CN110241501A - A kind of super cotton-simulated terylene fabric lining of hydrophily - Google Patents
A kind of super cotton-simulated terylene fabric lining of hydrophily Download PDFInfo
- Publication number
- CN110241501A CN110241501A CN201910446616.4A CN201910446616A CN110241501A CN 110241501 A CN110241501 A CN 110241501A CN 201910446616 A CN201910446616 A CN 201910446616A CN 110241501 A CN110241501 A CN 110241501A
- Authority
- CN
- China
- Prior art keywords
- filament
- fiber
- polyester
- hydrophily
- long filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of super cotton-simulated terylene fabric linings of hydrophily, including embryo cloth and preparation method, the embryo cloth is weaved as fabric construction using plain weave or twill-weave by warp and weft and is formed, the warp is using Hydrophilic Polyester Fiber long filament and silk fiber is blended forms, and the weft is by eliminating the unusual smell polyester filament and chitin fiber blended forms.The super cotton-simulated terylene fabric lining of hydrophily proposed by the present invention, FDY filament is merged using wool powder, atoleine is borrowed in fusion process ultimately forms the Hydrophilic Polyester Fiber long filament of high porosity surface texture wool powder and the polyester filament that eliminates the unusual smell, it is blended using chitin fiber and bamboo charcoal fiber difference again, final composition embryo cloth, since wool powder has highly porous characteristic with highly hygroscopic wet putting and the Hydrophilic Polyester Fiber long filament and the long filament that eliminates the unusual smell, the fabric for forming the super imitative cotton has the ability of high-efficiency water-absorbing ability moisture absorption.
Description
Technical field
The present invention relates to garment material technical field more particularly to a kind of super cotton-simulated terylene fabric linings of hydrophily.
Background technique
The fabric of hot our big more options ventilation and perspiration functions of summer better than general cotton fabric, especially pantie-corselette,
The fabric of this kind of personal clothing of nightwear primarily requires to be the quick moisture absorbing and sweat releasing of energy, while having certain warmth retention property, such as: cotton clothing
Object, since moisture absorption is without perspiring, sweat is attached to skin, fever easy to catch cold, and the probability of adjoint eczema and heat rash is also significantly
It improves;Chemical fibre class clothing, it is bright in luster although washing Yi Gan well, it is airtight, and have certain irritation to skin.Especially
It is for allergic constitution person, it is easier to cause allergy.
We research and develop a kind of super cotton-simulated terylene fabric lining of hydrophily thus, make its specific high-hydrophilic and ventilation and perspiration function simultaneously
And do not generate the effect of sweat peculiar smell.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and the super imitative cotton of a kind of hydrophily proposed is washed
Synthetic fibre fabric lining.
To achieve the goals above, present invention employs following technical solutions:
A kind of super cotton-simulated terylene fabric lining of hydrophily, including embryo cloth, the embryo cloth is by warp and weft with plain weave or twill
Tissue is weaved to be formed as fabric construction, and the warp is using Hydrophilic Polyester Fiber long filament and silk fiber is blended forms, described
Weft is by eliminating the unusual smell polyester filament and chitin fiber blended forms;The Hydrophilic Polyester Fiber long filament contains weight percent
Are as follows: 70-85% polyester FDY long filament and 15-30% wool powder;The average particle size of the wool powder is 20-30 μm, described except different
Taste polyester filament contains weight percent are as follows: 60-70% polyester FDY long filament and 30-40% bamboo charcoal fiber.
Preferably, the fiber number of the warp is 22.2dtex, and density is 316-334 root;The weft is
21.5dtex, and density is 292-310 root;The section of the polyester FDY long filament is " ten " font.
Preferably, the super cotton-simulated terylene fabric lining of hydrophily preparation method the following steps are included:
S1, the preparation of wool powder: the wool after organic solvent degreasing is used into vacuum machine method, sets vacuum degree are as follows: 2666pa,
It is ground into wool powder, control wool powder size is 10-20um, fibre-like morphology;
S2, production Hydrophilic Polyester Fiber long filament: the obtained wool powder of S1 and FDY filament melting is blended then molten with atoleine
Melt spinning, is immersed in ethane after stretching heat treatment and dissolves atoleine, obtain the porous hydrophilic terylene that porosity is up to 25%
Long filament;
S3, the polyester filament that eliminates the unusual smell is made: the obtained wool powder of S1 and FDY filament and bamboo charcoal fiber melting is blended, it is
Again with atoleine melt spinning, it is immersed in ethane after stretching heat treatment and dissolves atoleine, obtained porosity and be up to 25%
Porosity eliminates the unusual smell polyester filament;
S4, weaving embryo cloth: by Hydrophilic Polyester Fiber long filament and silk fiber in the blended warp for being 22.2dtex at fiber number of 8:2 ratio
Line, the weft for being 21.5dtex in the blended long fibre of 7:3 ratio by eliminate the unusual smell polyester filament and chitin fiber, by warp and latitude
Line is weaved to form embryo cloth using plain weave or twill-weave as fabric construction;
S5, it is directed to hydrophily final finishing: uniformly being melted using Ou Tefei hydrophilic softening agent HSD by 20g/L and ice vinegar 0.5g/L and water
It closes, mixed solution temperature is heated up to 130 DEG C, the embryo cloth of cold dome, washing, drying and shaping is placed in solution and stands 90min;It is right
Do hydrophily hydroscopic fast-drying function treatment in embryo cloth surface.
