CN110328996A - A kind of processing technology for hiding tea ornaments - Google Patents
A kind of processing technology for hiding tea ornaments Download PDFInfo
- Publication number
- CN110328996A CN110328996A CN201910725253.8A CN201910725253A CN110328996A CN 110328996 A CN110328996 A CN 110328996A CN 201910725253 A CN201910725253 A CN 201910725253A CN 110328996 A CN110328996 A CN 110328996A
- Authority
- CN
- China
- Prior art keywords
- ornaments
- tea
- brick
- hiding
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technologys for hiding tea ornaments, belong to ornaments processing technique field comprising following steps: (1) by the hiding tea after fermentating drying with steamed 5-8 minutes；(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, its pressed density is made to reach 0.5*103g/m3Brick；(3) brick tea of compression is demoulded after the subzero 22 degree of environment of 18 degrees below zero-are 5 days cooling；(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 millimeter of surface layer is gone in brick tea four directions when processing, takes brick tea middle to be prepared into all kinds of ornaments, ornaments density, hardness is made to reach best requirement；(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling is carried out in the warm pot of 40-50 degree, temperature rolls duration 120 minutes, and revolving speed is 20 revs/min；(6) ornaments for choosing the different size made carry out broken test.The present invention is suitable for hiding tea ornaments processing.
Description
Technical field
The invention belongs to ornaments processing technique fields, and in particular to a kind of processing technology for hiding tea ornaments.
Background technique
With the development of the times with the raising of living standards of the people, tea beverage by its health, it is quick, natural, facilitate
Feature, which receives, more and more to be pursued, and the drinking way of tea beverage can meet the allegro requirement of people's modern life.
Hiding tea is a kind of very typical dark green tea, brown color, modern research shows that hiding tea is rich in tea polyphenols, water-soluble fibre etc.
The inorganic matters such as organic compound and minerals, it is highly beneficial to human health.
However, tradition hiding tea contributes to drink, need that can be only achieved it wholesome to human body by drinking absorption
Effect, and ornaments decoration can not be made into and wear to play and reach wholesome effect.Since tea polyphenols and its oxidation product have
Absorb the ability that radioactive substance strontium 90 and Co 60 are poisoned.Therefore extended wear is smelt occlusion tea ornaments and can also be brought to people beneficial to strong
Kang Zuoyong.
Summary of the invention
It is an object of the invention to: a kind of processing technology for hiding tea ornaments is provided, the processing technology is obtained to hide tea ornaments
Have the effect of centainly refreshing oneself eye-catching, anti-radiation.
The technical solution adopted by the invention is as follows:
A kind of processing technology for hiding tea ornaments, comprising the following steps:
(1) by the hiding tea after fermentating drying with steamed 5-8 minutes；
(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, it is suppressed
Density reaches 0.5*103g/m3Brick；
(3) brick tea of compression is demoulded after the subzero 22 degree of environment of 18 degrees below zero-are 5 days cooling；
(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 milli of surface layer is removed in brick tea four directions when processing
Rice, takes brick tea middle to be prepared into all kinds of ornaments, ornaments density, hardness is made to reach best requirement；
(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling is carried out in the warm pot of 40-50 degree
Dynamic, temperature rolls duration 120 minutes, and revolving speed is 20 revs/min, and ornaments after molding is made to achieve the effect that glossy light；
(6) ornaments for choosing the different size made carry out broken test, and being crushed testing method is by different size
Ornaments are put into pressure testing under 5 tons of hydraulic press, and the pressure that ornaments can be born is qualification at 0.5 ton or more.
In conclusion by adopting the above-described technical solution, the beneficial effects of the present invention are:
1, the present invention in, will hiding tea be prepared into ornaments to people for a long time decorate wear play, the tea polyphenols of Zang Chazhong and its
Oxidation product has the ability for absorbing that radioactive substance strontium 90 and Co 60 are poisoned, and the aromatic substance of tealeaves by skin contact or is smelt
It is eye-catching that energy-absorbing enough allows people to refresh oneself, and smells suction for a long time or plays the radiation that can reduce mobile phone, computer, TV and sunlight to body bring
Adverse effect, extended wear, which smells occlusion tea ornaments, can bring the effect of beneficial human health.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that described herein, specific examples are only used to explain the present invention, is not used to limit
The fixed present invention.
