CN110295446A - A kind of textile technology of the ventilative knitting fabric of moisture absorption - Google Patents
A kind of textile technology of the ventilative knitting fabric of moisture absorption Download PDFInfo
- Publication number
- CN110295446A CN110295446A CN201910691311.XA CN201910691311A CN110295446A CN 110295446 A CN110295446 A CN 110295446A CN 201910691311 A CN201910691311 A CN 201910691311A CN 110295446 A CN110295446 A CN 110295446A
- Authority
- CN
- China
- Prior art keywords
- fiber
- moisture absorption
- parts
- textile technology
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of textile technologies of the ventilative knitting fabric of moisture absorption, belong to textile technology field.A kind of textile technology of the ventilative knitting fabric of moisture absorption, which is characterized in that including following raw materials according in parts by weight: 10~20 parts by weight of flax fiber, 5~10 parts of acid fiber by polylactic, 20~35 parts by weight of hair fiber；The hair fiber forms to be that cashmere is blended according to 20%~30% sheep's wool and surplus of mass percent meter.This simple process, the composite fibre item specially formed to hair fiber and acid fiber by polylactic carry out the processing of spray complex liquid to change its characteristic, keep its performance more excellent；After carrying out a series of processing and the progress drafting processing of composite fibre item to flax fiber item, then prolonged and twist the obtained linen blend yarn of process, Roving Frames and spinning process, then carry out longitude and latitude plain weave, obtains fabric.This fabric is soft, has good ventilative moisture absorption and wrinkle resistance.
Description
Technical field
The invention belongs to textile technology fields, and in particular to a kind of textile technology of the ventilative knitting fabric of moisture absorption.
Background technique
Flax fiber is the natural fiber that the mankind use earliest, is beam plant fiber, has natural spindle-type α-Fe2O3
With unique pectic substance bevel edge hole, unique ice is refreshing, absorbing sweat, breathes freely, low electrostatic, anti-corrosion function.Pure flax clothes wear to
The sendible temperature of people can and environment temperature differ 4~5 DEG C, being very suitable to summer wears, and people say that flax fiber is " fiber emperor
Afterwards ", it is a kind of all well and good selection that sucting wet air permeability fabric is produced in this, as substrate.
However, flax fiber is fiber most thin in crudefiber crop, fineness discreteness is big, length is different and long without ramie, fiber crops
Particle mostly fibrous fracture elongation simultaneously is low, leverages its product quality and application range.In trial it was found that using
Blended weave can be improved the quality of flax fiber type, be more widely applied it.
Summary of the invention
In view of the above problems, the present invention provides a kind of textile technology of the ventilative knitting fabric of moisture absorption, this works
Skill uses blended weave, and resulting knitting fabric is soft, has good ventilative moisture absorption and wrinkle resistance.
The technical solution adopted by the invention is as follows:
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following raw materials according in parts by weight: flax fiber
10~20 parts by weight, 5~10 parts of acid fiber by polylactic, 20~35 parts by weight of hair fiber；The hair fiber is according to quality hundred
Divide 20%~30% sheep's wool and surplus than counting to be that cashmere is blended to form.
Preferably, the textile technology of the ventilative knitting fabric of a kind of moisture absorption, it is following including in parts by weight
Raw material: 15 parts by weight of flax fiber, 8 parts of acid fiber by polylactic, 28 parts by weight of hair fiber；The hair fiber is according to quality hundred
Divide 25% sheep's wool and surplus than counting to be that cashmere is blended to form.
Preferably, the textile technology of the ventilative knitting fabric of a kind of moisture absorption, including following process steps:
S1. composite fibre item is made in the hair fiber and acid fiber by polylactic, spray complex liquid is placed 2 days；
S2. flax carded sliver is made by pickling-soda boiling-washing-softening-opening picking-comb fiber crops in flax fiber；
S3. composite fibre item and flax carded sliver are subjected to mixing in doubling step processing, obtain ripe bar；
S4. the ripe bar is prolonged and twists the obtained linen blend yarn of process, Roving Frames and spinning process；
S5. linen blend yarn is woven into fabric by plain weave by warp thread and weft yarn.
