CN110466219A - It is a kind of with anti-radiation, shellproof multifunctional glass - Google Patents
It is a kind of with anti-radiation, shellproof multifunctional glass Download PDFInfo
- Publication number
- CN110466219A CN110466219A CN201910726046.4A CN201910726046A CN110466219A CN 110466219 A CN110466219 A CN 110466219A CN 201910726046 A CN201910726046 A CN 201910726046A CN 110466219 A CN110466219 A CN 110466219A
- Authority
- CN
- China
- Prior art keywords
- glass
- layer
- radiation
- shellproof
- multifunctional
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind with anti-radiation, shellproof multifunctional glass, pass through the non-browning glass and multilayer bulletproof glass of setting, increase the function of glass, using the higher crystalline ceramics panel of hardness, for being crushed bullet or making its deformation, middle layer accompanies flexible isolating layer, additional protective capacities is provided in a manner of successively adding, alleviate the stress as caused by thermal expansion mispairing, and prevent crack propagation, the PET material layer of setting, improve the radiation-proof effect of non-browning glass, increase the intensity of glass, the high light transmission glass of setting, improve the translucency of non-browning glass, improve visual effect, the adhering film to glass of setting, increase the heat-insulated of glass, the functions such as heat preservation and antiultraviolet, finally using the higher polycarbonate of toughness as bottom plate, for absorbing the remaining kinetic energy of bullet and panel fragment, entire glass has height Hardness, high intensity, high tenacity, low-density, the i.e. characteristic of " three high and one low ".
Description
Technical field
The present invention relates to bulletproof glass technical fields, particularly relate to a kind of with anti-radiation, shellproof multifunctional glass.
Background technique
Bulletproof glass obtains large-scale popularization application in fields such as the windshield of surface car, side window and weapon shields.
Bulletproof glass is other than it can be applied to the protection of occupants' observation window such as driver, gunner, vehicle commander, it may also be used for production driver
It opens the cabin and drives shield, even protection shield and guided missile hanger shield of command car machine gunner etc..
Bulletproof glass is usually to be bonded float glass material layer with polyvinyl butyral, and with polyurethane by float glass process glass
Glass is Nian Jie with the polycarbonate at back or polymetylmetacrylate outer layer.According to shellproof theory, manufactured with identical material shellproof
Glass, influence of the thickness to bulletproof ability is maximum, and increase and the thickness of material bearing capacity have exponent relation, but as thickness increases
Add, transparent armor light transmittance reduces, optical distortion will will increase, and in practical applications, that there are surface densities is big, quality is big etc. no
Foot.
Summary of the invention
In view of this, it is a kind of with anti-radiation, shellproof multifunctional glass it is an object of the invention to propose, it is existing to solve
There is all or part of deficiency in technology.
It is provided by the invention a kind of with anti-radiation, shellproof multifunctional glass based on above-mentioned purpose, including adhering film to glass,
Crystalline ceramics panel, flexible isolating layer, polarized glass piece and Polycarbonate Layer, the adhering film to glass by middle film layer with it is transparent
Ceramic panel is fixedly connected, and the crystalline ceramics panel other side is successively fixedly installed flexible isolating layer and polarized glass piece,
The side of the polarized glass piece far from crystalline ceramics panel is fixedly installed non-browning glass, the anti-spoke by middle film layer
It penetrates the glass other side and is provided with high light transmission glass, the high light transmission glass other side is provided with hollow layer, and the hollow layer is separate
The side of high light transmission glass is fixedly installed Polycarbonate Layer, is provided with sealant at the top and bottom of the hollow layer, described
PET material layer, bearing layer are provided in non-browning glass, the bearing layer side is provided with safe protective covering.
Optionally, the crystalline ceramics panel be by signle crystal alumina, magnesium aluminate spinels and aluminum oxynitride constitute, and
The mass ratio of three is 1:0.5~0.8:1.2~2.2.
Optionally, the surface close to the bulletproof glass of the Polycarbonate Layer is honeycomb, the cellular diameter
For 0.1~0.5mm, depth is 0.2~0.5mm.
Optionally, polyurethane adhesive is filled in the honeycomb.
Optionally, the non-browning glass is fixedly connected by middle film layer with high light transmission glass, the middle film layer by
Polyurethane adhesive is made, the middle film layer with a thickness of 1~1.5mm.
Optionally, the size of the sealant and hollow layer top and bottom are open equal in magnitude.
Optionally, the bearing layer and safe protective covering are bonded by transparent glueing material.
Optionally, the adhering film to glass and crystalline ceramics panel is equal in magnitude.
Optionally, the PET material layer is at least arranged two layers.
