CN110116191A - A kind of casting method of churning driven mast - Google Patents
A kind of casting method of churning driven mast Download PDFInfo
- Publication number
- CN110116191A CN110116191A CN201910504821.1A CN201910504821A CN110116191A CN 110116191 A CN110116191 A CN 110116191A CN 201910504821 A CN201910504821 A CN 201910504821A CN 110116191 A CN110116191 A CN 110116191A
- Authority
- CN
- China
- Prior art keywords
- casting
- casting mould
- temperature
- mast
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of casting method of churning driven mast, include the following steps: to coat one layer of release agent in the inner cavity of casting mould;Steel ingot raw material is weighed, and steel ingot raw material is heated to the molten steel of molten condition, and carry out 0.2~0.5h of heat preservation;Casting mould is heated, so that its temperature is reached 1200~1400 DEG C, and keep the temperature 0.3~0.6h;And by the pouring molten steel in above-mentioned steps in casting mould;It pressurizes from sprue gate to the casting mould under constant temperature immediately after casting complete, pressing force is 0.015~0.02MPa, and pressing time keeps 1~1.5h;Casting mould is first cooled to 600~750 DEG C, constant temperature keeps 0.1~0.4h;Then casting mould is cooled to room temperature;The brill mast demoulding of casting and forming is handled, and it is machined out to be formed and bores mast finished product.The casting method improves the utilization rate of steel, improves casting accuracy, structural strength is high, improving production efficiency.
Description
Technical field
The present invention relates to casting field more particularly to a kind of casting methods of churning driven mast.
Background technique
Boring mast work is one of important component of churning driven, and in the prior art, boring mast can be damaged using of long duration, and one
Denier bore mast be damaged to the destructiveness of churning driven be it is self-evident, security risk is caused to entire churning driven, and existing
The utilization rate for boring the casting chinese raw materials of mast is not high, the inadequate defect of structural strength.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides the casting method of churning driven mast, which is mentioned
The utilization rate of high steel improves casting accuracy, and structural strength is high, improving production efficiency, securely and reliably.
To achieve the goals above, the present invention proposes a kind of casting method of churning driven mast, the casting of the churning driven mast
Method includes the following steps:
S10: one layer of release agent coating release agent: is coated in the inner cavity of casting mould;
S20: it forms molten steel: weighing steel ingot raw material, and steel ingot raw material is heated to the molten steel of molten condition, and carry out
Keep the temperature 0.2~0.5h;
S30: heating mould: heating casting mould makes its temperature reach 1200~1400 DEG C, and keeps the temperature 0.3~0.6h;And
By the pouring molten steel in S30 in casting mould;
S40: casting: immediately pressurizeing to the casting mould under constant temperature from sprue gate after casting complete, added
Pressure is 0.015~0.02MPa, and pressing time keeps 1~1.5h;
S50: cooling: casting mould to be first cooled to 600~750 DEG C, constant temperature keeps 0.1~0.4h;Then by casting die
Tool is cooled to room temperature;
S60: demoulding: the brill mast demoulding of casting and forming is handled, and is machined out to be formed to it and is bored mast finished product.
Preferably, in step S20, steel ingot raw material is heated to the molten steel of molten condition, and carries out heat preservation 0.35h.
Preferably, in step s 30, casting mould is carried out being heated to 1300 DEG C, and keeps the temperature 0.45h.
Preferably, in step s 40, the plus-pressure is 0.0175MPa, pressing time 1.25h.
Preferably, in step s 50, casting mould is first cooled to 680 DEG C, constant temperature keeps 0.25h.
By adopting the above-described technical solution, the present invention has the advantage that the casting method improve steel utilization rate,
Casting accuracy is improved, structural strength is high, improving production efficiency, securely and reliably.
Specific embodiment
The invention will be further described below.
