CN110239171A - Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof - Google Patents
Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof Download PDFInfo
- Publication number
- CN110239171A CN110239171A CN201910518553.9A CN201910518553A CN110239171A CN 110239171 A CN110239171 A CN 110239171A CN 201910518553 A CN201910518553 A CN 201910518553A CN 110239171 A CN110239171 A CN 110239171A
- Authority
- CN
- China
- Prior art keywords
- fabric
- antistatic
- electromagnetic radiation
- preparation
- radiation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses Antistatic electromagnetic radiation prevention garment fabrics and preparation method thereof; manufacturing process is simple and convenient; elasticity is good for fabric after production; the advantages that pro-skin is breathed freely, radiation resistance and excellent antistatic property; the various radiation in life can effectively be stopped; such as radiation of ultraviolet light, computer, mobile phone radiation, micro-wave oven radiation play the role of anti-spoke protection, are a Antistatic radiation-proof fabrics with comprehensive performance.
Description
Technical field
The present invention relates to fabric production method more particularly to Antistatic electromagnetic radiation prevention garment fabrics and preparation method thereof.
Background technique
In view of the harm of electromagnetic radiation and electrostatic, being developed much reduces its textile fabric endangered, including woollen sweater,
Underwear, work clothes etc..In recent years, studying more is to prepare textile using metal wire mixed spinning technique, to reach anti-electric
Magnetic radiation and antistatic effect.Wire has anti-electromagnetic radiation, not electromagnetic wave absorption, permanence antistatic, anti-oxidant, resistance to
The function of corrosion, wire is applied in weaving, and manufactured goods are just provided with anti-electromagnetic radiation and antistatic function simultaneously.
Wire in the prior art, which spins, to be haveed the defects that more, and mainly have: the metal component of wire is easy to fall,
It pollutes;It is poor with the binding ability of textile fabric, it is easy to separation;Soft comfortable is poor and Radiation-proof antistatic performance
Not high, in view of disadvantages described above, it is really necessary to design Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof.
Summary of the invention
Technical problem to be solved by the present invention lies in: Antistatic electromagnetic radiation prevention garment fabric and its production side are provided
Method, to solve the problems, such as that background technique proposes.
1, in order to solve the above technical problems, the technical scheme is that the group of Antistatic electromagnetic radiation prevention garment fabric
Become: terylene, conductive fiber, silver fiber fabric, natural material fabric.
2, the production method of Antistatic electromagnetic radiation prevention garment fabric sequentially includes the following steps:
(1) it works out: two kinds of raw materials of terylene and conductive fiber is worked out, with this by the terylene and conduction after establishment
Fiber forms Antistatic Fabric;
(2) it impregnates: the Antistatic Fabric after establishment being put into the container equipped with clear water and is impregnated;
(3) it dries: the Antistatic Fabric after immersion being subjected to drying and processing using drying equipment;
(4) examine: using electrostatic apparatus to after drying Antistatic Fabric carry out electrostatic inspection processing, tested with this resist it is quiet
The antistatic property of electric fabric;
(5) secondary establishment: silver fiber fabric and natural material fabric are worked out, with this by the silver fiber after establishment
Fabric and natural material fabric form anti-electromagnetic radiation fabric;
(6) it tests: resistance value test being carried out to anti-electromagnetic radiation fabric using multimeter, anti-electromagnetic radiation face is tested with this
The shielding property of material;
(7) it sutures: the fabric of the Antistatic Fabric after inspection and the anti-electromagnetic radiation after test is subjected to stitching processing, with
This obtains the garment material of antistatic anti-electromagnetic radiation.
Further, the time impregnated in described (2) soaking step is 10min.
Further, the time dried in described (3) baking step is 5min.
Further, natural material fabric is silk in described (5) the secondary establishment step.
Compared with prior art, Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof, manufacturing process are simply square
Just, the advantages that elasticity is good for the fabric after production, pro-skin, breathes freely, radiation resistance and excellent antistatic property, can effectively stop to give birth to
Various radiation in work, such as the radiation of ultraviolet light, computer, mobile phone radiation, micro-wave oven radiation, play the role of anti-spoke protection, are
A Antistatic radiation-proof fabric with comprehensive performance.
