CN110803388A - 一种个人护理用品外袋膜及其包装袋 - Google Patents
一种个人护理用品外袋膜及其包装袋 Download PDFInfo
- Publication number
- CN110803388A CN110803388A CN201911223039.9A CN201911223039A CN110803388A CN 110803388 A CN110803388 A CN 110803388A CN 201911223039 A CN201911223039 A CN 201911223039A CN 110803388 A CN110803388 A CN 110803388A
- Authority
- CN
- China
- Prior art keywords
- layer
- sealing
- area
- mixture
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种个人护理用品外袋膜，总膜厚为25～40μm，从上至下依次包括消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层；其中，消光层原料为90wt％EVA和10wt％消光材料的混合物；遮盖层原料为80wt％LDPE和20wt％白色母的混合物；上粘合层和下粘合层原料为30wt％TIE和70wt％LLDPE的混合物；高阻隔层原料为EVOH；阻水层原料为50wt％LDPE和50wt％LLDPE的混合物；热封层原料为70wt％MLLDPE和30wt％EVA的混合物。同时，本发明还提供了该外袋膜的制备方法以及由该外袋膜制成的包装袋。
Description
技术领域
本发明涉及护理用品包装技术领域，特别涉及一种个人护理用品外袋膜及其包装袋。
背景技术
个人护理用品如护理垫、尿不湿、卫生棉、防溢乳垫、一次性内裤等因护理方便、能有效杜绝交叉感染而被广泛用于医院手术、妇科检查、产妇护理、幼儿看护、瘫痪病人、大小便失禁和行动不便病人、女性生理期等特殊时期。这些护理用品通常都是直接与人体皮肤接触，因此都需要进行严格的杀菌消毒，然后包装以便于运输。这就要求包装这些护理用品的外袋具有极佳的阻隔、抗撕裂和热封性能，同时为了保护个人隐私防止选购和携带时产生尴尬，还需要一定的遮盖性。
现有的护理用品包装袋大多为铝塑复合包装膜，如中国专利公开号为CN204384012 U名称为卫生用品包装袋用的复合包装膜的专利，公开的包装膜由PE层和VMPE层复合而成，虽具有较好的阻隔性能、柔软性和热封性能，但抗撕裂性能和耐久性能差，也不具备遮盖性，不能满足市场需求。
另外，现有的护理用品包装袋不易揭开，且大多揭开后不可重新密封或密封效果差，从而导致护理用品被细菌侵入、潮解以及氧化，从而缩短了护理用品的储存寿命。
因此，有必要研究设计一种新的个人护理用品外袋膜及其包装袋，以解决上述问题。
发明内容
本发明的第一个目的在于提供一种个人护理用品外袋膜。
本发明的第二个目的在于提供一种上述个人护理用品外袋膜的制备方法。
本发明的第三个目的在于提供一种由上述外袋膜制成的包装袋。
为达到上述发明的目的，本发明的技术方案如下：
本发明的第一个方面提供了一种个人护理用品外袋膜，总膜厚为25～40μm，从上至下依次包括消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层；其中，
所述消光层的原料为90wt％EVA和10wt％消光材料的混合物；
所述遮盖层的原料为80wt％LDPE和20wt％白色母的混合物；
所述上粘合层和下粘合层所用原料相同，为30wt％TIE和70wt％LLDPE的混合物；
所述高阻隔层的原料为EVOH；
所述阻水层的原料为50wt％LDPE和50wt％LLDPE的混合物；
所述热封层的原料为70wt％MLLDPE和30wt％EVA的混合物。
进一步地，所述热封层的原料为70wt％Surlyn和30wt％EVA的混合物
进一步地，所述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层的厚度分别为总膜厚的10-20％、10-20％、5-10％、5-10％、5-10％、10-20％、10-20％。
更进一步地，所述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层的厚度分别为总膜厚的18％、17％、10％、7％、10％、18％、20％。
进一步地，所述TIE的密度范围0.91～0.925g/ml，熔融指数为1～5。
