CN111085183A - Silicon oxide and titanium oxide composite material and synthesis method thereof - Google Patents
Silicon oxide and titanium oxide composite material and synthesis method thereof Download PDFInfo
- Publication number
- CN111085183A CN111085183A CN201811239858.8A CN201811239858A CN111085183A CN 111085183 A CN111085183 A CN 111085183A CN 201811239858 A CN201811239858 A CN 201811239858A CN 111085183 A CN111085183 A CN 111085183A
- Authority
- CN
- China
- Prior art keywords
- titanium oxide
- composite material
- synthesizing
- silicon oxide
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a silicon oxide and titanium oxide composite material and a synthesis method thereof. The synthesis method comprises the steps of mixing titanium oxide and an alcohol solvent, adding a buffer solution and a silicon source, stirring, standing, washing, drying, and finally performing heat treatment to obtain the silicon oxide/titanium oxide composite material. The silicon oxide/titanium oxide composite material provided by the invention has a core-shell structure, the shell layer is stably coated and is not easy to fall off, and the synthesis method is simple and easy.
Description
Technical Field
The invention belongs to the field of synthesis of porous inorganic materials, and particularly relates to a silicon oxide-containing composite material and a synthesis method thereof.
Background
The material with a core-shell structure is an important novel material, and is characterized in that a certain material is used as a core phase, and a layer of material of the same kind or different kinds grows on the outer surface of the core phase to form a shell layer, so that a composite structure similar to an eggshell form is formed. The core-shell material has a unique structure, so that the core-shell material has the advantages which are not possessed by a single-structure material, and has good application prospects in the fields of chemical industry, environmental protection and optics. But because of its unique and complex structure, the synthesis difficulty is far higher than that of common materials, mainly its structure is difficult to control, and its structure control and functionalization still need further research.
The titanium oxide has the advantages of stable chemical property, safety, no toxicity, long service life, low price, direct utilization of solar energy and the like, and has wide application in the aspect of photocatalytic degradation of environmental pollutants. "synthesis of iron-doped titanium dioxide and its photocatalytic performance" (proceedings of Shanghai engineering and technology university, volume 29, 3, 2015) an iron-doped titanium dioxide was synthesized, and its photocatalytic performance was examined, and it was found that the addition of iron element could improve its catalytic performance.
CN103007847A discloses a composite particle based on magnetic nano immobilized laccase and ionic liquid, a preparation method thereof and application thereof in removing pollutants in water. Firstly, magnetic gamma-Fe is prepared2O3A nanoparticle; then, the nano magnetic particles are used as a core phase, tetraethoxysilane and silane coupling agent are used as silicon sources, and a sol-gel method is utilized to prepare the nano core-shell type magnetic silicon dioxide with the surface amino functionalized; then, magnetic nano immobilized laccase and ionic liquid composite particles are prepared through a series of functional operations and can be applied to treatment for removing pollutants in water.
CN105036070A discloses a gold nanorod-silicon dioxide core-shell structure nanomaterial, a preparation method and application thereof, wherein the preparation method comprises the steps of preparing a chiral gold nanorod shoulder-side assembly body, and taking the assembly body as a core; and then coating the chiral gold nanorod side-by-side assembly body with a silicon dioxide shell layer in an alcohol-water system to prepare the functional material with the shell layer structure.
CN102160985A discloses a magnetic silica microsphere with core-shell structure and surface anisotropic dual-functional groups and a preparation method thereof, wherein the preparation method comprises the steps of firstly preparing superparamagnetic microspheres as iron oxide cores by a solvothermal method; then coating a layer of silicon dioxide on the iron oxide by using a sol-gel method to obtain a material with a core-shell structure; then, the material is functionalized, and finally the magnetic silica core-shell material with high magnetic responsiveness and surface bifunctional groups is obtained.
CN101885493A discloses a method for synthesizing a ZSM-5/β core-shell type molecular sieve, which comprises the steps of treating a core-phase ZSM-5 molecular sieve to enable the surface of the core-phase ZSM-5 molecular sieve to adsorb β nano crystals, then adding other raw materials, and carrying out hydrothermal crystallization reaction to obtain the ZSM-5/β core-shell type zeolite molecular sieve.