Preferably, the complex liquid by according to mass percent meter 1% lauric acid diethyl amide, 0.2% six
Sodium metaphosphate, 1.5% polylysine and 0.4% sulfamic acid and excess water mix.
Preferably, acid used in pickling described in the S2 is the H that concentration is 0.06~0.09%2SO4；Temperature is 20 DEG C, when
Between be 20~28min.
Preferably, soda boiling-washing-soft condition described in the S2 are as follows: primary, pick-up is washed at 100 DEG C
100%, then to boil 80~100min in bath raio 1:25 investment lye, pick-up 100%, the then hot wash 2 in 50~60 DEG C
It is secondary, it adds softening agent and carries out 20~30min immersion, pull out, cold water washing 2 times, dried at 70 DEG C.
Preferably, opening picking described in the S2-comb ramie stripes part are as follows: cotton rolling quantity is 380~400g/m；The cotton carding carded sliver is fixed
Amount is 15.5g/5m~20.5g/5m.
Preferably, caustic soda mass concentration is 8~10% in the lye, YY-6 refining agent mass concentration is 2~5%,
Urea quality concentration is 3~5%.
Preferably, the softening agent are as follows: polyethylene wax softening agent.
Beneficial effects of the present invention: the present invention provides a kind of textile technology of the ventilative knitting fabric of moisture absorption, this techniques
Simply, in the process, the processing of spray complex liquid is carried out to the composite fibre item that hair fiber is formed with acid fiber by polylactic to change
Its characteristic keeps its performance more excellent；By carrying out a series of processing and composite fibre item progress drafting to flax fiber item
After processing, then prolonged and twist the obtained linen blend yarn of process, Roving Frames and spinning process, then carry out longitude and latitude plain weave, is obtained
Fabric.This fabric is soft, has good ventilative moisture absorption and wrinkle resistance.
Specific embodiment
Embodiment of the present invention can be replaced by the difference of specific range based on the above technical solution,
Available numerous embodiment, therefore, several embodiments as described below are only merely the more excellent reality in numerous embodiment
Example is applied, any technology replacement done in above-mentioned technical proposal all belongs to the scope of protection of the present invention.
Embodiment 1
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following raw materials according in parts by weight: flax fiber
10 parts by weight, 5 parts of acid fiber by polylactic, 20 parts by weight of hair fiber；The hair fiber is according to the 20% of mass percent meter
Sheep's wool and surplus be that cashmere is blended forms.
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following process steps:
S1. composite fibre item is made in the hair fiber and acid fiber by polylactic, complex liquid is prepared, according to mass percent
Meter, by 1% lauric acid diethyl amide, 0.2% calgon, 1.5% polylysine, 0.4% sulfamic acid and excess water
It is uniformly mixed to get complex liquid, is then sprayed on composite fibre item, the placement of composite fibre item 2 days spare；
It S2. is 20 DEG C by flax fiber immersion temperature, the H that concentration is 0.06%2SO4Normal-temperature water is carried out after middle 20min to wash,
It is washed to primary, pick-up 100% at 100 DEG C again, then with bath raio 1:25 investment caustic soda mass concentration for 8%, YY-
80min, pick-up 100%, then at 50 DEG C are boiled in 6 lye that refining agent mass concentration is 2%, urea quality concentration is 3%
Middle hot wash 2 times adds polyethylene wax softening agent and carries out 20min immersion, pulls out, cold water washing 2 times, dries at 70 DEG C, into
Row opening picking-comb fiber crops processing, cotton rolling quantity 380g/m；Cotton carding weight of card sliver is 15.5g/5m, obtains flax carded sliver；
S3. composite fibre item and flax carded sliver are subjected to mixing in doubling step processing, obtain ripe bar；
S4. the ripe bar is prolonged and twists the obtained linen blend yarn of process, Roving Frames and spinning process；
S5. linen blend yarn is woven into fabric by plain weave by warp thread and weft yarn.
Embodiment 2
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following raw materials according in parts by weight: flax fiber
15 parts by weight, 8 parts of acid fiber by polylactic, 28 parts by weight of hair fiber；The hair fiber is according to the 25% of mass percent meter
Sheep's wool and surplus be that cashmere is blended forms.
