CN110157335A - It is a kind of used for rail vehicle with anti-corrosion, damping, the water paint of fire-proof function and preparation method thereof - Google Patents
It is a kind of used for rail vehicle with anti-corrosion, damping, the water paint of fire-proof function and preparation method thereof Download PDFInfo
- Publication number
- CN110157335A CN110157335A CN201910615943.8A CN201910615943A CN110157335A CN 110157335 A CN110157335 A CN 110157335A CN 201910615943 A CN201910615943 A CN 201910615943A CN 110157335 A CN110157335 A CN 110157335A
- Authority
- CN
- China
- Prior art keywords
- fire
- damping
- agent
- corrosion
- proof function
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses it is a kind of it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, include following component by mass fraction (%): aqueous damping lotion 20-30；Mono-component aqueous acrylate polymer emulsion 20-30 with fire-proof function；PH adjusting agent 0.1-0.5；Defoaming agent 0.3-0.6；Dispersing agent 0.3-0.5；Filler 38-63；Rust resisting pigment 5-8；Auxiliary rheological agents 1-3；Fungicide 0.2-0.6；Anti- flash rusting agent 0.1-0.6；Deionized water 5-10；The invention also includes the preparation methods of coating described above.The present invention is used as using the low smell aqueous damping lotion of low Tg and the mono-component aqueous acrylate polymer emulsion blending with fire-proof function into film base material, it does not need plus coalescing agent can form a film, using water as solvent, ignition point relative to oil-based solvent system is higher, it is more fire retardant, VOC is lower, more environmentally friendly, while the two blending, so that film forming matrix system has both anti-corrosion, fire prevention, damps three-in-one function.
Description
Technical field
The present invention relates to a kind of coating and preparation method thereof, and in particular to one kind is used for rail vehicle to be had anti-corrosion, damping, prevent
The water paint and preparation method thereof of fiery function.
Background technique
With the continuous improvement that current domestic people require trip comfort level, people imitate the damping noise reduction of the vehicles
More stringent requirements are proposed for fruit, and domestic many automobiles, urban rail, motor-car, big passenger train all begin through the spraying of damping paint
To carry out damping noise reduction.
Urban rail transit in China development is swift and violent, ends the first half of the year in 2016, in Chinese city rail transportation operation
Journey has reached 3473.33km.On rail traffic vehicles are mainly runed in tunnel and are overhead, speed is fast and interior space is small operation
Environmental quality determines that fire once occurs for vehicle, and passenger will face the danger bigger compared with superficial fire；Types of functionality by force and
The nonmetallic materials of good decorative property are used on vehicle more and more, increase the wind of vehicle fire thereupon
Danger；Therefore to the fire protection design of rail traffic vehicles, more stringent requirements are proposed.
And it is domestic at present, the chassis of rail vehicle generally uses two kinds of painting designs, and one kind is etching priming paint+aqueous damping
Coating+closing finishing coat, another is then etching priming paint+aqueous fire-proof coating+closing finishing coat, both systems can not solve simultaneously
Certainly sound insulation and noise reduction and the problem of fire prevention, so develop a kind of while having both anti-corrosion, damping, fireproof water-soluble multifunctional coating will be
Very necessary, while the hot spot that will also be pursued as market, become the new trend of future development.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, provide a kind of used for rail vehicle with anti-
Rotten, damping, the water paint of fire-proof function and preparation method thereof, it is using the low smell aqueous damping lotion of low Tg and has fire prevention
Functional mono-component aqueous acrylate polymer emulsion blending is used as into film base material, does not need plus coalescing agent can be at
Film, using water as solvent, the ignition point relative to oil-based solvent system is higher, it more difficult to fire, VOC is lower, more environmentally friendly, while the two
Blending, so that film forming matrix system has both anti-corrosion, fire prevention, damps three-in-one function.
In order to solve the above technical problems, technical solution proposed by the present invention are as follows: a kind of used for rail vehicle with anti-corrosion, resistance
Buddhist nun, fire-proof function water paint, include following component by mass fraction (%):
Aqueous damping lotion 20-30；
Mono-component aqueous acrylate polymer emulsion 20-30 with fire-proof function；
PH adjusting agent 0.1-0.5；
Defoaming agent 0.3-0.6；
Dispersing agent 0.3-0.5；
Filler 38-63；
Rust resisting pigment 5-8；
Auxiliary rheological agents 1-3；
Fungicide 0.2-0.6；
Anti- flash rusting agent 0.1-0.6；
Deionized water 5-10.
