CN110628375A - Caulking agent for prefabricated part building decoration - Google Patents
Caulking agent for prefabricated part building decoration Download PDFInfo
- Publication number
- CN110628375A CN110628375A CN201910951662.XA CN201910951662A CN110628375A CN 110628375 A CN110628375 A CN 110628375A CN 201910951662 A CN201910951662 A CN 201910951662A CN 110628375 A CN110628375 A CN 110628375A
- Authority
- CN
- China
- Prior art keywords
- agent
- weighed
- prefabricated part
- building decoration
- caulking agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a caulking agent for prefabricated part building decoration, which comprises the following raw materials in parts by weight: 35-40% of polyurethane elastic glue, 10-15% of asparagus polyurea resin, 20-26% of epoxy resin, 15-20% of hydroxymethyl cellulose, 0.5-1.5% of pigment, 0.5-1.5% of matting powder, 1-3% of sand, 2-4% of silicate cement, 1-3% of polyurethane leveling agent and 0.1-0.3% of defoaming agent. Compared with the traditional caulking agents used in the current market, the caulking agent for prefabricated part building decoration has the advantages that the bonding strength of the caulking agent is greatly higher than that of concrete, the bonding strength of the caulking agent is guaranteed, cracks are not generated in an embedded channel, pigments are added, the colors of the pigments are different, the caulking agent for prefabricated part building decoration with different colors is manufactured, a better integral effect is brought to a wall surface, and the decoration performance is greatly higher than that of the traditional white cement and color caulking agents.
Description
Technical Field
The invention relates to the technical field of caulking agents, in particular to a caulking agent for prefabricated part building decoration.
Background
The jointing agent is a kind of gray powder prepared from high molecular material and base material, and is mainly used for the jointing of glazed tile, marble, granite and other stone materials.
The caulking agent used in the current market is monotonous in color, mostly grey or white, poor in decoration, poor in cohesive force, easy to open in a bonding part, and capable of causing permeability resistance, water resistance, temperature resistance and aging resistance, and cracks are easy to occur in a clamping path, so that the requirements of users cannot be met.
Disclosure of Invention
The invention aims to solve the defects in the prior art, and provides a caulking agent for prefabricated part building decoration and a preparation method thereof.
In order to achieve the purpose, the invention adopts the following technical scheme: a caulking agent for prefabricated part building decoration comprises the following raw materials by weight: 35-40% of polyurethane elastic glue, 10-15% of asparagus polyurea resin, 20-26% of epoxy resin, 15-20% of hydroxymethyl cellulose, 0.5-1.5% of pigment, 0.5-1.5% of matting powder, 1-3% of sand, 2-4% of silicate cement, 1-3% of polyurethane leveling agent and 0.1-0.3% of defoaming agent.
As a further description of the above technical solution:
the caulking agent for prefabricated part building decoration comprises the following raw materials in parts by weight: 36-39% of polyurethane elastic glue, 11-14% of asparagus polyurea resin, 21-22% of epoxy resin, 16-19% of hydroxymethyl cellulose, 0.6-1.4% of pigment, 0.6-1.4% of matting powder, 1.5-2.5% of sand, 2.5-3.5% of Portland cement, 1.5-2.5% of polyurethane leveling agent and 0.15-0.25% of defoaming agent.
As a further description of the above technical solution:
the caulking agent for prefabricated part building decoration comprises the following raw materials in parts by weight: 36% of polyurethane elastic glue, 11% of asparagus polyurea resin, 21% of epoxy resin, 16% of hydroxymethyl cellulose, 0.6% of pigment, 0.6% of matting powder, 1.5% of sand, 2.5% of Portland cement, 1.5% of polyurethane leveling agent and 0.15% of defoaming agent.
As a further description of the above technical solution:
the hydroxymethyl cellulose belongs to anionic cellulose ether, is white or yellowish flocculent fiber powder or white powder in appearance, is odorless, tasteless and nontoxic, is easily dissolved in cold water or hot water, is prepared by treating cellulose with sodium hydroxide to form alkali cellulose and then reacting with monochloroacetic acid, and has the viscosity of 20 ten thousand.
As a further description of the above technical solution:
the fineness modulus of the sand is 1.5-2.0.
As a further description of the above technical solution:
the defoaming agent is one or a mixture of more of emulsified silicone oil, a high-alcohol fatty acid ester compound, polyoxyethylene polyoxypropylene pentaerythritol ether, polyoxyethylene polyoxypropylene amine ether, polyoxypropylene glycerol ether, polyoxypropylene polyoxyethylene glycerol ether and polydimethylsiloxane.
