CN110468420A - 一种绿色环保清洗剂及其制备方法 - Google Patents
一种绿色环保清洗剂及其制备方法 Download PDFInfo
- Publication number
- CN110468420A CN110468420A CN201910879521.1A CN201910879521A CN110468420A CN 110468420 A CN110468420 A CN 110468420A CN 201910879521 A CN201910879521 A CN 201910879521A CN 110468420 A CN110468420 A CN 110468420A
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- environmentally protective
- fatty alcohol
- protective cleaning
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了本发明提供的一种绿色环保清洗剂前体，其特征在于，由包含：葡萄糖、磷酸、尿素等原料制备而成；其制备方法为：将葡萄糖和磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至180‑200℃，反应3‑4小时，反应过程中及时抽除酯化反应生成的水分；温度降到135‑140℃时，加入尿素敞口搅拌反应1‑2小时即可。本发明还提供了一种由绿色环保清洗剂前体制备的绿色环保清洗剂，还包括以下材料制备而成：椰油酰基肌氨酸钠；脂肪醇衣康酸酯磺酸盐；脂肪醇聚氧乙烯醚；乙二胺四乙酸钠；柠檬酸钠；消泡剂；去离子水。
Description
技术领域
本发明属于清洗技术领域，涉及一种绿色环保清洗剂及其制备方法。
背景技术
金属件在加工过程中往往要用各种润滑剂进行加工过程中的润滑和冷却，加工后工件要进行清洗后才能进入下道工序进行再加工。
由于法律法规和环保压力，传统的氟氯烃或强碱清洗已逐渐被禁止使用，对能够快速去除油污和其他污染物及表面氧化物的水性清洗剂的研究和应用越来越受到重视，使用对环境更加友好的清洗剂是非常紧迫的事情。
同时使用排放少、可常温清洗、可生物降解等要求成为目前清洗剂的一个研发方向。
发明内容
鉴于以上缺陷，本发明旨在克服现有技术的不足，制备一种绿色环保清洗剂。
为实现上述目的，本发明提供的一种绿色环保清洗剂前体，其特征在于，由包含：葡萄糖、磷酸、尿素等原料制备而成；
上述葡萄糖、磷酸、尿素摩尔比为1:2-3:1-2；最佳摩尔比为1:2.5:1。
本发明还提供一种绿色环保清洗剂前体的制备方法，其特征在于：
步骤一：将葡萄糖和磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至180-200℃，反应3-4小时，反应过程中及时抽除酯化反应生成的水分。及时抽除反应生成的水分有利于酯化反应的充分完成。
步骤二：将步骤一中温度降到135-140℃时，加入尿素敞口搅拌反应1-2小时，即为一种绿色环保清洗剂前体。
所制备的绿色环保清洗剂前体是一种特殊的含有N-P的阴离子型表面活性剂，其中由于N、P是有机生命体的重要组成部分，因此N、P组分的存在有利于清洗剂及其所清洗油污的生物降解。
本发明提供的一种绿色环保清洗剂，其特征还在于，由以下重量份数比的原料制备而成：