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following process steps:
S1. composite fibre item is made in the hair fiber and acid fiber by polylactic, complex liquid is prepared, according to mass percent
Meter, by 1% lauric acid diethyl amide, 0.2% calgon, 1.5% polylysine, 0.4% sulfamic acid and excess water
It is uniformly mixed to get complex liquid, is then sprayed on composite fibre item, the placement of composite fibre item 2 days spare；
It S2. is 20 DEG C by flax fiber immersion temperature, the H that concentration is 0.07%2SO4Normal-temperature water is carried out after middle 25min to wash,
It is washed to primary, pick-up 100% at 100 DEG C again, then with bath raio 1:25 investment caustic soda mass concentration for 9%, YY-
90min, pick-up 100%, then at 55 DEG C are boiled in 6 lye that refining agent mass concentration is 3%, urea quality concentration is 4%
Middle hot wash 2 times adds polyethylene wax softening agent and carries out 25min immersion, pulls out, cold water washing 2 times, dries at 70 DEG C, into
Row opening picking-comb fiber crops processing, cotton rolling quantity 390g/m；Cotton carding weight of card sliver is 18.5g/5m, obtains flax carded sliver；
S3. composite fibre item and flax carded sliver are subjected to mixing in doubling step processing, obtain ripe bar；
S4. the ripe bar is prolonged and twists the obtained linen blend yarn of process, Roving Frames and spinning process；
S5. linen blend yarn is woven into fabric by plain weave by warp thread and weft yarn.
Embodiment 3
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following raw materials according in parts by weight: flax fiber
20 parts by weight, 10 parts of acid fiber by polylactic, 35 parts by weight of hair fiber；The hair fiber is according to the 30% of mass percent meter
Sheep's wool and surplus be that cashmere is blended forms.
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following process steps:
S1. composite fibre item is made in the hair fiber and acid fiber by polylactic, complex liquid is prepared, according to mass percent
Meter, by 1% lauric acid diethyl amide, 0.2% calgon, 1.5% polylysine, 0.4% sulfamic acid and excess water
It is uniformly mixed to get complex liquid, is then sprayed on composite fibre item, the placement of composite fibre item 2 days spare；
It S2. is 20 DEG C by flax fiber immersion temperature, the H that concentration is 0.09%2SO4Normal-temperature water is carried out after middle 28min to wash,
It is washed to primary, pick-up 100% at 100 DEG C again, be then 10% with bath raio 1:25 investment caustic soda mass concentration,
YY-6 refining agent mass concentration is 5%, boils 100min in the lye that urea quality concentration is 5%, and pick-up 100% then exists
Hot wash 2 times in 60 DEG C add polyethylene wax softening agent and carry out 30min immersion, pull out, cold water washing 2 times, dry at 70 DEG C
It is dry, carry out opening picking-comb fiber crops processing, cotton rolling quantity 400g/m；Cotton carding weight of card sliver is 20.5g/5m, obtains flax carded sliver；
S3. composite fibre item and flax carded sliver are subjected to mixing in doubling step processing, obtain ripe bar；
S4. the ripe bar is prolonged and twists the obtained linen blend yarn of process, Roving Frames and spinning process；
S5. linen blend yarn is woven into fabric by plain weave by warp thread and weft yarn.
Comparative example 1
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following raw materials according in parts by weight: flax fiber 1
Parts by weight, 5 parts of acid fiber by polylactic, 20 parts by weight of hair fiber；The hair fiber is 20% according to mass percent meter
Sheep's wool and surplus, which are that cashmere is blended, to be formed.
