CN110527400A - A kind of aqueous weathering resistance coatings - Google Patents
A kind of aqueous weathering resistance coatings Download PDFInfo
- Publication number
- CN110527400A CN110527400A CN201910836713.4A CN201910836713A CN110527400A CN 110527400 A CN110527400 A CN 110527400A CN 201910836713 A CN201910836713 A CN 201910836713A CN 110527400 A CN110527400 A CN 110527400A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- weathering resistance
- resistance coatings
- aeroge
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of aqueous weathering resistance coatings, according to mass ratio, comprising: component A: usual resins 30%~50%, inorganic modified filler 10%~20%, modified silicasol 10%~20%, Modification on Al2O3Aeroge 3%~10%, ultraviolet absorber 1%~2%, other auxiliary agents 1.5%~3%;B component: polysiloxane copolymer: additive amount is the 5%~15% of component A total amount.Curing agent: additive amount is the 20%~50% of resin system.Inventive formulation system can be conducive to improve the weatherability of coating.
Description
Technical field
The present invention relates to a kind of aqueous weathering resistance coatings.
Background technique
Organic coating is influenced vulnerable to outside environmental elements, and coating is (ultraviolet, high temperature, wet oxygen etc.) easy to aging, and it is de- coating occur
A series of problems, such as falling, is eclipsed, turning to be yellow mostly uses addition aging auxiliary agent on formula at present, reduces function of easily turning to be yellow in formula
Group, or the weatherability that the methods of surface-crosslinked degree improves coating is improved using UV curing process, promote coating life.Wherein:
Scheme one: using composite assistants such as ultraviolet absorber, antioxidant, light stabilizers;But this method is on the one hand to old
It is limited to change performance improvement, especially surface layer is protected limited;On the other hand need to add a variety of anti-aging auxiliary agents, increased costs are bright
It is aobvious;
Scheme two: fluorocarbon coating;For example, 201810687354.6 disclose a kind of high rigidity aqueous fluorine-carbon paint: using poly-
Tetrafluoroethene prepares high rigidity, high-weatherability F-C paint, but this method have the disadvantage in that 1, not environmentally, dangerous, toxic cause
Cancer;2, poor adhesive force;3, at high cost;
The solidification of scheme three: UV+anti-aging auxiliary agent;For example, 201310506797.8 to disclose a kind of color inhibition UV woodenware clear
Paint: the excellent weatherability varnish coat of color inhibition is prepared using UV curing process, but this method has the disadvantage in that 1, technique is wanted
Ask high, at high cost, UV solidification can accelerated ageing;2, UV solidification can only make clear varnish, and difficulty does finishing coat/colored paint;
It is therefore desirable to have new weathering resistance coatings occur.
CN201410536151.9 discloses a kind of nanometer of thermostable heat-isolating coating, and thermal insulating filling selects SiO2 airsetting
Glue, modified crystal whisker of hexa potassium titanate, alumina silicate fibre, hollow tiny pearl, nano TiO 2, Al2O3, make filled insulation, utilize
SiO2 aeroge, cenosphere nanoporous structure constitute vacuum heat-insulating layer, done using alumina silicate fibre enhance, toughening material
Material, does the shielded layer of radiant heat using the infrared shading performance of crystal whisker of hexa potassium titanate, nano TiO 2, Al2O3, with resin emulsion
It is adhesive with acrylic emulsion compounding, resistance to 600 DEG C of nano heat-insulating thermal insulation coatings is prepared under the cooperation of multiple functions auxiliary agent.
The property such as the deficiency of the invention is, which only can be realized certain heat-insulating capability, cannot achieve weather-proof, color inhibition
Energy.
Summary of the invention
The present invention provides a kind of aqueous weathering resistance coatings, which overcome present in weathering resistance coatings aqueous in background technique not
Foot.