It is provided by the invention a kind of with anti-radiation, shellproof multifunctional glass, by the non-browning glass of setting and more
Layer bulletproof glass, increases the function of glass, prevents the impact force of radiation and bullet, extends the service life of glass itself, uses
The higher crystalline ceramics panel of hardness, for being crushed bullet or making its deformation, middle layer accompanies flexible isolating layer, successively to add
Mode additional protective capacities is provided, alleviate the stress as caused by thermal expansion mispairing, and prevent crack propagation, the PET of setting
Material layer improves the radiation-proof effect of non-browning glass, increases the intensity of glass, and the high light transmission glass of setting improves anti-spoke
The translucency of glass is penetrated, visual effect is improved, the adhering film to glass of setting increases the function such as the heat-insulated of glass, heat preservation and antiultraviolet
Can, finally using the higher polycarbonate of toughness as bottom plate, for absorbing the remaining kinetic energy of bullet and panel fragment, entire glass
With high rigidity, high intensity, high tenacity, low-density, i.e. the characteristic of " three high and one low ".
Detailed description of the invention
Fig. 1 is of the present invention a kind of with anti-radiation, shellproof multifunctional glass structural schematic diagram；
Fig. 2 is non-browning glass structural schematic diagram of the present invention；
Fig. 3 is bulletproof glass schematic diagram of internal structure of the present invention.
In figure: 1, adhering film to glass；2, middle film layer；3, crystalline ceramics panel；4, polarized glass piece；5, non-browning glass；
6, high light transmission glass；7, hollow layer；8, honeycomb, 9, flexible isolating laminate；11, sealant；12, PET material layer；13, bearing layer；
14, safe protective covering, 15, Polycarbonate Layer.
Specific embodiment
For below by the description to embodiment, for example related manufacturing process of a specific embodiment of the invention and operation
Application method etc., is described in further detail, to help those skilled in the art to inventive concept of the invention, technical solution
There is more complete, accurate and deep understanding.
In order to solve prior art bulletproof glass, all or part of shortcoming,
It is provided by the invention a kind of with anti-radiation, shellproof multifunctional glass, including adhering film to glass, crystalline ceramics face
Plate, flexible isolating layer, polarized glass piece and Polycarbonate Layer, the adhering film to glass are solid by middle film layer and crystalline ceramics panel
Fixed connection, the crystalline ceramics panel other side is successively fixedly installed flexible isolating layer and polarized glass piece, the polarization glass
Side of the glass piece far from crystalline ceramics panel is fixedly installed non-browning glass by middle film layer, and the non-browning glass is another
Side is provided with high light transmission glass, and the high light transmission glass other side is provided with hollow layer, and the hollow layer is far from high light transmission glass
Side be fixedly installed Polycarbonate Layer, be provided with sealant, the non-browning glass at the top and bottom of the hollow layer
It is inside provided with PET material layer, bearing layer, the bearing layer side is provided with safe protective covering.
Fig. 1-3 is please referred to, the present invention provides a kind of technical solution: a kind of with anti-radiation, shellproof multifunctional glass, packet
Adhering film to glass 1, crystalline ceramics panel 3, flexible isolating layer 9, polarized glass piece 4 and Polycarbonate Layer 15 are included, adhering film to glass 1 passes through
Middle film layer 2 is fixedly connected with crystalline ceramics panel 3, and 3 other side of crystalline ceramics panel is successively fixedly installed flexible isolating layer 9
With polarized glass piece 4, side of the polarized glass piece 4 far from crystalline ceramics panel 3 is fixedly installed radiation protection by middle film layer 2
Glass 5,5 other side of non-browning glass are provided with high light transmission glass 6, and 6 other side of high light transmission glass is provided with hollow layer 7, hollow
7 side far from high light transmission glass 6 of layer are provided with Polycarbonate Layer 15, and sealant 11 is provided at the top and bottom of hollow layer 7,
PET material layer 12, bearing layer 13 are provided in non-browning glass 5,13 side of bearing layer is provided with safe protective covering 14.By setting
The non-browning glass 5 and crystalline ceramics panel 3 and flexible isolating laminate 9 set, increase the function of glass, prevent radiation and bullet
Impact force, extend glass itself service life.Using the higher crystalline ceramics panel 3 of hardness, for being crushed bullet or making
It is deformed, and middle layer accompanies flexible isolating layer 9, and additional protective capacities is provided in a manner of successively adding, and is alleviated by thermally expanding
Stress caused by mispairing, and crack propagation is prevented, the PET material layer 12 of setting improves the radiation-proof effect of non-browning glass, increases
The intensity of glass is added, the high light transmission glass 6 of setting improves the translucency of non-browning glass, improves visual effect, the glass of setting
Glass pad pasting 1 increases the heat-insulated of glass, heat preservation and the functions such as antiultraviolet, finally using the higher Polycarbonate Layer 15 of toughness as
Bottom plate, for absorbing the remaining kinetic energy of bullet and panel fragment.Entire glass has high rigidity, high intensity, high tenacity, low close
Degree, the i.e. characteristic of " three high and one low ".
