CN110195367B - Method for manufacturing steel wire rope mark - Google Patents
Method for manufacturing steel wire rope mark Download PDFInfo
- Publication number
- CN110195367B CN110195367B CN201810944080.4A CN201810944080A CN110195367B CN 110195367 B CN110195367 B CN 110195367B CN 201810944080 A CN201810944080 A CN 201810944080A CN 110195367 B CN110195367 B CN 110195367B
- Authority
- CN
- China
- Prior art keywords
- steel wire
- wire rope
- strands
- mark
- grease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A method for manufacturing a steel wire rope mark comprises the steps of selecting 1-2 strands of strands to be twisted, not spraying grease on the surfaces of the strands, enabling the surfaces of the strands to be clean, melting light-color or colorless transparent high-dropping-point grease, mixing the light-color or colorless transparent high-dropping-point grease and red paint in a ratio of 1:1 by using a measuring tool, stirring uniformly, immersing the strands into the mixture, coating the mixture on the surfaces of the strands, and determining the thickness of the mixture according to the using environment of a steel wire rope and the requirements of a user. And after the coated steel wire rope strands are stored for 48 hours, twisting the coated steel wire rope strands with other strands to form a rope, and thus the steel wire rope mark is manufactured. The grease is not sticky as the mark of a steel wire rope manufacturer, and the steel wire rope is attractive and can improve the corrosion resistance and prolong the service life.
Description
Technical Field
The invention relates to a method for manufacturing a steel wire rope mark, and belongs to the technical field of metal cable rope processing.
Background
One or two strands of steel wire ropes are coated with red paint to facilitate purchasing or using of customers, manufacturers of the steel wire ropes clearly know that the steel wire ropes are coated with the red paint on the surfaces of the clean strands, so that the red paint is easily shed on the surfaces of the strands coated with the red paint through repeated bending and friction in the using process of the steel wire ropes, the lubricating and anti-corrosion properties are reduced, and the service life of the steel wire ropes is shortened. The red grease with light color or colorless transparency and high dropping point is mixed with the red paint according to the optimal ratio (1: 1) and uniformly coated on the surface of the steel wire rope strand, and the steel wire rope strand is twisted with other strands after being stored for two days, so that the red grease on the surface of the twisted steel wire rope is not sticky to hands and does not influence the appearance quality, and meanwhile, the lubricating and anticorrosive performance of the steel wire rope can be realized, and the harm of harmful materials to human bodies can be reduced. The application field is wider, the protectiveness is stronger, and the service life is prolonged.
The technology has no report of the same technical content on public media.
Disclosure of Invention
The invention aims to overcome the defects of the prior art, provides a manufacturing method of a steel wire rope mark, and solves the anti-counterfeiting problem of the steel wire rope mark.
The invention is used for the identification of steel wire rope manufacturers, and requires that after the strands coated with red grease are combined, the grease is not adhered to the steel wire rope by naked hands, and the grease is not adhered to the surface of the adjacent strands to influence the overall appearance quality of the steel wire rope, so that the steel wire rope has the characteristics of improving the corrosion resistance of the steel wire rope, prolonging the service life and the like. The components mainly consist ofLight or colorless transparent high dropping point grease and red paint. The high dropping point oil is light or colorless transparent, the dropping point is more than or equal to 100 ℃, and the kinematic viscosity (100 ℃) is more than or equal to 130 mm2And/s, six surfaces of the paint do not slide off and have no abnormal pungent smell, and the paint is red paint within the effective shelf life.
The invention relates to a method for manufacturing a steel wire rope mark, which comprises the following implementation steps:
(1) firstly, manufacturing a red anticorrosive material for a steel wire rope, melting light-colored or colorless transparent high dropping point grease, mixing the light-colored or colorless transparent high dropping point grease and red paint in a ratio of 1:1 by using a measuring tool, and uniformly stirring;
(2) one to two clean strands which are not sprayed with grease are immersed into the prepared red anticorrosive material of the steel wire rope, so that the red anticorrosive material is coated on the surfaces of the strands, the thickness of the red anticorrosive material is determined according to the use environment of the steel wire rope and the requirements of users, the strands are stored for 48 hours after being greased, and the steel wire rope is coated with a mark;
(3) and (3) combining the steel wire rope, namely combining one to two strands coated with the mark with the conventional steel wire rope strands to produce the steel wire rope, namely manufacturing the steel wire rope mark.
The invention has the beneficial effects that:
the grease is not sticky as the mark of a steel wire rope manufacturer, and the steel wire rope is attractive and can improve the corrosion resistance and prolong the service life.
Detailed Description
The specific implementation mode of the invention is as follows:
during stranding, no grease is sprayed on the surface of 1-2 strands of strand ropes, the surfaces of the strand ropes are required to be clean, after the light-color or colorless and transparent high dropping point grease is melted, the light-color or colorless and transparent high dropping point grease and the red paint are mixed according to the proportion of 1:1 by using a measuring tool, the mixture is uniformly stirred, the strand ropes are immersed in the mixture, the mixture is coated on the surfaces of the strand ropes, and the thickness of the mixture can be determined according to the using environment of the steel wire ropes and the requirements of users. The strands are generally thinly coated with grease and cannot be made too thick and are twisted with other strands after 48 hours of storage.
The invention relates to a method for manufacturing a steel wire rope mark, which specifically comprises the following implementation steps:
(1) firstly, manufacturing a red anticorrosive material for a steel wire rope, melting light-colored or colorless transparent high dropping point grease, mixing the light-colored or colorless transparent high dropping point grease and red paint in a ratio of 1:1 by using a measuring tool, and uniformly stirring;
(2) one to two clean strands which are not sprayed with grease are immersed into the prepared red anticorrosive material of the steel wire rope, so that the red anticorrosive material is coated on the surfaces of the strands, the thickness of the red anticorrosive material is determined according to the use environment of the steel wire rope and the requirements of users, the strands are stored for 48 hours after being greased, and the steel wire rope is coated with a mark;
(3) and (3) combining the steel wire rope, namely combining one to two strands coated with the mark with the conventional steel wire rope strands to produce the steel wire rope, namely manufacturing the steel wire rope mark.
Claims (1)
1. A method for manufacturing a steel wire rope mark is characterized by comprising the following implementation steps:
(1) firstly, manufacturing a red anticorrosive material for a steel wire rope, melting light-colored or colorless transparent high dropping point grease, mixing the light-colored or colorless transparent high dropping point grease and red paint in a ratio of 1:1 by using a measuring tool, and uniformly stirring;
(2) one to two clean strands which are not sprayed with grease are immersed into the prepared red anticorrosive material of the steel wire rope, so that the red anticorrosive material is coated on the surface of the strands, the thickness of the red anticorrosive material is determined according to the use environment of the steel wire rope and the requirements of users, the strands are stored for 48 hours after being coated with the red anticorrosive material, and the steel wire rope is coated with a mark;
(3) and (3) combining the steel wire rope, namely combining one to two strands coated with the mark with the conventional steel wire rope strands to produce the steel wire rope, namely manufacturing the steel wire rope mark.