CN110205795A - Prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric - Google Patents
Prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric Download PDFInfo
- Publication number
- CN110205795A CN110205795A CN201910493595.1A CN201910493595A CN110205795A CN 110205795 A CN110205795 A CN 110205795A CN 201910493595 A CN201910493595 A CN 201910493595A CN 110205795 A CN110205795 A CN 110205795A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven fabric
- dyeing
- prosperous
- finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, include the following steps: S1, desizing;S2, modification;S3, sizing;S4, dyeing: the woven fabric after drying and shaping in step S3 is impregnated in color pond, and concentration dye liquor is slowly added into color pond, carries out dyeing processing, then, bakes fixation;S5, cleaning: the woven fabric after baking fixation in step S4 is rinsed with clear water, then carries out reduction cleaning with reduction cleaning liquid;S6, final finishing: the woven fabric after reduction cleaning in step S5 is taken out, and is dehydrated, air-dries processing, post-finishing liquid is sprayed, to get woven fabric product after drying.The prosperous synthetic fibre T3000 of present invention process production is greatly improved with low elastic polyester filament intertexture woven fabric product moisture pick-up properties, and dirt-removing power is promoted, and the COLOR COMPOSITION THROUGH DISTRIBUTION of woven fabric is uniform, and the color difference between cloth is small, elastic stability, reliable product quality.
Description
Technical field
The present invention relates to the whole dyeing technique field of woven fabric, specifically prosperous synthetic fibre T3000 and low elastic polyester filament intertexture woven fabric connect
Continuous dyeing and finishing technology.
Background technique
Prosperous synthetic fibre T-3000 fiber is the compound bullet elastomer of novel polyether rouge, which has excellent elasticity and elastic recovery
Rate, soft, sun-resistant chlorine-resistant drift, hydroscopic fast-drying are good.It is processed into prosperous synthetic fibre T3000 and low elastic polyester filament intertexture cloth fabric
Afterwards, have the advantages that two kinds of fibers, have the characteristics that intensity is high, elongation is good, bulk softness, good hand feeling, shape is well-pressed;Height returns
Bullet and elastic lasting stability, broadwise elasticity is up to 20%;Only need 150 DEG C of sizings, low-carbon environment-friendly;Hydroscopic fast-drying wicks in 30 minutes
Height reaches 20cm;Color fastness is high, and chlorine-resistant floats not yellowing;Cloth cover is smooth smooth, wash and wear, and dimensionally stable is wear-resistant, anti-fluffing
Pilling, it is dust-proof antistatic, there is the refreshing sense of ice after dress, there is luster effect, taking is comfortable, and it is moderate, it is a kind of novel
Functional textile fabric.The appearance of the product solves the weakness and deficiency of original spandex stretch fabric, such as final finishing is afraid of
Chlorine drift, bad sizing, elastic instability, elasticity is superfluous, crease easily crimping etc..Prosperous synthetic fibre T3000 and DTY interwoven performance is excellent
It is different, can be applied to outdoor sports apparel, easy dress, fashionable dress, tooling novel fabric, future market has a extensive future.
However, prosperous synthetic fibre T3000 interweaves with low elastic polyester filament, the woven fabric detergency ability to be formed is poor, easy sticking oil stain, wherein
Polyester fiber can have the problems such as poor dyeing effect, poor color fastness, influenced tatting cloth fabric entirety dyeing efficiency and
Service life.
Summary of the invention
The purpose of the present invention is to provide prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, with solution
Certainly the problems mentioned above in the background art.
To achieve the above object, the invention provides the following technical scheme:
Prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, include the following steps:
S1, desizing: woven fabric is impregnated in desizing solution, carries out desizing treatment, after the completion of processing, clot is banked up, so
Afterwards, it is embathed with hot water;
S2, modification: the woven fabric after embathing in step S1 is put into microorganism modification liquid, carries out microorganism
Modification;
S3, sizing: the woven fabric after modification in step S2 is taken out, and handles removal terylene face by ultrasonic oscillation
The microorganism adhered on material, then, drying and shaping, drying temperature is 110-120 DEG C;
S4, dyeing: the woven fabric after drying and shaping in step S3 is impregnated in color pond, is slowly added into color pond
Dye liquor is concentrated, carries out dyeing processing, then, bakes fixation;
S5, cleaning: the woven fabric after baking fixation in step S4 is rinsed with clear water, then is restored with reduction cleaning liquid
Cleaning;
S6, final finishing: the woven fabric after reduction cleaning in step S5 is taken out, and is dehydrated, air-dries processing, whole after spraying
Liquid is managed, to get woven fabric product after drying.