The used technical solution that the present invention solves its technical problem is:
A kind of aqueous weathering resistance coatings, according to mass ratio, comprising:
Component A:
Usual resins 30%~50%, inorganic filler 10%~20%, modified silicasol 10%~20%,
Modification on Al2O3Aeroge 3%~10%, ultraviolet absorber 1%~2%,
Other auxiliary agents 1.5%~3%;
B component:
Polysiloxane copolymer: additive amount is the 5%~15% of component A total amount
Curing agent: additive amount is the 20%~50% of usual resins.
In the present invention, usual resins are hydrogenation/phenol aldehyde modified type epoxy resin, acrylic resin, polyurethane resin etc.
One of or two kinds of combination.
In a preferred embodiment of the invention, inorganic filler includes in nano-ceramic powder, calcining grade tripoli, mica powder etc.
One or several kinds of combinations, partial size are 1um~3um;Wherein preferably through organosilane-modified processing, this is organic for inorganic filler
Silane-modified processing is the prior art;Or inorganic modified filler can use commercial product.
In a preferred embodiment of the invention, silica solution is handled by methyltrimethoxysilane hydrophobically modified, silica solution
Partial size 10um~30um.
In a preferred embodiment of the invention, modified aerogels include in titania aerogel and aerosil
One or two kinds of combination, hole be 10nm~40nm, the porosity >=80%.
In a preferred embodiment of the invention, aeroge passes through following processing:
1) aluminum nitrate solution immersion treatment: 0.5-2mol.L is used-111%Al (NO3)3Solution impregnates aerogel powder
Handle 50-100h;
2) successively prepared by immersion treatment 12-36h, the drying 12-100h in 40-80 DEG C of insulating box for weak aqua ammonia, dehydrated alcohol
Al2O3- aeroge;
3) surface hydrophobicity modification;Above-mentioned preparation is sprayed or is immersed in using hydrophobing agents such as silanes, ketone, alcohols
Al2O3Aeroge system, uniform stirring mixing 30-90min, in 80 DEG C of -110 DEG C of progress drying and processings.Wherein, hydrophobing agent is preferred
Trim,ethylchlorosilane;
4) ultraviolet absorber coating modification is used to handle: the ultraviolet suction that aerogel powder is dissolved in concentration for 0.1-1.0%
It receives agent solution and stirs 20-40min, 90-110 DEG C of baking 1-3h;
5) modified aerogel powder is dissolved in acetone, airsetting sol solution is made.
In a preferred embodiment of the invention, ultraviolet absorber selects one or two kinds of any of UV-531/UV-326
Combination.
In a preferred embodiment of the invention, silane-modified polysiloxane copolymer partial size≤1um, hydroxyl or alkyl,
Using silane coupler modified processing, the compatibility with usual resins is improved, reacts to form stable siloxanes with epoxy resin
Key improves the heat resistance and weatherability of coating.
In a preferred embodiment of the invention, curing agent is amine curing agent (polyamide or diamines), anhydride solidifies
One or more of agent, HDI trimer.
In a preferred embodiment of the invention, other auxiliary agents include levelling agent, antistatic agent, at least one in foam inhibitor
Kind.
The present invention also provides a kind of preparation methods of aqueous weathering resistance coatings, include the following steps:
By component A, uniform stirring, mixing speed are 400-800 revs/min according to the proportion, stir 3-10min, then slowly add
Enter modified aeroge and be slowly stirred 3-10min, then dispersion preparation component A is carried out using ultrasonic wave;
After A/B component is proportionally mixed evenly, further dispersed using ultrasonic wave.
Coating carries out ultrasonic disperse to component A using preceding, is conducive to inorganic filler and modified aerogels and uniformly divides in system
Dissipate mixing;Amine/HDI trimer curing agent wherein is used to timber-work, preferentially anhydride is used to solidify metal class product
Agent.
