CN110527757A - A kind of color inhibition type perovskite oxide modified castor fat liquor and preparation method thereof - Google Patents
A kind of color inhibition type perovskite oxide modified castor fat liquor and preparation method thereof Download PDFInfo
- Publication number
- CN110527757A CN110527757A CN201910902171.6A CN201910902171A CN110527757A CN 110527757 A CN110527757 A CN 110527757A CN 201910902171 A CN201910902171 A CN 201910902171A CN 110527757 A CN110527757 A CN 110527757A
- Authority
- CN
- China
- Prior art keywords
- parts
- perovskite oxide
- added
- castor oil
- color inhibition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of color inhibition type perovskite oxide modified castor fat liquor and preparation method thereof, the environment-friendly type color inhibition lotion of preparation can effectively promote the anti-yellowing property of crust leather, and can enhance the binding ability and clean absorption rate of lotion after use.The present invention uses following raw material to be made: in terms of dry mass part, 43.3 parts -44.1 parts of castor oil;Nanometer zirconium-aluminium codope perovskite oxide Zr0.05Al0.1Ca0.85TiO31.7 parts -2.5 parts;14 parts -14.8 parts of maleic anhydride;The sodium metabisulfite solution that 14.9 parts -26.7 parts of pH is 8;Appropriate ammonium hydroxide;26.1 parts -26.9 parts of deionized water.
Description
Technical field
The present invention relates to a kind of modified castor oil based emulsions and preparation method thereof, and in particular to a kind of color inhibition type perovskite
Oxide modifying castor oil lotion and preparation method thereof.
Background technique
Lotion can assign the certain physical mechanical property of leather, plentiful soft feel, be widely used in leather processing and produced
Cheng Zhong.Currently, the common lotion oil base body of leather has mineral oil, vegetable and animals oils, mineral oil belongs to non-renewable resources, animal oil
It is difficult to be widely used because of its unhappy smell and it typically is solid-state due to, and vegetable oil has under from a wealth of sources, cheap, room temperature and is in
The advantages that liquid the first choice as lotion oil base body.
Castor-oil plant is one of the ten big oil crops that the current whole world is found, is a kind of higher plant of fat content.China
It is castor oil Fu Chan state, yield is located at third place in the world, and the main place of production concentrates on the ground such as Xinjiang, northeast.Castor oil belongs to non-food
With oil, it is uniquely to contain hydroxyl, renewable, biodegradable, cheap vegetable oil.Succinate sulfonated castor oil
The advantages that cheap environmentally friendly, from a wealth of sources with it, can be applied in leather processing technique, and can get good economic benefit.
And in practical applications, especially light leather is in use often due to the unsaturated bond in lotion is oxidized
Leather xanthochromia occurs, greatly limits the service life of light color leather.Therefore, in leather often with adding UV absorbing material in lotion
It is one of the key technology for improving leather color inhibition.
Perovskite type metal oxide chemical expression can be used to ABO3Expression, crystal structure are the compound gold of cubic system
Belong to oxide and can be used as excellent UV absorbing material with preferable structural stability and uv absorption property.This is received
Rice corpuscles is introduced into lotion, can be obviously improved the anti-yellowing property of crust leather after stuffing.Meanwhile the zirconium with flexibility, aluminium being doped into
Enter Ca-Ti ore type CaTiO3When middle, it often will appear cation vacancy, this will make active group on nanoparticle and collagen
And anionic emulsion is had an effect, make grease in conjunction with leather more closely, to increase the clean absorption rate cost of implementation of lotion
It reduces.
It is rarely reported at present about using the research of nanosized perovskite-type oxide modified castor fat liquor.
Summary of the invention
It is an object of the invention to overcome the shortcoming in above-mentioned background technique, a kind of nanometer calcium of color inhibition is provided
The preparation method of titanium ore oxide modifying castor oil lotion, the environment-friendly type color inhibition lotion of preparation, can effectively be promoted after use
The anti-yellowing property of crust leather, and the binding ability and clean absorption rate of lotion can be enhanced.