As a further solution of the present invention: desizing treatment temperature is 80-85 DEG C in the step S1, the desizing treatment time
It as mass fraction include sodium hydroxide 1.5-1.8%, sodium chloride 0.2-0.5%, quaternary ammonium salt in desizing solution for 20-30min
Surfactant 1.1-1.3%, neopelex 0.1-0.3%, remaining is water;The hot water temperature embathed is 85-90
DEG C, embathing the time is 5-10min.
As a further solution of the present invention: in the step S2 in microorganism modification liquid microorganism modifying agent matter
Amount score is 13-16%, the mass fraction of polyether polyol is 2-5%, the mass fraction of glucose is 0.4-0.6%, albumen
The mass fraction of peptone is 0.1-0.3%, remaining is water, wherein microorganism modifying agent includes 1-3 parts of yeast, rhizopus 15-18
Unicellular bacterium 1.1-1.3 parts, 28-31 parts of branch bacterium of Mycotoruloides column of part, vacation;Modification treatment temperature is 40-45 DEG C, when modification
Between be 120-130h.
As a further solution of the present invention: the concentration of the disperse dyes in the step S4 in color pond is 1.8-
2.1g/L, dyeing temperature are maintained at 85-90 DEG C, dyeing time 40-45min, be concentrated dye liquor the preparation method comprises the following steps: by weight
Number by 8-11 parts of dispersing agent, 6-9 parts of levelling agent, 2-5 parts of sodium chloride, 7-10 parts of sodium carbonate, 3-5 parts of zinc oxide,
5-8 parts of acetic acid, 2-5 parts of migration inhibitor, 23-27 parts of disperse dyes are added sequentially to 100-120 parts of distilled water, stirring
It is uniformly mixed, concentration dye liquor is made, after the completion of dyeing, take out woven fabric, carry out baking fixation, stoving temperature is 130-140 DEG C.
As a further solution of the present invention: reduction cleaning liquid the preparation method comprises the following steps: in parts by weight in the step S5
By 25-28 parts of reduction cleaner, 9-11 parts of sodium metasilicate, 2-5 parts of glacial acetic acid, 11-13 parts of anhydrous sodium sulphate and 3-6 parts
Magnesium chloride sequentially adds in 250-300 parts of distilled water, is uniformly mixed, and reduction cleaning liquid is made, and reduction cleaning temperature is
95-100 DEG C, the reduction cleaning time is 15-20min.
As a further solution of the present invention: post-finishing liquid in the step S6 the preparation method comprises the following steps: in parts by weight
7-10 parts of antistatic agent and 5-8 parts of moisture control agent LD-9020 are added in 120-130 parts of distilled water, mixed
After closing uniformly, post-finishing liquid is made, quantity for spray of the post-finishing liquid on woven fabric is 25-30g/m2。
As a further solution of the present invention: the migration inhibitor uses laruyl alcohol acrylate.
As a further solution of the present invention: the reduction cleaner uses the compound of sulfites compound.
