CN110204205A - Crude pottery and preparation method thereof - Google Patents
Crude pottery and preparation method thereof Download PDFInfo
- Publication number
- CN110204205A CN110204205A CN201910432341.9A CN201910432341A CN110204205A CN 110204205 A CN110204205 A CN 110204205A CN 201910432341 A CN201910432341 A CN 201910432341A CN 110204205 A CN110204205 A CN 110204205A
- Authority
- CN
- China
- Prior art keywords
- parts
- pottery
- green body
- component
- mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of crude pottery and preparation method thereof, crude pottery by the pottery material of following components in its preparation process wet ball grinding 5~8 hours and obtain, the component and each component mass parts of the pottery material are as follows: 15 parts~20 parts of potassium feldspar;25~30 parts of Jiepai clay;11~15 parts of kaolin;12~15 parts of Guangxi sand;Wash 12~15 parts of mud;8~10 parts of iron oxide red;2~3 parts of talcum;5~8 parts of Guangxi mud.Not only plasticity is good by the present invention, glossiness appropriateness, and iron-content is relatively high, has good facilitation effect with all kinds of iron series crystalline glazes.
Description
Technical field
The present invention relates to a kind of crude potteries and preparation method thereof.
Background technique
Currently, being particular about the security performance of ceramics in ceramic industry, lead cadmium content must not be exceeded;In addition, it is also necessary to control
The glossiness of its billet surface, it is also necessary to which it cooperates to reach its good facilitation effect with iron series crystalline glaze.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, a kind of crude pottery is provided, it is not only plastic
Property good, glossiness appropriateness, and iron-content is relatively high, has good facilitation effect with all kinds of iron series crystalline glazes.
In order to solve the above technical problems, the technical scheme is that a kind of crude pottery, it is existed by the pottery material of following components
Wet ball grinding 5~8 hours in its preparation process and obtain, the component and each component mass parts of the pottery material are as follows:
15 parts~20 parts of potassium feldspar;
25~30 parts of Jiepai clay;
11~15 parts of kaolin;
12~15 parts of Guangxi sand;
Wash 12~15 parts of mud;
8~10 parts of iron oxide red;
2~3 parts of talcum;
5~8 parts of Guangxi mud.
Another aspect, the present invention also provides a kind of preparation method of crude pottery, the step of method in include:
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 5~8 hours, the glaze after ball milling crossed 80
After mesh, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
Further, in the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
After above-mentioned technical proposal, in crude pottery of the present invention, Jiepai clay, kaolin, Guangxi is husky, washes mud, Guangxi mud
Silica needed for main offer building skeleton, aluminium oxide, and micro solvent and cosolvent are provided, potassium feldspar is main molten
Agent, talcum are major cosolvents, and iron oxide red is colorant, by, at the calculating and many experiments that are grouped as, obtaining to the glaze
Component proportion section: 15 parts~20 parts of potassium feldspar;25~30 parts of Jiepai clay;11~15 parts of kaolin;12~15 parts of Guangxi sand;It washes
12~15 parts of mud;8~10 parts of iron oxide red;2~3 parts of talcum;5~8 parts of Guangxi mud;For the glaze formula section of crude pottery, make it
There can be the iron of high-content, crude pottery plasticity of the invention is good, the distribution of particles in mud is controlled by ball-handling time consuming, and
The glossiness of billet surface is determined by distribution of particles, which, which can arrange in pairs or groups, reacts glaze, the coloured glaze with light series, leads to
The different middle layers of generation are crossed to form all kinds of decorative effects, and answer iron-content higher to have good rush to all kinds of iron series crystalline glazes
Into effect,
Specific embodiment
The present invention provides a kind of crude pottery and preparation method thereof, those skilled in the art can use for reference present disclosure, suitably
Improve realization of process parameters.In particular, it should be pointed out that all similar substitutions and modifications are for a person skilled in the art
It will be apparent that they shall fall within the protection scope of the present invention.Method of the invention and application passed through preferred embodiment into
Description is gone, related personnel can obviously not depart from the content of present invention, carried out in spirit and scope to methods herein and application
Change or appropriate changes and combinations, carry out implementation and application the technology of the present invention.
The present invention provides a kind of crude pottery, its wet ball grinding 5~8 hours in its preparation process by the pottery material of following components
And obtain, the component and each component mass parts of the pottery material are as follows:
15 parts~20 parts of potassium feldspar;
25~30 parts of Jiepai clay;
11~15 parts of kaolin;
12~15 parts of Guangxi sand;
Wash 12~15 parts of mud;
8~10 parts of iron oxide red;
2~3 parts of talcum;
5~8 parts of Guangxi mud.
The present invention also provides a kind of preparation method of crude pottery, the step of method in include:
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 5~8 hours, the glaze after ball milling crossed 80
After mesh, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
Further, in the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
In crude pottery of the present invention, Jiepai clay, kaolin, Guangxi is husky, washes mud, Guangxi mud mainly provides needed for constructing skeleton
Silica, aluminium oxide, and micro solvent and cosolvent are provided, potassium feldspar is primary solvent, and talcum is major cosolvents, oxidation
Iron oxide red is colorant, by the calculating and many experiments being grouped as, obtaining component proportion section to the glaze: 15 parts of potassium feldspar~
20 parts;25~30 parts of Jiepai clay;11~15 parts of kaolin;12~15 parts of Guangxi sand;Wash 12~15 parts of mud;Iron oxide red 8~10
Part;2~3 parts of talcum;5~8 parts of Guangxi mud;For the glaze formula section of crude pottery, there can be the iron of high-content, it is of the invention
Crude pottery plasticity is good, controls the distribution of particles in mud by ball-handling time consuming, and green body table is determined by distribution of particles
The glossiness in face, which, which can arrange in pairs or groups, reacts glaze, and the coloured glaze with light series is formed by the different middle layers of generation
All kinds of decorative effects, and answer iron-content higher to have good facilitation effect to all kinds of iron series crystalline glazes.