The technical scheme adopted by the invention is as follows:
A kind of color inhibition type perovskite oxide modified castor fat liquor, it is characterised in that be made of following raw material:
In terms of dry mass part, 43.3 parts -44.1 parts of castor oil;Nanometer zirconium-aluminium codope perovskite oxide
Zr0.05Al0.1Ca0.85TiO31.7 parts -2.5 parts;14 parts -14.8 parts of maleic anhydride;14.9 parts -26.7 parts of pH is 8
Sodium metabisulfite solution;Appropriate ammonium hydroxide;26.1 parts -26.9 parts of deionized water.
A kind of preparation method of color inhibition type perovskite oxide modified castor fat liquor, it is characterised in that by following steps
It realizes:
In terms of dry mass part, 43.3 parts -44.1 parts of castor oil and 1.7 parts -2.5 parts of nanometer zirconium-aluminium codope perovskite are taken
Oxide Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 65-80 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope
Perovskite oxide is scattered in castor oil;14 parts -14.8 parts of maleic anhydride is added, is warming up to 90-100 DEG C, reacts 3-
4.5 hour;65 DEG C are cooled to, the sodium metabisulfite solution that the pH for being added 14.9 parts -26.7 parts is 8 reacts 1 hour;Use ammonium hydroxide
Adjusting pH is 8, is reacted 2.5 hours;26.1 parts -26.9 parts of deionized water is added to adjust product solid content.
Compared with prior art, the present invention has the advantage that as follows with effect:
1, raw material sources are extensive, environmentally protective, cheap and easy to get, simple process;
2, crust leather anti-yellowing property is obviously improved after the lotion stuffing;
3, since nanoparticle can greatly enhance the binding ability and clean absorption rate of lotion, in reality in conjunction with grease and collagen
Lotion dosage, save the cost are reduced in production.
Specific embodiment
The present invention will be described in detail With reference to embodiment.
The present invention relates to a kind of color inhibition type perovskite oxide modified castor fat liquor and preparation method thereof, the present invention is first
Zirconium-aluminium codope perofskite type oxide is prepared using sol-gal process, and is introduced into the sulfonated castor-oil plant of succinate
In oil base body, a kind of nano-perovskite oxide modifying castor oil lotion of color inhibition is finally prepared.Zirconium-aluminium codope perovskite
Type oxide has excellent ultraviolet absorption ability, can assign leather higher anti-yellowing property.Additionally due to the oxide has
There is a flexibility, and aobvious cation vacancy, it can be with collagen and anionic emulsion in combination with considerably increasing the exhaustion of the lotion
Rate.The lotion is used for leather greasing process, and leather sample feel is smooth, soft, and fullness is good, and anti-yellowing property is promoted obvious.
The present invention is made of following raw material:
In terms of dry mass part, 43.3 parts -44.1 parts of castor oil;Nanometer zirconium-aluminium codope perovskite oxide
Zr0.05Al0.1Ca0.85TiO31.7 parts -2.5 parts;14 parts -14.8 parts of maleic anhydride;14.9 parts -26.7 parts of pH is 8
Sodium metabisulfite solution;Appropriate ammonium hydroxide;26.1 parts -26.9 parts of deionized water.
The present invention is realized by following steps:
In terms of dry mass part, 43.3 parts -44.1 parts of castor oil and 1.7 parts -2.5 parts of nanometer zirconium-aluminium codope perovskite are taken
Oxide Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 65-80 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope
Perovskite oxide is scattered in castor oil;14 parts -14.8 parts of maleic anhydride is added, is warming up to 90-100 DEG C, reacts 3-
4.5 hour;65 DEG C are cooled to, the sodium metabisulfite solution that the pH for being added 14.9 parts -26.7 parts is 8 reacts 1 hour;Use ammonium hydroxide
Adjusting pH is 8, is reacted 2.5 hours;26.1 parts -26.9 parts of deionized water is added to adjust product solid content.
Embodiment 1:
In terms of dry mass part, 43.3 parts of castor oil and 1.7 parts of nanometer zirconium-aluminium codope perovskite oxide are taken
Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 65 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope perovskite oxygen
Compound is scattered in castor oil;14 parts of maleic anhydride is added, is warming up to 90 DEG C, reacts 3 hours;65 DEG C are cooled to, is added
The sodium metabisulfite solution that 14.9 parts of pH is 8 reacts 1 hour;Adjusting pH with ammonium hydroxide is 8, is reacted 2.5 hours;It is added 26.1
The deionized water of part is to adjust product solid content.
