在珍珠贝类和珠母贝类软体动物体内;而由于内分泌作用而生成的含碳酸钙的矿物(文石)珠粒,是由大量微小的文石晶体集合而成的;种类丰富,形状各异,色彩斑斓;根据地质学和考古学的研究证明,在两亿年前,地球上就已经有了珍珠。具有瑰丽色彩和高雅气质的珍珠,象征着健康、纯洁、富有和幸福,自古以来为人们所喜爱。《中华人民共和国药典》及《中药大辞典》均指明:珍珠具有安神定惊、明目去翳、解毒生肌等功效,现代研究还表明珍珠在提高人体免疫力、延缓衰老、祛斑美白、补充钙质等方面都具有独特的作用。
玳瑁是一种有机宝石,成分:由角质和骨质等有机质组成;硬度:2-3;特指玳瑁的背甲,为非晶质体,呈微透明至半透明,具蜡质至油脂光泽。材料珍稀,质地晶莹剔透,花纹清晰美丽,色泽柔和明亮,用它做成的工艺饰品光彩夺目,宝气华盛,品位高贵典雅,是一种神奇而不可思议的“海洋瑰宝”。在东方人眼中,玳瑁就是吉祥长寿、辟邪纳福的象征,深得历代皇室贵族、富豪人家乃至广大民众的喜爱。若佩戴于身,可避露水风邪;入药则有清热解毒、定惊去风湿的特殊功效。因而是极具药材的经济价值、首饰、装饰品价值与收藏价值的上等佳品。
骨灰是人焚烧后骨骼化成的灰,人体骨灰X射线粉晶衍射中显示,和磷灰石很相近,因为火化后,人体的有机质已经全部燃烧,剩下的成分就是无机质,元素成分以钙、磷、氧、碳为主。
本发明实施例在第一方面提供一种纪念珠,包括如下重量份数的原料:骨灰粉50-70份(例如50、55、60、65或70份等);功能性原料粉20-80份(例如20、30、40、50、60、70或80份等);粘合剂5-8份(例如5、6、7或8份等);水25-30份(例如25、26、27、28、29或30份等);其中,所述功能性原料粉包括朱砂粉,糯米粉、黑曜石粉、孔雀石粉、碧玺粉、红珊瑚粉、水晶粉、石榴石粉、珍珠粉和玳瑁粉中的一种或多种原料。
本发明实施例的纪念珠是一种纪念物,是对逝去的亲属的一种有形的怀念,也是一种精神寄托。由于纪念珠中添加了功能性原料粉,因此能够起到缓解疲劳、安神、提高人体免疫力的作用。
本发明实施例的纪念珠可镶嵌在吊坠、手链、汽车摆件,以及挂坠等工艺品上,因此能够随时缅怀先人;这样不仅节约了土地资源,减轻了家属经济负担。而且传统的祭拜节日也不再需要去墓地,减缓由集中祭拜时导致的交通拥堵。
在可选的实施例中,为了使骨灰粉和功能性原料粉在高温条件下能够更好地融合,所述骨灰粉和功能性原料粉的粒径均为500-1000目(例如500、600、700、800、900或1000目等)。
在可选的实施例中,所述纪念珠还包括如下重量份数的原料:颗粒镶嵌物10-40份,所述颗粒镶嵌物的粒径为2-4mm(例如2、2.5、3、3.5或4mm等);所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种。
本发明实施例的纪念珠通过添加颗粒镶嵌物,不仅能够修饰纪念珠,使纪念珠绚丽多彩,而且还能够提高人体的免疫力。
在可选的实施例中,所述粘合剂为膨润土。
本发明实施例通过添加粘合剂,能够将骨灰粉和功能性原料粉进行有效的粘结。
在可选的实施例中,所述的纪念珠,包括如下重量份数的原料:骨灰粉50-70份(例如50、55、60、65或70份等),所述骨灰粉的粒径为500-800目(例如500、600、700或800目等);功能性原料粉20-80份,所述功能性原料粉的粒径为500-800目(例如500、600、700或800目等),所述功能性原料粉包括:朱砂粉2-8份(例如2、3、4、5、6、7或8份等),糯米粉2-8份(例如2、3、4、5、6、7或8份等)、黑曜石粉2-8份(例如2、3、4、5、6、7或8份等)、孔雀石粉2-8份(例如2、3、4、5、6、7或8份等)、碧玺粉