CN110357159A - A kind of device and method preparing electron level nanometer calcium molybdate - Google Patents
A kind of device and method preparing electron level nanometer calcium molybdate Download PDFInfo
- Publication number
- CN110357159A CN110357159A CN201910699776.XA CN201910699776A CN110357159A CN 110357159 A CN110357159 A CN 110357159A CN 201910699776 A CN201910699776 A CN 201910699776A CN 110357159 A CN110357159 A CN 110357159A
- Authority
- CN
- China
- Prior art keywords
- electric heating
- electron level
- calcium molybdate
- nanometer calcium
- level nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of device and methods for preparing electron level nanometer calcium molybdate, described device includes resonance mixing machine, the resonance mixing machine is connected to one end of electric heating converter by feeder, the other end of the electric heating converter connects finished bin, and the top of the electric heating converter of the electric heating converter connects recover.A kind of device and method preparing electron level nanometer calcium molybdate proposed by the present invention is directly synthesized in electric heating converter using high-purity nm molybdenum trioxide with high-purity nm calcium carbonate, simple to operate, combined coefficient nearly 100%, it is lossless, it is pollution-free, it can be achieved that large-scale production.
Description
Technical field
The present invention relates to calcium molybdates to produce correlative technology field, prepares electron level nanometer calcium molybdate more particularly to a kind of
Device and method.
Background technique
Industrially generally using calcium molybdate as the additive of steel-making, when a kind of means of molybdenum element supplement, therefore it is produced
Method is rougher.I.e. using the methods of Low Grade Molybdenum Concentrates or waste catalyst recovery as molybdenum source, general industry molybdic acid liquid is made
Body is added suitable calcium carbonate powder further according to molybdenum content, generates technical grade calcium molybdate mixed liquor, is separated, dries and be made into
Product.The granularity of products obtained therefrom is 8-10 microns general, purity 98-99% or so.But nearly ten years, discovery calcium molybdate has light to hair
Light, electricity to shine, the new features such as photocatalysis, and find the partial size of its photoelectric functional and calcium molybdate inversely,
That is its smaller function of partial size is more obvious, and important use aspect is light emitting diode, lithium ion battery negative material.
The Central China University of Science and Technology, Northwestern Polytechnical University and patent CN201510603430.7, CN201611230603.6 etc. are big
Quantity research shows to be difficult to realize industrialized production, and the secondary crystallization of wet production, and lotus shape crystal is coarse.
Therefore, how prepared sizes are thinner, the higher calcium molybdate of purity is problems solved by the invention.
Summary of the invention
In order to overcome the above-mentioned deficiency of the prior art, the invention proposes a kind of devices for preparing electron level nanometer calcium molybdate
And method, it solves existing calcium molybdate and prepares that existing combined coefficient is low, calcium molybdate partial size is big and cannot achieve large-scale production
Problem.
The present invention is achieved by the following technical solutions:
A kind of device preparing electron level nanometer calcium molybdate, including resonance mixing machine, the resonance mixing machine pass through feeding
Machine is connected to one end of electric heating converter, and the other end of the electric heating converter connects finished bin, the electricity of the electric heating converter
The top for heating converter connects recover.
Further, the top of the finished bin is equipped with the atomizer for spraying dispersing agent.
Further, drapery panel is additionally provided in the electric heating converter, stay flitch.
Further, the electric heating converter uses 2520 materials.
A method of preparing electron level nanometer calcium molybdate, specifically includes the following steps: by high-purity nm molybdenum trioxide with
It is sufficiently mixed in the high-purity nm calcium carbonate resonance mixing machine of 1:1.02 addition in molar ratio, the material mixed is sent by feeder
Enter in electric heating converter, furnace temperature is 540 ± 1 DEG C, and the electron level nanometer calcium molybdate finished product of generation enters in finished bin, other part
Material is with CO2It brings recover into, then send to feeder and continue to use.
Further, material stops 40min in electric heating converter.
Further, ethylene glycol nanometer of the atomizer for the injection 1% into electron level nanometer calcium molybdate finished product
Material dispersing agent.
Compared with prior art, the beneficial effects of the present invention are:
A kind of device and method preparing electron level nanometer calcium molybdate proposed by the present invention, using high-purity nm molybdenum trioxide
It is directly synthesized in electric heating converter with high-purity nm calcium carbonate, simple to operate, combined coefficient nearly 100%, lossless, nothing
Pollution is, it can be achieved that be mass produced, and calcium molybdate partial size obtained meets industrial production use demand.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram for the device for preparing electron level nanometer calcium molybdate described in the embodiment of the present invention.