Embodiment 1
The present invention proposes a kind of casting method of churning driven mast, includes the following steps: S10: coating release agent: in casting mould
Inner cavity coat one layer of release agent;S20: it forms molten steel: weighing steel ingot raw material, and steel ingot raw material is heated to molten condition
Molten steel, and carry out heat preservation 0.2h;S30: heating mould: heating casting mould makes its temperature reach 1200 DEG C, and keep the temperature
0.3h;And by the pouring molten steel in S30 in casting mould;S40: casting: after casting complete immediately from sprue gate to being in
Casting mould under constant temperature pressurizes, pressing force 0.015MPa, and pressing time keeps 1h;S50: cooling: first will casting
Mold is cooled to 600 DEG C, and constant temperature keeps 0.1h;Then casting mould is cooled to room temperature;S60: demoulding: by the brill of casting and forming
Mast demoulding processing, and it is machined out to be formed and bores mast finished product.
Embodiment 2
The present invention proposes a kind of casting method of churning driven mast, includes the following steps: S10: coating release agent: in casting mould
Inner cavity coat one layer of release agent;S20: it forms molten steel: weighing steel ingot raw material, and steel ingot raw material is heated to molten condition
Molten steel, and carry out heat preservation 0.5h;S30: heating mould: heating casting mould makes its temperature reach 1400 DEG C, and keep the temperature
0.6h;And by the pouring molten steel in S30 in casting mould;S40: casting: after casting complete immediately from sprue gate to being in
Casting mould under constant temperature pressurizes, pressing force 0.02MPa, and pressing time keeps 1.5h;S50: cooling: first will casting
Mold is cooled to 750 DEG C, and constant temperature keeps 0.4h;Then casting mould is cooled to room temperature;S60: demoulding: by the brill of casting and forming
Mast demoulding processing, and it is machined out to be formed and bores mast finished product.
Embodiment 3
The present invention proposes a kind of casting method of churning driven mast, includes the following steps: S10: coating release agent: in casting mould
Inner cavity coat one layer of release agent;S20: it forms molten steel: weighing steel ingot raw material, and steel ingot raw material is heated to molten condition
Molten steel, and carry out heat preservation 0.35h;S30: heating mould: heating casting mould makes its temperature reach 1300 DEG C, and keep the temperature
0.45h;And by the pouring molten steel in S30 in casting mould;S40: casting: after casting complete immediately from sprue gate to being in
Casting mould under constant temperature pressurizes, pressing force 0.0175MPa, and pressing time keeps 1.25h;S50: cooling: first will
Casting mould is cooled to 680 DEG C, and constant temperature keeps 0.25h;Then casting mould is cooled to room temperature;S60: it demoulding: will be cast as
The brill mast demoulding of type is handled, and is machined out to be formed to it and is bored mast finished product.
By adopting the above-described technical solution, the present invention has the advantage that the casting method improve steel utilization rate,
Casting accuracy is improved, structural strength is high, improving production efficiency, securely and reliably.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, modifies, replacement and variant.
Claims (5)
1. a kind of casting method of churning driven mast, which comprises the steps of:
S10: one layer of release agent coating release agent: is coated in the inner cavity of casting mould;
S20: it forms molten steel: weighing steel ingot raw material, and steel ingot raw material is heated to the molten steel of molten condition, and kept the temperature
0.2~0.5h;
S30: heating mould: heating casting mould makes its temperature reach 1200~1400 DEG C, and keeps the temperature 0.3~0.6h;And it will
Pouring molten steel in S30 is in casting mould;
S40: casting: immediately pressurizeing to the casting mould under constant temperature from sprue gate after casting complete, pressing force
For 0.015~0.02MPa, pressing time keeps 1~1.5h;
S50: cooling: casting mould to be first cooled to 600~750 DEG C, constant temperature keeps 0.1~0.4h;Then casting mould is cold
But to room temperature;
S60: demoulding: the brill mast demoulding of casting and forming is handled, and is machined out to be formed to it and is bored mast finished product.
2. the casting method of churning driven mast according to claim 1, which is characterized in that in step S20, steel ingot raw material is heated to melting
Melt the molten steel of state, and carries out heat preservation 0.35h.
3. the casting method of churning driven mast according to claim 1, which is characterized in that in step s 30, casting mould is added
Heat keeps the temperature 0.45h to 1300 DEG C.
4. the casting method of churning driven mast according to claim 1, which is characterized in that in step s 40, the plus-pressure is
0.0175MPa, pressing time 1.25h.
5. the casting method of churning driven mast according to claim 1, which is characterized in that in step s 50, first that casting mould is cooling
To 680 DEG C, constant temperature keeps 0.25h.