CN110459760B - 一种制备镍钴锰酸锂单晶三元材料的方法 - Google Patents
一种制备镍钴锰酸锂单晶三元材料的方法 Download PDFInfo
- Publication number
- CN110459760B CN110459760B CN201910767039.9A CN201910767039A CN110459760B CN 110459760 B CN110459760 B CN 110459760B CN 201910767039 A CN201910767039 A CN 201910767039A CN 110459760 B CN110459760 B CN 110459760B
- Authority
- CN
- China
- Prior art keywords
- mixture
- zirconium
- nickel cobalt
- single crystal
- particle size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例编号 | 首次充电比容量 | 首次放电比容量 | 首次效率 |
实施例1 | 200.18mAh/g | 175.45mAh/g | 88% |
实施例2 | 199.51mAh/g | 176.92mAh/g | 89% |
实施例3 | 198.32mAh/g | 175.29mAh/g | 88% |
实施例4 | 198.29mAh/g | 175.61mAh/g | 89% |
对比例1 | 198.10mAh/g | 174.55mAh/g | 88% |
对比例2 | 197.78mAh/g | 174.36mAh/g | 88% |
对比例3 | 196.12mAh/g | 173.48mAh/g | 88% |
实施例编号 | 放电比容量 | 容量保持率 |
实施例1 | 154.31mAh/g | 97% |
实施例2 | 155.83mAh/g | 97% |
实施例3 | 154.29mAh/g | 97% |
实施例4 | 154.03mAh/g | 97% |
对比例1 | 145.98mAh/g | 92% |
对比例2 | 146.61mAh/g | 92% |
对比例3 | 128.94mAh/g | 84% |
实施例编号 | 0.1C克容量 | 1C克容量 |
实施例1 | 175.45mAh/g | 159.80mAh/g |
实施例2 | 176.92mAh/g | 161.13mAh/g |
实施例3 | 175.29mAh/g | 159.08mAh/g |
实施例4 | 175.61mAh/g | 159.11mAh/g |
对比例1 | 174.55mAh/g | 159.01mAh/g |
对比例2 | 174.36mAh/g | 158.67mAh/g |
对比例3 | 173.48mAh/g | 154.18mAh/g |
Claims (11)