CN110508449A - A kind of automatically dropping glue technique of sealing ring - Google Patents
A kind of automatically dropping glue technique of sealing ring Download PDFInfo
- Publication number
- CN110508449A CN110508449A CN201910792375.9A CN201910792375A CN110508449A CN 110508449 A CN110508449 A CN 110508449A CN 201910792375 A CN201910792375 A CN 201910792375A CN 110508449 A CN110508449 A CN 110508449A
- Authority
- CN
- China
- Prior art keywords
- glue
- workpiece
- sealing ring
- dispensing
- automatically dropping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automatically dropping glue techniques of sealing ring, include the following steps;Step 1;Positioning, step 2;Glue selection, step 3;Dispensing needle head selection, step 4;Dispenser Parameter Modulation, step 5;Automatically dropping glue, step 6;Workpiece pressing, step 7;Workpiece finishing, step 8;Workpiece drying, solidification, step 9;Workpiece strength test, the present invention by will sealing ring dispensing pressing after, carry out workpiece finishing, by artificial or equipment automatically to repeatedly being wiped at sealing ring pressing, glue residual is overflowed after avoiding pressing, improve workpiece entirety aesthetics, while avoid overflow glue and other workpiece bonding, influence using.
Description
Technical field
The present invention relates to electronic product adhesive technology field, the automatically dropping glue technique of specially a kind of sealing ring.
Background technique
Electronic product is related to that welding, patch, assembling, gluing, the links such as screw, these rings in process of production
The quantity of coating process is big in section, and fineness is high, therefore need to spend more artificial, and short time consumption is long, is to influence an electronics to produce
The key link of the production efficiency of product;The factors such as the operating condition of worker and rugged environment simultaneously often influence electronics and produce
The quality of product.
There are two types of methods for the gluing of electronic product at present, and one is by manually gluing being gone to complete, another kind is to utilize dispensing
Machine dispensing, two kinds of glue spreading methods have disadvantage;Artificial application rate is slow, and completion rate is low, and spraying effect is uneven, and dispenser applies
Glue is that quantitative gluing is carried out by program, when recycling dispenser gluing, it is contemplated that glue can generate standing because of its resting period
Precipitating, the problem of making the glue of spot printing the more open the more dilute, influence bonding quality, the gel quantity being normally set up all can be higher (after preventing
Glue concentration dilution when phase dispensing, glue degree of adhesion reduce), thus make sealing ring in pressing, phenomena such as there are glue spillings,
It is light then influence beauty, it is serious that sealing ring and other workpiece is caused to bond, product quality is influenced, for this purpose, it is proposed that a kind of close
The automatically dropping glue technique of seal.
Summary of the invention
The purpose of the present invention is to provide a kind of automatically dropping glue techniques of sealing ring, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme: a kind of automatically dropping glue technique of sealing ring, including with
Lower step:
Step 1;Positioning, will need sealing ring for dispensing glue to be placed in the localization tool on dispensing machine table face;
Step 2;Glue selection, the glue of different model is selected according to different sealing loop material matter difference, and will be selected
Glue is placed in the glue bucket of dispenser;
Step 3;Dispensing needle head selection, carries out rotating various sizes of plastic pin according to the sealing ring of different size model numbers
Head;
Step 4;Dispenser Parameter Modulation sets dispensing parameter, puts glue laminated, gel quantity, dispensing temperature and point adhesiveness,
Glue rifle running track programming, to the running route editing procedure of glue rifle;
Step 5;Automatically dropping glue controls dispensing needle head displacement by the parameter of setting, and sprays quantitative glue to close
In seal;
Step 6;Workpiece pressing, presses the sealing ring that dispensing finishes, guarantees its adhesive strength;
Step 7;Workpiece finishing, by artificial or equipment automatically to repeatedly being wiped at sealing ring pressing, avoids pressing
Glue residual is overflowed after conjunction;
Step 8;Workpiece drying, solidification, the workpiece after finishing is placed in drying box, solidifies glue quickly, is increased
Production efficiency;
Step 9;Workpiece strength test, the gumminess of workpiece after detection solidification.
Preferably, heating rod is equipped in the dispenser glue bucket in the step 2, and heating rod temperature temperature is maintained at 22
℃-27℃。
Preferably, the dispensing parameter that dispenser is set in the step 4 are as follows: point glue laminated 0.15MPa-0.25MPa, dispensing go out
Glue amount 0.15g/s-0.32g/s, puts adhesiveness 58000cp by 23 DEG C of dispensing temperature.
Preferably, the route programming of glue rifle includes point movement programming in the step 4, and point movement programming includes data
Input, data processing, bring into operation, calculate umber of pulse needed for X-direction, calculate Y-direction needed for umber of pulse, positioning.
Preferably, workpiece pressing pressure is 0.1Mpa-0.5Mpa, pressing time 25s-50s in the step 6.
Preferably, workpiece finishing uses soft hairbrush to carry out wiping removal to surplus glue is overflowed in the step 7.
Preferably, workpiece is dried, in solidification in the step 8, drying time 8Min-15Min, drying temperature 80
℃-120℃。
Preferably, the tensile strength 3Mpa that workpiece strength is tested in the step 9.
Compared with prior art, the beneficial effects of the present invention are:
1, the present invention is by carrying out workpiece finishing, by artificial or equipment automatically to close for after sealing ring dispensing pressing
It is repeatedly wiped at seal pressing, overflows glue residual after avoiding pressing, improve the aesthetics of workpiece entirety, while avoiding overflowing
Glue out and other workpiece bind, influence using.
2, the present invention by the way that sealing ring is placed in the localization tool on dispenser workbench after, by glue amount size,
Dispensing pressure, dispensing temperature and the control for putting adhesiveness carry out dispensing to the dispensing region of product, can be improved precision for dispensing glue with
And the quality of product.