In figure:
1, resonate mixing machine;2, feeder;3, recover;4, electric heating converter;5, finished bin;6, atomizer.
Specific embodiment
It shows that example illustrates certain embodiments of the present invention, and should not be construed as limiting model of the invention
It encloses.Present disclosure can be improved from material, method and reaction condition simultaneously, all these improvement should all
It falls within spirit and scope of the invention.
As shown in Figure 1, a kind of device for preparing electron level nanometer calcium molybdate, including resonance mixing machine 1, the resonance mixing
Machine 1 is connected to one end of electric heating converter 4 by feeder 2, and the other end of the electric heating converter 4 connects finished bin 5, described
Electric heating converter 4 uses 2520 materials, is additionally provided with drapery panel in the electric heating converter 4, stays flitch, the top of the finished bin 5
Portion is equipped with the atomizer 6 for spraying dispersing agent, and the top of the electric heating converter 4 of the electric heating converter 4 connects recover
3。
It include: by high-purity nm molybdenum trioxide and height using the specific method that above-mentioned apparatus prepares electron level nanometer calcium molybdate
It is sufficiently mixed in the pure nanometer calcium carbonate resonance mixing machine 1 of 1:1.02 addition in molar ratio, the material mixed is sent by feeder
Enter in electric heating converter 4, furnace temperature is 540 ± 1 DEG C, and material stops 40min, the electron level nanometer of generation in electric heating converter 4
Calcium molybdate finished product enters in finished bin 5, and other part material is with CO2It brings recover 3 into, then send to feeder 2 and continue to use.
The drapery panel that sets in the electric heating converter 4 stays flitch, make material realize as far as possible in a short time uniformly, fill
Divide heating, multistage heating area is set in electric heating converter 4, material stops 10min in high-temperature region.
5 upper top of finished bin installs atomizer 6 additional, and 1% second two is sprayed into electron level nanometer calcium molybdate finished product
Alcohol nano material dispersing agent can increase and decrease according to demand or not add.
It is directly synthesized in electric heating converter using high-purity nm molybdenum trioxide with high-purity nm calcium carbonate, side easy to operate
Just, combined coefficient nearly 100%, it is lossless, it is pollution-free, it can be achieved that large-scale production, and calcium molybdate partial size obtained meets industry
Production and application demand.
The above description is only an embodiment of the present invention, is not intended to limit the scope of the invention, all to utilize this hair
Equivalent structure or equivalent flow shift made by bright specification and accompanying drawing content is applied directly or indirectly in other relevant skills
Art field, is included within the scope of the present invention.
Claims (7)
1. a kind of device for preparing electron level nanometer calcium molybdate, which is characterized in that including resonating mixing machine (1), the resonance is mixed
Conjunction machine (1) is connected to one end of electric heating converter (4) by feeder (2), and the other end of the electric heating converter (4) connects into
The top in product storehouse (5), the electric heating converter (4) of the electric heating converter (4) connects recover (3).
2. a kind of device for preparing electron level nanometer calcium molybdate according to claim 1, which is characterized in that the finished bin
(5) top is equipped with the atomizer (6) for spraying dispersing agent.
3. a kind of device for preparing electron level nanometer calcium molybdate according to claim 1, which is characterized in that the electric heating
It is additionally provided with drapery panel in converter (4), stays flitch, realizing material as far as possible in a short time and uniformly, sufficiently heat.
4. a kind of device for preparing electron level nanometer calcium molybdate according to claim 1, which is characterized in that the electric heating
Converter (4) uses 2520 materials.
5. the method for preparing electron level nanometer calcium molybdate using device described in claim 1-4 any one, which is characterized in that
Specifically includes the following steps: high-purity nm molybdenum trioxide is mixed with high-purity nm calcium carbonate 1:1.02 addition in molar ratio resonance
Machine is sufficiently mixed in (1), and the material mixed is sent into electric heating converter (4) by feeder, and furnace temperature is 540 ± 1 DEG C, is generated
Electron level nanometer calcium molybdate finished product enter in finished bin (5), other part material is with CO2Bring recover (3) into, then send to feed
Material machine (2) continues to use.
6. a kind of method for preparing electron level nanometer calcium molybdate according to claim 5, which is characterized in that material adds in electricity
40min is stopped in hot converter (4).
7. a kind of method for preparing electron level nanometer calcium molybdate according to claim 5, which is characterized in that the atomization spray
Ethylene glycol nano material dispersing agent of the head (6) for the injection 1% into electron level nanometer calcium molybdate finished product.