CN111018398A - 一种混凝土发泡剂及发泡混凝土 - Google Patents
一种混凝土发泡剂及发泡混凝土 Download PDFInfo
- Publication number
- CN111018398A CN111018398A CN201911358254.XA CN201911358254A CN111018398A CN 111018398 A CN111018398 A CN 111018398A CN 201911358254 A CN201911358254 A CN 201911358254A CN 111018398 A CN111018398 A CN 111018398A
- Authority
- CN
- China
- Prior art keywords
- parts
- foaming agent
- concrete
- resin
- cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种混凝土发泡剂及发泡混凝土。本发明的混凝土发泡剂，包括以下重量份的组分：憎水胶粉1‑5份、明胶1‑10份、改性硅藻土5‑15份、吸水树脂10‑20份、松香树脂5‑10份、阴离子型表面活性剂5‑15份、植物蛋白发泡剂15‑20份、纤维素1‑15份。使用本发明的发泡剂对混凝土进行发泡，所得到的发泡混凝土泛霜程度较小，且发泡剂的起泡高度高，泡沫稳定性好。
Description
技术领域
本发明涉及建筑领域，尤其涉及一种混凝土发泡剂及发泡混凝土。
背景技术
泡沫混凝土作为一种新型的节能环保型建筑材料，具有密度小、质量轻、保温、隔音、抗震等性能，被广泛应用于墙体材料中。在其制备过程中，需要添加混凝土发泡剂，使混凝土成孔。混凝土发泡剂可分为化学发泡剂、物理发泡剂和表面活性剂三大类。目前的发泡剂在发泡混凝土过程中，难以抑制混凝土在低温下的泛霜。因此，开发一种起泡性好、泡沫稳定性高且抑制混凝土泛霜的发泡剂十分必要。
发明内容
为解决上述技术问题，本发明的目的是提供一种混凝土发泡剂及发泡混凝土，使用该发泡剂对混凝土进行发泡，所得到的发泡混凝土泛霜程度较小，且发泡剂的起泡高度高，泡沫稳定性好。
本发明的一种混凝土发泡剂，包括以下重量份的组分：憎水胶粉1-5份、明胶1-10份、改性硅藻土5-15份、吸水树脂10-20份、松香树脂5-10份、阴离子型表面活性剂5-15份、植物蛋白发泡剂15-20份、纤维素1-15份。
优选地，混凝土发泡剂包括以下重量份的组分：憎水胶粉1-5份、明胶5-10份、改性硅藻土5-10份、吸水树脂15-20份、松香树脂5-10份、阴离子型表面活性剂5-10份、植物蛋白发泡剂15-20份、纤维素10-15份。
进一步地，憎水胶粉为乙烯-月桂酸酯憎水胶粉。
进一步地，吸水树脂为聚丙烯酸树脂、聚乙烯醇树脂和聚醋酸乙烯酯类树脂中的一种或几种。
进一步地，阴离子型表面活性剂为烷基苯磺酸盐、α-烯基磺酸盐、脂肪醇聚氧乙烯醚磷酸酯和脂肪醇聚氧乙烯醚硫酸酯中的一种或几种。
进一步地，植物蛋白发泡剂为茶皂素发泡剂和/或皂角苷型发泡剂。皂角苷不但起泡力较好，而且其与茶皂素相似，具有优异的稳泡性能。
进一步地，纤维素为甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素中的一种或几种。
进一步地，混凝土发泡剂中还包括增强剂5-10份，所述增强剂呈纤维状，其长度为10-50μm。
进一步地，增强剂为玻璃纤维、聚丙烯纤维和植物纤维中的一种或几种。增强剂的加入可以提高发泡剂在发泡混凝土时的发泡高度，提高泡沫稳定性和强度。
进一步地，植物纤维来源于植物秸秆、植物种子壳和木屑中的一种或几种。
本发明还提供了一种发泡混凝土，其采用本发明的上述混凝土发泡剂制得。
借由上述方案，本发明至少具有以下优点：
本发明的发泡剂复合了多种表面活性剂，如松香树脂、阴离子型表面活性剂和植物蛋白发泡剂，实现各组分的优势互补，使发泡剂的发泡稳定性大大提高。其中，植物蛋白发泡剂的泡沫特别稳定，可以长时间不消泡，完全消泡的时间大多长于24h。用植物性发泡剂制作的发泡混凝土相比其密封性和保温性较好，强度高。本发明的发泡剂通过添加憎水胶粉，可提高混凝土的抑制泛霜性。吸水树脂的加入，提高了发泡剂的吸水性和吸水速度。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，并可依照说明书的内容予以实施，以下以本发明的较佳实施例并配合详细说明如后。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步详细描述。以下实施例用于说明本发明，但不用来限制本发明的范围。