Detailed description of the invention
Fig. 1 is present invention process flow diagram.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, a kind of automatically dropping glue technique of sealing ring in diagram, comprising the following steps:
Step 1;Positioning, will need sealing ring for dispensing glue to be placed in the localization tool on dispensing machine table face;
Step 2;Glue selection, the glue of different model is selected according to different sealing loop material matter difference, and will be selected
Glue is placed in the glue bucket of dispenser;
Step 3;Dispensing needle head selection, carries out rotating various sizes of plastic pin according to the sealing ring of different size model numbers
Head;
Step 4;Dispenser Parameter Modulation sets dispensing parameter, puts glue laminated, gel quantity, dispensing temperature and point adhesiveness,
Glue rifle running track programming, to the running route editing procedure of glue rifle;
Step 5;Automatically dropping glue controls dispensing needle head displacement by the parameter of setting, and sprays quantitative glue to close
In seal;
Step 6;Workpiece pressing, presses the sealing ring that dispensing finishes, guarantees its adhesive strength;
Step 7;Workpiece finishing, by artificial or equipment automatically to repeatedly being wiped at sealing ring pressing, avoids pressing
Glue residual is overflowed after conjunction;
Step 8;Workpiece drying, solidification, the workpiece after finishing is placed in drying box, solidifies glue quickly, is increased
Production efficiency;
Step 9;Workpiece strength test, the gumminess of workpiece after detection solidification.
Heating rod is equipped in dispenser glue bucket in step 2, and heating rod temperature temperature is maintained at 22 DEG C -27 DEG C.
The dispensing parameter that dispenser is set in step 4 are as follows: point glue laminated 0.15MPa-0.25MPa, dispensing gel quantity 0.15g/
S-0.32g/s, puts adhesiveness 58000cp by 23 DEG C of dispensing temperature.
The route programming of glue rifle includes point movement programming in step 4, and point movement programming includes that data input, at data
Umber of pulse, positioning needed for managing, bring into operation, calculating umber of pulse needed for X-direction, calculate Y-direction.
Workpiece pressing pressure is 0.1Mpa-0.5Mpa, pressing time 25s-50s in step 6.
Workpiece finishing carries out wiping removal to surplus glue is overflowed using soft hairbrush in step 7.
Workpiece is dried, in solidification in step 8, drying time 8Min-15Min, and drying temperature is 80 DEG C -120 DEG C.
The tensile strength 3Mpa that workpiece strength is tested in step 9.
This programme is realized to glue wiping is overflowed by adding workpiece pre-shaping step, avoids two workpiece mutually viscous glutinous, shadow
Product quality is rung, and by testing effective removal workpiece inferior to workpiece strength.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of automatically dropping glue technique of sealing ring, it is characterised in that: the following steps are included:
Step 1;Positioning, will need sealing ring for dispensing glue to be placed in the localization tool on dispensing machine table face;
Step 2;Glue selection, the glue of different model is selected according to different sealing loop material matter difference, and by selected glue
It is placed in the glue bucket of dispenser;
Step 3;Dispensing needle head selection, carries out rotating various sizes of dispensing needle head according to the sealing ring of different size model numbers;
Step 4;Dispenser Parameter Modulation sets dispensing parameter, point glue laminated, gel quantity, dispensing temperature and point adhesiveness, glue rifle
Running track programming, to the running route editing procedure of glue rifle;
Step 5;Automatically dropping glue controls dispensing needle head displacement by the parameter of setting, and sprays quantitative glue to sealing ring
On;
Step 6;Workpiece pressing, presses the sealing ring that dispensing finishes, guarantees its adhesive strength;
Step 7;Workpiece finishing, by artificial or equipment automatically to repeatedly being wiped at sealing ring pressing, after avoiding pressing
Overflow glue residual;
Step 8;Workpiece drying, solidification, the workpiece after finishing is placed in drying box, solidifies glue quickly, increases production
Efficiency;
Step 9;Workpiece strength test, the gumminess of workpiece after detection solidification.
2. a kind of automatically dropping glue technique of sealing ring according to claim 1, it is characterised in that: the point in the step 2
Heating rod is equipped in glue machine glue bucket, and heating rod temperature temperature is maintained at 22 DEG C -27 DEG C.
3. a kind of automatically dropping glue technique of sealing ring according to claim 2, it is characterised in that: dispensing in the step 4
The dispensing parameter of machine setting are as follows: put glue laminated 0.15MPa-0.25MPa, dispensing gel quantity 0.15g/s-0.32g/s, dispensing temperature 23
DEG C, put adhesiveness 58000cp.
4. a kind of automatically dropping glue technique of sealing ring according to claim 3, it is characterised in that: glue rifle in the step 4
Route programming include point movement programming, point movement programming includes data input, data processing, brings into operation, calculates the side X
To umber of pulse, positioning needed for required umber of pulse, calculating Y-direction.
5. a kind of automatically dropping glue technique of sealing ring according to claim 4, it is characterised in that: workpiece in the step 6
Pressing pressure is 0.1Mpa-0.5Mpa, pressing time 25s-50s.
6. a kind of automatically dropping glue technique of sealing ring according to claim 5, it is characterised in that: workpiece in the step 7
Finishing carries out wiping removal to surplus glue is overflowed using soft hairbrush.
7. a kind of automatically dropping glue technique of sealing ring according to claim 6, it is characterised in that: workpiece in the step 8
In drying, solidification, drying time 8Min-15Min, drying temperature is 80 DEG C -120 DEG C.
8. a kind of automatically dropping glue technique of sealing ring according to claim 1, it is characterised in that: workpiece in the step 9
The tensile strength 3Mpa of strength test.