A preparation method of a caulking agent for prefabricated part building decoration comprises the following specific steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
As a further description of the above technical solution:
and (3) stirring structures are arranged in the stirring tank in the step (2) and the stirring barrel in the step (3).
Advantageous effects
The invention provides a caulking agent for prefabricated part building decoration and a preparation method thereof. The method has the following beneficial effects:
the caulking agent for prefabricated part building decoration is compared with a traditional caulking agent used in the current market, the bonding strength of the caulking agent is greatly higher than that of concrete, the bonding strength of a device is guaranteed, no crack is generated in an embedded channel, pigments are added, the colors of the pigments can be added to be different, the caulking agent for prefabricated part building decoration with different colors is prepared, a better overall effect is brought to a wall surface, the decoration performance is greatly higher than that of traditional white cement and color caulking agents, the caulking agent is glossy, the color is rich, natural and fine, and the caulking agent has good impermeability, water resistance, temperature resistance and aging resistance, and the service life of the caulking agent is prolonged.
Detailed Description
The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments.
Example 1:
a caulking agent for prefabricated part building decoration comprises the following raw materials by weight: 35% of polyurethane elastic glue, 10% of asparagus polyurea resin, 20% of epoxy resin, 15% of hydroxymethyl cellulose, 0.5% of pigment, 0.5% of matting powder, 1% of sand, 2% of portland cement, 1% of polyurethane leveling agent and 0.1% of defoaming agent.
A preparation method of a caulking agent for prefabricated part building decoration comprises the following specific steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
Example 2:
a caulking agent for prefabricated part building decoration comprises the following raw materials by weight: 36% of polyurethane elastic glue, 11% of asparagus polyurea resin, 21% of epoxy resin, 16% of hydroxymethyl cellulose, 0.6% of pigment, 0.6% of matting powder, 1.2% of sand, 2.2% of Portland cement, 1.2% of polyurethane leveling agent and 0.15% of defoaming agent.
A preparation method of a caulking agent for prefabricated part building decoration comprises the following specific steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
Example 3:
a caulking agent for prefabricated part building decoration comprises the following raw materials by weight: 37% of polyurethane elastic glue, 12% of asparagus polyurea resin, 22% of epoxy resin, 17% of hydroxymethyl cellulose, 0.7% of pigment, 0.7% of matting powder, 1.4% of sand, 2.4% of Portland cement, 1.5% of polyurethane leveling agent and 0.2% of defoaming agent.
A preparation method of a caulking agent for prefabricated part building decoration comprises the following specific steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
Example 4:
a caulking agent for prefabricated part building decoration comprises the following raw materials by weight: 38% of polyurethane elastic glue, 13% of asparagus polyurea resin, 23% of epoxy resin, 18% of hydroxymethyl cellulose, 0.8% of pigment, 0.8% of matting powder, 1.5% of sand, 2.6% of Portland cement, 1.6% of polyurethane leveling agent and 0.25% of defoaming agent.
A preparation method of a caulking agent for prefabricated part building decoration comprises the following specific steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
Example 5:
a caulking agent for prefabricated part building decoration comprises the following raw materials by weight: 40% of polyurethane elastic glue, 15% of asparagus polyurea resin, 26% of epoxy resin, 20% of hydroxymethyl cellulose, 1.5% of pigment, 1.5% of matting powder, 3% of sand, 4% of Portland cement, 3% of polyurethane flatting agent and 0.3% of defoaming agent.
A preparation method of a caulking agent for prefabricated part building decoration comprises the following specific steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
Hydroxymethyl cellulose belongs to anionic cellulose ether, is white or yellowish flocculent fiber powder or white powder in appearance, is odorless, tasteless and nontoxic, is easily dissolved in cold water or hot water, is prepared by treating cellulose with sodium hydroxide to form alkali cellulose, and then reacting with monochloroacetic acid, and has a viscosity of 20 ten thousand.
The sand fineness modulus is 1.5-2.0, and the defoaming agent is one or more of emulsified silicone oil, high alcohol fatty acid ester compound, polyoxyethylene polyoxypropylene pentaerythritol ether, polyoxyethylene polyoxypropylene amine ether, polyoxypropylene glycerol ether, polyoxypropylene polyoxyethylene glycerol ether and polydimethylsiloxane.
And (3) stirring structures are arranged in the stirring tank in the step (2) and the stirring barrel in the step (3).
