CN110982272A - 一种用于充电宝内部电池固定的填充胶体 - Google Patents
一种用于充电宝内部电池固定的填充胶体 Download PDFInfo
- Publication number
- CN110982272A CN110982272A CN201911384740.9A CN201911384740A CN110982272A CN 110982272 A CN110982272 A CN 110982272A CN 201911384740 A CN201911384740 A CN 201911384740A CN 110982272 A CN110982272 A CN 110982272A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- battery
- iron oxide
- proportion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于充电宝内部电池固定的填充胶体，由以下组分组成：基料：羟基聚二甲基硅氧烷100‑120份；纳米级碳酸钙粉末60‑80份，氧化锌5‑10份；色母：镉红、镉黄、钛白粉、炭黑、氧化铁红或氧化铁黄中的一种；交联剂：甲基三甲氧基硅烷1‑8份、四甲氧基硅烷1‑8份、乙稀基三乙氧基硅烷1‑8份；偶联剂：氨丙基三乙氧基硅烷1份；催化剂：苯胺基甲基三乙氧基硅烷1‑8份、二乙胺基甲基三乙氧基硅烷1‑6份，所述的组分还包括发泡剂，所述的发泡剂为碳酸钙、碳酸镁、碳酸氢钠中的一种或任意比例的组合，所述的组分还包括散热剂，所述的散热剂为氧化铝导热剂或硅微粉中的一种或任意比例的组合。本发明具有硬度低、抗拉强度高、具有弹性等优点。
Description
技术领域
本发明涉及自来水过滤技术领域，具体为一种用于充电宝内部电池固定的填充胶体。
背景技术
充电宝是一种个人可随身携带，自身能储备电能，主要为手持式移动设备等消费电子产品，例如无线电话、笔记本电脑等电子产品，充电的便携充电器，特别应用在没有外部电源供应的场合。其主要组成部分包括：用作电能存储的电池，稳定输出电压的电路(直流-直流转换器)，绝大部分的行动电源带有充电器，用作为内置电池充电。
充电宝都会内置需电池，而外部是采用壳体将蓄电池套接，在使用一段时间后，内部的蓄电池在出现松动，并且使用中若出现摔落，内部的松动，会导致蓄电池的损坏，甚至会破坏内部的电路板，从而引起充电宝的损坏。
发明内容
本发明的目的在于提供一种用于充电宝内部电池固定的填充胶体，以解决上述背景技术中提出的问题。
为实现上述目的，本发明提供如下技术方案：一种用于充电宝内部电池固定的填充胶体，由以下组分组成：
基料：羟基聚二甲基硅氧烷100-120份；纳米级碳酸钙粉末60-80份，氧化锌5-10份；
色母：镉红、镉黄、钛白粉、炭黑、氧化铁红或氧化铁黄中的一种；
交联剂：甲基三甲氧基硅烷1-8份、四甲氧基硅烷1-8份、乙稀基三乙氧基硅烷1-8份；
偶联剂：氨丙基三乙氧基硅烷1份；
催化剂：苯胺基甲基三乙氧基硅烷1-8份、二乙胺基甲基三乙氧基硅烷1-6份。
进一步的，优选的，所述的组分还包括发泡剂，所述的发泡剂为碳酸钙、碳酸镁、碳酸氢钠中的一种或任意比例的组合。
进一步的，优选的，所述的组分还包括散热剂，所述的散热剂为氧化铝导热剂或硅微粉中的一种或任意比例的组合。
与现有技术相比，本发明的有益效果是：本发明提供的充电宝内部电池固定的填充胶体，能很好的将内置电池与壳体进行连接，并且硬度低、抗拉强度高、具有弹性；能很好的防止内置电池在壳体内松动，具有缓冲冲击力的效果，起到保护充电宝内部的作用，而增加的发泡剂可让胶体内部充满气泡，进一步提高弹性效果；而散热剂可增大胶体的散热效果，对电池起到过热保护的作用。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种用于充电宝内部电池固定的填充胶体，由以下组分组成：
基料：羟基聚二甲基硅氧烷100份；纳米级碳酸钙粉末60份，氧化锌5份；
色母：镉红、镉黄、钛白粉、炭黑、氧化铁红或氧化铁黄中的一种；
交联剂：甲基三甲氧基硅烷1份、四甲氧基硅烷1份、乙稀基三乙氧基硅烷1份；
偶联剂：氨丙基三乙氧基硅烷1份；
催化剂：苯胺基甲基三乙氧基硅烷1份、二乙胺基甲基三乙氧基硅烷1份。
进一步的，优选的，所述的组分还包括发泡剂，所述的发泡剂为碳酸钙。
进一步的，优选的，所述的组分还包括散热剂，所述的散热剂为氧化铝导热剂。
实施例2
一种用于充电宝内部电池固定的填充胶体，由以下组分组成：
基料：羟基聚二甲基硅氧烷100份；纳米级碳酸钙粉末60份，氧化锌5份；
色母：镉红、镉黄、钛白粉、炭黑、氧化铁红或氧化铁黄中的一种；
交联剂：甲基三甲氧基硅烷1份、四甲氧基硅烷1份、乙稀基三乙氧基硅烷1份；
偶联剂：氨丙基三乙氧基硅烷1份；
催化剂：苯胺基甲基三乙氧基硅烷1份、二乙胺基甲基三乙氧基硅烷1份。
进一步的，优选的，所述的组分还包括发泡剂，所述的发泡剂为碳酸镁、碳酸氢钠的任意比例的组合。
进一步的，优选的，所述的组分还包括散热剂，所述的散热剂为硅微粉中的一种或任意比例的组合。
实施例3
一种用于充电宝内部电池固定的填充胶体，由以下组分组成：
基料：羟基聚二甲基硅氧烷100-120份；纳米级碳酸钙粉末60-80份，氧化锌5-10份；
色母：镉红、镉黄、钛白粉、炭黑、氧化铁红或氧化铁黄中的一种；
交联剂：甲基三甲氧基硅烷8份、四甲氧基硅烷8份、乙稀基三乙氧基硅烷8份；
偶联剂：氨丙基三乙氧基硅烷1份；
催化剂：苯胺基甲基三乙氧基硅烷8份、二乙胺基甲基三乙氧基硅烷6份。
进一步的，优选的，所述的组分还包括发泡剂，所述的发泡剂为碳酸镁。
进一步的，优选的，所述的组分还包括散热剂，所述的散热剂为氧化铝导热剂与硅微粉的任意比例的组合。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (3)
1.一种用于充电宝内部电池固定的填充胶体，其特征在于，由以下组分组成：
基料：羟基聚二甲基硅氧烷100-120份；纳米级碳酸钙粉末60-80份，氧化锌5-10份；
色母：镉红、镉黄、钛白粉、炭黑、氧化铁红或氧化铁黄中的一种；
交联剂：甲基三甲氧基硅烷1-8份、四甲氧基硅烷1-8份、乙稀基三乙氧基硅烷1-8份；
偶联剂：氨丙基三乙氧基硅烷1份；
催化剂：苯胺基甲基三乙氧基硅烷1-8份、二乙胺基甲基三乙氧基硅烷1-6份。
2.根据权利要求1所述的一种用于充电宝内部电池固定的填充胶体，其特征在于，所述的组分还包括发泡剂，所述的发泡剂为碳酸钙、碳酸镁、碳酸氢钠中的一种或任意比例的组合。
3.根据权利要求1所述的一种用于充电宝内部电池固定的填充胶体，其特征在于，优选的，所述的组分还包括散热剂，所述的散热剂为氧化铝导热剂或硅微粉中的一种或任意比例的组合。