CN111018470B - 一种载体及其制备方法和应用 - Google Patents
一种载体及其制备方法和应用 Download PDFInfo
- Publication number
- CN111018470B CN111018470B CN201911416896.0A CN201911416896A CN111018470B CN 111018470 B CN111018470 B CN 111018470B CN 201911416896 A CN201911416896 A CN 201911416896A CN 111018470 B CN111018470 B CN 111018470B
- Authority
- CN
- China
- Prior art keywords
- parts
- carrier
- powder
- sand
- preservative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种载体及其制备方法和应用，所述载体包括以下重量份的组分：填充粉80‑120份；已发泡热膨胀微球5‑20份；砂20‑50份；水80‑120份；硝酸银2‑8份，纤维素环糊精10‑20份；防腐剂0.5‑1.5份；色浆0‑0.15份。本发明通过添加已发泡热膨胀微球，一方面可以显著降低载体的重量，在同等体积的情况下，本发明的载体重量只有传统载体的1/3‑1/5；另一方面和添加的纤维素环糊精协调作用，能够保证载体兼具质地疏松和不易碎的特性，并且有效降低扬尘，可用于考古玩具的载体中，也可用于其他挖掘类玩具或工艺品中。
Description
技术领域
本发明涉及工艺品载体领域，尤其涉及一种载体及其制备方法和应用。
背景技术
随着社会的进步，玩具的种类也越来越多，从手动玩具到电动玩具，从纯粹娱乐玩具到益智玩具，其中，益智玩具是最受家长所青睐的。但是现在的益智玩具大多被机械化、电动化及形态化，从而局限了该玩具的特性，比如拼图玩具，玩家通过思考将其拼装成一副完整的图，这类玩具只具有益智性和收藏性；而又如棋类或牌类玩具，只能起到智力的开发作用。然而，现在我们不仅要求小孩在玩玩具取乐的同时能得到智力的开发，还要让小孩能从中学到知识，并且还要能提高小孩的动手能力，让小孩从小就养成胆大心细的习惯。而且目前大多数玩具是由人为的几何图形组成，并无法针对如古生物、古文物等历史与文明进行深入研究与探讨，例如对古生物的形成状态、古文物的挖掘与重组等，而一般此类的丛书、或其它玩具等亦难提供考古的实际体验。
现有授权公告号为CN 201510754 U的中国专利公开了一种可挖掘的考古景观模型玩具，该模型玩具包括陶泥土料和考古挖掘主体，所述考古挖掘主体由任意个分体构成，各分体混杂在该陶泥土料内的。
但是，现有技术中提供的制造考古玩具或工艺品的主要原料比重大，会导致玩具或工艺品出现硬度高、重量大、粉尘严重、微生物超标等问题，不适合低年龄儿童的使用，甚至会危害使用者的健康。
发明内容
本发明的目的是针对现有技术中的不足，提供一种载体及其制备方法和应用，利用本发明中的方法制备出来的载体具有轻质无毒防菌、显著降低扬尘的特性。
为实现上述目的，本发明采取的技术方案是：
本发明第一方面提供一种载体，所述载体包括以下重量份的组分：填充粉80-120份；已发泡热膨胀微球5-20份；砂20-50份；水80-120份；硝酸银2-8份，纤维素环糊精10-20份；防腐剂0.5-1.5份；色浆0-0.15份。
优选的，所述载体包括以下重量份的组分：填充粉100份；已发泡热膨胀微球12份；砂40份；水100份；硝酸银5份，纤维素环糊精15份；防腐剂1.0份；色浆0.07份。
优选的，所述填充粉为石膏粉、陶土粉、滑石粉、云母粉、凹凸棒土粉和蒙脱土粉中的一种或几种的混合物；所述砂为河砂、湖砂、海砂、山砂和机制砂中的一种或几种的混合物。
优选的，所述填充粉为陶土粉或石膏粉。
优选的，所述已发泡热膨胀微球为干粉状或滤饼状，且其粒径为50-70μm。
优选的，所述水为无菌自来水或纯水。
优选的，所述防腐剂为IPBC-Ⅱ、QT-50、GM115中一种或几种的混合物。
更优选的，所述防腐剂中IPBC-Ⅱ、QT-50、GM115的质量比为(4～5):1:(1～3)。