Embodiment 2:
In terms of dry mass part, 43.5 parts of castor oil and 1.9 parts of nanometer zirconium-aluminium codope perovskite oxide are taken
Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 70 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope perovskite oxygen
Compound is scattered in castor oil;14.2 parts of maleic anhydride is added, is warming up to 90 DEG C, reacts 3 hours;65 DEG C are cooled to, is added
The sodium metabisulfite solution that the pH for entering 15.1 parts is 8, reacts 1 hour;Adjusting pH with ammonium hydroxide is 8, is reacted 2.5 hours;It is added
26.3 parts of deionized water is to adjust product solid content.
Embodiment 3:
In terms of dry mass part, 43.7 parts of castor oil and 2.1 parts of nanometer zirconium-aluminium codope perovskite oxide are taken
Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 70 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope perovskite oxygen
Compound is scattered in castor oil;14.4 parts of maleic anhydride is added, is warming up to 95 DEG C, reacts 3.5 hours;65 DEG C are cooled to,
The sodium metabisulfite solution that the pH for being added 15.3 parts is 8, reacts 1 hour;Adjusting pH with ammonium hydroxide is 8, is reacted 2.5 hours;It is added
26.5 parts of deionized water is to adjust product solid content.
Embodiment 4:
In terms of dry mass part, 43.9 parts of castor oil and 2.3 parts of nanometer zirconium-aluminium codope perovskite oxide are taken
Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 75 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope perovskite oxygen
Compound is scattered in castor oil;14.6 parts of maleic anhydride is added, is warming up to 95 DEG C, reacts 4 hours;65 DEG C are cooled to, is added
The sodium metabisulfite solution that the pH for entering 15.5 parts is 8, reacts 1 hour;Adjusting pH with ammonium hydroxide is 8, is reacted 2.5 hours;It is added
26.7 parts of deionized water is to adjust product solid content.
Embodiment 5:
In terms of dry mass part, 44.1 parts of castor oil and 2.5 parts of nanometer zirconium-aluminium codope perovskite oxide are taken
Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 80 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope perovskite oxygen
Compound is scattered in castor oil;14.8 parts of maleic anhydride is added, is warming up to 100 DEG C, reacts 4.5 hours;65 DEG C are cooled to,
The sodium metabisulfite solution that the pH for being added 15.7 parts is 8, reacts 1 hour;Adjusting pH with ammonium hydroxide is 8, is reacted 2.5 hours;It is added
26.9 parts of deionized water is to adjust product solid content.
The contents of the present invention are not limited to cited by embodiment, and those of ordinary skill in the art are by reading description of the invention
And to any equivalent transformation that technical solution of the present invention is taken, all are covered by the claims of the invention.
Claims (2)
1. a kind of color inhibition type perovskite oxide modified castor fat liquor, it is characterised in that be made of following raw material:
In terms of dry mass part, 43.3 parts -44.1 parts of castor oil;Nanometer zirconium-aluminium codope perovskite oxide
Zr0.05Al0.1Ca0.85TiO31.7 parts -2.5 parts;14 parts -14.8 parts of maleic anhydride;14.9 parts -26.7 parts of pH is 8
Sodium metabisulfite solution;Appropriate ammonium hydroxide;26.1 parts -26.9 parts of deionized water.
2. a kind of preparation method of color inhibition type perovskite oxide modified castor fat liquor, it is characterised in that by following steps reality
It is existing:
In terms of dry mass part, 43.3 parts -44.1 parts of castor oil and 1.7 parts -2.5 parts of nanometer zirconium-aluminium codope perovskite are taken
Oxide Zr0.05Al0.1Ca0.85TiO3, three-necked flask is added, being warming up to 65-80 DEG C of 25 min of stirring makes a nanometer zirconium-aluminium codope
Perovskite oxide is scattered in castor oil;14 parts -14.8 parts of maleic anhydride is added, is warming up to 90-100 DEG C, reacts 3-
4.5 hour;65 DEG C are cooled to, the sodium metabisulfite solution that the pH for being added 14.9 parts -26.7 parts is 8 reacts 1 hour;Use ammonium hydroxide
Adjusting pH is 8, is reacted 2.5 hours;26.1 parts -26.9 parts of deionized water is added to adjust product solid content.