A kind of processing technology for hiding tea ornaments, comprising the following steps:
(1) by the hiding tea after fermentating drying with steamed 5-8 minutes；
(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, it is suppressed
Density reaches 0.5*103g/m3Brick；
(3) brick tea of compression is demoulded after the subzero 22 degree of environment of 18 degrees below zero-are 5 days cooling；
(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 milli of surface layer is removed in brick tea four directions when processing
Rice, takes brick tea middle to be prepared into all kinds of ornaments, ornaments density, hardness is made to reach best requirement；
(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling is carried out in the warm pot of 40-50 degree
Dynamic, temperature rolls duration 120 minutes, and revolving speed is 20 revs/min, and ornaments after molding is made to achieve the effect that glossy light；
(6) ornaments for choosing the different size made carry out broken test, and being crushed testing method is by different size
Ornaments are put into pressure testing under 5 tons of hydraulic press, and the pressure that ornaments can be born is qualification at 0.5 ton or more.
Embodiment 1
A kind of processing technology for hiding tea ornaments, comprising the following steps:
(1) by the hiding tea after fermentating drying with steamed 5 minutes；
(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, it is suppressed
Density reaches 0.5*103g/m3Brick；
(3) brick tea of compression is demoulded after 18 degrees below zero environment is 5 days cooling；
(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 milli of surface layer is removed in brick tea four directions when processing
Rice, takes brick tea middle to be prepared into all kinds of ornaments, ornaments density, hardness is made to reach best requirement；
(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling, temperature is carried out in 50 degree of warm pot
It rolls duration 120 minutes, revolving speed is 20 revs/min, and ornaments after molding is made to achieve the effect that glossy light；
(6) ornaments for choosing the different size made carry out broken test, and being crushed testing method is by different size
Ornaments are put into pressure testing under 5 tons of hydraulic press, and the pressure that ornaments can be born is qualification at 0.5 ton or more.
Embodiment 2
A kind of processing technology for hiding tea ornaments, comprising the following steps:
(1) by the hiding tea after fermentating drying with steamed 6 minutes；
(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, it is suppressed
Density reaches 0.5*103g/m3Brick；
(3) brick tea of compression is demoulded after minus 20 degrees environment is 5 days cooling；
(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 milli of surface layer is removed in brick tea four directions when processing
Rice, takes brick tea middle to be prepared into all kinds of ornaments, ornaments density, hardness is made to reach best requirement；
(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling, temperature is carried out in 40 degree of warm pot
It rolls duration 120 minutes, revolving speed is 20 revs/min, and ornaments after molding is made to achieve the effect that glossy light；
(6) ornaments for choosing the different size made carry out broken test, and being crushed testing method is by different size
Ornaments are put into pressure testing under 5 tons of hydraulic press, and the pressure that ornaments can be born is qualification at 0.5 ton or more.
Embodiment 3
A kind of processing technology for hiding tea ornaments, comprising the following steps:
(1) by the hiding tea after fermentating drying with steamed 8 minutes；
(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, it is suppressed
Density reaches 0.5*103g/m3Brick；
(3) brick tea of compression is demoulded after subzero 22 degree of environment are 5 days cooling；
(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 milli of surface layer is removed in brick tea four directions when processing
Rice, takes brick tea middle to be prepared into all kinds of ornaments, ornaments density, hardness is made to reach best requirement；
(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling, temperature is carried out in 45 degree of warm pot
It rolls duration 120 minutes, revolving speed is 20 revs/min, and ornaments after molding is made to achieve the effect that glossy light；
(6) ornaments for choosing the different size made carry out broken test, and being crushed testing method is by different size
Ornaments are put into pressure testing under 5 tons of hydraulic press, and the pressure that ornaments can be born is qualification at 0.5 ton or more.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (1)
1. a kind of processing technology for hiding tea ornaments, which comprises the following steps:
(1) by the hiding tea after fermentating drying with steamed 5-8 minutes；
(2) 5 minutes loading molds are steamed in cooling again after so that tealeaves is softened, and are suppressed with 100 t hydraulic press, make its pressed density
Reach 0.5*103g/m3Brick；
(3) brick tea of compression is demoulded after the subzero 22 degree of environment of 18 degrees below zero-are 5 days cooling；
(4) will brick tea after demoulding stand 24 hours after carry out processing and forming, 0.5 millimeter of surface layer is gone in brick tea four directions when processing, is taken
Brick tea middle is prepared into all kinds of ornaments, and ornaments density, hardness is made to reach best requirement；
(5) ornaments after molding are put into equipped in the dryer for dissipating hiding tea, warm rolling, temperature is carried out in the warm pot of 40-50 degree
It rolls duration 120 minutes, revolving speed is 20 revs/min, and ornaments after molding is made to achieve the effect that glossy light；
(6) ornaments for choosing the different size made carry out broken test, and being crushed testing method is by the ornaments of different size
It is put into pressure testing under 5 tons of hydraulic press, the pressure that ornaments can be born is qualification at 0.5 ton or more.