Compared with prior art, the beneficial effects of the present invention are: slurry is removed by desizing treatment, after modification
The surface pilling effect of prosperous synthetic fibre T3000 and low elastic polyester filament intertexture woven fabric be effectively improved, moisture pick-up properties has obtained greatly
Big to improve, lipophilicity decline, dirt-removing power is improved, it helps the dyeing effect of enhancing later period dyeing improves production
Dyeing efficiency and woven fabric whole service life;Woven fabric COLOR COMPOSITION THROUGH DISTRIBUTION after dyeing is uniform, the color difference between cloth
Small, glossiness is good, elastic stability, reliable product quality.The prosperous synthetic fibre T3000 and low elastic polyester filament intertexture shuttle of present invention process production
Woven fabric product moisture pick-up properties is greatly improved, and dirt-removing power is promoted, and the COLOR COMPOSITION THROUGH DISTRIBUTION of woven fabric is uniform, the color difference between cloth
It is small, elastic stability, reliable product quality.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1:
Prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, include the following steps:
S1, desizing: woven fabric is impregnated in desizing solution, carries out desizing treatment, after the completion of processing, clot is banked up, so
Afterwards, it is embathed with hot water;
Wherein, desizing treatment temperature is 80 DEG C, and the desizing treatment time is 20min, is wrapped as mass fraction in desizing solution
Sodium hydroxide 1.5%, sodium chloride 0.2%, quaternary surfactant 1.1%, neopelex 0.1% are included, remaining
For water;The hot water temperature embathed is 85 DEG C, and embathing the time is 5min.
S2, modification: the woven fabric after embathing in step S1 is put into microorganism modification liquid, carries out microorganism
Modification;
Wherein, the mass fraction of microorganism modifying agent is the 13%, quality of polyether polyol in microorganism modification liquid
Score is 2%, the mass fraction of glucose is 0.4%, the mass fraction of peptone is 0.1%, remaining is water, wherein micro- life
Object modifying agent includes 1 part of yeast, 15 parts of rhizopus, false unicellular 1.1 parts of bacterium, 28 parts of bacterium of Mycotoruloides column branch;Modification temperature
Degree is 40 DEG C, and the modification time is 120h.
S3, sizing: the woven fabric after modification in step S2 is taken out, and handles removal terylene face by ultrasonic oscillation
The microorganism adhered on material, then, drying and shaping, drying temperature is 110 DEG C;
S4, dyeing: the woven fabric after drying and shaping in step S3 is impregnated in color pond, is slowly added into color pond
Dye liquor is concentrated, carries out dyeing processing, then, bakes fixation;
Wherein, the concentration of the disperse dyes in color pond is 1.8g/L, and dyeing temperature is maintained at 85 DEG C, and dyeing time is
40min, be concentrated dye liquor the preparation method comprises the following steps: in parts by weight by 8 parts of dispersing agent, 6 parts of levelling agent, 2 parts of sodium chloride, 7
The sodium carbonate, 3 parts of zinc oxide, 5 parts of acetic acid, 2 parts of migration inhibitor, 23 parts of disperse dyes of part are added sequentially to 100 parts
Distilled water, be uniformly mixed, concentration dye liquor be made, after the completion of dyeing, take out woven fabric, carry out baking fixation, bake temperature
Degree is 130 DEG C.The migration inhibitor uses laruyl alcohol acrylate.
S5, cleaning: the woven fabric after baking fixation in step S4 is rinsed with clear water, then is restored with reduction cleaning liquid
Cleaning;
Wherein, reduction cleaning liquid the preparation method comprises the following steps: in parts by weight by 25 parts of reduction cleaner, 9 parts of sodium metasilicate,
2 parts of glacial acetic acid, 11 parts of anhydrous sodium sulphate and 3 parts of magnesium chloride sequentially add in 250 parts of distilled water, are uniformly mixed,
Reduction cleaning liquid is made, reduction cleaning temperature is 95 DEG C, and the reduction cleaning time is 15min.
S6, final finishing: the woven fabric after reduction cleaning in step S5 is taken out, and is dehydrated, air-dries processing, whole after spraying
Liquid is managed, to get woven fabric product after drying.
Wherein, post-finishing liquid the preparation method comprises the following steps: in parts by weight that 7 parts of antistatic agent and 5 parts of moisture absorbing and sweat releasing is whole
Reason agent LD-9020 is added in 120 parts of distilled water, after mixing, post-finishing liquid is made, post-finishing liquid is on woven fabric
Quantity for spray is 25g/m2.The reduction cleaner uses the compound of sulfites compound.
The soaping fastness of the woven fabric product is 5 grades, and fastness to chlorine-bleaching is 4 grades, and dyeing is firmly combined, and K/S value is 9.1,
Dyeability is good.
