CN110156401A - A kind of inorganic dry powder painting and its production technology - Google Patents
A kind of inorganic dry powder painting and its production technology Download PDFInfo
- Publication number
- CN110156401A CN110156401A CN201910471083.5A CN201910471083A CN110156401A CN 110156401 A CN110156401 A CN 110156401A CN 201910471083 A CN201910471083 A CN 201910471083A CN 110156401 A CN110156401 A CN 110156401A
- Authority
- CN
- China
- Prior art keywords
- parts
- dry powder
- inorganic dry
- powder
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inorganic dry powder painting and its production technologies, belong to architectural decoration material field, solves the harmful substance that existing indoor interior wall coating contains the heavy metals such as fungicide, mould inhibitor, deodorant, coalescing agent, flavouring agent, lotion is also to have the problem of volatile hazardous substances；Its constitutive material includes coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose；The invention also discloses the production technology of inorganic dry powder painting and application method, the present invention prevents the above harmful substance and participates in, and is replaced with miberal powder, the feature of environmental protection is solved the problems, such as from source, and inorganic dry powder painting is physical agitation processing, and storage is convenient, construction is simple, spraying, roller coating is all can be with being directly watered stirring can construct, it decomposes rapidly, does not agglomerate, it is water-fastness, adhesive force is good, alkali resistant is good, anti-oxidant, is suitble to do coating for internal and external wall.
Description
Technical field
The present invention relates to architectural decoration material field, specifically a kind of inorganic dry powder painting and its production technology.
Background technique
As social and economic condition is become better and better, living environment is increased accordingly, and people increasingly pay attention to decorating, but very much
Material contains harmful substance ingredient, constantly pollutes our living space, because ornamental tape come many diseases, as leukaemia,
Lung cancer, fetal anomaly, respiratory diseases etc., all the time all in the health for endangering us, country to ornament materials want index by
Step improves, but being stepped up with ornament materials materials, all environmental protection indexs that add up still are difficult to control, avoid not
Or it is exceeded, cause the serious room air seriously to pollute.Existing indoor wall material mainly uses wallpaper, wall cloth, cream
The materials such as shellac varnish are decorated, and the fire prevention index of wall cloth is extremely difficult to, and wallpaper and emulsion paint also enclose wall, if by external
Humidity influences, it is easy to big bulge, peeling, peeling etc. occurs.
The indoor green inner wall coating material to circulate on the market at this stage is many kinds of, there is fungicide, mould inhibitor, deodorization
Agent, coalescing agent, flavouring agent etc., are all the harmful substances containing plurality of heavy metal, and lotion is also to have volatile hazardous substances.
For this reason, it may be necessary to design a kind of inorganic dry powder painting and its production technology, participated in preventing the above harmful substance, and more
It changes miberal powder into, prevents not environmentally property from source.
Summary of the invention
The purpose of the present invention is to provide a kind of inorganic dry powder painting and its production technologies, to solve in above-mentioned background technique
The problem of proposition.
To achieve the above object, the invention provides the following technical scheme:
A kind of inorganic dry powder painting, constitutive material include coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate,
Defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose.
Specifically, the inorganic dry powder painting includes the following raw material according to parts by weight: 30-60 parts of coarse whiting, kaolin 5-
20 parts, 4-18 parts of silica flour, 4-18 parts of talcum powder, 5-20 parts of titanium dioxide, 5-20 parts of barium sulfate, 0.1-0.6 parts of defoaming agent, dispersion
0.01-0.2 parts of agent, 6-11 parts of polymer dispersion powder, 3-20 parts of white cement, 0.02-0.05 parts of suspending agent, hydrophober 0.01-0.3
Part and hydroxyethyl cellulose 0.1-0.6 parts.
As a further solution of the present invention: including below according to the raw material of parts by weight: 40-50 parts of coarse whiting, kaolin 10-
15 parts, 8-14 parts of silica flour, 8-14 parts of talcum powder, 10-15 parts of titanium dioxide, 10-15 parts of barium sulfate, 0.2-0.5 parts of defoaming agent, point
0.05-0.15 parts of powder, 7-10 parts of polymer dispersion powder, 7-15 parts of white cement, 0.03-0.04 parts of suspending agent, hydrophober 0.1-
0.2 part and hydroxyethyl cellulose 0.3-0.4 parts.
As further scheme of the invention: including below according to the raw material of parts by weight: 45 parts of coarse whiting, kaolin 13
Part, 0.1 part of dispersing agent, can divide 11 parts of silica flour, 11 parts of talcum powder, 13 parts of titanium dioxide, 13 parts of barium sulfate, 0.35 part of defoaming agent
Scattered 8.5 parts of latex powder, 11 parts of white cement, 0.035 part of suspending agent, 0.15 part of hydrophober and 0.35 part of hydroxyethyl cellulose.