所述的脂肪醇衣康酸酯磺酸盐的制备方法：
步骤一、将脂肪醇和衣康酸加入到反应釜内，加入催化剂。在惰性气体保护的情况下，于180～220℃的反应温度反应3～5小时；减压排除水分；即为脂肪醇衣康酸酯。
其中，惰性气体一般选择氮气、氩气等可用作为保护气的惰性气体。
其中，脂肪醇和衣康酸的摩尔比为1.8～2：1，优选为2：1。
所述的脂肪醇选择C8-C20的脂肪醇，优选：异辛醇、异癸醇、月桂醇、异构十三醇、异构十六醇、异构二十醇、油醇中的一种或几种混合物。
所述催化剂可以选用Lewis酸、金属盐或阳离子交换树脂。
所述的催化剂优选磷酸，所述的磷酸用量为反应物总重量的0.5-1％。选择磷酸的好处是反应后催化剂无需进行分离，可以节省因去除催化剂所需的水、电、化学试剂等，节能环保效益显著。
步骤二、将步骤一中得到的脂肪醇衣康酸酯和亚硫酸氢盐溶液充分搅拌，加热去除水分，反应生成脂肪醇衣康酸酯磺酸盐。
其中，亚硫酸氢盐和衣康酸的摩尔比为1～1.2：1，优选为1：1。亚硫酸氢盐溶液的浓度为20～30％。
所述的亚硫酸氢盐可以是亚硫酸氢钠或亚硫酸氢钾。
以上工艺制备的脂肪醇衣康酸酯磺酸盐是优良的阴离子表面活性剂，抗硬水能力强。
所述脂肪醇聚氧乙烯醚是C8-C20的脂肪醇与环氧乙烷进行加成反应的产物，优选：AEO-6、AEO-9、AEO-10、AEO-12、AEO-15中的一种或几种的混合物。
所述的乙二胺四乙酸钠可以选择乙二胺四乙酸二钠或乙二胺四乙酸四钠。
所述消泡剂选自聚醚类消泡剂、二甲基硅油、聚醚改性硅中的一种或几种的混合物。
本发明提供一种绿色环保清洗剂的制备方法，其特征在于，将乙二胺四乙酸钠、柠檬酸钠溶于去离子水中，加入绿色环保清洗剂前体、椰油酰基肌氨酸钠、脂肪醇衣康酸酯磺酸盐、脂肪醇聚氧乙烯醚、消泡剂在不超过100℃下搅拌至透明即可。
本发明提供一种绿色环保清洗剂的使用方法，其特征在于，加水5-200倍稀释后使用。
本发明的作用和效果：
本发明方法制备的绿色环保清洗剂前体是一种特殊的含有N-P的阴离子型表面活性剂，其中由于N、P是有机生命体的重要组成部分，因此N、P组分的存在有利于清洗剂及其所清洗油污的生物降解。具有良好的阻垢性能，同时又是一种很好的螯合剂，在清洗金属制品时可在金属表面形成一层保护膜，防止金属的腐蚀。
在本发明中椰油酰肌氨酸钠是两性表面活性剂，生物降解性好，和其他表面活性剂有很好的协同效应，同时还有很好的防锈效果，可以保护被清洗的金属表面在短时间内不被腐蚀。
在本发明中脂肪醇衣康酸酯磺酸盐是优良的阴离子表面活性剂，抗硬水能力强。
在本发明中脂肪醇聚氧乙烯醚是良好的非离子型表面活性剂，生物降解性好，和非离子型表面活性剂一起使用具有很好的协同效应。
在本发明中乙二胺四乙酸钠是良好的重金属离子螯合剂，可防止清洗时污垢在清洗物体表面的沉积。
在本发明中柠檬酸钠是良好的缓冲剂和螯合剂。
当制备的清洗剂的体系中泡沫太多或泡沫对清洗有影响时，加入消泡剂起消泡作用。
上述各组分发挥其应有效能的同时，可产生协同效应，提高产品的综合性能，可生物降解，减少对自然环境的污染，且能进一步的获得寿命长、可常温清洗的特点。
具体实施方式
实施例一
称取1801.6g(10mol)葡萄糖和2450g(25mol)磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至200℃，反应4小时，反应过程中及时抽除酯化反应生成的水分。反应后将温度降到140℃时，加入1201.2g(20mol)尿素敞口搅拌反应1小时，即为一种绿色环保清洗剂前体。