Embodiment 2:
Prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, include the following steps:
S1, desizing: woven fabric is impregnated in desizing solution, carries out desizing treatment, after the completion of processing, clot is banked up, so
Afterwards, it is embathed with hot water;
Wherein, desizing treatment temperature is 85 DEG C, and the desizing treatment time is 30min, is wrapped as mass fraction in desizing solution
Sodium hydroxide 1.8%, sodium chloride 0.5%, quaternary surfactant 1.3%, neopelex 0.3% are included, remaining
For water;The hot water temperature embathed is 90 DEG C, and embathing the time is 10min.
S2, modification: the woven fabric after embathing in step S1 is put into microorganism modification liquid, carries out microorganism
Modification;
Wherein, the mass fraction of microorganism modifying agent is the 16%, quality of polyether polyol in microorganism modification liquid
Score is 5%, the mass fraction of glucose is 0.6%, the mass fraction of peptone is 0.3%, remaining is water, wherein micro- life
Object modifying agent includes 3 parts of yeast, 18 parts of rhizopus, false unicellular 1.3 parts of bacterium, 31 parts of bacterium of Mycotoruloides column branch;Modification temperature
Degree is 45 DEG C, and the modification time is 130h.
S3, sizing: the woven fabric after modification in step S2 is taken out, and handles removal terylene face by ultrasonic oscillation
The microorganism adhered on material, then, drying and shaping, drying temperature is 120 DEG C;
S4, dyeing: the woven fabric after drying and shaping in step S3 is impregnated in color pond, is slowly added into color pond
Dye liquor is concentrated, carries out dyeing processing, then, bakes fixation;
Wherein, the concentration of the disperse dyes in color pond is 2.1g/L, and dyeing temperature is maintained at 90 DEG C, and dyeing time is
45min, be concentrated dye liquor the preparation method comprises the following steps: in parts by weight by 11 parts of dispersing agent, 9 parts of levelling agent, 5 parts of sodium chloride,
10 parts of sodium carbonate, 5 parts of zinc oxide, 8 parts of acetic acid, 5 parts of migration inhibitor, 27 parts of disperse dyes are added sequentially to 120
The distilled water of part, is uniformly mixed, and concentration dye liquor is made, and after the completion of dyeing, takes out woven fabric, carries out baking fixation, bakes
Temperature is 140 DEG C.The migration inhibitor uses laruyl alcohol acrylate.
S5, cleaning: the woven fabric after baking fixation in step S4 is rinsed with clear water, then is restored with reduction cleaning liquid
Cleaning;
Wherein, reduction cleaning liquid the preparation method comprises the following steps: in parts by weight by 28 parts of reduction cleaner, 11 parts of silicic acid
Sodium, 5 parts of glacial acetic acid, 13 parts of anhydrous sodium sulphate and 6 parts of magnesium chloride sequentially add in 300 parts of distilled water, are stirred
It is even, reduction cleaning liquid is made, reduction cleaning temperature is 100 DEG C, and the reduction cleaning time is 20min.
S6, final finishing: the woven fabric after reduction cleaning in step S5 is taken out, and is dehydrated, air-dries processing, whole after spraying
Liquid is managed, to get woven fabric product after drying.
Wherein, post-finishing liquid the preparation method comprises the following steps: in parts by weight that 10 parts of antistatic agent and 8 parts of moisture absorbing and sweat releasing is whole
Reason agent LD-9020 is added in 130 parts of distilled water, after mixing, post-finishing liquid is made, post-finishing liquid is on woven fabric
Quantity for spray is 30g/m2.The reduction cleaner uses the compound of sulfites compound.
The soaping fastness of the woven fabric product is 5 grades, and fastness to chlorine-bleaching is 4 grades, and dyeing is firmly combined, and K/S value is 9.0,
Dyeability is good.