CN106475134A discloses a core-shell catalyst with hydrotalcite as shell/molecular sieve as core, its preparation and application, the preparation process is mixing hydrogen type molecular sieve with deionized water, ultrasonic processing to make A solution; mixing nitrate, ammonium salt and deionized water to prepare a solution B; then mixing the solution A and the solution B, and dropwise adding ammonia water to prepare a solution C; and then stirring the solution C at a high temperature to finally obtain the molecular sieve with the shape of the core-shell structure, wherein the molecular sieve is used as a core and the petal-shaped hydrotalcite is used as a shell. Can be used for the catalytic reaction of m-dinitrobenzene hydrogenation to synthesize m-phenylenediamine.
In summary, some core-shell structure materials and preparation methods thereof have been disclosed in the prior art, but the materials obtained by the currently disclosed preparation methods have some defects, and the preparation methods are relatively complex and have high cost.
Disclosure of Invention
Aiming at the defects of the prior art, the invention provides a silicon oxide/titanium oxide composite material and a synthesis method thereof. The silicon oxide/titanium oxide composite material provided by the invention has a core-shell structure, the shell layer is stably coated and is not easy to fall off, and the synthesis method is simple and easy.
The invention provides a silicon oxide/titanium oxide composite material, which takes titanium oxide as a nuclear layer and silicon oxide as a shell layer, wherein the diameter of the nuclear layer is 0.5-4 mu m; the thickness of the shell layer is 10-300 nm; the specific surface area is 50-100 m2/g。
The second aspect of the present invention provides a method for synthesizing a silicon oxide/titanium oxide composite material, which comprises the following steps:
(1) mixing titanium oxide and a micromolecular alcohol solvent, and adding a pH buffer solution after uniformly mixing;
(2) adding a silicon source into the material obtained in the step (1) under the condition of stirring, uniformly mixing, and then standing;
(3) and (3) washing, drying and thermally treating the material obtained in the step (2) to obtain the silicon oxide/titanium oxide composite material.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the titanium oxide is common titanium oxide, the particle size range of the titanium oxide is 0.5-4 mu m, the titanium oxide is subjected to purification treatment before use, impurities adsorbed in zeolite are removed, the purification treatment can be realized by adopting the existing purification means in the field, such as water washing or solvent washing, and the selection of the purification means is well known to those skilled in the art.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the titanium oxide is preferably prepared by the following method: mixing urea, an auxiliary agent and water, adding titanium sulfate after uniformly mixing, then placing the mixture into a reaction kettle for treatment, and obtaining titanium oxide after separation, washing and drying.
In the method, the auxiliary agent is cetyl trimethyl ammonium bromide or polyethylene glycol. The molecular weight of the polyethylene glycol is 200-600.
In the method, the mass ratio of urea to an auxiliary agent to water to titanium sulfate is 0.1-1: 0.5-3: 10-80: 1, preferably 0.2 to 0.8: 0.6-2.5: 15-70: 1.
in the method, the treatment temperature is 100-180 ℃, and preferably 110-170 ℃; the treatment time is 10-35 h, preferably 15-30 h.
In the above-described process, the separation and washing are conventional procedures well known to those skilled in the art. If the separation is carried out by filtration, washing is generally referred to as washing with deionized water. Usually comprises a plurality of separation and washing operations, generally 1 to 6 times. The drying condition is generally drying for 5-15 h at 100-140 ℃.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the micromolecular alcohol solvent in the step (1) is C2-C4 alcohol, and specifically can be one or more of ethanol, propanol, isopropanol, n-butanol, isobutanol, ethylene glycol, propylene glycol and butanediol.
In the synthesis method of the silicon oxide/titanium oxide composite material, the mass ratio of the micromolecular alcohol solvent to the titanium oxide in the step (1) is 5-40: 1, preferably 10 to 30: 1.
in the synthesis method of the silicon oxide/titanium oxide composite material, the mixing treatment in the step (1) can adopt any means capable of realizing full mixing, such as one or more of stirring and ultrasonic treatment, preferably adopts a stirring and ultrasonic treatment combined mode, more preferably adopts a method of firstly stirring and then mixing in ultrasonic, the frequency of the ultrasonic is 15KHz-10MHz, and the power is 20-100W/L according to the volume of the solution. The stirring time is 0.1-2 h, preferably 0.2-1.8 h; the ultrasonic time is 1-6 h, preferably 2-5 h.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the pH value of the pH buffer solution in the step (1) is 4-6, and preferably 4.5-5.8. The pH buffer may be one or more of sodium dihydrogen phosphate-citric acid pH buffer, sodium acetate pH buffer, potassium hydrogen phthalate-sodium hydroxide pH buffer, preferably sodium dihydrogen phosphate-citric acid pH buffer. The method of formulating the pH buffer is well known to those skilled in the art and can be carried out by methods known in the art.