As further scheme of the invention: the coarse whiting is the heavy calcium carbonate of 1250 mesh, coating can be made not sink
Drop is easily dispersed, the characteristics such as good luster.
As further scheme of the invention: the kaolinic granularity is 4000 mesh, and the granularity of silica flour is 2000
Mesh, the granularity of talcum powder are 2000 mesh, and the granularity of barium sulfate is 3000 mesh, and the granularity of white cement is 2000 mesh.
Based on the production technology of the inorganic dry powder painting, steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, dispersible latex
Powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and according to the ratio of 1:1.2-1.5
It is watered and is mixed, inorganic dry powder painting is made.
Easy to operate when construction, spraying, roller coating are ok.
The application method of the inorganic dry powder painting, method includes the following steps:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.2-1.5 ratio, and mixed after stirring with water
Inorganic dry powder painting is made；
Step 2: being painted on inside and outside metope by way of spraying or roller coating for coating made from step 1, per kilogram without
Machine dry powder paint product construction square number is 10-15 squares, more than emulsion paint square.Cost reduces very much.
Compared with prior art, the beneficial effects of the present invention are:
The present invention prevents the above harmful substance and participates in, and is replaced with miberal powder, prevents not environmentally property from source.
Inorganic dry powder painting of the invention is physical agitation processing.
It is convenient that inorganic dry powder painting of the invention stores, and plastic bag packaging, inorganic dry powder painting of the invention is not contained and killed
Microbial inoculum, mould inhibitor, deodorant, coalescing agent, flavouring agent etc..
Inorganic dry powder painting construction is simple of the invention, spraying, roller coating is all can be with being directly watered stirring can apply
Work, the ratio of being watered are 1:1.2-1.5, can decompose rapidly, not agglomerate.
Inorganic dry powder painting per kilogram of the invention is constructed 10-15 squares of square number, and more than emulsion paint square, cost is reduced
Very much.
Inorganic dry powder painting of the invention is water-fastness, and adhesive force is good, and alkali resistant is good, anti-oxidant, is suitble to do coating for internal and external wall.
Specific embodiment
Technical solution of the present invention is described in more detail With reference to embodiment.
Embodiment 1
A kind of inorganic dry powder painting, constitutive material include coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate,
Defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose.
Specifically, the inorganic dry powder painting includes the following raw material according to parts by weight: 30 parts of coarse whiting, 5 parts of kaolin, stone
4 parts of English powder, 4 parts of talcum powder, 5 parts of titanium dioxide, 5 parts of barium sulfate, 0.1 part of defoaming agent, 0.01 part of dispersing agent, polymer dispersion powder 6
Part, 3 parts of white cement, 0.02 part of suspending agent, 0.01 part of hydrophober and 0.1 part of hydroxyethyl cellulose.
Further, the coarse whiting is the heavy calcium carbonate of 1250 mesh, coating can be made not settle, and is easily dispersed, good luster
Etc. characteristics.
Further, the kaolinic granularity is 4000 mesh, and the granularity of silica flour is 2000 mesh, and the granularity of talcum powder is
2000 mesh, the granularity of barium sulfate are 3000 mesh, and the granularity of white cement is 2000 mesh.
Based on the production technology of the inorganic dry powder painting, steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, dispersible latex
Powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and are watered according to the ratio of 1:1.2
It is mixed, inorganic dry powder painting is made.
Easy to operate when construction, spraying, roller coating are ok.
The application method of the inorganic dry powder painting, method includes the following steps:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.2 ratio, and it is mixed to prepare after stirring with water
Inorganic dry powder painting；
Step 2: being painted on inside and outside metope by way of spraying or roller coating for coating made from step 1, per kilogram without
Machine dry powder paint product construction square number is 10 squares, more than emulsion paint square.Cost reduces very much.
Embodiment 2
A kind of inorganic dry powder painting, constitutive material include coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate,
Defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose.
Further, including below according to the raw material of parts by weight: 40 parts of coarse whiting, 10 parts of kaolin, 8 parts of silica flour, talcum
8 parts of powder, 10 parts of titanium dioxide, 10 parts of barium sulfate, 0.2 part of defoaming agent, 0.05 part of dispersing agent, 7 parts of polymer dispersion powder, white cement 7
Part, 0.03 part of suspending agent, 0.1 part of hydrophober and 0.3 part of hydroxyethyl cellulose.
Further, the coarse whiting is the heavy calcium carbonate of 1250 mesh, coating can be made not settle, and is easily dispersed, good luster
Etc. characteristics.