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one
A kind of crude pottery, it by the pottery material of following components in its preparation process wet ball grinding 5 hours and obtain, the pottery material
Component and each component mass parts are as follows:
15 parts of potassium feldspar;
25 parts of Jiepai clay;
11 parts of kaolin;
Guangxi is 12 parts husky;
Wash 12 parts of mud;
8 parts of iron oxide red;
2 parts of talcum;
5 parts of Guangxi mud.
Include: in the step of preparation method of the crude pottery
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 5 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
In the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
The crude pottery that the present embodiment is prepared, FINAL APPEARANCE are listed in Table 1 below.
Embodiment two
A kind of crude pottery, it by the pottery material of following components in its preparation process wet ball grinding 8 hours and obtain, the pottery material
Component and each component mass parts are as follows:
20 parts of potassium feldspar;
30 parts of Jiepai clay;
15 parts of kaolin;
Guangxi is 15 parts husky;
Wash 15 parts of mud;
10 parts of iron oxide red;
3 parts of talcum;
8 parts of Guangxi mud.
Include: in the step of preparation method of the crude pottery
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 8 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
In the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
The crude pottery that the present embodiment is prepared, FINAL APPEARANCE are listed in Table 1 below.
Embodiment three
A kind of crude pottery, it by the pottery material of following components in its preparation process wet ball grinding 5~8 hours and obtain, the pottery
The component and each component mass parts of material are as follows:
17 parts of potassium feldspar;
27 parts of Jiepai clay;
13 parts of kaolin;
Guangxi is 13 parts husky;
Wash 13 parts of mud;
9 parts of iron oxide red;
2 parts of talcum;
7 parts of Guangxi mud.
Include: in the step of preparation method of the crude pottery
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 6 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
In the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
The crude pottery that the present embodiment is prepared, FINAL APPEARANCE are listed in Table 1 below.
Comparative example one
A kind of crude pottery, it by the pottery material of following components in its preparation process wet ball grinding 5 hours and obtain, the pottery material
Component and each component mass parts are as follows:
25 parts of potassium feldspar;
20 parts of Jiepai clay;
11 parts of kaolin;
Guangxi is 12 parts husky;
Wash 12 parts of mud;
8 parts of iron oxide red;
2 parts of talcum;
5 parts of clues mud.
Include: in the step of preparation method of the crude pottery
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 5 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
In the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
The crude pottery that this comparative example is prepared, FINAL APPEARANCE are listed in Table 1 below.
Comparative example two
A kind of crude pottery, it by the pottery material of following components in its preparation process wet ball grinding 8 hours and obtain, the pottery material
Component and each component mass parts are as follows:
20 parts of potassium feldspar;
30 parts of Jiepai clay;
15 parts of kaolin;
Guangxi is 25 parts husky;
Wash 15 parts of mud;
10 parts of iron oxide red;
3 parts of talcum.
Include: in the step of preparation method of the crude pottery
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 8 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
In the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
The crude pottery that this comparative example is prepared, FINAL APPEARANCE are listed in Table 1 below.
Comparative example three
A kind of crude pottery, it by the pottery material of following components in its preparation process wet ball grinding 4 hours and obtain, the pottery material
Component and each component mass parts are as follows:
17 parts of potassium feldspar;
27 parts of Jiepai clay;
13 parts of kaolin;
Guangxi is 13 parts husky;
Wash 13 parts of mud;
9 parts of iron oxide red;
2 parts of talcum;
7 parts of Guangxi mud.
Include: in the step of preparation method of the crude pottery
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 4 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
In the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.
Crude pottery visual condition | |
Embodiment one | Meet design requirement |
Embodiment two | Meet design requirement |
Embodiment three | Meet design requirement |
Comparative example one | Refractoriness is too low, and when high temperature firing deforms larger |
Comparative example two | Plasticity is poor |
Comparative example three | Too coarse, glossiness is inadequate |
As can be known from the above table, crude pottery plasticity of the invention is good, and glossiness appropriateness, iron-content is relatively high, with all kinds of iron series knots
Brilliant glaze has good facilitation effect.
Particular embodiments described above has carried out further in detail the purpose of the present invention, technical scheme and beneficial effects
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to restrict the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in guarantor of the invention
Within the scope of shield.
Claims (3)
1. a kind of crude pottery, it is characterised in that it by the pottery material of following components in its preparation process wet ball grinding 5~8 hours and
, the component and each component mass parts of the pottery material are as follows:
15 parts~20 parts of potassium feldspar;
25~30 parts of Jiepai clay;
11~15 parts of kaolin;
12~15 parts of Guangxi sand;
Wash 12~15 parts of mud;
8~10 parts of iron oxide red;
2~3 parts of talcum;
5~8 parts of Guangxi mud.
2. a kind of preparation method of crude pottery as described in claim 1, it is characterised in that include: in the step of method
It stocks up according to each component and each component mass parts:
According to 1.7 ︰ 0.4 of mass ratio=1 ︰ of You Liao ︰ Qiu ︰ water, wet ball grinding 5~8 hours, the glaze after ball milling crossed 80 meshes
Afterwards, the slurry for being modulated into 60~65 Baume concentration is stand-by;
Slurry is formed into green body by slip casting or green body is formed by hand throwing.
3. preparation method according to claim 2, it is characterised in that in the step of method further include:
Green body is decorated to the glaze colours needed;
The green body of first-class glaze colours is fired in 1270 DEG C of shuttle kiln.