In the synthesis method of the silicon oxide/titanium oxide composite material, the mass ratio of the pH buffer solution to the titanium oxide in the step (1) is 9-36: 1, preferably 9.5 to 35: 1. .
In the method for synthesizing the silicon oxide/titanium oxide composite material, an auxiliary agent can be added in the step (1), wherein the auxiliary agent comprises one or more of tween-20, tween-60 and tween-80; the mass ratio of the auxiliary agent to the micromolecular alcohols is 1: 5-40, preferably 1: 10 to 30.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the silicon source in the step (2) is one or more of methyl orthosilicate, ethyl orthosilicate and propyl orthosilicate, and preferably ethyl orthosilicate.
In the synthesis method, the mass ratio of the silicon source in the step (2) to the titanium oxide in the step (1) is 0.1-1.5: 1, preferably 0.18 to 1.4: 1.
in the method for synthesizing the silicon oxide/titanium oxide composite material, the silicon source is added in the step (2) under the condition of 45-80 ℃, preferably 50-70 ℃.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the silicon source is added under the stirring condition in the step (2), the stirring speed is 100-300 r/min, preferably 120-280 r/min, the stirring is continued for a period of time after the silicon source is dripped, and the stirring speed is 10-60 r/min, preferably 20-50 r/min; the stirring time is 1-10 h, preferably 2-9 h.
In the method for synthesizing the silicon oxide/titanium oxide composite material, the standing condition in the step (2) is as follows: the temperature is 25-40 ℃, and preferably 25-35 ℃; the time is 5-24 h, preferably 6-20 h.
In the method for synthesizing the silica/titania composite material according to the present invention, the separation and washing in step (3) are conventional procedures well known to those skilled in the art. If the separation is carried out by filtration, washing is generally referred to as washing with deionized water. Usually, the method comprises more than one separation and washing operation, and the number of the separation and washing operations is generally 1-6. The drying condition is generally drying for 5-15 h at 100-140 ℃.
In the synthesis method of the silicon oxide/titanium oxide composite material, the heat treatment temperature in the step (3) is 180-300 ℃, and preferably 200-280 ℃; the heat treatment time is 1-6 h, preferably 2-5 h.
The silicon oxide-titanium oxide composite material provided by the invention can be used as a carrier of a photocatalytic material or other catalytic materials, and can be widely applied to the field of photocatalysis.
Compared with the prior art, the silicon oxide/titanium oxide composite material and the synthesis method thereof provided by the invention have the following advantages:
(1) the silicon oxide/titanium oxide composite material provided by the invention is a composite material with a core-shell structure, and the shell layer of the composite material is stably coated and is not easy to fall off.
(2) According to the method for synthesizing the silicon oxide/titanium oxide composite material, the pH buffer solution is used for providing protons for silicon source hydrolysis, the concentration of the protons in a synthesis system can be kept unchanged by adding the pH buffer solution, the hydrolysis speed of an organic silicon source can be kept constant, the particle size of silicon oxide particles is kept consistent at all reaction time points, and further, the shell layer of the core-shell structure formed by uniformly covering the silicon oxide particles with uniform particle sizes on the outer surface of titanium oxide is compact and ordered, so that the generated core-shell structure composite material is not easy to damage. The problems that in the prior art, the size of the obtained silicon oxide particles is not uniform, so that the accumulated silicon oxide shell layer is loose and easy to damage, and the finally formed core-shell structure composite material is unstable in structure are solved.
(3) In the method for synthesizing the silicon oxide/titanium oxide composite material, the operation of adding the silicon source in the step (2) is particularly important for controlling the stirring condition, the stirring process needs to be carried out in a limited mode, the stirring speed is controlled to ensure the hydrolysis speed of the organic silicon source, and the phenomenon that the organic silicon source is hydrolyzed too fast due to too fast stirring to generate large-particle silicon oxide particles which cannot be adsorbed by the outer surface of titanium oxide and are not beneficial to generating a shell structure is avoided, so that a mechanical mixture of titanium oxide and large-particle silicon oxide is easily generated.