将乙二胺四乙酸二钠5g、柠檬酸钠5g溶于600g去离子水中，加入上述制备的绿色环保清洗剂前体1000g、椰油酰基肌氨酸钠300g、异辛醇衣康酸酯磺酸钠200g、脂肪醇聚氧乙烯醚(AEO-6)200g在不超过100℃下搅拌至透明即为一种绿色环保清洗剂。
上述异辛醇衣康酸酯磺酸钠的制备方法：
步骤一、将260.46g(2mol)异辛醇和130.1g(1mol)衣康酸加入到反应釜内，加入4g磷酸。在氮气保护的情况下，于220℃的反应温度反应3小时；减压排除水分；即为异辛醇衣康酸酯。
步骤二、将有效浓度30％亚硫酸氢钠溶液346g加入步骤一充分搅拌，加热去除水分，反应生成脂肪醇衣康酸酯磺酸钠。
将上述绿色环保清洗剂和水按重量比1：30混合搅拌后用于常温超声波清洗铝合金元器件，铝合金元器件加工前由菜籽油80％加煤油20％进行钻铣加工后用四氯乙烯清洗。
洗净率：
本实施例清洗：20分钟100％；四氯乙烯清洗：10分钟100％。
因此，本绿色环保清洗剂完全可以用来取代对环境和工人健康有害的氯化物金属清洗剂。
实施例二
称取1801.6g(10mol)葡萄糖和2940g(30mol)磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至180℃，反应5小时，反应过程中及时抽除酯化反应生成的水分。反应后将温度降到135℃时，加入600.6g(10mol)尿素敞口搅拌反应2小时，即为一种绿色环保清洗剂前体。
将乙二胺四乙酸四钠2g、柠檬酸钠2g溶于500g去离子水中，加入上述制备的绿色环保清洗剂前体1000g、椰油酰基肌氨酸钠200g、异癸醇衣康酸酯磺酸钾100g、脂肪醇聚氧乙烯醚(AEO-9)100g、消泡剂(二甲基硅油)2g在不超过100℃下搅拌至透明即为一种绿色环保清洗剂。
上述异癸醇衣康酸酯磺酸钾的制备方法：
步骤一、将284.9g(1.8mol)异癸醇和130.1g(1mol)衣康酸加入到反应釜内，加入2.5g磷酸。在氮气保护的情况下，于180℃的反应温度反应5小时；减压排除水分；即为异癸醇衣康酸酯。
步骤二、将有效浓度20％亚硫酸氢钾溶液600.85g加入步骤一充分搅拌，加热去除水分，反应生成脂肪醇衣康酸酯磺酸钾。
将上述绿色环保清洗剂和水按重量比1：20混合搅拌后用于常温超声波清洗不锈钢部件，不锈钢部件加工前由46#机械油加氯化石蜡进行攻丝而成，原使用某品牌清洗剂和水按1：20在60℃左右的温度超声波清洗。
洗净率：
本实施例清洗：18分钟100％；对比某清洗剂清洗：20分钟100％。
实施例三
称取1801.6g(10mol)葡萄糖和1960g(20mol)磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至220℃，反应3小时，反应过程中及时抽除酯化反应生成的水分。反应后将温度降到138℃时，加入901g(15mol)尿素敞口搅拌反应1.5小时，即为一种绿色环保清洗剂前体。
将乙二胺四乙酸二钠3g、柠檬酸钠3g溶于550g去离子水中，加入上述制备的绿色环保清洗剂前体1000g、椰油酰基肌氨酸钠250g、月桂醇衣康酸酯磺酸钠150g、脂肪醇聚氧乙烯醚(AEO-10)150g、消泡剂聚醚改性硅1g在不超过100℃下搅拌至透明即为一种绿色环保清洗剂。
上述月桂醇衣康酸酯磺酸盐的制备方法：