Aeroge (titania aerogel or aerosil) itself is there are micro nano structure, wherein Al2O3Doping
In aeroge, multiple polycondensation reaction can occur with aerogel pores, by the barrier of big abscess at several small cells, increase abscess number
Amount reduces abscess-size, dramatically increases the specific surface area of aeroge, while Al2O3Uniform Doped in aeroge reticular structure,
Aeroge and Al2O3The reticular structure of construction can be obviously improved coating to ultraviolet light/hot spoke after ultraviolet absorber is handled
Screening ability, absorbability and the imparting good isolating power of coating penetrated, principle are as follows:
1. micro-pore wall reflection/scattering:
There are the small hole of a large amount of nanoscales, Al for aeroge itself2O3Aeroge further promotes abscess quantity and Bi Biao
Area, a large amount of hole walls become ultraviolet radiation reflecting surface and scattering surface, can fine shielding ultraviolet rays, reduce it is ultraviolet to coating
Irradiation;
2. effective UV absorption agent covers:
After ultraviolet absorber is handled, surface more uniformly coats ultraviolet absorption material, therefore purple on aeroge surface
The specific surface area of outside line absorbing material further increases, and ultraviolet light is after a large amount of hole walls, gradually by ultraviolet absorber absorption/screen
It covers, reduces influence of the ultraviolet light to coating;
3. surface migration, tridimensional network:
In text message, aeroge density is extremely low, and film forming Shi Yixiang coating surface gradually migrates aggregation, in coating surface shape
At tridimensional network, not only have good ultraviolet absorption ability and ultraviolet shielded ability, also have fabulous heat shielding
Ability, reduces phenomena such as External Heat Flux causes the thermo-oxidative ageing of the excessively high appearance of Coated Surface Temperature, so promoted product because
Jaundice and aging phenomenon caused by high temperature;
4. inorganic filler performance is stablized:
Through overdoping Al2O3After processing, strength of coating after film forming, Al can not only be increased2O3It is steady as inorganic material performance
It is fixed, the reflecting effect (shielding) of coating can be further promoted, influence of the ultraviolet light to coating is reduced, increases the weather-proof of coating
Property.
The technical program compared with the background art, it has the following advantages:
Inventive formulation system can be conducive to improve the weatherability (high temperature resistant, UV resistant lamp) of coating, and guarantee to apply
Layer has excellent adhesive force and shock resistance effect;Wherein modified aerogels, silica solution and nano inorganic filler can be mentioned significantly
Shielding action of the high coating to ultraviolet light and heat radiation inhibits product because aging caused by the environment such as ultraviolet light, high temperature is turned to be yellow;
In addition to this coating has certain hydrophobic ability, can reduce the surface energy of coating, reduces influence of the liquid substance to coating,
The service life for promoting product can assign the function of coating hydrophobic oleophobic simultaneously.
Specific embodiment
Embodiment one:
The preparation of modified aerogels:
Using 1.0mol.L-111%AlNO3Solution uses weak aqua ammonia, nothing to aerosil immersion treatment 72h
Successively for 24 hours, dry 72h, prepares Al to immersion treatment to water-ethanol in 70 DEG C of insulating boxs2O3Aeroge;By the aeroge after drying
Powder handles 60min using silane coupling agent (trim,ethylchlorosilane) hydrophobically modified, promotes the dispersibility of aeroge;Finally using purple
Outer absorbent UV-326 carries out cladding processing to aeroge surface;The cladding processing is using sprinkling, immersion: sprinkling is equal
Even or immersion makes liquid ultraviolet absorber uniformly be attached to aeroge surface;
Modified silicasol: being slowly added to 60 DEG C of reaction 1h of silicon sol solution constant temperature for 10% methyltrimethoxysilane,
2% MethylethoxylsiliconFluid Fluid is added the reaction was continued 1h, hydrophobic colloidal silica is made;
Weathering resistance coatings preparation: by hydrogenated bisphenol A epoxy resin 50%, modified aerogels 3%, inorganic modified filler (nanometer
Ceramic powder) 18%, modified silicasol 15%, ultraviolet absorber (UV-531) 1.5%, other auxiliary agents (levelling agent, antistatic agent,
Defoaming agent each 0.5%, levelling agent use cationic surfactant 1827- using organosilicon levelling agent HY5057, antistatic agent
Stearyl dimethyl benzyl ammonium chloride, defoaming agent are uniformly mixed using silicon class defoaming agent TEGO Antifoam X 206) 1.5%
Merge stirring 5min, the modified aerogels for being then slowly added into 3% are slowly stirred 5min, then carry out dispersion preparation using ultrasonic wave
Component A;BASF- isophorone diamine curing agent (the 40% of usual resins) and polysiloxane copolymer 11% are added to A group
Point, after mixing evenly, evenly dispersed 3min is carried out using ultrasonic wave;Timber/gold of prime treatment is sprayed into using spraying process
Metal surface, after levelling 15min, hot setting 1h carries out Performance Evaluation after 5 days.