2-8份(例如2、3、4、5、6、7或8份等)、红珊瑚粉2-8份(例如2、3、4、5、6、7或8份等)、水晶粉2-8份(例如2、3、4、5、6、7或8份等)、石榴石粉2-8份(例如2、3、4、5、6、7或8份等)、珍珠粉2-8份(例如2、3、4、5、6、7或8份等)和玳瑁粉2-8份(例如2、3、4、5、6、7或8份等);颗粒镶嵌物10-40份(例如10、15、20、25、30或40份等),所述颗粒镶嵌物的粒径为2-4mm(例如2、2.5、3、3.5或4mm等),所述颗粒镶嵌物包括黑曜石2-8份(例如2、3、4、5、6、7或8份等)、孔雀石2-8份(例如2、3、4、5、6、7或8份等)、碧玺2-8份(例如2、3、4、5、6、7或8份等)、水晶2-8份(例如2、3、4、5、6、7或8份等),以及石榴石2-8份(例如2、3、4、5、6、7或8份等);粘合剂5-8份(例如5、6、7或8份等);水25-30份(例如25、26、27、28、29或30份等)。
本发明实施例的纪念珠通过添加由多种药物组分组合形成的功能性原料粉、骨灰粉,以及颗粒镶嵌物,不仅能够实现随时随地缅怀先人,而且具有美观性,能够起到缓解疲劳、安神、提高人体免疫力的作用。
本发明实施例在第二方面还提供一种纪念珠的制备方法,包括如下步骤:将所述功能性原料中每种原料组分进行研磨,得到功能性原料粉;其中,所述功能性原料包括朱砂,糯米、黑曜石、孔雀石、碧玺、红珊瑚、水晶、石榴石、珍珠和玳瑁中的一种或多种原料;将人体骨灰进行研磨,得到骨灰粉;将所述功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体;对所述中间体进行烧结,得到纪念珠。
本发明实施例通过粘结剂将功能性原料粉和骨灰粉进行连接;而后通过注塑成型使中间体具有特定的形状;最后通过对中间体进行烧结,从而使得功能性原料粉、骨灰粉和粘结剂能够更好的融合,进而获得外表光泽,质地坚硬的纪念珠。
在可选的实施例中,所述对所述中间体进行烧结,得到纪念珠,包括:对所述中间体的表面嵌入颗粒镶嵌物,其中,所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种;将所述嵌入颗粒镶嵌物的中间体进行烧结,然后降温至室温后得到纪念珠。
本发明实施例通过对注塑成型的中间体的外表面镶嵌颗粒镶嵌物,从而使制得的纪念珠绚丽多彩,具有美观性,能够满足不同使用者对纪念珠的视觉需求。
在可选的实施例中,所述将所述功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体,包括:将所述功能性原料粉和骨灰粉按比例混合均匀,得到第一混合原料;将所述第一混合原料、粘合剂和水混合均匀,得到第二混合原料;将所述第二混合原料通过模具注塑成型,得到中间体。
本发明实施例先将功能性原料粉和骨灰粉按比例混合均匀,而后再同粘合剂、水进行混合,从而使得功能性原料粉和骨灰粉你能够均匀分散在粘合剂水溶液中,进而获得质地均匀的纪念珠。
在优选的实施例中,所述烧结的温度为1000-2000℃(例如1000、1300、1500或2000℃等),所述烧结的时间为2-3h(例如2、2.3、2.5、2.8或3h等)。
本发明实施例通过选择合适的烧结温度和烧结时间,从而能够使得功能性原料粉、骨灰粉和粘合剂能够更好地融合,进而获得外表晶莹光泽,质地坚硬,绚丽多彩的纪念珠。本实施例的纪念珠还具有缓解疲劳、安神、提高人体免疫力的作用。
在进一步的实施例中,所述模具的材料为耐火陶瓷材料;在进一步优选的实施例中,所述模具为耐火的球形模具、柱形模具或其他造型的模具。
本发明实施例的纪念珠经过二次加工后制成可随身佩戴的吊坠、手链、以及汽车上摆件、挂坠等工艺品,从而能够随时缅怀先人,进而节约土地资源。