进一步地，所述EVOH的密度范围为1.17～1.25g/ml，且其中的乙烯含量低于44％。
本发明的第二个方面提供了一种上述个人护理用品外袋膜的制备方法，包括如下步骤：
根据上述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层结构的组分准备原料颗粒，按照从上而下的顺序将各层原料颗粒分别送入对应的挤出机料斗中，经熔融后通过对应的模口挤出吹胀形成膜泡，经定径笼通过风环冷却确定膜泡直径和膜泡厚度，然后分切收卷，即得到所述个人护理用品外袋膜。
进一步地，所述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层的熔融温度分别为170-220℃、180-230℃、180-230℃、180-210℃、180-230℃、180-220℃、180-220℃。
本发明的第三个方面提供了一种上述外袋膜制成的包装袋，包括袋体，在所述袋体的正面设有开口区，在开口区的正上方设有揭启条；所述开口区包括第一子胶黏区、封口线、密封槽和第二子胶黏区；在封口线至开口区上缘段，以及封口线至开口区下缘端水平设有一组密封槽；所述揭启条包括揭启条主体，揭启条主体的一端与开口区的最右端呈一体设计，揭启条主体的另一端设有起揭段；在揭启条主体的里侧与第一子胶黏区、密封槽以及第二子胶黏区相对应处分别设有第一母胶黏区、密封凸棱和第二母胶黏区。
进一步地，所述第一子胶黏区、第二子胶黏区分别设置在开口区的左右两端；所述封口线设置在开口区的中心线上，且封口线的两端分别与第一子胶黏区和第二子胶黏区相接。
进一步地，所述揭启条主体的长度和宽度均与所述开口区的长度和宽度相一致。
进一步地，所述开口区的长度与袋体的正面的长度相一致。
进一步地，所述密封凸棱的长度、厚度和高度均与密封槽的长度、宽度和深度相匹配。
本发明跟现有技术相比，其优势和有益效果在于：
1、本发明的外袋膜通过多层共挤出吹膜工艺生产，表层采用EVA和消光材料的混合物制成，不仅使表层具有哑光效果，且柔软性佳，从而使外袋膜更具市场性；同时，采用LDP E和白色母的混合物制成遮盖层的设计可以很好地遮住所装产品，从而有效地防止了客户挑选以及携带时产生尴尬；而采用LDPE和LLDPE的混合物制成的阻水层，有效地防止了空气中的水汽通过表层聚积在阻隔层表面导致阻隔层被侵蚀而失效，进而延长了袋装膜的使用寿命；热封层采用MLLDPE和EVA的混合设计，不仅起到了低温封口作用，还具有防菌功能；此外，粘合层采用TIE和LLDPE的混合设计，大大提高了外袋膜的粘合度，从而提高了外袋膜的抗撕裂性能；
2、本发明的包装袋，其开口区和揭启条的设计方便了开袋取物，且其重新密封功能更是很好地阻隔了外部细菌的进入以及对产品的潮解和氧化，延长了产品的储存期限。
附图说明
图1为本发明实施例1的结构层次示意图；
图2为本发明实施例3的结构层次示意图；
图3为本发明实施例6的包装袋的整体结构示意图一；
图4为本发明实施例6的包装袋的整体结构示意图二；
图5为本发明实施例6的包装袋正面封口结构示意图；
附图标记：袋体1、揭启条2、起揭段3、第一子胶黏区4、封口线5、密封槽6、第二子胶黏区7、第一母胶黏区8、密封凸棱9、第二母胶黏区10。
具体实施方式
以下结合附图和具体实施例，对本发明做进一步说明。
本发明实施例所用原料如下表1所示，但不以此为限：
表1
实施例1
如图1所示为本发明的一种膜厚为30μm的个人护理用品外袋膜，从上至下依次包括消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层；
其中，所述消光层的原料为EVA和消光材料的混合物，厚度为总膜厚的18％，消光材料的加入使得表层具有哑光效果，且柔软性佳，从而使外袋膜更具市场性；
所述遮盖层的原料为LDPE和白色母的混合物，厚度为总膜厚的17％，由于个人护理用品是具有隐私性的商品，遮盖层的设计可以很好地遮住所装产品，从而有效地防止了客户挑选以及携带时产生尴尬；
所述上粘合层和下粘合层的原料均为TIE和LLDPE的混合物，厚度均为总膜厚的10％，粘合层采用TIE和LLDPE的混合设计，大大提高了外袋膜的粘合度，从而提高了外袋膜的抗撕裂性能；
所述高阻隔层的原料为EVOH，厚度为总膜厚的7％，确保了包装产品的较长保质期和保存效果，且薄膜有较好的柔韧性、抗拉强度和低温热封性能；
所述阻水层的原料为LDPE和LLDPE的混合物，厚度为总膜厚的18％，阻水层的设计防止了空气中的水汽通过表层聚积在EVOH层导致EVOH被侵蚀而失效，进而延长了袋装膜的使用寿命；