Comparative example one:
The preparation of modified aerogels:
Using 1.0mol.L-111%AlNO3Solution uses weak aqua ammonia, nothing to aerosil immersion treatment 72h
Successively for 24 hours, dry 72h, prepares Al to immersion treatment to water-ethanol in 70 DEG C of insulating boxs2O3Aeroge;By the aeroge after drying
Powder is handled using silane coupling agent hydrophobically modified, promotes the dispersibility of aeroge;Finally using ultraviolet absorber UV-326 to gas
Gel surface carries out cladding processing;
Hydrophobic colloidal silica: being slowly added to 60 DEG C of reaction 1h of silicon sol solution constant temperature for 10% methyltrimethoxysilane,
2% MethylethoxylsiliconFluid Fluid is added the reaction was continued 1h, hydrophobic colloidal silica is made;
Weathering resistance coatings preparation: by hydrogenated bisphenol A epoxy resin 53%, inorganic modified filler 18%, modified silicasol 15%,
Ultraviolet absorber 1.5%, other auxiliary agents 1.5% are uniformly mixed and stirred for 5min, then carry out dispersion preparation A group using ultrasonic wave
Point;Anhydride curing agent is added to component A (curing agent: A=1:2.5), then polysiloxane copolymer 11% is added to A group
Point, after mixing evenly, evenly dispersed 3min is carried out using ultrasonic wave;Timber/gold of prime treatment is sprayed into using spraying process
Metal surface, after levelling 15min, hot setting 1h carries out Performance Evaluation after 5 days
Coating template performance indicator obtained by each embodiment and comparative example is as shown in table 1, verifies the coating for convenience
Weatherability, use is heat-resisting, color inhibition test method, and template substrate selects stainless steel plate, and wherein anti-yellowing property is according to GB/
16422.2 are tested, and heat resistance observes cosmetic variation after using 180 DEG C of baking 30min of high temperature.
Table 1: each component ratio in embodiment and comparative example
Component | Comparative example one | Embodiment one | Embodiment two | Embodiment three | Comparative example two |
Epoxy resin | 53 | 50 | 47 | 44 | 41 |
Polysiloxanes | 11 | 11 | 11 | 11 | 11 |
Inorganic filler | 18 | 18 | 18 | 18 | 18 |
Modified silicasol | 15 | 15 | 15 | 15 | 15 |
Modification on Al2O3Aeroge | 0 | 3 | 6 | 9 | 12 |
Ultraviolet absorber | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 |
Other auxiliary agents | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 |
Table 2: the corresponding test performance of each embodiment
Performance | Comparative example one | Embodiment one | Embodiment two | Embodiment three | Comparative example two |
△E | 6.52 | 0.42 | 0.35 | 0.3 | 0.33 |
Heat resistance | Loss of gloss jaundice, cracking | It is unchanged | It is unchanged | It is unchanged | Slight cracking |
CA | 85° | 92° | 96° | 102° | 103° |
△ E is value of chromatism, and value of chromatism is got over large surface color change and is more obvious, and anti-yellowing property, weather resistance are poor;With changing
Property Al2O3The increase of aeroge ratio, Modification on Al2O3Aeroge is obviously improved the absorbability of ultraviolet light, screening ability, together
When can completely cut off heat and further conducted to coat inside and substrate, can effectively avoid leading because of ultraviolet irradiation and temperature raising
Some column aging phenomena such as coating jaundice, cracking are caused, but since aeroge brittleness itself is bigger, excessive addition will lead to anti-open
Split reduced performance.