本发明第二方面提供一种载体的制备方法，包括以下步骤：
(1)按比例，分别称取已发泡热膨胀微球、水、硝酸银、纤维素环糊精、色浆、填充粉、砂、防腐剂；
(2)将步骤(1)中称好的已发泡热膨胀微球和水混合，并搅拌均匀；
(3)向步骤(2)中添加按组分配比称取的防腐剂、硝酸银，杀菌充分，并搅拌均匀；
(4)向步骤(3)中依次加入按组分配比分别称取的填充粉、纤维素环糊精、色浆和砂，混合均匀后待用；
(5)将步骤(4)中所得的浆料缓慢注入模具，至与模具平齐；当需要放入物品时，浆料浇筑至模具体积的一半时，放入埋藏物品，继续浇注浆料至与模具平齐；
(6)烘干处理。
本发明第三方面提供根据上述方法制备的载体用于挖掘类玩具或工艺品中。
本发明采用以上技术方案，与现有技术相比，具有如下技术效果：
(1)本发明通过添加已发泡热膨胀微球，一方面可以显著降低载体的重量，在同等体积的情况下，本发明的载体只有传统载体的1/3-1/5；另一方面和添加的纤维素环糊精协调作用，能够保证载体兼具质地疏松和不易碎的特性，并且有效降低扬尘。
(2)本发明使用灭菌自来水或者纯水，同时添加防菌剂可以有效避免载体内部和表面滋生细菌，便于人们的使用。
(3)本发明采用的原料均具有无味、无腐蚀性和无刺激性等优点，不会造成使用者感官上的任何不适。
(4)采用本发明的制备方法，可以在标准化、流水线作业条件下，高效生产载体，有效降低产品的不良品率。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
需要说明的是，在不冲突的情况下，本发明中的实施例及实施例中的特征可以相互组合。
下面结合具体实施例对本发明作进一步说明，但不作为本发明的限定。
实施例1：
一种载体，所述载体包括以下重量份的组分：脱硫石膏粉80份；已发泡热膨胀微球干粉5份；河砂20份；纯水80份；硝酸银2份，纤维素环糊精10份；(IPBC-Ⅱ：QT-50：GM115)质量比为4:1:1的防腐剂0.5份；色浆0.05份；
上述载体的制备方法，具体包含以下步骤：
(1)按上述比例，分别称取已发泡热膨胀微球干粉、纯水、硝酸银、纤维素环糊精、色浆、脱硫石膏粉、河砂、(IPBC-Ⅱ：QT-50：GM115)质量比为4:1:1的防腐剂；
(2)将步骤(1)中称好的纯水和已发泡热膨胀微球干粉倒入搅拌器，搅拌45s，保证已发泡热膨胀微球干粉均匀分散在纯水中；
(3)向步骤(2)中所得混合物添加(IPBC-Ⅱ：QT-50：GM115)质量比为4:1:1的防腐剂和硝酸银，杀菌10min，再次进行搅拌60s；
(4)将步骤(3)所得混合物转移至混料机，依次加入脱硫石膏粉、河砂、纤维素环糊精和色浆，混合均匀，打开放料阀，将所得浆料放至料筒内，待用；
(5)将步骤(4)中所得浆料缓慢注入模具至与模具平齐；当用于考古玩具时，浆料浇筑至模具体积的一半时，放入待挖掘的物品，继续浇注浆料至与模具平齐；
(6)将步骤(5)中所得模具从流水线转移至烘房进行烘干，制备得到仿真考古工艺品，测试硬度的测试。
实施例2：
一种载体，所述载体包括以下重量份的组分：磷硫石膏粉100份；已发泡热膨胀微球滤饼12份；河砂和湖砂的混合物40份；无菌自来水100份；硝酸银5份，纤维素环糊精15份；(IPBC-Ⅱ：QT-50：GM115)质量比为4.5:1:2的防腐剂1.0份；色浆0.07份；
上述载体的制备方法，具体包含以下步骤：
(1)按上述比例，分别称取已发泡热膨胀微球滤饼、无菌自来水、硝酸银、纤维素环糊精、色浆、磷硫石膏粉、河砂和湖砂的混合物、(IPBC-Ⅱ：QT-50：GM115)质量比为4.5:1:2的防腐剂；
(2)将步骤(1)中称好的无菌自来水和已发泡热膨胀微球滤饼倒入搅拌器，搅拌30s，保证已发泡热膨胀微球均匀分散在无菌自来水中；
(3)向步骤(2)中所得混合物中添加(IPBC-Ⅱ：QT-50：GM115)质量比为4.5:1:2的防腐剂和硝酸银，杀菌20min，再次进行搅拌30s；
(4)将步骤(3)所得混合物转移至混料机，依次加入磷硫石膏粉、河砂和湖砂的混合物、纤维素环糊精和色浆，混合均匀，打开放料阀，将所得浆料放至料筒内，待用；
