CN1103358A - Magnesium composite for building - Google Patents
Magnesium composite for building Download PDFInfo
- Publication number
- CN1103358A CN1103358A CN 93115602 CN93115602A CN1103358A CN 1103358 A CN1103358 A CN 1103358A CN 93115602 CN93115602 CN 93115602 CN 93115602 A CN93115602 A CN 93115602A CN 1103358 A CN1103358 A CN 1103358A
- Authority
- CN
- China
- Prior art keywords
- binder materials
- construction material
- glass cloth
- keel
- described construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The building composition is made up through binding layers of glass fibre cloth with cementing material, adhering the processed glass fibre cloth to both sides of wooden keel, filling the cavities of keel with filler and pressing, and features flame retardation, resisting worm-eating, moisture and ageing, easy machining and painting, light weight and high strength.
Description
The present invention relates to a kind of construction material.
People usually use timber in daily life or engineering construction, such as building template, and the door of dwelling house, wall, frame etc. also have to be used in decorative panel, but timber resources is limited, especially, and over cutting, with the heavy damage ecological balance, in recent years, people are just striving to find various substitute materials for wood.As utilize bamboo wood production template, decorative panel, utilize wood chip, bamboo bits or the high plant debris of other fiber content to suppress various fiberboards.Timber or existing substitute materials for wood are because therefore the organic fibrous material that belongs to, exists the deficiency of fire prevention, protection against the tide, anticorrosion, mothproof, anti-aspect, crack to some extent.
The purpose of this invention is to provide a kind of magnesium composite for building.This construction material is fire-retardant, moistureproof, anticorrosion, mothproof, crack not.
The present invention is achieved in that
Glass cloth is bonded together with Binder Materials, the glass cloth that is glued together is sticked to the two sides of timber keel, keel hollow place is filled out with inserts, suppresses forming under certain pressure.
Describe the present invention in detail below in conjunction with embodiment.
The composition of Binder Materials and prescription (percentage by weight)
MgSio
3MgCl·6H
2O MgO MgSO
4FeO
5%-8% 30%-40% 45%-55% 7%-10% 0.2%-2%
Use flat panel form, on template (bed die), be coated with the anti-skidding oil of last layer earlier, the brushing last layer shines the Binder Materials that above-mentioned prescription is modulated equably again, put middle alkali 02 a grid glass cloth,, cover middle alkali 02 a grid glass cloth more again at glass cloth proofing gel material, and coat Binder Materials thereon, then, put the frame-like keel of making of timber thereon, it is full of with inserts.The wooden frame keel require corner angle clearly demarcated, and two Diagonal Dimension equate.Inserts can adopt three kinds of modes to solve: 1, adopt calcium to mould sheet and be processed into the framework filling; 2, adopt interior empty measure-alike filling of foam section and wooden keel; 3,, be used for then filling with empty measure-alike in perlite gelling one-tenth and the keel.After populated, brushing one deck Binder Materials is put middle alkali 02 a glass cloth, is coated with the last layer Binder Materials again, puts middle alkali 02 a glass cloth, is coated with the last layer Binder Materials again, covers the flat panel form (cover mold) that lastblock is brushed with anti-lubricating oil then.Bed die and cover mold tightened up with securing member suppress, the pressure of compacting is 25N/cm
2Press time is 8 hours, opens mould then, it is sidelong maintenance 2 days after opening mould, keeps flat maintenance fringing after 10 days, and fringing is reinforced fringing with seccotine gummed back with the taper bamboo nail.
That the present invention has is fire-retardant, mothproof, anticorrosion, moistureproof, anti-aging, can follow closely, can saw, can dig, can paint, in light weight, advantage that intensity is high.
Claims (7)
1, magnesium composite for building, characteristics of the present invention are to be coated with the anti-skidding oil of last layer on bed die earlier, brushing last layer Binder Materials equably again, put middle alkali 02 a grid glass cloth, again at glass cloth proofing gel material, cover middle alkali 02 a grid glass cloth again and coat Binder Materials thereon, then, put the frame-like keel of making of timber thereon, with inserts it is full of, populated after, brushing one deck Binder Materials, put middle alkali 02 a glass cloth, be coated with the last layer Binder Materials again, put middle alkali 02 a glass cloth, be coated with the last layer Binder Materials again, cover the cover mold that is brushed with anti-lubricating oil, bed die and cover mold are tightened up with securing member suppress.Maintenance, fringing then behind the mould are opened in compacting.
2,, it is characterized in that the composition and the prescription (percentage by weight) of Binder Materials by the described construction material of claim 1:
MgSiO
3MgCl·6H
2O MgO MgSO
4FeO
5%-8% 30%-40% 45%-55% 7%-10% 0.2%-2%
3, by the described construction material of claim 1, it is characterized in that the keel corner angle are clearly demarcated, two Diagonal Dimension equate.
4,, it is characterized in that inserts adopts one of following three kinds of methods to solve by the described construction material of claim 1:
A, employing calcium are moulded sheet and are processed into the framework filling;
B, section of employing foam and interior empty measure-alike filling of wooden keel;
C, sky in perlite gelling one-tenth and the keel is measure-alike is used for filling then.
5, by the described construction material of claim 1, it is characterized in that the pressure of suppressing is 25N/cm
2, the press time is 8 hours.
6, by the described construction material of claim 1, it is characterized in that opening mould after the compacting, it was sidelong maintenance 2 days after opening mould, kept flat maintenance 10 days.
7, construction material according to claim 1 is characterized in that fringing with behind the seccotine gummed, reinforces fringing with the taper bamboo nail.