CN110643111A - 一种高细腻度tpv材料 - Google Patents
一种高细腻度tpv材料 Download PDFInfo
- Publication number
- CN110643111A CN110643111A CN201810673691.XA CN201810673691A CN110643111A CN 110643111 A CN110643111 A CN 110643111A CN 201810673691 A CN201810673691 A CN 201810673691A CN 110643111 A CN110643111 A CN 110643111A
- Authority
- CN
- China
- Prior art keywords
- parts
- vulcanizing agent
- mixing
- eva
- embs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及TPV材料制备技术领域,是一种高细腻度TPV材料,它由下述重量份原料组成:PP 20‑30,EPDM 20‑30,EVA 2‑5,EMBS 2‑5,碳酸钙5‑10,硫化剂2‑5,助硫化剂2‑4,氧化锌1‑4,抗氧剂1‑5,硫酸钡1‑10,紫外线吸收剂2‑5,润滑剂2‑5,分散剂1‑4,色母粒1‑5;制备时,将EPDM、PP、EVA、EMBS、硫化剂、助硫化剂、碳酸钙、硫酸钡加入混炼机内混炼15‑20分钟,混炼完成后加入双螺杆挤出机熔融、挤出、切粒、干燥,包装,即得;本发明产品力学性能优良,手感细腻,可广泛用于各种产品的外表面装饰使用。
Description
技术领域
本发明属于TPV材料制备技术领域,具体是一种高细腻度TPV材料。
背景技术
目前,TPV材料因具有良好的低压缩变形性能、优良的耐酸碱性、优异的抗冲击性能及热塑性塑料易加工特性,被大量地应用在各种产品外表面装饰材料使用,但是,它也存在一些不可忽视的缺点:成品表面粗糙度较高,产品边缘锯齿感较强,导致其作为表面材料使用时表面不够细腻,限制了其使用范围,因此,研发一种具有高细腻度的TPV材料,来拓展其应用范围,同时对TPV材料的发展是十分有必要的。
发明内容
本发明的目的就是针对目前TPV材料在用于外表面装饰材料使用时,由于其表面较粗糙,限制了其应用范围的问题,提供一种高细腻度TPV材料。
本发明的一种高细腻度TPV材料,由下述重量份原料组成:
PP 20-30 EPDM 20-30
EVA 2-5 EMBS 2-5
碳酸钙 5-10 硫化剂 2-5
助硫化剂 2-4 氧化锌 1-4
抗氧剂 1-5 硫酸钡 1-10
紫外线吸收剂 2-5 润滑剂 2-5
分散剂 1-4 色母粒 1-5;
制备时,将EPDM、PP、EVA、EMBS、硫化剂、助硫化剂、碳酸钙、硫酸钡加入混炼机内混炼15-20分钟,混炼完成后加入双螺杆挤出机内在温度为210-230℃条件下动态硫化1-3分钟,然后加入剩余原料混合后在温度为210-230℃下混合1-3分钟,切粒、干燥,包装,即得。
本发明的一种高细腻度TPV材料,其优选配方由下述重量份原料组成:
PP 25 EPDM 25
EVA 3 EMBS 3
碳酸钙 7 硫化剂 3
助硫化剂 3 氧化锌 2
抗氧剂 3 硫酸钡 5
紫外线吸收剂 3 润滑剂 3
分散剂 2 色母粒 2。
本发明产品在制备时,加入了润滑剂,使其具有光滑、细腻的手感,加入EVA提高其柔软性,加入的其他助剂,使TPV表面获得高细腻度。通过上述改进的共同作用,使本发明产品具有更优良的力学性能、抗冲击性能,且手感更细腻舒适,能够更广泛地应用于各场合产品的表面装饰使用。
具体实施方式
实施例1
本实施例的一种高细腻度TPV材料,由下述重量份原料组成:
PP 25 EPDM 25
EVA 3 EMBS 3
碳酸钙 7 硫化剂 3
助硫化剂 3 氧化锌 2
抗氧剂 3 硫酸钡 5
紫外线吸收剂 3 润滑剂 3
分散剂 2 色母粒 2;
制备时,将EPDM、PP、EVA、EMBS、硫化剂、助硫化剂、碳酸钙、硫酸钡加入混炼机内混炼15-20分钟,混炼完成后加入双螺杆挤出机内在温度为210-230℃条件下动态硫化1-3分钟,然后加入剩余原料混合后在温度为210-230℃下混合1-3分钟,切粒、干燥,包装,即得。
实施例2
本实施例的一种高细腻度TPV材料,由下述重量份原料组成:
PP 20 EPDM 30
EVA 2 EMBS 5
碳酸钙 5 硫化剂 5
助硫化剂 2 氧化锌 4
抗氧剂 1 硫酸钡 10
紫外线吸收剂 2 润滑剂 5
分散剂 1 色母粒 5。
实施例3
本实施例的一种高细腻度TPV材料,由下述重量份原料组成:
PP 30 EPDM 20
EVA 5 EMBS 2
碳酸钙 10 硫化剂 2
助硫化剂 4 氧化锌 1
抗氧剂 5 硫酸钡 1
紫外线吸收剂 5 润滑剂 2
分散剂 4 色母粒 1。
Claims (2)
1.一种高细腻度TPV材料,其特征在于由下述重量份原料组成:
PP 20-30 EPDM 20-30
EVA 2-5 EMBS 2-5
碳酸钙 5-10 硫化剂 2-5
助硫化剂 2-4 氧化锌 1-4
抗氧剂 1-5 硫酸钡 1-10
紫外线吸收剂 2-5 润滑剂 2-5
分散剂 1-4 色母粒 1-5;
制备时,将EPDM、PP、EVA、EMBS、硫化剂、助硫化剂、碳酸钙、硫酸钡加入混炼机内混炼15-20分钟,混炼完成后加入双螺杆挤出机内在温度为210-230℃条件下动态硫化1-3分钟,然后加入剩余原料混合后在温度为210-230℃下混合1-3分钟,切粒、干燥,包装,即得。
2.根据权利要求1所述的一种高细腻度TPV材料,其特征在于由下述重量份原料组成:
PP 25 EPDM 25
EVA 3 EMBS 3
碳酸钙 7 硫化剂 3
助硫化剂 3 氧化锌 2
抗氧剂 3 硫酸钡 5
紫外线吸收剂 3 润滑剂 3
分散剂 2 色母粒 2。