A kind of textile technology of the ventilative knitting fabric of moisture absorption, including following process steps:
S1. composite fibre item is made in the hair fiber and acid fiber by polylactic, complex liquid is prepared, according to mass percent
Meter, by 1% lauric acid diethyl amide, 0.2% calgon, 1.5% polylysine, 0.4% sulfamic acid and excess water
It is uniformly mixed to get complex liquid, is then sprayed on composite fibre item, the placement of composite fibre item 2 days spare；
It S2. is 20 DEG C by flax fiber immersion temperature, the H that concentration is 0.9g/L2SO4Normal-temperature water is carried out after middle 20min to wash,
It is washed to primary, pick-up 100% at 100 DEG C again, then with bath raio 1:25 investment caustic soda mass concentration for 8%, YY-
80min, pick-up 100%, then at 50 DEG C are boiled in 6 lye that refining agent mass concentration is 2%, urea quality concentration is 3%
Middle hot wash 2 times adds polyethylene wax softening agent and carries out 20min immersion, pulls out, cold water washing 2 times, dries at 70 DEG C, into
Row opening picking-comb fiber crops processing, cotton rolling quantity 380g/m；Cotton carding weight of card sliver is 15.5g/5m, obtains flax carded sliver；
S3. composite fibre item and flax carded sliver are subjected to mixing in doubling step processing, obtain ripe bar；
S4. the ripe bar is prolonged and twists the obtained linen blend yarn of process, Roving Frames and spinning process；
S5. linen blend yarn is woven into fabric by plain weave by warp thread and weft yarn.
Correlated performance test is carried out to above-described embodiment and the resulting fabric of comparative example, from comparative example it is found that flax fiber
Dosage directly affect the performance of final gained fabric；The resulting fabric of the present invention is soft, has good ventilative moisture absorption and resists
Wrinkle property, acquired results are as shown in table 1.
1 test result of table
The invention is not limited to specific embodiments above-mentioned.The present invention, which expands to, any in the present specification to be disclosed
New feature or any new combination, and disclose any new method or process the step of or any new combination.
Claims (9)
1. a kind of textile technology of the ventilative knitting fabric of moisture absorption, which is characterized in that including following raw materials according in parts by weight:
10~20 parts by weight of flax fiber, 5~10 parts of acid fiber by polylactic, 20~35 parts by weight of hair fiber；The hair fiber be by
20%~30% sheep's wool according to mass percent meter and surplus cashmere is blended forms.
2. a kind of textile technology of the ventilative knitting fabric of moisture absorption as described in claim 1, which is characterized in that including according to weight
The following raw materials according of number meter: 15 parts by weight of flax fiber, 8 parts of acid fiber by polylactic, 28 parts by weight of hair fiber；The hair fiber
It is that cashmere is blended for 25% sheep's wool and surplus according to mass percent meter to form.
3. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 1 or 2, which is characterized in that including following
Processing step:
S1. composite fibre item is made in the hair fiber and acid fiber by polylactic, spray complex liquid is placed 2 days；
S2. flax carded sliver is made by pickling-soda boiling-washing-softening-opening picking-comb fiber crops in flax fiber；
S3. composite fibre item and flax carded sliver are subjected to mixing in doubling step processing, obtain ripe bar；
S4. the ripe bar is prolonged and twists the obtained linen blend yarn of process, Roving Frames and spinning process；
S5. linen blend yarn is woven into fabric by plain weave by warp thread and weft yarn.
4. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 3, which is characterized in that the complex liquid by
According to 1% lauric acid diethyl amide, 0.2% calgon, 1.5% polylysine and 0.4% of mass percent meter
Sulfamic acid and excess water mix.
5. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 3, which is characterized in that pickling described in S2
Acid used is the H that concentration is 0.06~0.09%2SO4；Temperature is 20 DEG C, and the time is 20~28min.
6. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 3, which is characterized in that described in the S2
Soda boiling-washing-soft condition are as follows: primary, pick-up 100% is washed at 100 DEG C, then to boil in bath raio 1:25 investment lye
80~100min, pick-up 100%, then hot wash 2 times in 50~60 DEG C add softening agent and carry out 20~30min immersion,
It pulls out, cold water washing 2 times, is dried at 70 DEG C.
7. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 3, which is characterized in that described in the S2
Opening picking-comb ramie stripes part are as follows: cotton rolling quantity is 380~400g/m；Cotton carding weight of card sliver is 15.5g/5m~20.5g/5m.
8. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 6, which is characterized in that severe in the lye
Property sodium mass concentration is 8~10%, YY-6 refining agent mass concentration is 2~5%, urea quality concentration is 3~5%.
9. a kind of textile technology of the ventilative knitting fabric of moisture absorption as claimed in claim 6, which is characterized in that the softening agent
Are as follows: polyethylene wax softening agent.