(4) In the synthesis method of the silicon oxide/titanium oxide composite material, the auxiliary agent is added and used in combination with other means such as pH buffer solution and a silicon source adding control mode, so that a shell layer is formed, the shell layer distribution is ensured to be more uniform, mesoporous channels can be formed in the silicon oxide shell layer, and the transmission of substances can be accelerated.
Drawings
FIG. 1 is a TEM photograph of a synthesized sample of example 2.
FIG. 2 is a TEM photograph of a synthesized sample of comparative example 1.
Detailed Description
The synthesis of the analcime of the present invention is described in detail below by way of specific examples, but is not limited thereto.
The structural characteristics and the sizes of the composite materials in the embodiments and the comparative examples are characterized and tested by a transmission electron microscope, and the surface area is characterized and tested by a physical adsorption instrument.
Example 1: preparation of buffers of different pH
preparation of buffer solution at pH 4.5: 18g of sodium acetate and 9.8mL of glacial acetic acid are taken and diluted by adding distilled water until the total volume is 1000 mL.
preparation of pH4.8 buffer: mixing 19.96g of sodium dihydrogen phosphate with 99.8mL of distilled water to form solution A; mixing 10.14g of citric acid with 101.4mL of distilled water to form solution B; and mixing the solution A and the solution B to obtain a buffer solution.
preparation of pH5.0 buffer: mixing 20.6g of sodium dihydrogen phosphate with 103mL of distilled water to form solution A; mixing 9.7g of citric acid with 97mL of distilled water to form solution B; and mixing the solution A and the solution B to obtain a buffer solution.
preparation of pH5.2 buffer: 21.44g of sodium dihydrogen phosphate is mixed with 107.2mL of distilled water to form solution A; mixing 9.28g of citric acid with 92.8mL of distilled water to form solution B; and mixing the solution A and the solution B to obtain a buffer solution.
preparation of pH5.6 buffer: mixing 23.2g of sodium dihydrogen phosphate with 116mL of distilled water to form solution A; mixing 8.4g of citric acid with 84mL of distilled water to form solution B; and mixing the solution A and the solution B to obtain a buffer solution.
Example 2
1g of urea, 4g of hexadecyl trimethyl ammonium bromide and 100mL of distilled water are uniformly mixed, then 3g of titanium sulfate is added, and stirring is carried out for 1 h; then the mixture is put into a reaction kettle for processing for 20 hours at the temperature of 140 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
taking 1.87g of the titanium oxide, putting the titanium oxide into 65mL of ethanol, stirring for 0.5h, and then carrying out ultrasonic treatment for 3h, wherein the frequency of ultrasonic waves is 1MHz, and the power is 50W/L according to the volume of the solution; then placed in a water bath at 58 ℃ and 50mL of pH4.8 buffer was added at 120Dripping 1.35 mL of tetraethoxysilane under the stirring condition of rotation/min, stirring for 5 hours at the speed of 20 rotation/min after dripping is finished, and standing for 12 hours in a water bath at the temperature of 30 ℃; washing the obtained product with distilled water for 4 times to neutrality, drying at 120 deg.C for 12h, and heat treating at 260 deg.C for 3h to obtain SiO2The titanium oxide composite material has the obtained sample number CL1, the properties of the sample are shown in Table 1, and the TEM photograph of the sample CL1 is shown in FIG. 1. As can be seen from fig. 1, the obtained sample has a core-shell structure.
Example 3
Uniformly mixing 0.6g of urea, 7.4g of hexadecyl trimethyl ammonium bromide and 45mL of distilled water, adding 3g of titanium sulfate, and stirring for 0.2 h; then the mixture is put into a reaction kettle for treatment for 15 hours at the temperature of 110 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product for 12 hours at 120 ℃ to obtain titanium oxide;
2g of the titanium oxide is taken and placed in 20mL of ethanol to be stirred for 0.2h, and then ultrasonic treatment is carried out for 2h, the frequency of ultrasonic waves is 15KHz, and the power is 100W/L according to the volume of the solution; then placing the mixture into a water bath at 70 ℃, adding 19mL of buffer solution with pH5.0, and dropwise adding 0.36mL of tetraethoxysilane under the stirring condition of 280 revolutions per minute; stirring at the speed of 50 r/min for 2h after the dropwise addition is finished, and standing in a water bath at the temperature of 25 ℃ for 6 h; washing the obtained product with distilled water for 4 times to neutrality, drying at 120 deg.C for 12h, and treating at 280 deg.C for 2h to obtain SiO2The titanium oxide composite material obtained is sample No. CL2, the properties of the sample are shown in Table 1.