Embodiment 3:
Prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, include the following steps:
S1, desizing: woven fabric is impregnated in desizing solution, carries out desizing treatment, after the completion of processing, clot is banked up, so
Afterwards, it is embathed with hot water;
Wherein, desizing treatment temperature is 83 DEG C, and the desizing treatment time is 25min, is wrapped as mass fraction in desizing solution
Sodium hydroxide 1.6%, sodium chloride 0.4%, quaternary surfactant 1.2%, neopelex 0.2% are included, remaining
For water;The hot water temperature embathed is 88 DEG C, and embathing the time is 8min.
S2, modification: the woven fabric after embathing in step S1 is put into microorganism modification liquid, carries out microorganism
Modification;
Wherein, the mass fraction of microorganism modifying agent is the 15%, quality of polyether polyol in microorganism modification liquid
Score is 4%, the mass fraction of glucose is 0.5%, the mass fraction of peptone is 0.2%, remaining is water, wherein micro- life
Object modifying agent includes 2 parts of yeast, 17 parts of rhizopus, false unicellular 1.2 parts of bacterium, 30 parts of bacterium of Mycotoruloides column branch;Modification temperature
Degree is 42 DEG C, and the modification time is 125h.
S3, sizing: the woven fabric after modification in step S2 is taken out, and handles removal terylene face by ultrasonic oscillation
The microorganism adhered on material, then, drying and shaping, drying temperature is 115 DEG C;
S4, dyeing: the woven fabric after drying and shaping in step S3 is impregnated in color pond, is slowly added into color pond
Dye liquor is concentrated, carries out dyeing processing, then, bakes fixation;
Wherein, the concentration of the disperse dyes in color pond is 2.0g/L, and dyeing temperature is maintained at 88 DEG C, and dyeing time is
43min, be concentrated dye liquor the preparation method comprises the following steps: in parts by weight by 9 parts of dispersing agent, 8 parts of levelling agent, 3 parts of sodium chloride, 9
The sodium carbonate, 4 parts of zinc oxide, 7 parts of acetic acid, 3 parts of migration inhibitor, 24 parts of disperse dyes of part are added sequentially to 110 parts
Distilled water, be uniformly mixed, concentration dye liquor be made, after the completion of dyeing, take out woven fabric, carry out baking fixation, bake temperature
Degree is 135 DEG C.The migration inhibitor uses laruyl alcohol acrylate.
S5, cleaning: the woven fabric after baking fixation in step S4 is rinsed with clear water, then is restored with reduction cleaning liquid
Cleaning;
Wherein, reduction cleaning liquid the preparation method comprises the following steps: in parts by weight by 27 parts of reduction cleaner, 10 parts of silicic acid
Sodium, 3 parts of glacial acetic acid, 12 parts of anhydrous sodium sulphate and 5 parts of magnesium chloride sequentially add in 280 parts of distilled water, are stirred
It is even, reduction cleaning liquid is made, reduction cleaning temperature is 98 DEG C, and the reduction cleaning time is 18min.
S6, final finishing: the woven fabric after reduction cleaning in step S5 is taken out, and is dehydrated, air-dries processing, whole after spraying
Liquid is managed, to get woven fabric product after drying.
Wherein, post-finishing liquid the preparation method comprises the following steps: in parts by weight that 9 parts of antistatic agent and 7 parts of moisture absorbing and sweat releasing is whole
Reason agent LD-9020 is added in 125 parts of distilled water, after mixing, post-finishing liquid is made, post-finishing liquid is on woven fabric
Quantity for spray is 28g/m2.The reduction cleaner uses the compound of sulfites compound.
The soaping fastness of the woven fabric product is 4 grades, and fastness to chlorine-bleaching is 4 grades, and dyeing is firmly combined, and K/S value is 8.7,
Dyeability is good.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Benefit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent elements of the claims
Variation is included within the present invention.