所述热封层的原料为MLLDPE和EVA的混合物，厚度为总膜厚的20％，热封层采用MLLDPE和EVA的混合设计，不仅起到了低温封口作用，还具有防菌功能。
进一步地，所述TIE的密度范围0.91～0.925g/ml，熔融指数为1～5；所述EVOH的密度范围为1.17～1.25g/ml，且其中的乙烯含量低于44％。
上述个人护理用品外袋膜的制备方法，包括如下步骤：
消光层，将EVA和消光料材料按质量比9:1混合均匀，加入对应的挤出机料斗中，温度为170-220℃的条件下熔融，进入口模；
遮盖层，将LDPE和白色母按质量比4:1混合均匀，加入对应的挤出机料斗中，温度为180-230℃条件下熔融，进入口模；
上粘合层，将TIE和LLDPE按质量比3:7混合均匀，加入对应的挤出机料斗中，温度为180-230℃的条件下熔融，进入口模；
阻隔层，将EVOH加入对应的挤出机料斗中，温度为180-210℃条件下熔融，进入口模；
下粘合层，将TIE和LLDPE按质量比3:7混合均匀，加入对应的挤出机料斗中，温度为180-230℃的条件下熔融，进入口模；
阻水层，将LDPE和LLDPE的原料PE按质量比1:1混合均匀，加入对应的挤出机料斗中，温度为180-220℃条件下熔融，进入口模；
热封层，将MLLDPE和EVA按质量比7:3混合均匀，加入对应的挤出机料斗中，温度为180-220℃条件下熔融，进入口模；
然后经过模口挤出多层共挤膜的膜泡，模口上方膜泡外侧的定径笼通过风环冷却确定膜泡直径，定径笼上方的若干个气垫辊喷出的气流支持浮起膜泡；定径笼和气垫辊对经过膜泡进行降温，使膜泡具有一定的结构强度，确定其固定的直径大小和膜泡厚度；同时，膜泡由气垫辊和定径笼的气流支撑浮起，不会与膜泡产生摩擦，避免膜泡表面产生拉丝等现象，确保膜边的最佳质量：将膜泡定径冷却后，分切成为片状的膜，收卷后得到所述外袋膜。
实施例2
相较于实施例1的区别仅在于：制备了一种膜厚为40μm的个人护理用品外袋膜，其层次结构、各层厚度所占膜厚的比例以及各层原料配方均与实施例1相同。
实施例3
相较于实施例1的区别仅在于：所述热封层的原料为Surlyn和EVA按质量比7:3混合而成，其余均同实施例1，如图2所示。
实施例4
相较于实施例2的区别仅在于：制备了一种膜厚为40μm的个人护理用品外袋膜，其层次结构、各层厚度所占膜厚的比例以及各层原料配方均与实施例2相同。
实施例5
相较于实施例1的区别仅在于：制备了一种膜厚为25μm的个人护理用品外袋膜，其层次结构、各层厚度所占膜厚的比例以及各层原料配方均与实施例1相同。
对比例1
相较于实施例1的区别仅在于：所述消光层的原料为LDPE和消光材料按质量比9:1混合而成，其余均同实施例1。
实施例1-5和对比例1的性能测试
根据中华人民共和国国家标准GB/T 10004-2008《包装用塑料复合膜、袋干法复合、挤出复合》对上述实施例1-5和对比例1所制备的外袋膜进行抗拉强度、断裂伸长率、遮盖度、剥离强度、热封强度和氧气透过率测试，标准GB/T 10004-2008中各项性能相对应地具体测试规范分别为：GB/T 1040.3-2006、GB/T 1040.3-2006、GB/T 2410-2008、GB/T8808-1988、QB/T 2358-1998、GB/T 1038-2000，测试数据如下表2所示：
表2
根据表2可知：实施例1-5和对比例1的剥离强度测试结果均为剥不出，说明实施例1-5和对比例1所制得的外袋膜各层之间的粘合的特别牢固，通过其配方可知，粘合层采用TIE和LLDPE(质量比3:7)的混合物是最佳配方；此外，通过对比实施例1和对比例1的其他性能数据可知，实施例1的各项性能均优于对比例1，由此可知，消光层采用EVA与消光材料混合比PE更优；另外，通过分别对比实施例1与实施例3、实施例2与实施例4的各项性能数据可知，热封层采用Surlyn与EVA混合比用MLLDPE更优。
本发明的外袋膜通过多层共挤出吹膜工艺生产，表层具有消光效果，内层具有遮盖效果，热封层具有低温封口和防菌功能，且柔软性佳、阻隔性好、不易撕裂。
实施例6
如图3-5所示为本发明用上述外袋膜制成的一种包装袋，包括袋体1，在所述袋体1的正面设有开口区，在开口区的正上方设有揭启条2；所述开口区的长度与袋体1的正面的长度相一致，包括第一子胶黏区4、封口线5、密封槽6和第二子胶黏区7；所述第一子胶黏区4、第二子胶黏区7分别设置在开口区的左右两端；所述封口线5设置在开口区的中心线上，且封口线5的两端分别相接于第一子胶黏区4和第二子胶黏区7；在封口线5至开口区上缘段，以及封口线5至开口区下缘端水平设有一组密封槽6；所述揭启条2包括揭启条主体，揭启条主体的长度和宽度均与所述开口区的长度和宽度相一致；揭启条主体的一端与开口区的最右端呈一体设计，揭启条主体的另一端设有起揭段3；在揭启条主体的里侧与第一子胶黏区4、密封槽6以及第二子胶黏区7相对应处分别设有第一母胶黏区8、密封凸棱9和第二母胶黏区10；所述密封凸棱9的长度、厚度和高度均与密封槽6的长度、宽度和深度相匹配。