Detailed description of the invention
Fig. 1 is production flow diagram of the present invention
Specific embodiment
Hereinafter, a variety of specific details are elaborated, in order to provide to the saturating of the concept for constituting described embodiment basis
Thorough understanding.However, it will be apparent to those skilled in the art that described embodiment can be in these no specific details
In some or all situations get off practice.In other cases, well-known processing step is not specifically described.
Embodiment
The Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof that the present embodiment is enumerated, is made as follows, will
Two kinds of raw materials of terylene and conductive fiber are worked out, with this by after establishment terylene and conductive fiber form antistatic face
Material, the Antistatic Fabric after establishment is put into the container equipped with clear water and is impregnated, will be anti-after immersion using drying equipment
Electrostatic fabric carries out drying and processing, carries out electrostatic inspection processing to the Antistatic Fabric after drying using electrostatic apparatus, is surveyed with this
The antistatic property for trying Antistatic Fabric, silver fiber fabric and natural material fabric are worked out, will be after establishment with this
Silver fiber fabric and natural material fabric form anti-electromagnetic radiation fabric, carry out electricity to anti-electromagnetic radiation fabric using multimeter
Resistance value test, the shielding property of anti-electromagnetic radiation fabric is tested with this, is prevented by the Antistatic Fabric after inspection and after test
The fabric of electromagnetic radiation carries out stitching processing, obtains the garment material of antistatic anti-electromagnetic radiation with this.
The Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof, manufacturing process is simple and convenient, the fabric after production
The advantages that elasticity is good, pro-skin, breathes freely, radiation resistance and excellent antistatic property, can effectively stop the various radiation in life,
Anti- spoke protection is played the role of in such as radiation of ultraviolet light, computer, mobile phone radiation, micro-wave oven radiation, is a with comprehensive performance
Antistatic radiation-proof fabric.
The present invention is not limited to above-mentioned specific embodiment, those skilled in the art from the above idea,
Without creative labor, the various transformation made are within the scope of the present invention.
Claims (5)
1. Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof, which is characterized in that the antistatic anti-electromagnetic radiation
The composition of garment material are as follows: terylene, conductive fiber, silver fiber fabric, natural material fabric.
2. Antistatic electromagnetic radiation prevention garment fabric and preparation method thereof, it is characterised in that: sequentially include the following steps:
(1) it works out: two kinds of raw materials of terylene and conductive fiber is worked out, with this by the terylene and conductive fiber after establishment
Form Antistatic Fabric;
(2) it impregnates: the Antistatic Fabric after establishment being put into the container equipped with clear water and is impregnated;
(3) it dries: the Antistatic Fabric after immersion being subjected to drying and processing using drying equipment;
(4) it examines: electrostatic inspection processing being carried out to the Antistatic Fabric after drying using electrostatic apparatus, antistatic face is tested with this
The antistatic property of material;
(5) secondary establishment: silver fiber fabric and natural material fabric are worked out, with this by the silver fiber fabric after establishment
And natural material fabric forms anti-electromagnetic radiation fabric;
(6) it tests: resistance value test being carried out to anti-electromagnetic radiation fabric using multimeter, anti-electromagnetic radiation fabric is tested with this
Shielding property;
(7) it sutures: the fabric of the Antistatic Fabric after inspection and the anti-electromagnetic radiation after test being subjected to stitching processing, is obtained with this
To the garment material of antistatic anti-electromagnetic radiation.
3. Antistatic electromagnetic radiation prevention garment fabric according to claim 2 and preparation method thereof, it is characterised in that described
(2) soaking step in time for impregnating be 10min.
4. Antistatic electromagnetic radiation prevention garment fabric according to claim 2 and preparation method thereof, it is characterised in that described
(3) baking step in time for drying be 5min.
5. Antistatic electromagnetic radiation prevention garment fabric according to claim 2 and preparation method thereof, it is characterised in that described
(5) secondary establishment step in natural material fabric be silk.