CN110117425A - A kind of Segment rehabilitation engineering water-repellent paint - Google Patents
A kind of Segment rehabilitation engineering water-repellent paint Download PDFInfo
- Publication number
- CN110117425A CN110117425A CN201910395154.8A CN201910395154A CN110117425A CN 110117425 A CN110117425 A CN 110117425A CN 201910395154 A CN201910395154 A CN 201910395154A CN 110117425 A CN110117425 A CN 110117425A
- Authority
- CN
- China
- Prior art keywords
- styrene
- petropols
- butadiene
- pitch
- dimethicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Segment rehabilitation engineering water-repellent paints, including high alumina cement powder, polypropylene fiber, polyacrylamide dimethicone, butadiene-styrene rubber, epoxide-resin glue, Petropols, pitch, hydroxy silicon oil, ethylene-vinyl acetate copolymer, turpentine oil, styrene-acrylic emulsion and poly- milling to press;Compared with prior art, the present invention can effectively be directed to the reparation in tunnel, have the characteristics that hardness is high, water proof type is high, cementability is strong, improve construction quality, have the value of popularization and application.
Description
Technical field
The present invention relates to a kind of construction material more particularly to a kind of Segment rehabilitation engineering water-repellent paints.
Background technique
Tunnel is the engineering works being embedded in stratum, is a kind of form of human use's underground space.Tunnel can divide
For traffic tunnel, Hydraulic Tunnel, municipal tunnel, mining tunnel.In the prior art, tunnel leak or cracking situations such as can accidental hair
It is raw, but tunnel is moist, and common renovation agent is easy failure under wet conditions, and accordingly, there exist rooms for improvement.
Summary of the invention
The object of the invention is that providing a kind of Segment rehabilitation engineering water-repellent paint to solve the above-mentioned problems.
The present invention through the following technical solutions to achieve the above objectives:
The present invention includes high alumina cement powder, polypropylene fiber, polyacrylamide dimethicone, butadiene-styrene rubber, epoxy resin
Glue, Petropols, pitch, hydroxy silicon oil, ethylene-vinyl acetate copolymer, turpentine oil, styrene-acrylic emulsion and poly- milling are pressed;
Preparation method the following steps are included:
(1) butadiene-styrene rubber, epoxide-resin glue, Petropols, pitch are added in heating container, 220-240 DEG C of heating is molten
Solution;
(2) high alumina cement powder, polypropylene fiber, polyacrylamide dimethicone are added after dissolving in the state for keeping temperature
Under with 500r/min stir 20min;
(3) hydroxy silicon oil, ethylene-vinyl acetate copolymer, turpentine oil, styrene-acrylic emulsion and poly- milling is added by with 2000r/
The speed that min turns stirs 30min;
(4) stop stirring, get product after cooling.
Preferably, by weight, contain the high alumina cement powder 25%, the polypropylene fiber 5%, the polyacrylamide for every part
Amine dimethicone 8%, the butadiene-styrene rubber 15%, the epoxide-resin glue 10%, the Petropols 5%, the pitch
12%, the hydroxy silicon oil 5%, the ethylene-vinyl acetate copolymer 2%, the turpentine oil 5%, the styrene-acrylic emulsion
5%, the poly- milling presses 3%.
The beneficial effects of the present invention are:
The present invention is a kind of Segment rehabilitation engineering water-repellent paint, and compared with prior art, the present invention can be effectively directed to
Reparation in tunnel has the characteristics that hardness is high, water proof type is high, cementability is strong, improves construction quality, have the valence promoted and applied
Value.
Specific embodiment
The invention will be further described below:
The present invention includes high alumina cement powder, polypropylene fiber, polyacrylamide dimethicone, butadiene-styrene rubber, epoxy resin
Glue, Petropols, pitch, hydroxy silicon oil, ethylene-vinyl acetate copolymer, turpentine oil, styrene-acrylic emulsion and poly- milling are pressed;
Preparation method the following steps are included:
(1) butadiene-styrene rubber, epoxide-resin glue, Petropols, pitch are added in heating container, 220-240 DEG C of heating is molten
Solution;
(2) high alumina cement powder, polypropylene fiber, polyacrylamide dimethicone are added after dissolving in the state for keeping temperature
Under with 500r/min stir 20min;
(3) hydroxy silicon oil, ethylene-vinyl acetate copolymer, turpentine oil, styrene-acrylic emulsion and poly- milling is added by with 2000r/
The speed that min turns stirs 30min;
(4) stop stirring, get product after cooling.
Preferably, by weight, contain the high alumina cement powder 25%, the polypropylene fiber 5%, the polyacrylamide for every part
Amine dimethicone 8%, the butadiene-styrene rubber 15%, the epoxide-resin glue 10%, the Petropols 5%, the pitch
12%, the hydroxy silicon oil 5%, the ethylene-vinyl acetate copolymer 2%, the turpentine oil 5%, the styrene-acrylic emulsion
5%, the poly- milling presses 3%.
Research is found: 1, Segment rehabilitation engineering water-repellent paint prepared in the present invention is soaked in water after construction,
Water-tight, surface amorphism changes, this is because butadiene-styrene rubber, epoxide-resin glue, Petropols, pitch add first in the present invention
Enter to heat in container, 220-240 DEG C of heating for dissolving, by adding high alumina cement powder, polypropylene fiber, polyacrylamide two after heating
Methyl-silicone oil can effectively promote pretreated reaction and live the study found that different materials are added in the variation by this temperature
Property, to promote the mixture homogeneity of material.
Basic principles and main features and advantages of the present invention of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of Segment rehabilitation engineering water-repellent paint, it is characterised in that: including high alumina cement powder, polypropylene fiber, polyacrylamide
Amine dimethicone, butadiene-styrene rubber, epoxide-resin glue, Petropols, pitch, hydroxy silicon oil, ethylene-vinyl acetate copolymer,
Turpentine oil, styrene-acrylic emulsion and poly- milling are pressed;
Preparation method the following steps are included:
(1) butadiene-styrene rubber, epoxide-resin glue, Petropols, pitch are added in heating container, 220-240 DEG C of heating for dissolving;
(2) dissolve after be added high alumina cement powder, polypropylene fiber, polyacrylamide dimethicone in the state of keeping temperature with
500r/min stirs 20min;
(3) hydroxy silicon oil, ethylene-vinyl acetate copolymer, turpentine oil, styrene-acrylic emulsion and poly- milling is added to turn by with 2000r/min
Speed stir 30min;
(4) stop stirring, get product after cooling.
2. Segment rehabilitation engineering water-repellent paint according to claim 1, it is characterised in that: by weight, every part contains institute
State high alumina cement powder 25%, the polypropylene fiber 5%, the polyacrylamide dimethicone 8%, the butadiene-styrene rubber
15%, the epoxide-resin glue 10%, the Petropols 5%, the pitch 12%, the hydroxy silicon oil 5%, the second
Alkene-acetate ethylene copolymer 2%, the turpentine oil 5%, the styrene-acrylic emulsion 5%, the poly- milling press 3%.