Example 4
Uniformly mixing 2.4g of urea, 1.8g of hexadecyl trimethyl ammonium bromide and 210mL of distilled water, adding 3g of titanium sulfate, and stirring for 1.8 h; then the mixture is put into a reaction kettle for treatment for 30 hours at the temperature of 170 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
2g of the titanium oxide is taken and placed in 60mL of propanol to be stirred for 1.8h, and then ultrasonic treatment is carried out for 5h, wherein the frequency of ultrasonic waves is 10MHz, and the power is 20W/L according to the volume of the solution; then placing the mixture into a water bath at 50 ℃, adding 70mL of buffer solution with pH5.2, and dropwise adding 2.8mL of tetraethoxysilane under the stirring condition of 120 revolutions per minute; stirring at the speed of 20 r/min for 9h after the dropwise addition is finished, and standing in a water bath at the temperature of 35 ℃ for 20 h; the obtained product is treated with distilled waterWashing for 4 times to neutrality, drying at 120 deg.C for 12 hr, and treating at 220 deg.C for 3 hr to obtain SiO2The titanium oxide composite material obtained is sample number CL 3, and the properties of the sample are shown in Table 1.
Example 5
1.2g of urea, 4.5g of hexadecyl trimethyl ammonium bromide and 100mL of distilled water are uniformly mixed, then 3g of titanium sulfate is added, and the mixture is stirred for 1 hour; then the mixture is put into a reaction kettle for processing for 20 hours at the temperature of 140 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
putting 1.65g of the titanium oxide into 35 mL of butanol, then adding 2.4g of Tween-80, stirring for 0.5h, and then carrying out ultrasonic treatment for 3h, wherein the frequency of ultrasonic waves is 1MHz, and the power is 50W/L according to the volume of the solution; then placing the mixture into a water bath at 55 ℃, adding 37mL of buffer solution with pH5.6, and then dropwise adding 1 mL of tetraethoxysilane while stirring at the speed of 240 revolutions per minute; then stirring the mixture for 5 hours at the speed of 30 r/min, and standing the mixture in a water bath at the temperature of 35 ℃ for 12 hours; washing the obtained product with distilled water for 4 times to neutrality, drying at 120 deg.C for 12h, and treating at 270 deg.C for 4h to obtain SiO2The titanium oxide composite material was obtained in sample No. CL 4.
Example 6
1g of urea, 4g of polyethylene glycol (molecular weight 200) and 100mL of distilled water are uniformly mixed, then 3g of titanium sulfate is added, and stirring is carried out for 1 h; then the mixture is put into a reaction kettle for processing for 20 hours at the temperature of 140 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
putting 1.67g of the titanium oxide in 33 mL of butanol, adding 2.56g of Tween-60, stirring for 1h, and then carrying out ultrasonic treatment for 2.5h, wherein the frequency of ultrasonic waves is 1MHz, and the power is 50W/L according to the volume of the solution; then placing the mixture into a water bath at 60 ℃, adding 51 mL of buffer solution with pH4.5, and then dropwise adding 0.7 mL of tetraethoxysilane while stirring at the speed of 260 revolutions per minute; then stirring the mixture for 5 hours at the speed of 30 r/min, and standing the mixture in a water bath at the temperature of 30 ℃ for 12 hours; washing the obtained product with distilled water for 4 times to neutrality, drying at 120 deg.C for 12h, and treating at 230 deg.C for 2.5h to obtain SiO2Titanium oxide composite material, obtained sample No. CL 5.
Comparative example 1
Referring to the material ratio of example 2, 1g of urea, 4g of hexadecyl trimethyl ammonium bromide and 100mL of distilled water are uniformly mixed, 3g of titanium sulfate is added, and the mixture is stirred for 1 hour; then the mixture is put into a reaction kettle for processing for 20 hours at the temperature of 140 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
taking 1.87g of the titanium oxide, putting the titanium oxide into 65mL of ethanol, stirring for 0.5h, and then carrying out ultrasonic treatment for 3h, wherein the frequency of ultrasonic waves is 1MHz, and the power is 50W/L according to the volume of the solution; then placing the mixture into a water bath at 58 ℃, adding 50mL of hydrochloric acid solution with pH4.8, dropwise adding 1.35 mL of ethyl orthosilicate under the stirring condition of 120 r/min, stirring the mixture for 5 hours at the speed of 20 r/min after the dropwise adding is finished, and then placing the mixture into a water bath at 30 ℃ for standing for 12 hours; the obtained product was washed 4 times with distilled water to neutrality, dried at 120 ℃ for 12 hours, heat-treated at 260 ℃ for 3 hours, and obtained sample No. CL 6.
