CN110788568A - 一种高压容器用不锈钢锻件的加工方法 - Google Patents
一种高压容器用不锈钢锻件的加工方法 Download PDFInfo
- Publication number
- CN110788568A CN110788568A CN201911018301.6A CN201911018301A CN110788568A CN 110788568 A CN110788568 A CN 110788568A CN 201911018301 A CN201911018301 A CN 201911018301A CN 110788568 A CN110788568 A CN 110788568A
- Authority
- CN
- China
- Prior art keywords
- forging
- ring
- blank
- size
- machining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高压容器用不锈钢锻件的加工方法,包括以下步骤:S1:下料:对钢锭进行锯切,作为锻造的坯料,坯料的尺寸为能够锻造出N个锻件的尺寸,且坯料的尺寸小于N个单元坯料的尺寸,所述单元坯料的尺寸为按照单个锻件尺寸进行下料的尺寸;S2:锻前加热;S3:锻造;S4:冲孔;S5:碾环成型,碾环的锻造比为12‑13,碾环完成后空冷至室温;S6:将碾环后的环锻件通过机械手输送机床上进行粗加工,将粗加工后的环锻件件无损检测,对无损检测后的环锻件进行精加工;S7:将精加工后的环锻件输送至锯床上进行锯切成N个目标环锻件。
Description
技术领域
本发明涉及一种高压容器用不锈钢锻件的加工方法。
背景技术
现有技术中的环锻件加工,由于环锻件在锻造过程中,较薄的环锻件环极易发生变形,因此目前都是将环锻件造厚度大于设计厚度,而后通过机加工,如切削的方式使其达到设计标准,采用上述方法,不仅效率低下,而且造成大量的原材料浪费,大大增加了生产成本。
发明内容
本发明的目的在于,克服现有技术中存在的缺陷,提供一种高压容器用不锈钢锻件的加工方法。
为实现上述目的,本发明的技术方案是设计一种高压容器用不锈钢锻件的加工方法,包括以下步骤:
S1:下料:对钢锭进行锯切,作为锻造的坯料,坯料的尺寸为能够锻造出N个锻件的尺寸,且坯料的尺寸小于N个单元坯料的尺寸,所述单元坯料的尺寸为按照单个锻件尺寸进行下料的尺寸;
S2:锻前加热:采用天然气加热炉对坯料进行加热,以每小时 50℃升温到 650℃保温2.5 小时,然后再以每小时 100℃ ~120℃,升温至 1180℃,保 温 2 小时后,出炉开始锻造;
S3:锻造,利用机械手将坯料从炉中取出后置于压力即上进行锻造,采用三拔三墩进行作业,锻造比大于4.5;
S4:冲孔:在压力机上用冲头进行冲孔;
S5:碾环成型,碾环的锻造比为12-13,碾环完成后空冷至室温;
S6:将碾环后的环锻件通过机械手输送机床上进行粗加工,将粗加工后的环锻件件无损检测,对无损检测后的环锻件进行精加工;
S7:将精加工后的环锻件输送至锯床上进行锯切成N个目标环锻件。
本发明的优点和有益效果在于:将多个环锻件一次进行下料、锻造以及精加工成型,最后再将成型后的环锻件通过锯床锯切呈多个目标环锻件,不仅用料节省,而且大大提高了生产效率。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
一种高压容器用不锈钢锻件的加工方法,包括以下步骤:
S1:下料:对钢锭进行锯切,作为锻造的坯料,坯料的尺寸为能够锻造出N个锻件的尺寸,且坯料的尺寸小于N个单元坯料的尺寸,所述单元坯料的尺寸为按照单个锻件尺寸进行下料的尺寸;
S2:锻前加热:采用天然气加热炉对坯料进行加热,以每小时 50℃升温到 650℃保温2.5 小时,然后再以每小时 100℃ ~120℃,升温至 1180℃,保 温 2 小时后,出炉开始锻造;
S3:锻造,利用机械手将坯料从炉中取出后置于压力即上进行锻造,采用三拔三墩进行作业,锻造比大于4.5;
S4:冲孔:在压力机上用冲头进行冲孔;
S5:碾环成型,碾环的锻造比为12-13,碾环完成后空冷至室温;
S6:将碾环后的环锻件通过机械手输送机床上进行粗加工,将粗加工后的环锻件件无损检测,对无损检测后的环锻件进行精加工;
S7:将精加工后的环锻件输送至锯床上进行锯切成N个目标环锻件。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.一种高压容器用不锈钢锻件的加工方法,其特征在于,包括以下步骤:
S1:下料:对钢锭进行锯切,作为锻造的坯料,坯料的尺寸为能够锻造出N个锻件的尺寸,且坯料的尺寸小于N个单元坯料的尺寸,所述单元坯料的尺寸为按照单个锻件尺寸进行下料的尺寸;
S2:锻前加热:采用天然气加热炉对坯料进行加热,以每小时 50℃升温到 650℃保温2.5 小时,然后再以每小时 100℃ ~120℃,升温至 1180℃,保 温 2 小时后,出炉开始锻造;
S3:锻造,利用机械手将坯料从炉中取出后置于压力即上进行锻造,采用三拔三墩进行作业,锻造比大于4.5;
S4:冲孔:在压力机上用冲头进行冲孔;
S5:碾环成型,碾环的锻造比为12-13,碾环完成后空冷至室温;
S6:将碾环后的环锻件通过机械手输送机床上进行粗加工,将粗加工后的环锻件件无损检测,对无损检测后的环锻件进行精加工;
S7:将精加工后的环锻件输送至锯床上进行锯切成N个目标环锻件。