步骤一、将372.76g(2mol)月桂醇和130.1g(1mol)衣康酸加入到反应釜内，加入5g磷酸。在氮气保护的情况下，于200℃的反应温度反应4小时；减压排除水分；即为月桂醇醇衣康酸酯。
步骤二、将有效浓度25％亚硫酸氢钠溶液416g加入步骤一充分搅拌，加热去除水分，反应生成月桂醇衣康酸酯磺酸钠。
将上述绿色环保清洗剂加100倍水清洗食品不锈钢储藏罐(1T)外壁，储藏罐外壁主要污染物为：牛奶、食用油、糖、灰尘等，洗净时间和表面光亮度均优于某品牌家用洗洁精。
实施例四
称取180.16g(1mol)葡萄糖和245g(2.5mol)磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至200℃，反应3小时，反应过程中及时抽除酯化反应生成的水分。反应后将温度降到140℃时，加入60.06g(1mol)尿素敞口搅拌反应1小时，即为一种绿色环保清洗剂前体。
将乙二胺四乙酸二钠0.4g、柠檬酸钠0.4g溶于53g去离子水中，加入上述制备的绿色环保清洗剂前体100g、椰油酰基肌氨酸钠26g、异构十三醇衣康酸酯磺酸钠16g、脂肪醇聚氧乙烯醚(AEO-12)14g、聚醚消泡剂0.1g在不超过100℃下搅拌至透明即为一种绿色环保清洗剂。
上述异构十三醇衣康酸酯磺酸钠的制备方法：
步骤一、将400.74g(2mol)异构十三醇和130.1g(1mol)衣康酸加入到反应釜内，加入4g磷酸。在氮气保护的情况下，于220℃的反应温度反应3小时；减压排除水分；即为异构十三醇衣康酸酯。
步骤二、将有效浓度25％亚硫酸氢钠溶液416g加入步骤一充分搅拌，加热去除水分，反应生成异构十三醇衣康酸酯磺酸钠。
实施例五
称取180.16g(1mol)葡萄糖和245g(2.5mol)磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至200℃，反应3小时，反应过程中及时抽除酯化反应生成的水分。反应后将温度降到140℃时，加入60.06g(1mol)尿素敞口搅拌反应1小时，即为一种绿色环保清洗剂前体。
将乙二胺四乙酸四钠0.3g、柠檬酸钠0.4g溶于56g去离子水中，加入上述制备的绿色环保清洗剂前体100g、椰油酰基肌氨酸钠28g、异十六醇衣康酸酯磺酸钠20g、脂肪醇聚氧乙烯醚(AEO-15)12g在不超过100℃下搅拌至透明即为一种绿色环保清洗剂。
上述异十六醇衣康酸酯磺酸钠的制备方法：
步骤一、将485g(2mol)异十六醇和130.1g(1mol)衣康酸加入到反应釜内，加入6g磷酸。在氮气保护的情况下，于220℃的反应温度反应3小时；减压排除水分；即为异十六醇衣康酸酯。
步骤二、将有效浓度25％亚硫酸氢钠溶液420g加入步骤一充分搅拌，加热去除水分，反应生成异十六醇衣康酸酯磺酸盐。
实施例六
称取180.16g(1mol)葡萄糖和245g(2.5mol)磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至200℃，反应3小时，反应过程中及时抽除酯化反应生成的水分。反应后将温度降到140℃时，加入60.06g(1mol)尿素敞口搅拌反应1小时，即为一种绿色环保清洗剂前体。
将乙二胺四乙酸二钠0.35g、柠檬酸钠0.35g溶于52g去离子水中，加入上述制备的绿色环保清洗剂前体100g、椰油酰基肌氨酸钠22g、油醇衣康酸酯磺酸钠18g、脂肪醇聚氧乙烯醚(AEO-6)18g在不超过100℃下搅拌至透明即为一种绿色环保清洗剂。