The further technical solution of the present invention are as follows: the filler includes following component by mass fraction (%):
Mica powder 5-10；
Cenosphere 5-10；
Melamine 6-9；
Pentaerythrite 9-12；
Ammonium polyphosphate 9-12；
Diatomite 1-5；
Expansible graphite 3-5；
Aluminium triphosphate 5-8.
Further, the pH adjusting agent is ammonium hydroxide or ammonia.
Further, the Tg of the aqueous damping lotion is -20~0 °.
Further, the defoaming agent is DH-202 general defoaming agent, Tego Airex 902W defoaming agent, BYK-024 aqueous
The combination of one or more of defoaming agent.
Further, the dispersing agent is POLYRON NC dispersing agent, TegoDispers 760W dispersing agent, EFKA PU
The combination of one or more of 4010 AN dispersing agents.
Further, the rust resisting pigment is aluminium triphosphate, ZF02 zinc-iron powder Composite Anticorrosive Pigment Using, SN-S800 efficiently prevent
One or more of the pigment that becomes rusty combines.
Further, the auxiliary rheological agents are 837 anti-settling rheological agents, the aqueous auxiliary rheological agents of RHEOLATE299, RHEOLATE
The combination of one or more of aqueous auxiliary rheological agents of 350D；The fungicide is DEUADD MB-11 waterborne preservative；It is described anti-
Flash rusting agent is one or both of the anti-flash rusting agent of SC2190Z type, A3601 sudden strain of a muscle erosion agent combination.
It is a kind of it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint preparation method, using above-mentioned rail
Road vehicle use with anti-corrosion, damping, fire-proof function water paint component, and including following operating procedure:
1) aqueous damping lotion and mono-component aqueous acrylate polymer emulsion are added in dispersion tank and are dispersed with stirring uniformly
Afterwards, the pH value that pH adjusting agent adjustment mixed emulsion is added is 9.5-10；
2) defoaming agent and dispersing agent is added in the mixed emulsion after adjusting pH to step 1), is dispersed with stirring 20-30min, makes
System is uniformly dispersed；
3) filler, rust resisting pigment and auxiliary rheological agents are added in gained system into step 2), and stir evenly, then add again
Enter fungicide and anti-flash rusting agent, the consistency that mixed system is adjusted with deionized water is 8-14cm, is finally ground to carefully with colloid mill
Discharge packaging after degree is qualified.
Further, the step 1), 2) and 3) in temperature be no more than 50 DEG C, it is broken to will appear water-based emulsion more than 50 DEG C
Newborn phenomenon, step 1), 2) and 3) in mixing speed be 1000-1200r/min.
Compared with the prior art, the advantages of the present invention are as follows:
The present invention is poly- using the low smell aqueous damping lotion of low Tg and the mono-component aqueous acrylic acid with fire-proof function
It closes object latex blend to be used as into film base material, does not need plus coalescing agent can form a film, it is molten relative to oiliness using water as solvent
The ignition point of agent system is higher, it more difficult to fire, VOC is lower, more environmentally friendly, while the two blending so that film forming matrix system have both it is anti-
Corruption prevents fires, damps three-in-one function.
Specific embodiment
To facilitate the understanding of the present invention, present invention work more comprehensively, is meticulously described below in conjunction with preferred embodiment,
But the protection scope of the present invention is not limited to the following specific embodiments.
It is a kind of it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, by mass fraction (%) including as follows
Component (as shown in table 1):
Table 1: the present embodiment it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint component
It is above-mentioned it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint the preparation method comprises the following steps: serial number is hindered
1000-1200r/min high-speed stirred point in dispersion tank is added in damping paint lotion 0928, EXP-5510 acrylate polymer emulsion
It dissipates uniformly, it is 9.5-10 that DeuAdd MA-95, which is added, and adjusts pH value.While stirring be added serial number DH-202 versatility defoaming agent,
POLYRONNC dispersing agent, 1000-1200r/min disperse 20-30 minutes, and system is made to be uniformly dispersed.GB-2 wind is added while stirring
Select sericite in powder, 200 mesh cenospheres, melamine, pentaerythrite, ammonium polyphosphate, diatomite, expansible graphite, trimerization phosphorus
Powder materials are sufficiently stirred in sour aluminium and the aqueous auxiliary rheological agents of RHEOLATE299,1000-1200r/min high-speed stirred 20-30min
Uniformly, DEUADD MB-11 waterborne preservative, the anti-flash rusting agent of SC2190Z type is added, adjusts consistency to 8-14cm with deionized water,
Fineness qualification, discharging packaging are ground to colloid mill.Temperature is no more than 50 DEG C in above-mentioned entire production process.
