CN110703578A - 具有由非磁性合金制成的轴状部分的钟表部件 - Google Patents

具有由非磁性合金制成的轴状部分的钟表部件 Download PDF

Info

Publication number
CN110703578A
CN110703578A CN201910620260.1A CN201910620260A CN110703578A CN 110703578 A CN110703578 A CN 110703578A CN 201910620260 A CN201910620260 A CN 201910620260A CN 110703578 A CN110703578 A CN 110703578A
Authority
CN
China
Prior art keywords
mass
component
silver
palladium
magnetic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910620260.1A
Other languages
English (en)
Other versions
CN110703578B (zh
Inventor
A·德利兹
C·雷蒙德
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Blancpain SA
Original Assignee
Blancpain SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Blancpain SA filed Critical Blancpain SA
Publication of CN110703578A publication Critical patent/CN110703578A/zh
Application granted granted Critical
Publication of CN110703578B publication Critical patent/CN110703578B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种钟表部件(1)，其包括轴状部分(2)，该轴状部分(2)包括围绕枢转轴线(D)的至少一个枢轴(3)，至少形成该轴状部分(2)的材料是至少包含银和钯且维氏硬度大于450HV的非磁性合金。

Description

具有由非磁性合金制成的轴状部分的钟表部件
技术领域
本发明涉及一种钟表部件，其包括轴状部分，该轴状部分包括围绕枢转轴线的至少一个枢轴。
本发明还涉及一种包括至少一个这种部件的钟表振荡器。
本发明还涉及一种钟表机芯，其包括至少一个这样的振荡器和/或至少一个这样的部件。
本发明还涉及一种钟表，其包括至少一个这样的机芯，和/或至少一个这样的振荡器，和/或至少一个这样的部件。
本发明涉及钟表部件和轮副的领域，更具体地涉及包括在振荡器或钟表机芯中的轮副的制造。
背景技术
制造非磁性钟表轮副不是常规做法。然而，这在依赖于磁性定律的各种类型的机芯中是需要的，以特别是减少或消除摩擦，尤其是在意图取消传统的杠杆类型止动机构的振荡器中，所述摩擦对于动力储备非常有害。
发明内容
本发明提出提供针对具有钢心轴的传统钟表轮副的替代方案，其可以在磁性类型的机构不能受干扰的环境中使用。
为此，本发明涉及一种根据权利要求1所述的钟表部件，其包括轴状部分，所述轴状部分包括围绕枢转轴线的至少一个枢轴。
本发明还涉及一种包括至少一个这种部件的钟表振荡器。
本发明还涉及一种钟表机芯，其包括至少一个这样的振荡器和/或至少一个这样的部件。
本发明还涉及一种钟表，其包括至少一个这样的机芯，和/或至少一个这样的振荡器，和/或至少一个这样的部件。
附图说明
参考附图阅读以下详细描述后，本发明的其他特征和优点将显现出来，其中：
-图1表示根据本发明的钟表部件的示意性侧视图，该钟表部件在此是形成摆轮的轮副，并且包括贯穿的轴状部分，该轴状部分在其旋转轴线上的远端处具有两个枢轴，该轴状部分在第一肩部上承载摆轮轮缘，在第二肩部上承载摆轮圆盘，该摆轮轮缘沿侧向被支承在轴环(即轴肩，collar)的第一侧上，该轴环形成轴状部分的最大直径的区域；摆轮圆盘被支承在轴环的与第一侧相对的第二侧上，并且摆轮圆盘承载有冲击销；
-图2是表示包括钟表机芯的钟表的方框图，该钟表机芯包括具有一个这样的轮副的振荡器。
具体实施方式
除非另有说明，否则本说明书中的组合物是质量百分比组合物。
本发明涉及一种钟表部件1，特别是一种轮副，其包括轴状部分2，该轴状部分2包括围绕枢转轴线D的至少一个枢轴3。
关于该轴状部分的材料，优选其维氏硬度介于铜/铍合金的维氏硬度(380HV+/-20)和20AP钢或类似物的维氏硬度(740HV+/-30)之间。
根据本发明，至少形成该轴状部分2的材料是至少含有银和钯并且维氏硬度大于450HV的非磁性合金。
在一个特定实施例中，部件1是完全非磁性的。
在一个特定实施例中，轴状部分2在枢转轴线D的方向上贯穿部件1的整个长度。