上述油醇衣康酸酯磺酸钠的制备方法：
步骤一、将536.98g(2mol)油醇和130.1g(1mol)衣康酸加入到反应釜内，加入6g磷酸。在氮气保护的情况下，于200℃的反应温度反应4小时；减压排除水分；即为油醇衣康酸酯。
步骤二、将有效浓度25％亚硫酸氢钠溶液416g加入步骤一充分搅拌，加热去除水分，反应生成油醇衣康酸酯磺酸钠。
上述实施例一至六所用原料可以采用工业品原料制备，使用时具体参考外包装中标注实际有效成分的含量计算确定使用量。
上述实施例四至六均能获得实施例一至三中相类似的性能测试结果。
Claims (10)
1.一种绿色环保清洗剂前体，其特征在于，由包含：葡萄糖、磷酸、尿素制备而成；
所述葡萄糖、磷酸、尿素摩尔比为1:2-3:1-2。
2.如权利要求1所述的一种绿色环保清洗剂前体，其特征在于：
所述葡萄糖、磷酸、尿素摩尔比为1:2.5:1。
3.如权利要求1所述的一种绿色环保清洗剂前体，其特征在于：
其制备方法如下：
步骤一：将葡萄糖和磷酸加入反应釜中，抽除釜中空气，在低于100mmHg压力下的加热搅拌至180-200℃，反应3-4小时，反应过程中及时抽除酯化反应生成的水分；
步骤二：将步骤一中温度降到135-140℃时，加入尿素敞口搅拌反应1-2小时，即为一种绿色环保清洗剂前体。
4.如权利要求1-3任一项所述的一种绿色环保清洗剂前体制造的绿色环保清洗剂，其特征在于：由以下重量份数比的原料制备而成：
5.如权利要求4所述的一种绿色环保清洗剂，其特征在于：
所述的脂肪醇衣康酸酯磺酸盐的制备方法：
步骤一、将脂肪醇和衣康酸加入到反应釜内，加入催化剂；在惰性气体保护的情况下，于180～220℃的反应温度反应3～5小时；减压排除水分；即为脂肪醇衣康酸酯；
步骤二、将步骤一中得到的脂肪醇衣康酸酯和亚硫酸氢盐溶液充分搅拌，加热去除水分，反应生成脂肪醇衣康酸酯磺酸盐。
6.如权利要求5所述的一种绿色环保清洗剂，其特征在于：
所述惰性气体选择氮气或氩气；
所述脂肪醇和衣康酸的摩尔比为1.8～2：1；优选为2：1；
所述的脂肪醇选择C8-C20的脂肪醇，优选：异辛醇、异癸醇、月桂醇、异构十三醇、异构十六醇、异构二十醇、油醇中的一种或几种混合物。
7.如权利要求5所述的一种绿色环保清洗剂，其特征在于：
所述催化剂可以选用Lewis酸、金属盐或阳离子交换树脂；
所述催化剂优选磷酸，所述的磷酸用量优选为反应物总重量的0.5-1％。
8.如权利要求5所述的一种绿色环保清洗剂，其特征在于，
所述亚硫酸氢盐和衣康酸的摩尔比为1～1.2：1，优选为1：1；其中亚硫酸氢盐溶液的浓度优选为20～30％；
所述的亚硫酸氢盐可以是亚硫酸氢钠或亚硫酸氢钾。
9.如权利要求4所述的一种绿色环保清洗剂，其特征在于：
所述脂肪醇聚氧乙烯醚是C8-C20的脂肪醇与环氧乙烷进行加成反应的产物，优选：AEO-6、AEO-9、AEO-10、AEO-12、AEO-15中的一种或几种的混合物；
所述的乙二胺四乙酸钠可以选择乙二胺四乙酸二钠或乙二胺四乙酸四钠；
所述消泡剂优选自聚醚类消泡剂、二甲基硅油、聚醚改性硅中的一种或几种的混合物。
10.如权利要求4-9任一项所述的一种绿色环保清洗剂的制备方法，其特征在于：
将乙二胺四乙酸钠、柠檬酸钠溶于去离子水中，加入绿色环保清洗剂前体、椰油酰基肌氨酸钠、脂肪醇衣康酸酯磺酸盐、脂肪醇聚氧乙烯醚、消泡剂在不超过100℃下搅拌至透明即可。