Comparative example 2
1g of urea, 4g of hexadecyl trimethyl ammonium bromide and 100mL of distilled water are uniformly mixed, then 3g of titanium sulfate is added, and stirring is carried out for 1 h; then the mixture is put into a reaction kettle for processing for 20 hours at the temperature of 140 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
taking 1.87g of the titanium oxide, putting the titanium oxide into 65mL of ethanol, stirring for 0.5h, and then carrying out ultrasonic treatment for 3h, wherein the frequency of ultrasonic waves is 1MHz, and the power is 50W/L according to the volume of the solution; then placing the mixture into a water bath at 58 ℃, adding 50mL of buffer solution with pH4.8, dropwise adding 1.35 mL of tetraethoxysilane under the stirring condition of 120 r/min, stirring for 5h at the speed of 2 r/min after dropwise adding, and then placing the mixture into a water bath at 30 ℃ for standing for 12 h; the obtained product was washed 4 times with distilled water to neutrality, dried at 120 ℃ for 12 hours, heat-treated at 260 ℃ for 3 hours, and obtained sample No. CL 7.
Comparative example 3
1g of urea, 4g of hexadecyl trimethyl ammonium bromide and 100mL of distilled water are uniformly mixed, then 3g of titanium sulfate is added, and stirring is carried out for 1 h; then the mixture is put into a reaction kettle for processing for 20 hours at the temperature of 140 ℃; then washing the solid product with distilled water for 4 times until the solid product is neutral, and drying the solid product at 120 ℃ for 12 hours to obtain titanium oxide;
taking 1.87g of the titanium oxide, putting the titanium oxide into 65mL of ethanol, stirring for 0.5h, and then carrying out ultrasonic treatment for 3h, wherein the frequency of ultrasonic waves is 1MHz, and the power is 50W/L according to the volume of the solution; then placing the mixture into a water bath at 58 ℃, adding 50mL of buffer solution with pH4.8, dropwise adding 1.35 mL of tetraethoxysilane under the stirring condition of 120 r/min, stirring for 5h at the speed of 350 r/min after dropwise adding, and then placing the mixture into a water bath at 30 ℃ for standing for 12 h; the obtained product was washed 4 times with distilled water to neutrality, dried at 120 ℃ for 12 hours, heat-treated at 260 ℃ for 3 hours, and obtained sample No. CL 8.
Stability evaluation test:
in order to further verify the stability of the structure of the samples obtained in the above examples and comparative examples, the samples were subjected to ultrasonic treatment for 24 hours, the frequency of the ultrasonic wave was 10MHz, and the power was 100W/L based on the volume of the solution. Through tests, the shell layer of the sample obtained in the example 2-6 is not dropped after ultrasonic treatment, which shows that the sample prepared by the invention has very stable structure, the shell layer is combined with the core very tightly, and the sample is not easy to be damaged by external force.
TABLE 1 physicochemical Properties of samples obtained in examples and comparative examples
Claims (26)
1. The silicon oxide/titanium oxide composite material takes titanium oxide as a core layer and silicon oxide as a shell layer.
2. The silica/titania composite of claim 1, wherein: in the composite material, the diameter of a nuclear layer is 0.5-4 mu m; the thickness of the shell layer is 10-300 nm.
3. The silica/titania composite of claim 1, wherein: the specific surface area of the composite material is 50-100 m2/g。
4. A synthesis method of a silicon oxide/titanium oxide composite material comprises the following steps:
(1) mixing titanium oxide and a micromolecular alcohol solvent, and adding a pH buffer solution after uniformly mixing;
(2) adding a silicon source into the material obtained in the step (1) under the condition of stirring, uniformly mixing, and then standing;
(3) and (3) washing, drying and thermally treating the material obtained in the step (2) to obtain the silicon oxide/titanium oxide composite material.
5. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the particle size range of the titanium oxide is 0.5-4 mu m.
6. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the titanium oxide is prepared by adopting the following method: mixing urea, an auxiliary agent and water, adding titanium sulfate after uniformly mixing, then placing the mixture into a reaction kettle for treatment, and obtaining titanium oxide after separation, washing and drying.
7. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 6, wherein: the auxiliary agent is cetyl trimethyl ammonium bromide or polyethylene glycol.
8. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 6, wherein: the mass ratio of the urea to the auxiliary agent to the water to the titanium sulfate is 0.1-1: 0.5-3: 10-80: 1, preferably 0.2 to 0.8: 0.6-2.5: 15-70: 1.
9. a method for synthesizing a silicon oxide/titanium oxide composite material according to claim 6, wherein: the polyethylene glycol is required to be limited to have a molecular weight of 200-600.
10. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 6, wherein: the treatment temperature is 100-180 ℃, and preferably 110-170 ℃; the treatment time is 4-20 h, preferably 5-18 h.
11. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the small molecular alcohol solvent in the step (1) is C2-C4 alcohol.
12. A method for synthesizing a silica/titania composite material according to claim 4 or 11, characterized in that: the micromolecular alcohol solvent in the step (1) is one or more of ethanol, propanol, isopropanol, n-butanol, isobutanol, ethylene glycol, propylene glycol and butanediol.
13. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: in the step (1), the mass ratio of the micromolecular alcohol solvent to the titanium oxide is 5-40: 1, preferably 10 to 30: 1.
14. a method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the mixing treatment in the step (1) adopts one or more of stirring and ultrasonic treatment, preferably adopts a combined mode of stirring and ultrasonic treatment, and more preferably adopts a method of firstly stirring and then ultrasonically mixing.
15. A method of synthesizing a silica/titania composite material according to claim 12, wherein: the frequency of the ultrasonic wave is 15KHz-10MHz, the power is 20-100W/L according to the volume of the solution, and the stirring time is 0.1-2 h, preferably 0.2-1.8 h; the ultrasonic time is 1-6 h, preferably 2-5 h.
16. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the pH value of the pH buffer solution in the step (1) is 4-6, and preferably 4.5-5.8.
17. A method for synthesizing a silica/titania composite material according to claim 4 or 14, characterized in that: the pH buffer solution in the step (1) is one or more of sodium dihydrogen phosphate-citric acid pH buffer solution, sodium acetate pH buffer solution and potassium hydrogen phthalate-sodium hydroxide pH buffer solution, and is preferably sodium dihydrogen phosphate-citric acid pH buffer solution.
18. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the mass ratio of the pH buffer solution to the titanium oxide in the step (1) is 9-36: 1, preferably 9.5 to 35: 1.
19. a method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: and (2) adding an auxiliary agent in the step (1), wherein the auxiliary agent comprises one or more of tween-20, tween-60 and tween-80.
20. A method of synthesizing a silica/titania composite material according to claim 17, wherein: the mass ratio of the auxiliary agent to the micromolecular alcohols is 1: 5-40, preferably 1: 10 to 30.
21. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the silicon source in the step (2) is one or more of methyl orthosilicate, ethyl orthosilicate and propyl orthosilicate, and preferably ethyl orthosilicate.
22. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the mass ratio of the silicon source in the step (2) to the titanium oxide in the step (1) is 0.1-1.5: 1, preferably 0.18 to 1.4: 1.
23. a method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the condition for adding the silicon source in the step (2) is that the silicon source is added at the temperature of 45-80 ℃, preferably 50-70 ℃.
24. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: adding a silicon source under the stirring condition in the step (2), wherein the stirring speed is 100-300 r/min, preferably 120-280 r/min, and stirring is continued for a period of time after the silicon source is dropwise added, wherein the stirring speed is 10-60 r/min, preferably 20-50 r/min; the stirring time is 1-10 h, preferably 2-9 h.
25. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the standing condition in the step (2) is as follows: the temperature is 25-40 ℃, and preferably 25-35 ℃; the time is 5-24 h, preferably 6-20 h.
26. A method for synthesizing a silicon oxide/titanium oxide composite material according to claim 4, wherein: the heat treatment temperature in the step (3) is 180-300 ℃, and preferably 200-280 ℃; the heat treatment time is 1-6 h, preferably 2-5 h.