The invention has the following advantages:
1, the super cotton-simulated terylene fabric lining of hydrophily proposed by the present invention merges FDY filament using wool powder, in fusion process
It borrows atoleine and ultimately forms the Hydrophilic Polyester Fiber long filament of high porosity surface texture wool powder and the polyester filament that eliminates the unusual smell,
It is blended using chitin fiber and bamboo charcoal fiber difference again, embryo cloth is finally formed, since wool powder has highly hygroscopic wet putting
With the Hydrophilic Polyester Fiber long filament and the long filament that eliminates the unusual smell with highly porous characteristic, the fabric for forming the super imitative cotton has efficient
The ability of water absorbing capacity moisture absorption.
2, the super cotton-simulated terylene fabric lining of hydrophily proposed by the present invention is proposed close using Ou Tefei by preparation method
Water softening agent HSD and ice vinegar for the fabric moisture absorbable and breathable finishing, using Ou Tefei hydrophilic softening agent HSD molecular structure with wash
The identical phenyl ring of synthetic fibre molecular structure, under high temperature action molecule segment by anchor jail on the surface of terylene, by the water repellent of terylene itself
Type surface becomes durable hydrophilic surface, but since the water repellent property of terylene component itself is not changed, so absorb
Moisture cracking can be dispersed into atmosphere again, thus the fabric while hydrophilic with the performance of quick-drying wet-permeable.
3, the super cotton-simulated terylene fabric lining of hydrophily proposed by the present invention is made by the moisture absorbable and breathable finishing of preparation method
Moisture in sweat, which is quickly eliminated, to be prevented from breeding bacterium, by setting chitin fiber and bamboo charcoal fiber, inhibits its in sweat
He gives off a peculiar smell at ingredient, so that the super cotton-simulated terylene fabric lining of the hydrophily be made to have the effect of eliminating the unusual smell.
Detailed description of the invention
Fig. 1 is a kind of structural schematic diagram of the super cotton-simulated terylene fabric lining of hydrophily proposed by the present invention.
In figure: 1 embryo cloth, 2 warps, 3 wefts.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
In the description of the present invention, it is to be understood that, term " on ", "lower", "front", "rear", "left", "right", "top",
The orientation or positional relationship of the instructions such as "bottom", "inner", "outside" is to be based on the orientation or positional relationship shown in the drawings, merely to just
In description the present invention and simplify description, rather than the device or element of indication or suggestion meaning must have a particular orientation, with
Specific orientation construction and operation, therefore be not considered as limiting the invention.
One, embodiment part
Embodiment 1
A kind of super cotton-simulated terylene fabric lining of hydrophily, including embryo cloth 1, embryo cloth 1 is by warp 2 and weft 3 with plain weave or twill
Tissue is weaved to be formed as fabric construction, and warp 2 is using Hydrophilic Polyester Fiber long filament and silk fiber is blended forms, warp 2
Fiber number is 22.2dtex, and density is 316-334 root;Weft 3 be by eliminating the unusual smell polyester filament and chitin fiber blended forms,
Weft 3 is 21.5dtex, and density is 292-310 root;Hydrophilic Polyester Fiber long filament contains weight percent are as follows: 70-85% terylene
FDY filament and 15-30% wool powder;The average particle size of wool powder is 20-30 μm, and the polyester filament that eliminates the unusual smell contains gravity hundred
Divide ratio are as follows: 60-70% polyester FDY long filament and 30-40% bamboo charcoal fiber;The section of polyester FDY long filament is " ten " font.