CA is water contact angle, and the bigger hydrophobicity of water contact angle is better, other liquid such as sewage are less susceptible to hang over plate surface;
Modification on Al2O3After hydrophobically modified is handled, surface can reduce aeroge, and CA increases, and hydrophobicity improves, and liquid can be made in receipts
Contracting state is slid by plate surface, is effectively avoided liquid pollutant or corrosive liquid from dividing in plate surface, is improved coating life
And ageing resistance.
The above is only the preferred embodiment of the present invention, the range implemented of the present invention that therefore, it cannot be limited according to, i.e., according to
Equivalent changes and modifications made by the invention patent range and description, should still be within the scope of the present invention.
Claims (11)
1. a kind of aqueous weathering resistance coatings, according to mass ratio, comprising:
Component A:
Usual resins 30%~50%, inorganic filler 10%~20%,
Modified silicasol 10%~20%, Modification on Al2O3Aeroge 3%~10%,
Ultraviolet absorber 1%~2%, other auxiliary agents 1.5%~3%;
B component:
Polysiloxane copolymer: additive amount is the 5%~15% of component A total amount
Curing agent: additive amount is the 20%~50% of usual resins.
2. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: usual resins be hydrogenation/it is phenol aldehyde modified
One of type epoxy resin, acrylic resin or polyurethane resin or two kinds of combination.
3. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: inorganic filler include nano-ceramic powder,
One of grade tripoli, mica powder or several combinations are calcined, partial size is 1um~3um.
4. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: silica solution passes through methyl trimethoxy oxygroup silicon
The processing of alkane hydrophobically modified, silica solution partial size 10um~30um.
5. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: modified aerogels include titanium dioxide gas
One of gel and aerosil or two kinds of combination, hole are 10nm~40nm, the porosity >=80%.
6. a kind of aqueous weathering resistance coatings according to claim 5, it is characterised in that: the modification of aeroge includes:
1) aluminum nitrate solution immersion treatment: 0.5-2mol.L is used-111%Al (NO3)3Solution impregnates aerogel powder processing
50-100h;
2) successively prepared by immersion treatment 12-36h, the drying 24-100h in 40-80 DEG C of insulating box respectively for weak aqua ammonia, dehydrated alcohol
Al2O3Aeroge;
3) surface hydrophobicity modification;The Al of above-mentioned preparation is sprayed or is immersed in using hydrophobing agent2O3Aeroge system, is uniformly stirred
Mixing 30-90min is mixed, the hydrophobing agent includes at least one of silanes, ketone, alcohols;In 80 DEG C of -110 DEG C of progress
Drying and processing;
4) ultraviolet absorber coating modification is handled: aerogel powder is dissolved in the ultraviolet absorber solution that concentration is 0.1-1.0%
And 20-40min is stirred, 80-110 DEG C of baking 1-3h;
5) modified aerogel powder is dissolved in acetone, airsetting sol solution is made.
7. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: ultraviolet absorber selects UV-531/UV-
326 one or two kinds of combinations.
8. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: silane-modified polysiloxane copolymer grain
Diameter≤1um.
9. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: curing agent is amine curing agent, acid anhydrides
One or more of class curing agent, HDI trimer.
10. a kind of aqueous weathering resistance coatings according to claim 1, it is characterised in that: other auxiliary agents include levelling agent, resist it is quiet
At least one of electric agent, foam inhibitor.
11. the preparation method of a kind of aqueous weathering resistance coatings according to any of claims 1 to 10, includes the following steps:
By component A, uniform stirring, mixing speed are 400-800 revs/min according to the proportion, stir 3-10min, are then slowly added into and change
Property after aeroge be slowly stirred 3-10min, then dispersion preparation component A is carried out using ultrasonic wave;
After A/B component is proportionally mixed evenly, further dispersed using ultrasonic wave.