Non-browning glass 5 is fixedly connected by middle film layer 2 with high light transmission glass 6, and middle film layer 2 is by polyurethane adhesive
Be made, middle film layer 2 with a thickness of 1~1.5mm, the size phase that is open at the top and bottom of the size and hollow layer 7 of sealant 11
Deng bearing layer 13 and safe protective covering 14 are bonded by transparent glueing material, adhering film to glass 1 and crystalline ceramics panel 3
Equal in magnitude, PET material layer 12 is at least arranged two layers.
Crystalline ceramics panel 3 be by signle crystal alumina, magnesium aluminate spinels and aluminum oxynitride constitute, and the quality of three
Than for 1:0.5~0.8:1.2~2.2, by the test of Ballistic tests, the best proportion of three is 1:0.65:1.85.Poly- carbonic acid
The surface of the close hollow layer 7 of ester layer 15 is honeycomb, and the diameter of honeycomb 8 is 0.1~0.5mm, and depth is 0.2~0.5mm, is surveyed
Examination performance shows that optimal ratio be the diameter of honeycomb 8 is 0.3mm, depth 0.3mm.Polyurethane gluing is filled in honeycomb 8
Agent, for carrying out gluing combination with bulletproof glass.
Concrete principle: in use, adhering film to glass 1 is bonded on crystalline ceramics panel 3, it can heat-insulated, heat preservation and anti-purple
The functions such as outside line are bonded in 3 polarized glass piece 4 of crystalline ceramics panel the middle film layer 2 made of polyurethane adhesive
Together, 4 other side of polarized glass piece is bonded with non-browning glass 5, PET material layer 12, the bearing layer being arranged in non-browning glass 5
13 and safe protective covering 14, guarantee that bullet is not passed through this layer safe protective covering 14 2 times, increases the radiation proof function and glass of glass
The intensity of glass, bearing layer 13 absorb impact, and the high light transmission glass 6 of another side bonds of non-browning glass 5 setting increases radiation protection glass
The translucency of glass 5, improves visual effect, and the hollow layer 7 that high light transmission glass 6 and Polycarbonate Layer 15 are formed increases the antiknock of glass
Fried ability, sealant 11 seal the opening of hollow layer 7, the Polycarbonate Layer 15 of setting as glass substrate be convenient for other layers into
Row location and installation.This kind of glass structure is simple, and function is more, has high rigidity, high intensity, high tenacity, low-density, i.e., " three is high
One is low " characteristic.It is applied widely.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
It should be understood by those ordinary skilled in the art that: the discussion of any of the above embodiment is exemplary only, not
It is intended to imply that the scope of the present disclosure (including claim) is limited to these examples；Under thinking of the invention, above embodiments
Or can also be combined between the technical characteristic in different embodiments, step can be realized with random order, and be existed such as
Many other variations of the upper different aspect of the invention, for simplicity, they are not provided in details.
The embodiment of the present invention be intended to cover fall into all such replacements within the broad range of appended claims,
Modifications and variations.Therefore, all within the spirits and principles of the present invention, any omission, modification, equivalent replacement, the improvement made
Deng should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that one include adhering film to glass, crystalline ceramics panel,
Flexible isolating layer, polarized glass piece and Polycarbonate Layer, the adhering film to glass are fixed by middle film layer and crystalline ceramics panel
Connection, the crystalline ceramics panel other side is successively fixedly installed flexible isolating layer and polarized glass piece, the polarized glass
Side of the piece far from crystalline ceramics panel is fixedly installed non-browning glass, the non-browning glass other side by middle film layer
It is provided with high light transmission glass, the high light transmission glass other side is provided with hollow layer, and the hollow layer is far from high light transmission glass
Side is fixedly installed Polycarbonate Layer, is provided with sealant at the top and bottom of the hollow layer, in the non-browning glass
It is provided with PET material layer, bearing layer, the bearing layer side is provided with safe protective covering.
2. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that described transparent
Ceramic panel be by signle crystal alumina, magnesium aluminate spinels and aluminum oxynitride constitute, and the mass ratio of three be 1:0.5~
0.8:1.2~2.2.
3. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the poly- carbon
Acid esters layer close to the hollow layer surface be honeycomb, the cellular diameter be 0.1~0.5mm, depth be 0.2~
0.5mm。
4. according to claim 3 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the honeycomb
It is interior to be filled with polyurethane adhesive.
5. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the anti-spoke
Penetrate glass and be fixedly connected by middle film layer with high light transmission glass, the middle film layer is made of polyurethane adhesive, it is described in
Between film layer with a thickness of 1~1.5mm.
6. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the sealing
What is be open at the top and bottom of the size and hollow layer of glue is equal in magnitude.
7. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the load
Layer and safe protective covering are bonded by transparent glueing material.
8. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the glass
Pad pasting and crystalline ceramics panel it is equal in magnitude.
9. according to claim 1 a kind of with anti-radiation, shellproof multifunctional glass, which is characterized in that the PET material
The bed of material is at least arranged two layers.