A kind of preparation method of the super cotton-simulated terylene fabric lining of hydrophily the following steps are included:
S1, the preparation of wool powder: the wool after organic solvent degreasing is used into vacuum machine method, sets vacuum degree are as follows: 2666pa,
It is ground into wool powder, control wool powder size is 10-20um, fibre-like morphology;
S2, production Hydrophilic Polyester Fiber long filament: the obtained wool powder of S1 and FDY filament melting is blended then molten with atoleine
Melt spinning, is immersed in ethane after stretching heat treatment and dissolves atoleine, obtain the porous hydrophilic terylene that porosity is up to 25%
Long filament;
S3, the polyester filament that eliminates the unusual smell is made: the obtained wool powder of S1 and FDY filament and bamboo charcoal fiber melting is blended, it is
Again with atoleine melt spinning, it is immersed in ethane after stretching heat treatment and dissolves atoleine, obtained porosity and be up to 25%
Porosity eliminates the unusual smell polyester filament;
S4, weaving embryo cloth: by Hydrophilic Polyester Fiber long filament and silk fiber in the blended warp for being 22.2dtex at fiber number of 8:2 ratio
2, the weft 3 for being 21.5dtex in the blended long fibre of 7:3 ratio by eliminate the unusual smell polyester filament and chitin fiber, by 2 He of warp
Weft 3 is weaved to form embryo cloth 3 as fabric construction using plain weave or twill-weave;
S5, it is directed to hydrophily final finishing: uniformly being melted using Ou Tefei hydrophilic softening agent HSD by 20g/L and ice vinegar 0.5g/L and water
It closes, mixed solution temperature is heated up to 130 DEG C, the embryo cloth 1 of cold dome, washing, drying and shaping is placed in solution and stands 90min;
Hydrophily hydroscopic fast-drying function treatment is done to 1 surface of embryo cloth.
Embodiment 2
A kind of super cotton-simulated terylene fabric lining of hydrophily, including embryo cloth 1, embryo cloth 1 is by warp 2 and weft 3 with plain weave or twill
Tissue is weaved to be formed as fabric construction, and warp 2 is using Hydrophilic Polyester Fiber long filament and silk fiber is blended forms, warp 2
Fiber number is 21.3dtex, and density is 310-320 root;Weft 3 be by eliminating the unusual smell polyester filament and chitin fiber blended forms,
Weft 3 is 22dtex, and density is 280-290 root;Hydrophilic Polyester Fiber long filament contains weight percent are as follows: 65-80% terylene
FDY filament and 20-35% wool powder;The average particle size of wool powder is 15-20 μm, and the polyester filament that eliminates the unusual smell contains gravity hundred
Divide ratio are as follows: 65-75% polyester FDY long filament and 25-35% bamboo charcoal fiber;The section of polyester FDY long filament is " Y " font.
A kind of preparation method of the super cotton-simulated terylene fabric lining of hydrophily the following steps are included:
S1, the preparation of wool powder: the wool after organic solvent degreasing is used into vacuum machine method, sets vacuum degree are as follows: 2666pa,
It is ground into wool powder, control wool powder size is 10-20um, fibre-like morphology;
S2, production Hydrophilic Polyester Fiber long filament: the obtained wool powder of S1 and FDY filament melting is blended then molten with atoleine
Melt spinning, is immersed in ethane after stretching heat treatment and dissolves atoleine, obtain the porous hydrophilic terylene that porosity is up to 25%
Long filament;
S3, the polyester filament that eliminates the unusual smell is made: the obtained wool powder of S1 and FDY filament and bamboo charcoal fiber melting is blended, it is
Again with atoleine melt spinning, it is immersed in ethane after stretching heat treatment and dissolves atoleine, obtained porosity and be up to 25%
Porosity eliminates the unusual smell polyester filament;
S4, weaving embryo cloth: by Hydrophilic Polyester Fiber long filament and silk fiber in the blended warp for being 21.3dtex at fiber number of 7:3 ratio
2, the weft 3 for being 22dtex in the blended long fibre of 7:3 ratio by eliminate the unusual smell polyester filament and chitin fiber, by warp 2 and latitude
Line 3 is weaved to form embryo cloth 3 as fabric construction using plain weave or twill-weave;
S5, it is directed to hydrophily final finishing: uniformly being melted using Ou Tefei hydrophilic softening agent HSD by 20g/L and ice vinegar 0.5g/L and water
It closes, mixed solution temperature is heated up to 100 DEG C, the embryo cloth 1 of cold dome, washing, drying and shaping is placed in solution and stands 120min;
Hydrophily hydroscopic fast-drying function treatment is done to 1 surface of embryo cloth.
Two, detection part
Choose with embodiment 1 and compared with super imitative cotton color that embodiment 2 produces, grammes per square metre similar in fabric out of ink compare test
Obtain data:
Ultimate strength presses GB/T3923.1-1997 " textile fabric tensile property part 1 ultimate strength and elongation at break
Measurement " tested;Tearing brute force is by GB/T3917.2-2009 " textile fabric tear properties part 2: pants type examination
The measurement of sample (single seam) tearing brute force " it is tested;Stiffness presses ASTM D1388-200- " fabric endures with all one's will type test method "
Option A is tested;Size changing rate is by the GB/T 8629-2001 " preparation of sample, label when measurement fabric size variation
And measurement " and GB/T 8629-2001 " when Textile Test using home washings and drying program " tested, test structure
As follows,
By table 1, it can be seen that, super cotton-simulated terylene fabric lining has ultimate strength similar with pure cotton fabric, and force value is more than
National product standard provides 200N requirement, and super cotton-simulated terylene fabric lining tears fracture with stronger than pure cotton fabric
Strongly;Super cotton-simulated terylene fabric lining has regain more smaller than pure cotton fabric, has the water more more excellent than pure cotton fabric
Wash shrinkage.