A series of performances are carried out to the above-mentioned resulting water paint used for rail vehicle with anti-corrosion, damping, fire-proof function
Detection, acquired results are as shown in table 2 below:
Table 2: the resulting water paint used for rail vehicle with anti-corrosion, damping, fire-proof function of the present embodiment carries out a system
Column performance test results
By above-mentioned performance detection structure it can be seen that properties can meet the requirement of fireproof coating, while again
Good damping capacity and antiseptic property are had both, is the good damping of one kind, anti-corrosion, fire prevention three-in-one multifunctional coating.
Claims (10)
1. it is a kind of it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, which is characterized in that press mass fraction
(%) includes following component:
Aqueous damping lotion 20-30；
Mono-component aqueous acrylate polymer emulsion 20-30 with fire-proof function；
PH adjusting agent 0.1-0.5；
Defoaming agent 0.3-0.6；
Dispersing agent 0.3-0.5；
Filler 38-63；
Rust resisting pigment 5-8；
Auxiliary rheological agents 1-3；
Fungicide 0.2-0.6；
Anti- flash rusting agent 0.1-0.6；
Deionized water 5-10.
2. it is according to claim 1 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature exists
In the filler includes following component by mass fraction (%):
Mica powder 5-10；
Cenosphere 5-10；
Melamine 6-9；
Pentaerythrite 9-12；
Ammonium polyphosphate 9-12；
Diatomite 1-5；
Expansible graphite 3-5；
Aluminium triphosphate 5-8.
3. it is according to claim 1 or 2 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature
It is, the pH adjusting agent is ammonium hydroxide or ammonia.
4. it is according to claim 1 or 2 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature
It is, the Tg of the aqueous damping lotion is -20~0 °.
5. it is according to claim 1 or 2 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature
It is, the defoaming agent is DH-202 general defoaming agent, in Tego Airex 902W defoaming agent, BYK-024 aqueous defoamer
One or more combination.
6. it is according to claim 1 or 2 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature
It is, the dispersing agent is POLYRON NC dispersing agent, TegoDispers 760W dispersing agent, 4010 AN of EFKA PU dispersion
One or more of agent combination.
7. it is according to claim 1 or 2 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature
It is, the rust resisting pigment is aluminium triphosphate, in ZF02 zinc-iron powder Composite Anticorrosive Pigment Using, SN-S800 high-efficiency rust-preventive pigment
One or more combination.
8. it is according to claim 1 or 2 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint, feature
It is, the auxiliary rheological agents are 837 anti-settling rheological agents, the aqueous auxiliary rheological agents of RHEOLATE299, RHEOLATE 350D aqueous flow
Become the combination of one or more of auxiliary agent；The fungicide is DEUADD MB-11 waterborne preservative；The anti-flash rusting agent is
One or both of erosion agent combination is dodged in the anti-flash rusting agent of SC2190Z type, A3601.
9. it is a kind of it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint preparation method, which is characterized in that adopt
Described in any one of the claims 1-8 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint group
Point, and including following operating procedure:
1) aqueous damping lotion and mono-component aqueous acrylate polymer emulsion are added in dispersion tank after being dispersed with stirring uniformly, are added
The pH value for entering pH adjusting agent adjustment mixed emulsion is 9.5-10；
2) defoaming agent and dispersing agent is added in the mixed emulsion after adjusting pH to step 1), is dispersed with stirring 20-30min, makes system
It is uniformly dispersed；
3) filler, rust resisting pigment and auxiliary rheological agents are added in gained system into step 2), and stir evenly, then add and kill
Microbial inoculum and anti-flash rusting agent, the consistency that mixed system is adjusted with deionized water is 8-14cm, is finally ground to fineness with colloid mill and closes
Discharge packaging after lattice.
10. it is according to claim 9 it is used for rail vehicle with anti-corrosion, damping, fire-proof function water paint preparation side
Method, which is characterized in that the step 1), 2) and 3) in temperature be no more than 50 DEG C, step 1), 2) and 3) in mixing speed
It is 1000-1200r/min.