另外注意的是,如果没有特别说明,本发明所记载的任何范围包括端值以及端值之间的任何数值以及以端值或者端值之间的任意数值所构成的任意子范围。
实施例1
一种纪念珠,其特征在于,包括如下重量份数的原料:粒径为500-1000目的骨灰粉50-70份;粒径为500-1000目的功能性原料粉20-80份;膨润土5-8份;水25-30份;其中,所述功能性原料粉包括朱砂粉,糯米粉、黑曜石粉、孔雀石粉、碧玺粉、红珊瑚粉、水晶粉、石榴石粉、珍珠粉和玳瑁粉中的一种或多种原料。
本发明实施例对纪念珠的制备方法不作限定,只要通过上述原料能够获得纪念珠即可。本发明实施例基于骨灰制备的纪念珠外表晶莹光泽,质地坚硬;具有缓解疲劳、安神、提高人体免疫力的作用。
实施例2
一种纪念珠,其特征在于,包括如下重量份数的原料:粒径为500-1000目的骨灰粉50-70份;粒径为500-1000目的功能性原料粉20-80份;膨润土5-8份;水25-30份;颗粒镶嵌物10-40份;其中,所述功能性原料粉包括朱砂粉,糯米粉、黑曜石粉、孔雀石粉、碧玺粉、红珊瑚粉、水晶粉、石榴石粉、珍珠粉和玳瑁粉中的一种或多种原料;所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种。
本发明实施例对纪念珠的制备方法不作限定,只要通过上述原料能够获得纪念珠即可。
本发明实施例基于骨灰制备的纪念珠外表具有多种天然矿物颜色,绚丽多彩。
实施例3
一种纪念珠,其特征在于,包括如下重量份数的原料:骨灰粉50-70份,所述骨灰粉的粒径为500-800目;功能性原料粉20-80份,所述功能性原料粉的粒径为500-800目,所述功能性原料粉包括:朱砂粉2-8份,糯米粉2-8份、黑曜石粉2-8份、孔雀石粉2-8份、碧玺粉2-8份、红珊瑚粉2-8份、水晶粉2-8份、石榴石粉2-8份、珍珠粉2-8份和玳瑁粉2-8份;颗粒镶嵌物10-40份,所述颗粒镶嵌物的粒径为2-4mm,所述颗粒镶嵌物包括黑曜石2-8份、孔雀石2-8份、碧玺2-8份、水晶2-8份,以及石榴石2-8份;膨润土5-8份;水25-30份。
如图1所示,一种纪念珠的制备方法,包括如下步骤:
S101:将功能性原料中每种原料组分进行研磨,得到功能性原料粉;其中,功能性原料包括朱砂,糯米、黑曜石、孔雀石、碧玺、红珊瑚、水晶、石榴石、珍珠和玳瑁;
具体地,所述功能性原料粉的粒径为500-800目;
S102:将人体骨灰进行研磨,得到骨灰粉;
具体地,骨灰粉的粒径为500-800目。
S103:将功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体;
具体地,将所述功能性原料粉和骨灰粉按比例混合均匀,得到第一混合原料;将所述第一混合原料、粘合剂和水混合均匀,得到第二混合原料;将所述第二混合原料通过球形模具注塑成型,得到中间体。
S104:对中间体进行烧结,得到纪念珠。
具体地,对所述中间体的表面嵌入颗粒镶嵌物,其中,所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石;将所述嵌入颗粒镶嵌物的中间体进行烧结,然后降温至室温后得到纪念珠。所述烧结的温度为1000-2000℃,所述烧结的时间为2-3h。
本发明实施例的基于骨灰制备的纪念珠可镶嵌在吊坠、手链、汽车摆件,以及挂坠等工艺品上,以便随时缅怀先人;剩余的骨灰可以选择生态节地葬,使得骨灰的处理方式不再拘泥于购买墓地安放。这样不仅节约了土地资源,减轻了家属经济负担。而且传统的祭拜节日也不再需要去墓地,减缓由集中祭拜时导致的交通拥堵。