By table 2, it can be seen that, the moisture pick-up properties of super cotton-simulated terylene fabric lining is excellent, has reached and has been more than pure cotton
The quick-drying of the level of fabric, super cotton-simulated terylene fabric lining is essentially identical to pure cotton fabric.
The present invention merges FDY filament using wool powder, borrows atoleine in fusion process and ultimately forms high porosity
The Hydrophilic Polyester Fiber long filament of surface texture wool powder and the polyester filament that eliminates the unusual smell, then using chitin fiber and bamboo charcoal fiber point
It is not blended, embryo cloth is finally formed, since wool powder has highly hygroscopic wet putting and the Hydrophilic Polyester Fiber long filament and the length that eliminates the unusual smell
Silk has highly porous characteristic, and the fabric for forming the super imitative cotton has the ability of high-efficiency water-absorbing ability moisture absorption;Using Ou Te
Luxuriant and rich with fragrance hydrophilic softening agent HSD and ice vinegar utilize Ou Tefei hydrophilic softening agent HSD molecular structure for the moisture absorbable and breathable finishing of the fabric
Phenyl ring identical with terylene molecular structure, under high temperature action molecule segment by anchor jail on the surface of terylene, by terylene itself
Water repellent type surface becomes durable hydrophilic surface, but since the water repellent property of terylene component itself is not changed, so inhaling
The moisture of receipts cracking can be dispersed into atmosphere again, thus the fabric while hydrophilic with the performance of quick-drying wet-permeable.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (3)
1. a kind of super cotton-simulated terylene fabric lining of hydrophily, including embryo cloth (1), it is characterised in that: the embryo cloth (1) is by warp
(2) and weft (3) is weaved to be formed as fabric construction using plain weave or twill-weave, and the warp (2) is washed using hydrophily
Synthetic fibre long filament and silk fiber is blended forms, the weft (3) are by eliminating the unusual smell polyester filament and chitin fiber blended forms;Institute
It states Hydrophilic Polyester Fiber long filament and contains weight percent are as follows: 70-85% polyester FDY long filament and 15-30% wool powder;The wool powder
End average particle size be 20-30 μm, the polyester filament that eliminates the unusual smell contains weight percent are as follows: 60-70% polyester FDY long filament and
30-40% bamboo charcoal fiber.
2. the super cotton-simulated terylene fabric lining of a kind of hydrophily according to claim 1, it is characterised in that: the warp (2)
Fiber number be 22.2dtex, and density be 316-334 root;The weft (3) is 21.5dtex, and density is 292-310 root,
The section of the polyester FDY long filament is " ten " font.
3. a kind of preparation method of the super cotton-simulated terylene fabric lining of hydrophily according to claim 1 the following steps are included:
S1, the preparation of wool powder: the wool after organic solvent degreasing is used into vacuum machine method, sets vacuum degree are as follows: 2666pa,
It is ground into wool powder, control wool powder size is 10-20um, fibre-like morphology;
S2, production Hydrophilic Polyester Fiber long filament: the obtained wool powder of S1 and FDY filament melting is blended then molten with atoleine
Melt spinning, is immersed in ethane after stretching heat treatment and dissolves atoleine, obtain the porous hydrophilic terylene that porosity is up to 25%
Long filament;
S3, the polyester filament that eliminates the unusual smell is made: the obtained wool powder of S1 and FDY filament and bamboo charcoal fiber melting is blended, it is
Again with atoleine melt spinning, it is immersed in ethane after stretching heat treatment and dissolves atoleine, obtained porosity and be up to 25%
Porosity eliminates the unusual smell polyester filament;
S4, weaving embryo cloth: by Hydrophilic Polyester Fiber long filament and silk fiber in the blended warp for being 22.2dtex at fiber number of 8:2 ratio
(2), the weft (3) for being 21.5dtex in the blended long fibre of 7:3 ratio by eliminate the unusual smell polyester filament and chitin fiber, by warp
(2) and weft (3) is weaved to form embryo cloth (3) using plain weave or twill-weave as fabric construction;
S5, it is directed to hydrophily final finishing: uniformly being melted using Ou Tefei hydrophilic softening agent HSD by 20g/L and ice vinegar 0.5g/L and water
It closes, mixed solution temperature is heated up to 130 DEG C, the embryo cloth (1) of cold dome, washing, drying and shaping is placed in solution and is stood
90min;Hydrophily hydroscopic fast-drying function treatment is done to embryo cloth (1) surface.