Further, the kaolinic granularity is 4000 mesh, and the granularity of silica flour is 2000 mesh, and the granularity of talcum powder is
2000 mesh, the granularity of barium sulfate are 3000 mesh, and the granularity of white cement is 2000 mesh.
Based on the production technology of the inorganic dry powder painting, steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, dispersible latex
Powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and are watered according to the ratio of 1:1.3
It is mixed, inorganic dry powder painting is made.
Easy to operate when construction, spraying, roller coating are ok.
The application method of the inorganic dry powder painting, method includes the following steps:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.3 ratio, and it is mixed to prepare after stirring with water
Inorganic dry powder painting；
Step 2: being painted on inside and outside metope by way of spraying or roller coating for coating made from step 1, per kilogram without
Machine dry powder paint product construction square number is 11 squares, more than emulsion paint square.Cost reduces very much.
Embodiment 3
A kind of inorganic dry powder painting, constitutive material include coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate,
Defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose.
Further, including below according to the raw material of parts by weight: 45 parts of coarse whiting, 13 parts of kaolin, 11 parts of silica flour, talcum
11 parts of powder, 13 parts of titanium dioxide, 13 parts of barium sulfate, 0.35 part of defoaming agent, 0.1 part of dispersing agent, 8.5 parts of polymer dispersion powder, plain boiled water
11 parts of mud, 0.035 part of suspending agent, 0.15 part of hydrophober and 0.35 part of hydroxyethyl cellulose.
Further, the coarse whiting is the heavy calcium carbonate of 1250 mesh, coating can be made not settle, and is easily dispersed, good luster
Etc. characteristics.
Further, the kaolinic granularity is 4000 mesh, and the granularity of silica flour is 2000 mesh, and the granularity of talcum powder is
2000 mesh, the granularity of barium sulfate are 3000 mesh, and the granularity of white cement is 2000 mesh.
Based on the production technology of the inorganic dry powder painting, steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, dispersible latex
Powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and are watered according to the ratio of 1:1.4
It is mixed, inorganic dry powder painting is made.
Easy to operate when construction, spraying, roller coating are ok.
The application method of the inorganic dry powder painting, method includes the following steps:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.4 ratio, and it is mixed to prepare after stirring with water
Inorganic dry powder painting；
Step 2: being painted on inside and outside metope by way of spraying or roller coating for coating made from step 1, per kilogram without
Machine dry powder paint product construction square number is 12 squares, more than emulsion paint square.Cost reduces very much.
Embodiment 4
A kind of inorganic dry powder painting, constitutive material include coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate,
Defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose.
Further, including below according to the raw material of parts by weight: 50 parts of coarse whiting, 15 parts of kaolin, 14 parts of silica flour, talcum
14 parts of powder, 15 parts of titanium dioxide, 15 parts of barium sulfate, 0.5 part of defoaming agent, 0.15 part of dispersing agent, 10 parts of polymer dispersion powder, white cement
15 parts, 0.04 part of suspending agent, 0.2 part of hydrophober and 0.4 part of hydroxyethyl cellulose.
Further, the coarse whiting is the heavy calcium carbonate of 1250 mesh, coating can be made not settle, and is easily dispersed, good luster
Etc. characteristics.
Further, the kaolinic granularity is 4000 mesh, and the granularity of silica flour is 2000 mesh, and the granularity of talcum powder is
2000 mesh, the granularity of barium sulfate are 3000 mesh, and the granularity of white cement is 2000 mesh.
Based on the production technology of the inorganic dry powder painting, steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, dispersible latex
Powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and are watered according to the ratio of 1:1.4
It is mixed, inorganic dry powder painting is made.
Easy to operate when construction, spraying, roller coating are ok.
The application method of the inorganic dry powder painting, method includes the following steps:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.4 ratio, and it is mixed to prepare after stirring with water
Inorganic dry powder painting；
Step 2: being painted on inside and outside metope by way of spraying or roller coating for coating made from step 1, per kilogram without
Machine dry powder paint product construction square number is 13 squares, more than emulsion paint square.Cost reduces very much.
Embodiment 5
A kind of inorganic dry powder painting, constitutive material include coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate,
Defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose.
Specifically, the inorganic dry powder painting includes the following raw material according to parts by weight: 60 parts of coarse whiting, 20 parts of kaolin,
18 parts of silica flour, 18 parts of talcum powder, 20 parts of titanium dioxide, 20 parts of barium sulfate, 0.6 part of defoaming agent, 0.2 part of dispersing agent, dispersible cream
11 parts of rubber powder, 20 parts of white cement, 0.05 part of suspending agent, 0.3 part of hydrophober and 0.6 part of hydroxyethyl cellulose.
Further, the coarse whiting is the heavy calcium carbonate of 1250 mesh, coating can be made not settle, and is easily dispersed, good luster
Etc. characteristics.