更具体地，轴状部分2承载同样非磁性的至少一个附加元件4,40。更特别地，每个附加元件4,40都是非磁性的。更特别地，形成每个所述附加元件4,40的材料是至少含有银和钯的非磁性合金，其维氏硬度大于450HV。
在一个特定实施例中，形成至少一个——更特别地是每个——附加元件4,40的材料与形成轴状部分2的材料相同。
在一个变型中，形成至少一个附加元件4,40的材料是陶瓷。
在另一个变型中，形成至少一个附加元件4,40的材料是硅和/或二氧化硅，或者金属玻璃或非晶态金属或基本非晶态的金属，或类似物，例如DLC(类金刚石碳)或其他材料。
在一个特定的组合物中，轴状部分2的至少含有银和钯的该非磁性合金含有以质量计50％-60％的钯和25％-40％的银。
在另一种特定的组合物中，轴状部分2的至少含有银和钯的该非磁性合金含有以质量计25％-35％的钯和65％-75％的银，其中至少银和钯的总质量占比小于或等于100％。
在另一种特定的组合物中，轴状部分2的至少含有银和钯的该非磁性合金含有以质量计至少50％的钯或至少80％的银，其中所述合金的组分的总质量占比等于100％。在这种情况下，合金可以针对纯度进行分级。
在另一种特定的组合物中，轴状部分2的至少含有银和钯的该非磁性合金是含有银、钯和铜的三元合金，其含有以质量计20％-50％的钯和20％-50％的银以及20％-40％的铜，其中银、铜和钯的总质量占比小于或等于100％。铜具有显著提高合金硬度的作用。
在一个有利的变型中，这种非磁性三元合金含有以质量计36％-40％的钯、38％-42％的银、19％-23％的铜，其中银、钯和铜的总质量占比小于或等于100％。该合金的维氏硬度在450HV-510HV之间，更具体地，在470HV-490HV之间。因此，该合金形成用于任何车削轮廓的钟表部件的有利材料，因为它具有良好的机械加工性并且其机械性能接近于钢的机械性能。因此，它更特别适用于非磁性轮副，或至少适用于非磁性轮副心轴。
在一个特定的变型中，至少含有银和钯的该合金不含规定在“针对危险物质和制剂的瑞士化学品保护条例”(ChemO)附录3和“减少化学产品风险条例(ORRChim)”附录1.17(REACH法规(EC)No 1907/2006的附录XIV中列出的物质)中的SVHC(高度关注物质)。
在一个特定的变型中，轴状部分2的这种至少含有银和钯的非磁性合金的弹性模量在95GPa-105GPa之间。
在一个特定的变型中，轴状部分2的这种至少含有银和钯的非磁性合金的膨胀系数在14.10-6-17.10-6之间。
在一个特定的变型中，轴状部分2的这种至少含有银和钯的非磁性合金的泊松比在0.35-0.39之间。
在一个变型中，这种至少含有银和钯的非磁性合金含有以质量计0％-2％的铟，以增强合金，其中所述合金的组分的总质量占比等于100％。
在一个变型中，这种至少含有银和钯的非磁性合金含有以质量计0％-2％的锡，以增强合金，其中所述合金的组分的总质量占比等于100％。
在一个变型中，这种至少含有银和钯的非磁性合金含有以质量计0％-2％的铂，更特别是0％-0.8％的铂，更特别是0％-0.5％的铂，其中合金组分的总质量占比等于100％。
在仅用于手表中的用途的一个变型中，这种至少含有银和钯的非磁性合金含有以质量计0％-1.0％的镍，其中合金组分的总质量占比等于100％。
在一个变型中，这种至少含有银和钯的非磁性合金含有以质量计0％-0.1％的锌，以获得更高的强度和硬度，其中合金组分的总质量占比等于100％。
在一个变型中，这种至少含有银和钯的非磁性合金含有以质量计0.01％-0.03％的硼，以获得更高的强度和硬度，其中合金组分的总质量占比等于100％。
在一个变型中，这种至少含有银和钯的非磁性合金含有以质量计总量小于或等于1％的金和/或铂和/或钌和/或铼、改性剂，其中合金组分的总质量占比等于100％。
因此，取决于合金的组分，可以获得接近500HV或大于500HV的硬度。
在一种特定情况下，如图1所示，该部件1是摆轮，并且在其轴状部分2上承载至少一个轮缘4和至少一个圆盘40，其分别被支承在承载表面50和60上。
合金的选择使得可以生产直径非常小——特别是小于70微米——的枢轴柄(pivot-shank)。
本发明还涉及一种钟表振荡器100，其包括至少一个这样的部件1。
本发明还涉及一种钟表机芯200，其包括至少一个这样的振荡器100，和/或至少一个这样的部件1。
本发明还涉及一种钟表1000，其包括至少一个这样的机芯200，和/或至少一个这样的振荡器100，和/或至少一个这样的部件1。
更具体地，该钟表1000是手表。
简而言之，选择可以按纯度分级的贵重材料来制造钟表轮副心轴，这克服了关于贵金属合金磨损快的技术偏见。从上面描述中选择含有至少银和钯的合金，对于磨损问题而言提供了意料不到的解决方案，因为这些合金在正常使用条件下显示出非常小的磨损，同时如期望的那样是非磁性的。
当然，尽管上面的描述主要集中在具有附加元件(这降低了材料成本)的轮副的实施例上，但是完全可以使用至少包含银和钯的这些合金来制造单件式轮副。
本发明对于之前仍然困难的制造小直径非磁性轮副的问题提供了一个很好的解决方案，所述小直径非磁性轮副特别是用于振荡器轮副、计时器心轴等。