实施例1
一种混凝土发泡剂，由以下重量份的组分组成：
憎水胶粉1份、明胶2份、改性硅藻土5份、吸水树脂10份、松香树脂5份、阴离子型表面活性剂8份、植物蛋白发泡剂16份、纤维素3份。
其中，憎水胶粉为乙烯-月桂酸酯憎水胶粉。吸水树脂为聚丙烯酸树脂。阴离子型表面活性剂为烷基苯磺酸盐。植物蛋白发泡剂为茶皂素发泡剂。纤维素为甲基纤维素。
实施例2
一种混凝土发泡剂，由以下重量份的组分组成：
憎水胶粉2份、明胶5份、改性硅藻土11份、吸水树脂14份、松香树脂8份、阴离子型表面活性剂5份、植物蛋白发泡剂15份、纤维素3份，增强剂5份。
其中，憎水胶粉为乙烯-月桂酸酯憎水胶粉。吸水树脂为聚丙烯酸树脂。阴离子型表面活性剂为烷基苯磺酸盐。植物蛋白发泡剂为皂角苷型发泡剂。纤维素为甲基纤维素。增强剂呈纤维状，其长度为10-50μm。增强剂为玻璃纤维和植物纤维。植物纤维来源于植物秸秆、植物种子壳和木屑中的一种或几种。
实施例3
一种混凝土发泡剂，由以下重量份的组分组成：
憎水胶粉5份、明胶7份、改性硅藻土10份、吸水树脂15份、松香树脂8份、阴离子型表面活性剂12份、植物蛋白发泡剂11份、纤维素10份，增强剂7份。
其中，憎水胶粉为乙烯-月桂酸酯憎水胶粉。吸水树脂为聚醋酸乙烯酯类树脂。阴离子型表面活性剂为等质量的烷基苯磺酸盐和α-烯基磺酸盐。植物蛋白发泡剂为茶皂素发泡剂。纤维素为甲基纤维素。增强剂呈纤维状，其长度为10-50μm。增强剂为聚丙烯纤维。
实施例4
一种混凝土发泡剂，由以下重量份的组分组成：
憎水胶粉5份、明胶8份、改性硅藻土15份、吸水树脂18份、松香树脂8份、阴离子型表面活性剂15份、植物蛋白发泡剂20份、纤维素15份，增强剂9份。
其中，憎水胶粉为乙烯-月桂酸酯憎水胶粉。吸水树脂为等质量的聚丙烯酸树脂和聚醋酸乙烯酯类树脂。阴离子型表面活性剂为脂肪醇聚氧乙烯醚磷酸酯。植物蛋白发泡剂为茶皂素发泡剂。纤维素为羟丙基甲基纤维素。增强剂呈纤维状，其长度为10-50μm。增强剂为玻璃纤维和聚丙烯纤维。
实施例5
一种混凝土发泡剂，由以下重量份的组分组成：
憎水胶粉5份、明胶8份、改性硅藻土5份、吸水树脂10份、松香树脂8份、阴离子型表面活性剂15份、植物蛋白发泡剂20份、纤维素15份，增强剂6份。
其中，憎水胶粉为乙烯-月桂酸酯憎水胶粉。吸水树脂为等质量的聚丙烯酸树脂和聚醋酸乙烯酯类树脂。阴离子型表面活性剂为脂肪醇聚氧乙烯醚磷酸酯。植物蛋白发泡剂为茶皂素发泡剂。纤维素为羟丙基甲基纤维素。增强剂呈纤维状，其长度为10-50μm。增强剂为玻璃纤维和聚丙烯纤维。
采用以上实施例中的混凝土发泡剂制备发泡混凝土，按照常规方法即可，所得到的发泡混凝土泛霜程度较小，且发泡剂的起泡高度高，泡沫稳定性好。
以上所述仅是本发明的优选实施方式，并不用于限制本发明，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变型，这些改进和变型也应视为本发明的保护范围。
Claims (10)
1.一种混凝土发泡剂，其特征在于，包括以下重量份的组分：憎水胶粉1-5份、明胶1-10份、改性硅藻土5-15份、吸水树脂10-20份、松香树脂5-10份、阴离子型表面活性剂5-15份、植物蛋白发泡剂15-20份、纤维素1-15份。
2.根据权利要求1所述的混凝土发泡剂，其特征在于，包括以下重量份的组分：憎水胶粉1-5份、明胶5-10份、改性硅藻土5-10份、吸水树脂15-20份、松香树脂5-10份、阴离子型表面活性剂5-10份、植物蛋白发泡剂15-20份、纤维素10-15份。
3.根据权利要求1所述的混凝土发泡剂，其特征在于：所述憎水胶粉为乙烯-月桂酸酯憎水胶粉。
4.根据权利要求1所述的混凝土发泡剂，其特征在于：所述吸水树脂为聚丙烯酸树脂、聚乙烯醇树脂和聚醋酸乙烯酯类树脂中的一种或几种。
5.根据权利要求1所述的混凝土发泡剂，其特征在于：所述阴离子型表面活性剂为烷基苯磺酸盐、α-烯基磺酸盐、脂肪醇聚氧乙烯醚磷酸酯和脂肪醇聚氧乙烯醚硫酸酯中的一种或几种。
6.根据权利要求1所述的混凝土发泡剂，其特征在于：所述植物蛋白发泡剂为茶皂素发泡剂和/或皂角苷型发泡剂。
7.根据权利要求1所述的混凝土发泡剂，其特征在于：所述纤维素为甲基纤维素、羟乙基纤维素和羟丙基甲基纤维素中的一种或几种。
8.根据权利要求1所述的混凝土发泡剂，其特征在于：所述混凝土发泡剂中还包括增强剂5-10份，所述增强剂呈纤维状，其长度为10-50μm；所述增强剂为玻璃纤维、聚丙烯纤维和植物纤维中的一种或几种。
9.根据权利要求8所述的混凝土发泡剂，其特征在于：所述植物纤维来源于植物秸秆、植物种子壳和木屑中的一种或几种。
10.一种发泡混凝土，其特征在于：其采用权利要求1-9中任一项所述的混凝土发泡剂制得。