在本说明书的描述中,描述的具体特征、结构、材料或者特点可以在任一个或多个实施例或示例中以合适的方式结合。此外,在不相互矛盾的情况下,本领域的技术人员可以将本说明书中描述的不同实施例或示例以及不同实施例或示例的特征进行结合和组合。
此外,术语“第一”、“第二”仅用于描述目的,而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量。由此,限定有“第一”、“第二”的特征可以明示或隐含地包括至少一个该特征。在本发明的描述中,“多个”的含义是两个或两个以上,除非另有明确具体的限定。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应以所述权利要求的保护范围为准。
Claims (10)
1.一种纪念珠,其特征在于,包括如下重量份数的原料:
骨灰粉50-70份;功能性原料粉20-80份;粘合剂5-8份;水25-30份;
其中,所述功能性原料粉包括朱砂粉,糯米粉、黑曜石粉、孔雀石粉、碧玺粉、红珊瑚粉、水晶粉、石榴石粉、珍珠粉和玳瑁粉中的一种或多种原料。
2.根据权利要求1所述的纪念珠,其特征在于,所述骨灰粉和功能性原料粉的粒径均为500-1000目。
3.根据权利要求2所述的纪念珠,其特征在于,还包括如下重量份数的原料:
颗粒镶嵌物10-40份,所述颗粒镶嵌物的粒径为2-4mm;
所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种。
4.根据权利要求2所述的纪念珠,其特征在于,所述粘合剂为膨润土。
5.根据权利要求3所述的纪念珠,其特征在于,包括如下重量份数的原料:
骨灰粉50-70份,所述骨灰粉的粒径为500-800目;
功能性原料粉20-80份,所述功能性原料粉的粒径为500-800目,所述功能性原料粉包括:朱砂粉2-8份,糯米粉2-8份、黑曜石粉2-8份、孔雀石粉2-8份、碧玺粉2-8份、红珊瑚粉2-8份、水晶粉2-8份、石榴石粉2-8份、珍珠粉2-8份和玳瑁粉2-8份;
颗粒镶嵌物10-40份,所述颗粒镶嵌物的粒径为2-4mm,所述颗粒镶嵌物包括黑曜石2-8份、孔雀石2-8份、碧玺2-8份、水晶2-8份,以及石榴石2-8份;
粘合剂5-8份;
水25-30份。
6.一种如权利要求1至5任一所述纪念珠的制备方法,其特征在于,包括如下步骤:
将所述功能性原料中每种原料组分进行研磨,得到功能性原料粉;其中,所述功能性原料包括朱砂,糯米、黑曜石、孔雀石、碧玺、红珊瑚、水晶、石榴石、珍珠和玳瑁中的一种或多种原料;
将人体骨灰进行研磨,得到骨灰粉;
将所述功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体;
对所述中间体进行烧结,得到纪念珠。
7.根据权利要求6所述的制备方法,其特征在于,所述对所述中间体进行烧结,得到纪念珠,包括:
对所述中间体的表面嵌入颗粒镶嵌物,其中,所述颗粒镶嵌物包括黑曜石、孔雀石、碧玺、水晶,以及石榴石中的一种或多种;
将所述嵌入颗粒镶嵌物的中间体进行烧结,然后降温至室温后得到纪念珠。
8.根据权利要求6或7所述的制备方法,其特征在于,所述将所述功能性原料粉、骨灰粉、粘合剂和水混合均匀后注塑成型,得到中间体,包括:
将所述功能性原料粉和骨灰粉按比例混合均匀,得到第一混合原料;
将所述第一混合原料、粘合剂和水混合均匀,得到第二混合原料;
将所述第二混合原料通过模具注塑成型,得到中间体。
9.根据权利要求6或7所述的制备方法,其特征在于,所述烧结的温度为1000-2000℃,所述烧结的时间为2-3h。
10.根据权利要求6所述的制备方法,其特征在于,所述模具的材料为耐火陶瓷材料;优选地,所述模具为耐火的球形模具、柱形模具或其他造型的模具。