Claims (26)

1.一种钟表部件(1)，其包括轴状部分(2)，所述轴状部分(2)包括围绕枢转轴线(D)的至少一个枢轴(3)，其特征在于，至少形成所述轴状部分(2)的材料是至少含有银和钯并且维氏硬度大于450HV的非磁性合金。
2.根据权利要求1所述的部件(1)，其特征在于，所述部件(1)是完全非磁性的。
3.根据权利要求1所述的部件(1)，其特征在于，所述轴状部分(2)在所述枢转轴线(D)的方向上贯穿所述部件(1)的整个长度。
4.根据权利要求1所述的部件(1)，其特征在于，所述轴状部分(2)承载至少一个非磁性的附加元件(4；40)。
5.根据权利要求4所述的部件(1)，其特征在于，形成每个所述附加元件(4,40)的材料是至少含有银和钯并且维氏硬度大于450HV的非磁性合金。
6.根据权利要求4所述的部件(1)，其特征在于，形成每个所述附加元件(4；40)的材料与形成所述轴状部分(2)的材料相同。
7.根据权利要求4所述的部件(1)，其特征在于，形成至少一个所述附加元件(4；40)的材料是陶瓷。
8.根据权利要求4所述的部件(1)，其特征在于，形成至少一个所述附加元件(4；40)的材料是硅和/或二氧化硅，或者金属玻璃或非晶态金属或基本非晶态的金属。
9.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计50％-60％的钯和25％-40％的银。
10.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计25％-35％的钯和65％-75％的银，其中至少银和钯的总和按质量计≤100％。
11.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金是银、钯和铜的非磁性三元合金，所述非磁性三元合金包含按质量计20％-50％的钯和20％-50％的银和20％-40％的铜，其中银、铜和钯的总和按质量计≤100％。
12.根据权利要求11所述的部件(1)，其特征在于，所述非磁性三元合金包含按质量计36％-40％的钯、38％-42％的银和19％-23％的铜，其中银、钯和铜的总和按质量计≤100％，并且所述非磁性三元合金的维氏硬度在450HV-510HV之间。
13.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计至少50％的钯或至少80％的银，其中合金组分的总和按质量计等于100％。
14.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金的弹性模量在95GPa-105GPa之间。
15.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计0％-2％的铟，其中合金组分的总和按质量计等于100％。
16.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计0％-2％的锡，其中合金组分的总和按质量计等于100％。
17.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含以质量计0％-1.0％的镍，其中合金组分的总和按质量计等于100％。
18.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计0％-2％的铂，其中合金组分的总和按质量计等于100％。
19.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计0％-0.1％的锌，其中合金组分的总和按质量计等于100％。
20.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计0.01％-0.03％的硼，其中合金组分的总和按质量计等于100％。
21.根据权利要求1所述的部件(1)，其特征在于，至少含有银和钯的所述非磁性合金包含按质量计总和小于或等于1％的金和/或铂和/或钌和/或铼，其中合金组分的总和按质量计等于100％。
22.根据权利要求1所述的部件(1)，其特征在于，所述部件(1)是摆轮，并且所述部件在所述轴状部分(2)上承载至少一个轮缘(4)和至少一个圆盘(40)。
23.一种钟表振荡器(100)，其包括至少一个根据权利要求1所述的部件(1)。
24.一种钟表机芯(200)，其包括至少一个根据权利要求23所述的振荡器(100)。
25.一种钟表(1000)，其包括至少一个根据权利要求24所述的机芯(200)。
26.根据权利要求25所述的钟表(1000)，其特征在于，所述钟表是手表。
CN201910620260.1A 2018-07-10 2019-07-10 具有由非磁性合金制成的轴状部分的钟表部件 Active CN110703578B (zh)