本发明的包装袋在使用时，捏住起揭段3将揭启条2打开，然后拉扯封口线5的上下两侧形成开口，便可从袋中取出物品，取完后，立即将揭启条2合上，此时，揭启条2的第二母胶黏区10与第二子胶黏区7重合粘接在一起，然后密封凸棱9从根部起嵌入密封槽6内，最后将第一母胶黏区8与第一子胶黏区4相重合粘接在一起，便可重新起到密封作用。
以上已对本发明创造的较佳实施例进行了具体说明，但本发明创造并不仅限于所述的实施例，熟悉本领域的技术人员在不违背本发明创造精神的前提下还可以作出种种的等同的变型或替换，这些等同变型或替换均包含在本申请权利要求所限定的范围内。
Claims (10)
1.一种个人护理用品外袋膜，其特征在于，总膜厚为25～40μm，从上至下依次包括消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层；其中，
所述消光层的原料为90wt％EVA和10wt％消光材料的混合物；
所述遮盖层的原料为80wt％LDPE和20wt％白色母的混合物；
所述上粘合层和下粘合层所用原料相同，为30wt％TIE和70wt％LLDPE的混合物；
所述高阻隔层的原料为EVOH；
所述阻水层的原料为50wt％LDPE和50wt％LLDPE的混合物；
所述热封层的原料为70wt％MLLDPE和30wt％EVA的混合物。
2.根据权利要求1所述的一种个人护理用品外袋膜，其特征在于，所述热封层的原料为70wt％Surlyn和30wt％EVA的混合物。
3.根据权利要求1所述的一种个人护理用品外袋膜，其特征在于，所述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层的厚度分别为总膜厚的10-20％、10-20％、5-10％、5-10％、5-10％、10-20％、10-20％。
4.根据权利要求3所述的一种个人护理用品外袋膜，其特征在于，所述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层的厚度分别为总膜厚的18％、17％、10％、7％、10％、18％、20％。
5.根据权利要求1所述的一种个人护理用品外袋膜，其特征在于，所述TIE的密度范围0.91～0.925g/ml，熔融指数为1～5；所述EVOH的密度范围为1.17～1.25g/ml，且其中的乙烯含量低于44％。
6.根据权利要求1-5任一项所述的一种个人护理用品外袋膜的制备方法，其特征在于，包括如下步骤：
根据消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层结构的组分准备原料颗粒，按照从上而下的顺序将各层原料颗粒分别送入对应的挤出机料斗中，经熔融后通过对应的模口挤出吹胀形成膜泡，经定径笼通过风环冷却确定膜泡直径和膜泡厚度，然后分切收卷，即得到所述个人护理用品外袋膜；其中，所述消光层、遮盖层、上粘合层、高阻隔层、下粘合层、阻水层、热封层的熔融温度分别为170-220℃、180-230℃、180-230℃、180-210℃、180-230℃、180-220℃、180-220℃。
7.一种由权利要求1-6任一项所述的外袋膜制成的包装袋，其特征在于，包括袋体，在所述袋体的正面设有开口区，在开口区的正上方设有揭启条；所述开口区包括第一子胶黏区、封口线、密封槽和第二子胶黏区；所述第一子胶黏区、第二子胶黏区分别设置在开口区的左右两端；所述封口线设置在开口区的中心线上，且封口线的两端分别与第一子胶黏区和第二子胶黏区相接；在封口线至开口区上缘段，以及封口线至开口区下缘端水平设有一组密封槽；所述揭启条包括揭启条主体，揭启条主体的一端与开口区的最右端呈一体设计，揭启条主体的另一端设有起揭段；在揭启条主体的里侧与第一子胶黏区、密封槽以及第二子胶黏区相对应处分别设有第一母胶黏区、密封凸棱和第二母胶黏区。
8.根据权利要求7所述的包装袋，其特征在于，所述揭启条主体的长度和宽度均与所述开口区的长度和宽度相一致。
9.根据权利要求7所述的包装袋，其特征在于，所述开口区的长度与袋体的正面的长度相一致。
10.根据权利要求7所述的包装袋，其特征在于，所述密封凸棱的长度、厚度和高度均与密封槽的长度、宽度和深度相匹配。