The invention uses the materials of different components such as extinction powder, defoaming agent, polyurethane flatting agent and the like to finish the application performance of the caulking agent, the invention is used for the caulking agent for prefabricated part building decoration, compared with the traditional caulking agent used in the current market, the bonding strength of the caulking agent is greatly higher than the bonding strength of concrete, the bonding strength of the caulking agent is ensured, no crack is generated in the embedded channel, the color of the pigment is more different, the caulking agent for prefabricated part building decoration with different colors is prepared, and a better integral effect is brought to the wall surface, so the decoration is greatly stronger than the traditional white cement and color caulking agents, the color is rich, natural and fine, and has good anti-permeability, water-resistant, temperature-resistant and aging-resistant performances, and the service life of the paint is prolonged.
In the description herein, references to the description of "one embodiment," "an example," "a specific example," etc., mean that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the invention. In this specification, the schematic representations of the terms used above do not necessarily refer to the same embodiment or example. Rather, the particular features, structures, materials, or characteristics described may be combined in any suitable manner in any one or more embodiments or examples.
The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and equivalent alternatives or modifications according to the technical solution and the inventive concept of the present invention should be covered by the scope of the present invention.
Claims (8)
1. A caulking agent for prefabricated part building decoration is characterized by comprising the following raw materials in parts by weight: 35-40% of polyurethane elastic glue, 10-15% of asparagus polyurea resin, 20-26% of epoxy resin, 15-20% of hydroxymethyl cellulose, 0.5-1.5% of pigment, 0.5-1.5% of matting powder, 1-3% of sand, 2-4% of silicate cement, 1-3% of polyurethane leveling agent and 0.1-0.3% of defoaming agent.
2. The caulking agent for prefabricated part building decoration according to claim 1, which is characterized by comprising the following raw materials in parts by weight: 36-39% of polyurethane elastic glue, 11-14% of asparagus polyurea resin, 21-22% of epoxy resin, 16-19% of hydroxymethyl cellulose, 0.6-1.4% of pigment, 0.6-1.4% of matting powder, 1.5-2.5% of sand, 2.5-3.5% of Portland cement, 1.5-2.5% of polyurethane leveling agent and 0.15-0.25% of defoaming agent.
3. The caulking agent for prefabricated part building decoration according to claim 1, which is characterized by comprising the following raw materials in parts by weight: 36% of polyurethane elastic glue, 11% of asparagus polyurea resin, 21% of epoxy resin, 16% of hydroxymethyl cellulose, 0.6% of pigment, 0.6% of matting powder, 1.5% of sand, 2.5% of Portland cement, 1.5% of polyurethane leveling agent and 0.15% of defoaming agent.
4. The caulking agent for prefabricated parts for building decoration according to claims 1 to 3, wherein the hydroxymethyl cellulose belongs to anionic cellulose ethers, has an appearance of white or yellowish flocculent fiber powder or white powder, is odorless, tasteless, nontoxic and easily soluble in cold water or hot water, is prepared by treating cellulose with sodium hydroxide to form alkali cellulose, and reacting with monochloroacetic acid to obtain the caulking agent with a viscosity of 20 ten thousand.
5. A caulking agent for prefabricated part building finishing according to claims 1 to 3, wherein the fineness modulus is 1.5 to 2.0.
6. The caulking agent for prefabricated part building decoration according to claims 1 to 3, wherein the defoaming agent is one or a mixture of several of silicone emulsion, higher alcohol fatty acid ester compound, polyoxyethylene polyoxypropylene pentaerythritol ether, polyoxyethylene polyoxypropylene amine ether, polyoxypropylene glycerol ether, polyoxypropylene polyoxyethylene glycerol ether and polydimethylsiloxane.
7. The method for preparing a caulking agent for prefabricated part building decoration according to any one of claims 1 to 3, comprising the following steps:
(1): weighing the raw materials in parts by weight;
(2): putting the weighed polyurethane elastic glue, the weighed asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose into a stirring tank, opening a stirrer, and stirring and mixing until the polyurethane elastic glue, the asparagus polyurea resin, the weighed epoxy resin and the weighed hydroxymethyl cellulose are uniformly stirred and dispersed;
(3): adding the weighed pigment, flatting powder, sand and portland cement into a stirring barrel, opening a stirrer, and uniformly stirring and mixing;
(4): and (3) adding the mixed product obtained in the step (3) into the stirring tank obtained in the step (2), and stirring and dispersing uniformly again to obtain a finished product.
8. The method for preparing a caulking agent for prefabricated part building decoration according to claim 7, wherein stirring structures are arranged in the stirring tank in the step (2) and the stirring barrel in the step (3).