Claims (8)
1. prosperous synthetic fibre T3000 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, which comprises the steps of:
S1, desizing: woven fabric is impregnated in desizing solution, carries out desizing treatment, and after the completion of processing, clot is banked up, and then, is used
Hot water is embathed;
S2, modification: the woven fabric after embathing in step S1 is put into microorganism modification liquid, and it is modified to carry out microorganism
Processing;
S3, sizing: the woven fabric after modification in step S2 is taken out, and is handled on removal polyester fabric by ultrasonic oscillation
The microorganism of attachment, then, drying and shaping, drying temperature is 110-120 DEG C;
S4, dyeing: the woven fabric after drying and shaping in step S3 is impregnated in color pond, is slowly added to be concentrated into color pond
Dye liquor carries out dyeing processing, then, bakes fixation;
S5, cleaning: the woven fabric after baking fixation in step S4 is rinsed with clear water, then restore clearly with reduction cleaning liquid
It washes;
S6, final finishing: the woven fabric after reduction cleaning in step S5 is taken out, and is dehydrated, air-dries processing, sprays final finishing
Liquid, to get woven fabric product after drying.
2. prosperous synthetic fibre T3000 according to claim 1 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In desizing treatment temperature is 80-85 DEG C in the step S1, and the desizing treatment time is 20-30min, presses quality in desizing solution
Score meter includes sodium hydroxide 1.5-1.8%, sodium chloride 0.2-0.5%, quaternary surfactant 1.1-1.3%, dodecane
Base benzene sulfonic acid sodium salt 0.1-0.3%, remaining is water;The hot water temperature embathed is 85-90 DEG C, and embathing the time is 5-10min.
3. prosperous synthetic fibre T3000 according to claim 1 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In the mass fraction of microorganism modifying agent is 13-16%, polyether polyol in microorganism modification liquid in the step S2
Mass fraction is 2-5%, the mass fraction of glucose is 0.4-0.6%, the mass fraction of peptone is 0.1-0.3%, remaining
For water, wherein microorganism modifying agent includes 1-3 parts of yeast, 15-18 parts of rhizopus, false unicellular bacterium 1.1-1.3 parts, candida albicans
Belong to 28-31 parts of column branch bacterium;Modification treatment temperature is 40-45 DEG C, and the modification time is 120-130h.
4. prosperous synthetic fibre T3000 according to claim 1 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In the concentration of the disperse dyes in the step S4 in color pond is 1.8-2.1g/L, and dyeing temperature is maintained at 85-90 DEG C, dye
The color time be 40-45min, be concentrated dye liquor the preparation method comprises the following steps: in parts by weight by 8-11 parts of dispersing agent, 6-9 parts of level dyeing
Agent, 2-5 parts of sodium chloride, 7-10 parts of sodium carbonate, 3-5 parts of zinc oxide, 5-8 parts of acetic acid, 2-5 parts of migration inhibitor, 23-
27 parts of disperse dyes are added sequentially to 100-120 parts of distilled water, are uniformly mixed, and concentration dye liquor is made, and dyeing is completed
Afterwards, woven fabric is taken out, baking fixation is carried out, stoving temperature is 130-140 DEG C.
5. prosperous synthetic fibre T3000 according to claim 1 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In reduction cleaning liquid the preparation method comprises the following steps: in parts by weight by 25-28 parts of reduction cleaner, 9-11 parts in the step S5
Sodium metasilicate, 2-5 parts of glacial acetic acid, 11-13 parts of anhydrous sodium sulphate and 3-6 parts of magnesium chloride sequentially add 250-300 parts of steaming
It in distilled water, is uniformly mixed, reduction cleaning liquid is made, reduction cleaning temperature is 95-100 DEG C, and the reduction cleaning time is 15-
20min。
6. prosperous synthetic fibre T3000 according to claim 1 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In, post-finishing liquid in the step S6 the preparation method comprises the following steps: in parts by weight by 7-10 parts of antistatic agent and 5-8 parts of suction
Wet absorbable and breathable finishing agent LD-9020 is added in 120-130 parts of distilled water, after mixing, post-finishing liquid, post-finishing liquid is made
Quantity for spray on woven fabric is 25-30g/m2。
7. prosperous synthetic fibre T3000 according to claim 4 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In the migration inhibitor uses laruyl alcohol acrylate.
8. prosperous synthetic fibre T3000 according to claim 5 and the continuous dyeing and finishing technology of low elastic polyester filament intertexture woven fabric, feature exist
In the reduction cleaner uses the compound of sulfites compound.