(5)将步骤(4)中所得浆料缓慢注入模具至与模具平齐；当用于考古玩具时，浆料浇筑至模具体积的一半时，放入待挖掘的物品，继续浇注浆料至与模具平齐；
(6)将步骤(5)中所得模具从流水线转移至烘房进行烘干，制备得到仿真考古工艺品，测试硬度的测试。
实施例3：
一种载体，所述载体包括以下重量份的组分：脱硫石膏粉120份；已发泡热膨胀微球滤饼15份；河砂40份；纯水120份；硝酸银8份，纤维素环糊精20份；(IPBC-Ⅱ：QT-50：GM115)质量比为4.5:1:3的防腐剂1.5份；色浆0.15份；
上述载体的制备方法，具体包含以下步骤：
(1)按上述比例，分别称取已发泡热膨胀微球滤饼、纯水、硝酸银、纤维素环糊精、色浆、脱硫石膏粉、河砂、(IPBC-Ⅱ：QT-50：GM115)质量比为4.5:1:3的防腐剂；
(2)将步骤(1)中称好的纯水和已发泡热膨胀微球滤饼倒入搅拌器，搅拌30s，保证已发泡热膨胀微球均匀分散在纯水中；
(3)向步骤(2)中所得混合物中添加(IPBC-Ⅱ：QT-50：GM115)质量比为4.5:1:3的防腐剂和硝酸银，杀菌20min，再次进行搅拌30s；
(4)将步骤(3)所得混合物转移至混料机，依次加入脱硫石膏粉和河砂、纤维素环糊精和色浆，混合均匀，打开放料阀，将所得浆料放至料筒内，待用；
(5)将步骤(4)中所得浆料缓慢注入模具至与模具平齐；当用于考古玩具时，浆料浇筑至模具体积的一半时，放入待挖掘的物品，继续浇注浆料至与模具平齐；
(6)将步骤(5)中所得模具从流水线转移至烘房进行烘干，制备得到仿真考古工艺品，测试硬度的测试。
应用例：
a硬度测试采用洛氏硬度法；
b测试方法为USP 40-(61/62)，总细菌量检测标准为5000，胆汁酸耐受革兰氏阴性杆菌检测标准为negative，测试结果如表1所示。
表1
从表1中可以看出普通载体的重量是本发明的的3-5倍，硬度也明显高于本发明的产品。从微生物检测结果看，普通的总细菌量超标，且检测到了胆汁酸耐受革兰氏阴性杆菌。从颜色来看，本发明的颜色更为均匀。
以上所述仅为本发明较佳的实施例，并非因此限制本发明的实施方式及保护范围，对于本领域技术人员而言，应当能够意识到凡运用本发明说明书内容所作出的等同替换和显而易见的变化所得到的方案，均应当包含在本发明的保护范围内。
Claims (10)
1.一种载体，所述载体包括以下重量份的组分：填充粉80-120份；已发泡热膨胀微球5-20份；砂20-50份；水80-120份；硝酸银2-8份，纤维素环糊精10-20份；防腐剂0.5-1.5份；色浆0-0.15份；所述填充粉为石膏粉、陶土粉、滑石粉、云母粉、凹凸棒土粉和蒙脱土粉中的一种或几种的混合物。
2.根据权利要求1所述的载体，其特征在于，所述载体包括以下重量份的组分：填充粉100份；已发泡热膨胀微球12份；砂40份；水100份；硝酸银5份，纤维素环糊精15份；防腐剂1.0份；色浆0.07份。
3.根据权利要求1所述的载体，其特征在于，所述砂为河砂、湖砂、海砂、山砂和机制砂中的一种或几种的混合物。
4.根据权利要求1所述的载体，其特征在于，所述填充粉为陶土粉或石膏粉。
5.根据权利要求1所述的载体，其特征在于，所述已发泡热膨胀微球为干粉状或滤饼状，且其粒径为50-70μm。
6.根据权利要求1所述的载体，其特征在于，所述水为无菌自来水或纯水。
7.根据权利要求1所述的载体，其特征在于，所述防腐剂为IPBC-Ⅱ、QT-50、GM115中一种或几种的混合物。
8.根据权利要求7所述的载体，其特征在于，所述防腐剂中IPBC-Ⅱ:QT-50:GM115的质量比为(4～5):1:(1～3)。
9.根据权利要求1-8任一项所述载体的制备方法，其特征在于，包括以下步骤：
(1)按比例，分别称取已发泡热膨胀微球、水、硝酸银、纤维素环糊精、色浆、填充粉、砂、防腐剂；
(2)将步骤(1)中称好的已发泡热膨胀微球和水混合，并搅拌均匀；
(3)向步骤(2)中添加按组分配比称取的防腐剂、硝酸银，杀菌充分，并搅拌均匀；
(4)向步骤(3)中依次加入按组分配比分别称取的填充粉、纤维素环糊精、色浆和砂，混合均匀后待用；
(5)将步骤(4)中所得浆料缓慢注入模具至与模具平齐；
(6)烘干处理。
10.根据权利要求9的方法制备的载体，其特征在于，用于挖掘类玩具或工艺品中。