CN111116139B - 一种环保透水性混凝土及其制备方法 - Google Patents
一种环保透水性混凝土及其制备方法 Download PDFInfo
- Publication number
- CN111116139B CN111116139B CN201911397150.XA CN201911397150A CN111116139B CN 111116139 B CN111116139 B CN 111116139B CN 201911397150 A CN201911397150 A CN 201911397150A CN 111116139 B CN111116139 B CN 111116139B
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- zinc oxide
- permeable concrete
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
项目 | 透水系数(15℃) | 连续孔隙率 | 弯拉强度(28d) |
单位 | mm/s | % | MPa |
标准值 | ≥0.5 | ≥10 | ≥2.5 |
实施例1 | 18 | 33 | 5.3 |
实施例2 | 19 | 33 | 5.4 |
实施例3 | 19 | 35 | 5.6 |
实施例4 | 20 | 36 | 5.8 |
实施例5 | 22 | 38 | 6.0 |
对比例1 | 14 | 30 | 4.6 |
对比例2 | 13 | 28 | 4.8 |
对比例3 | 15 | 30 | 4.5 |
对比例4 | 12 | 26 | 5.0 |
Claims (5)