Further, the kaolinic granularity is 4000 mesh, and the granularity of silica flour is 2000 mesh, and the granularity of talcum powder is
2000 mesh, the granularity of barium sulfate are 3000 mesh, and the granularity of white cement is 2000 mesh.
Based on the production technology of the inorganic dry powder painting, steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, dispersible latex
Powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and are watered according to the ratio of 1:1.5
It is mixed, inorganic dry powder painting is made.
Easy to operate when construction, spraying, roller coating are ok.
The application method of the inorganic dry powder painting, method includes the following steps:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.5 ratio, and it is mixed to prepare after stirring with water
Inorganic dry powder painting；
Step 2: being painted on inside and outside metope by way of spraying or roller coating for coating made from step 1, per kilogram without
Machine dry powder paint product construction square number is 15 squares, more than emulsion paint square.Cost reduces very much.
Better embodiment of the invention is explained in detail above, but the present invention is not limited to above-mentioned embodiment party
Formula within the knowledge of one of ordinary skill in the art can also be without departing from the purpose of the present invention
It makes a variety of changes.
Claims (9)
1. a kind of inorganic dry powder painting, which is characterized in that constitutive material includes coarse whiting, kaolin, silica flour, talcum powder, titanium white
Powder, barium sulfate, defoaming agent, dispersing agent, polymer dispersion powder, white cement, suspending agent, hydrophober and hydroxyethyl cellulose；
It includes the following raw material according to parts by weight: 30-60 parts of coarse whiting, 5-20 parts of kaolin, 4-18 parts of silica flour, talcum powder 4-
18 parts, 5-20 parts of titanium dioxide, 5-20 parts of barium sulfate, 0.1-0.6 parts of defoaming agent, 0.01-0.2 parts of dispersing agent, polymer dispersion powder
6-11 parts, 3-20 parts of white cement, 0.02-0.05 parts of suspending agent, 0.01-0.3 parts of hydrophober and hydroxyethyl cellulose 0.1-0.6
Part.
2. inorganic dry powder painting according to claim 1, which is characterized in that including below according to the raw material of parts by weight: weight
40-50 parts of calcium, 10-15 parts of kaolin, 8-14 parts of silica flour, 8-14 parts of talcum powder, 10-15 parts of titanium dioxide, barium sulfate 10-15
Part, 0.2-0.5 parts of defoaming agent, 0.05-0.15 parts of dispersing agent, 7-10 parts of polymer dispersion powder, 7-15 parts of white cement, suspending agent
0.03-0.04 parts, 0.1-0.2 parts of hydrophober and 0.3-0.4 parts of hydroxyethyl cellulose.
3. inorganic dry powder painting according to claim 2, which is characterized in that including below according to the raw material of parts by weight: weight
Ca45 part, 13 parts of kaolin, 11 parts of silica flour, 11 parts of talcum powder, 13 parts of titanium dioxide, 13 parts of barium sulfate, defoaming agent 0.35 part, point
0.1 part of powder, 8.5 parts of polymer dispersion powder, 11 parts of white cement, 0.035 part of suspending agent, 0.15 part of hydrophober and hydroxy ethyl fiber
0.35 part of element.
4. inorganic dry powder painting according to claim 3, which is characterized in that the coarse whiting is the powdered whiting of 1250 mesh
Powder.
5. inorganic dry powder painting according to claim 4, which is characterized in that the kaolinic granularity is 4000 mesh.
6. inorganic dry powder painting according to claim 5, which is characterized in that the silica flour, talcum powder and white cement
Granularity is 2000 mesh.
7. inorganic dry powder painting according to claim 6, which is characterized in that the granularity of the barium sulfate is 3000 mesh.
8. a kind of production technology of inorganic dry powder painting as claimed in claim 1, which is characterized in that steps are as follows:
1) by coarse whiting, kaolin, silica flour, talcum powder, titanium dioxide, barium sulfate, defoaming agent, dispersing agent, polymer dispersion powder, white
Cement, suspending agent, hydrophober and hydroxyethyl cellulose are by weight ratio；
2) by after formulation ratio, above-mentioned raw materials is added in blender and are stirred, and are watered according to the ratio of 1:1.2-1.5
It is mixed, inorganic dry powder painting is made.
9. a kind of application method of inorganic dry powder painting as claimed in claim 1, which is characterized in that steps are as follows:
Step 1: the inorganic dry powder painting product and water are mixed according to 1:1.2-1.5 ratio, and it is mixed to prepare after stirring with water
Inorganic dry powder painting；
Step 2: coating made from step 1 is painted on inside and outside metope, per kilogram inorganic dry by way of spraying or roller coating
Powder coating product construction square number is 10-15 squares.